• 한국전기전자재료학회논문지
• /
• 제24권3호
• /
• pp.219-223
• /
• 2011

Rhenium-Iridium(Re-Ir) thin films were deposited onto the tungsten carbide(WC) molding core by sputtering system. The Re-Ir films were prepared by multi-target sputtering with iridium, rhenium and chromium as the sources. Argon and nitrogen were inlet into the chamber to be the plasma and reactive gases. The Re-Ir thin films were prepared with targets having atomic percent of 3:7 and the Re-Ir thin films were formed with 240 nm thickness. The Re-Ir thin films on tungsten carbide molding core were analyzed by scanning electron microscope(SEM) and surface roughness. Also, adhesion strength and coefficient friction of Re-Ir thin film were examined. The Re-Ir coating technique has been intensive efforts in the field of coating process because the coating technique and process have been their feature, like hardness, high elasticity, abrasion resistance and mechanical stability and also have been applied widely the industrial and biomedical areas. In this report, tungsten carbide(WC) molding core was manufactures using high performance precision machining and the efforts of Re-Ir coating on the surface roughness.

• 한국입자에어로졸학회지
• /
• 제5권4호
• /
• pp.153-158
• /
• 2009

Tungsten carbide powder was fabricated with carbothermal reaction by pulsed electric current flowing in compact of tunsten oxide and carbon. The mixed powder of tunsten oxide and carbon was ball-milled into ultrafine powders. The mixed powder of tungsten oxide and carbon was put into carbon mold and heat-treated at $1050{\sim}1200^{\circ}C$ by pulsed electric current flowing. The formation of tungsten carbide powder could be achieved by heat treatment at $1200^{\circ}C$ for 10 minitues.

• 한국분말재료학회지
• /
• 제9권3호
• /
• pp.174-181
• /
• 2002

Nanosized tungsten carbide powders were synthesized by the chemical vapor condensation(CVC) process using the pyrolysis of tungsten hexacarbonyl($W(CO)_6$). The effect of CVC parameters on the formation and the microstructural change of as-prepared powders were studied by XRD, BET and TEM. The loosely agglomerated nanosized tungsten-carbide($WC_{1-x}$) particles having the smooth rounded tetragonal shape could be obtained below $1000^{\circ}C$ in argon and air atmosphere respectively. The grain size of powders was decreased from 53 nm to 28 nm with increasing reaction temperature. The increase of particle size with reaction temperature represented that the condensation of precursor vapor dominated the powder formation in CVC reactor. The powder prepared at $1000^{\circ}C$ was consisted of the pure W and cubic tungsten-carbide ($WC_{1-x}$), and their surfaces had irregular shape because the pure W was formed on the $WC_{1-x}$ powders. The $WC_{1-x}$ and W powders having the average particles size of about 5 nm were produced in vacuum.

• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2006년도 Extended Abstracts of 2006 POWDER METALLURGY World Congress Part 1
• /
• pp.355-356
• /
• 2006

WC-TiC-TaC binderless cemented carbide was oxidized under low partial pressure of oxygen (50ppm) at 873K for 1 to 20 h. Surface roughness was measured using atomic force microscope, and effect of TiC amount on oxidation behavior of the carbide was investigated. WC phase was oxidized more easily than WC-TiC-TaC solid solution phase. With an increase in TiC amount, WC-TiC-TaC phase increased and the oxidation resistance of the carbide increased.

• 한국분말재료학회지
• /
• 제15권5호
• /
• pp.359-364
• /
• 2008

To satisfy the demand of higher cutting performance, mechanical properties with tungsten carbide (WC-Co) tool materials were investigated. Hardness and transverse rupture strength with WC grain size, Co content and density were measured. Compared to H, K, and S manufacture maker as tungsten carbide (WC-Co) tool materials were used for high-speed machining of end-milling operation. The three tungsten carbide (WC-Co) tool materials were evaluated by cutting of STD 11 cold-worked die steel (HRC25) under high-speed cutting condition. Also, tool life was obtained from measuring flank wear by CCD wear measuring system. Tool dynamometer was used to measure cutting force. The cutting force and tool wear are discussed along with tool material characteristics. Consequently, the end-mill of K, H manufacture maker showed higher wear-resistance due to its higher hardness, while the S maker endmill tool showed better performance for high metal removal.

• 한국소성가공학회:학술대회논문집
• /
• 한국소성가공학회 2004년도 추계학술대회논문집
• /
• pp.315-318
• /
• 2004

The Advantages of hot machining are the reduction of cutting forces, tool wear, and the increase of material removal rates. In this study, a hot-machining characteristics of milling by CBN tip was exprimentely analyzed, and the influence of the surface temperature and the depth of cut on the tool life were investigated. The selection of a heating method for obtaining ideal temperature of metals in machining is important. Faulty heating methods could induce unwanted structural changes in the workpiece and increase the cost. This study uses gas flame heating. It is obtained that tungsten carbide-alloyed has a recrystallisation temperature range of $800-1000^{\circ}C$ which is the high heating temperature that might induce unwanted structural changes. If it is performed at temperatures higher than $800^{\circ}C$ in machining, the possibility of unwanted structural changes and the increased wear of tool can be shown. Consequently, in hot machining of tungsten carbide-alloy, this study has chosen $400^{\circ}C-600^{\circ}C$ because the heating temperature might be appropriate in view of the cost and workpiece considerations. The results of this study experimentally shows a new machining method for tungsten carbide-alloyed that decreases the wear rate of machining tools

• 한국소성가공학회:학술대회논문집
• /
• 한국소성가공학회 2003년도 추계학술대회논문집
• /
• pp.76-79
• /
• 2003

Glass molding is an advantageous method to manufacture glass micro optical components. However, it is difficult to make tungsten carbide core for glass molded micro optics way. We have developed novel method to fabricate tungsten carbide core for glass molding of glass micro optical components. Silicon masters were fabricated by micro machining. Tungsten Carbide cores were fabricated by forming, sintering and coating. Finally we fabricated glass molded V-groove with pitch of 192$\mu\textrm{m}$ and glass microlens way with lens diameter of 36∼225$\mu\textrm{m}$ by the present method.

• 소성∙가공
• /
• 제15권7호
• /
• pp.518-523
• /
• 2006

Wet wire drawing of brass coated steel wire, used for tire reinforcement, is realized with Tungsten Carbide(WC) dies sintered with a cobalt(Co) binder. Dies wear represents an important limitation to the production process and cost savings. Several parameters, such as Co content, WC grain size of tungsten carbide, sintering conditions, and so on, affect on the wear of the drawing die. In this study, the effect of the diamond abrasive particle size on the life of the WC centered dies of the wet wire drawing was investigated. Wet wire drawing experiments were carried out on a wet wire drawing machine. From the experiments, the dies life, dies fracture, wire surface roughness, and wire breaks were investigated. From the results, it was found that the wear of the WC dies increased with the increase in the diamond abrasive particle size.

• 한국정밀공학회지
• /
• 제23권12호
• /
• pp.111-116
• /
• 2006

Micro machining of tungsten carbide by electrochemical machining was studied. In ECM, machining conditions and electrolyte should be chosen carefully according to the property of workpiece materials. In this paper, sulfuric acid and nitric acid were used for tungsten carbide machining and machining characteristics were investigated according to machining conditions such as electrolyte, workpiece potential and applied pulse voltage. By using mixture of sulfuric acid and nitric acid, micro structures with sharp edge and good surface quality were obtained. Micro electrochemical turning was also introduced to fabricate micro shafts.

• 한국정밀공학회:학술대회논문집
• /
• 한국정밀공학회 1997년도 추계학술대회 논문집
• /
• pp.865-869
• /
• 1997

In recent years, there has been increasing demand of ultra-fine grain graded cemented tungsten carbide material with high hardness and toughness which is used as high speed cutting tool for development in semiconductor, electronics and die/mold industry, which bring into limelight high-precision, high-efficient machining of sculptured surfaces. This paper deals with the performance of variation in the ultra-fine grain graded cemented tungsten carbide material such as grain size, hardness and density varied according to the volume of added elements, Co or TaC, and he changing of mixing, sintering process. Also, the performance of developing material with uniformed grain size of 0.5${\mu}{\textrm}{m}$ is compared with other domestics' & foreign companies' with analyzing and cutting performance testing.