• Proceedings of the Korean Society of Tribologists and Lubrication Engineers Conference
• /
• 2002.10b
• /
• pp.137-138
• /
• 2002

The benefits of using DLC coatings on steel in dry sliding are well known. The present study has investigated the effects of using the same materials but in a boundary lubricated environment. Tribological tests were performed using a load-scanning device and a lubricant with an extreme-pressure (EP) additive. XPS and grazing incidence XRD are used for chemical analysis. The chemical composition of the resulting tribofilm is correlated to different friction behaviors and contact loads, and indicates that high loads are beneficial for formation of low friction tribofilm.

• Tribology and Lubricants
• /
• v.24 no.6
• /
• pp.302-307
• /
• 2008

The running-in behaviour of the metal carbon coating (WC/C) was evaluated with regard to its applicability as wear-resistant coating for key components in engines. Reciprocating wear tests under lubricated condition employing an oscillating friction wear tester were performed to investigate the tribological behaviors of the coatings in ambient environment. Confocal microscopy and scanning electron microscopy were used to observe worn surfaces and the wear scars on the steel balls. Elemental composition of the coating and worn surfaces were characterized using Auger electron spectroscopy. The friction behavior of WC/C coating was comparable to common carbon-based coatings. Thin tribofilm was formed on the worn surface of the steel ball due to material transfer and tribochemical reaction whereas there was no evidence of tribofilm generation on the coating surface. indicating the chemical innertness of WC/C coating.

• Tribology and Lubricants
• /
• v.18 no.2
• /
• pp.138-143
• /
• 2002

Abstract - Tribofilms formed on won surface protect the DLC coating surface and decrease the fiction coefficient. However it is very difficult to evaluate their micromechanical properties due to their small thickness, inhomogeneity and discontinuity. The phase contrast images in tapping mode atomic farce microscopy allow an estimation of inhomogeneity in micromechanical properties of the sample surface. The purpose of this investigation is to demonstrate how the phase contrast images contribute to the characterization of thin tribofilms.

• Proceedings of the Korean Society of Tribologists and Lubrication Engineers Conference
• /
• 2001.06a
• /
• pp.299-304
• /
• 2001

Tribofilms formed on worn surface protect the DLC coating surface and decrease the friction coefficient. However it is very difficult to evaluate their micromechanical properties due to their small thickness, inhomogeneity and discontinuity. The phase contrast images in tapping mode atomic force microscopy allow an estimation of inhomogeneity in micromechanical properties of the sample surface. The purpose of this investigation is to demonstrate how the phase contrast images contribute to the characterization of thin tribofilms.

• Proceedings of the KSR Conference
• /
• 2011.10a
• /
• pp.975-985
• /
• 2011

Cu-Matrix sintered brake pads and low alloyed heat resistance steel are most applied to basic brake system for high energy moving machine. In this research, we analyzed tribological characteristics for influence of air velocity between disk and pad. At low brake pressure with air flow, friction stability was decreased due to no formation of tribofilm at disk surface. But there are no significant change of friction coefficient at all test conditions. Wear rate of friction materials were decreased with increasing of air flow velocity. In result, air flow velocity influenced friction stability, wear rate of friction materials and disk but not friction coefficient.

• Tribology and Lubricants
• /
• v.29 no.1
• /
• pp.19-26
• /
• 2013

Cu-matrix sintered brake pads and low-alloy heat-resistant steel are commonly applied to basic brake systems in high-energy moving machines. In this research, we analyzed the tribological characteristics to determine the influence of the air velocity between the disk and pad. At a low brake pressure with airflow, the friction stability was decreased as a result of the lack of tribofilm formation at the disk surface. However, there were no significant changes in the friction coefficient under any of the test conditions. The wear rates of the friction materials were decreased with an increase in the airflow velocity. As a result, the airflow velocity influenced the friction stability, as well as the wear rate of the friction materials and disk, but not the friction coefficient.

• Tribology and Lubricants
• /
• v.30 no.4
• /
• pp.240-245
• /
• 2014

Low alloy heat resistant brake disk and sintered brake pad are applied to mechanical brake system for the speed-up of urban rapid transit. In this research, we analyzed how the frictional characteristics between brake disk and pad are influenced by the disk mass. At a high disk mass, the friction stability was the lower value as a result of the lack of tribofilm formation at the disk surface. Wear rates of friction materials showed the higher value at a low disk mass and wear rates of 10 mm and 15 mm showed the similar level. Average friction coefficient was the lower value at the 10 mm disk thickness and range of variation of average friction coefficient was also the smaller value at the 10 mm disk thickness. However, there were no significant changes in the friction coefficients under any of test conditions. Surface roughness of a disk showed the highest value at the 5 mm disk and surface roughnesses of 10 mm and 15 mm showed the similar level. As a result, friction characteristics of disk mass influenced the friction stability, as well as the wear rate of friction pad and disk, but not the friction coefficient.

• Nano
• /
• v.13 no.12
• /
• pp.1850144.1-1850144.13
• /
• 2018

A nano-$MoS_2$/montmorillonite K-10 (K10) composite was prepared and characterized. The composite contains two types of 2H-$MoS_2$ nanoparticles. One is the hollow spherical $MoS_2$ with a size range of 75 nm, and the other is the spherical nano cluster of $MoS_2$ with a size range of 30 nm. The two kinds of nano-$MoS_2$ were formed via assembly of numerous $MoS_2$ nano-platelets with a size of ~10 nm. A tribological comparison was then made among nano-$MoS_2$/K10, K10, nano-$MoS_2$ and a mechanical mixture of K10 and nano-$MoS_2$. K10 reduced the wear but slightly increased the friction. Nano-$MoS_2$ remarkably reduced both friction and wear. The mechanical mixture demonstrated better wear resistance than nano-$MoS_2$, indicating a synergistic anti-wear effect of nano-$MoS_2$ and K10. The synergistic effect was reinforced using nano-$MoS_2$/K10 instead of the mechanical mixture. A part of the $MoS_2$ in the contact region always lubricated the friction pair, and the rest formed a tribofilm. K10 segregated the friction pair to alleviate the ablation wear but magnified the abrasive wear. S-$MoS_2$ protects K10 and they together function as both a lubricant and an isolating agent to reduce the ablation and abrasive wear.

• Applied Chemistry for Engineering
• /
• v.27 no.6
• /
• pp.583-589
• /
• 2016

Lubricant additives including zinc dialkyldithiophosphate (ZDDP) containing metal have been widely used due to the advantage of very low cost, but they can generate impurities such as ash. In this work, ZDDP containing metals was partially replaced with bis[3-(dialkyloxyphosphorothionyl) thio-2-methylpropanyloxy] butane (BAP4s) which was synthesized conveniently and effectively from alkanediol without any metal components. Also, the wear resistance property of synthesized BAP4s were studied. Wear scar diameter (WSD) values of BAP4s with butyl, octyl, decyl, dodecyl or tetradecyl groups were also measured by four-ball test. As the length of the alkyl group increased from 4 to 8, the WSD value of BAP4s decreased rapidly from 0.59 to 0.45 mm, but from 8 to 14, the value increased very slowly from 0.45 to 0.50 mm. Thus, among all BAP4s, B8P4 having BAP4 with the octyl group, showed the lowest WSD value. Furthermore, the WSD values were measured in a lubricant base oil mixed with a 0.50 percent concentration (w/w) of either BAP4 or ZDDP. The former was 0.55 mm, and the latter was 0.45 mm. The thermal stability and tribofilm formation peroperty were also measured by thermogravimetric analyzer (TGA) and energy-dispersive X-rays spectroscopy (EDS), respectively.

• Applied Chemistry for Engineering
• /
• v.29 no.4
• /
• pp.405-412
• /
• 2018

Three types of bis[3-(dialkyloxylphosphorothionyl) thio-2-methylpropanyloxy]alkane (BAPA) drived from alkane diol were synthesized. The principal chain of each BAPA had a different carbon number, i.e., 6, 9, and 11. The three types of synthesized BAPA were compared to zinc dialkyl dithiophosphates (ZDDPs) in terms of abrasion resistance. A four-ball test was conducted to evaluate the anti-abrasion performance of the synthesized BAPA according to the length of the principal carbon chain. Each product was added to an additive at a concentration of 1% of the base oil weight, and the wear scar diameter (WSD) was measured as 0.472, 0.459, and 0.480 mm, respectively. Among the BAPA compounds, dialkyl dithiophosphoric acid (DDP), which is the side chain of bis[methacryloyloxy] nonane (BMOO9), was synthesized by varying the carbon number, i.e., 4, 8, and 12, and subsequently the 4-ball test was carried out. The WSD was determined as 0.537, 0.459, and 0.531 mm, respectively. As a result, it was found that when a side chain is short, a thin film is formed. In contrast, a long side chain hindered the formation of a film, and hence the best result was achieved when the carbon number was 8. As for the ZDDPs, the WSD was determined to be 0.563 mm, when measured under the same conditions. The measurements confirm that the synthesized BAPA compounds are superior to the ZDDPs as abrasion resistance additives.