• Journal of the Korean Vacuum Society
• /
• v.19 no.3
• /
• pp.224-229
• /
• 2010

Indium oxide $(In_2O_3)$ thin films have been prepared on glass substrate by using radio-frequency reactive magnetron sputtering with changing the oxygen flow ratio. The substrate temperature was kept at a fixed value of $400^{\circ}C$, and the sputtering gas and reactive gas were supplied with argon and oxygen, respectively. The oxygen partial flow ratio was varied by controlling the amount of oxygen with respect to the total mixed gases, 10%, 20%, 30%, 40%, and 50%. The optical, electrical, and structural properties of the deposited thin films were investigated by using ultraviolet-visible-near infrared spectrophotometer, Hall measurement, and X-ray diffractometer and scanning electron microscopy. The $In_2O_3$ thin film deposited at 20% of oxygen flow ratio showed an average transmittance of 86% in the wavelength range of 430~1,100 nm, an electrical resistivity of $1.1{\times}10^{-1}{\Omega}cm$. The results show that the transparent conducting films with optimum conditions can be achieved by controlling the oxygen flow ratio.

• Journal of the Korean Vacuum Society
• /
• v.19 no.2
• /
• pp.128-133
• /
• 2010

ZnO:Al films were deposited by DC-pulsed magnetron sputtering using a two-step process involving the control of the oxygen pressure. The seed layers were prepared with various Ar to oxygen flow ratios and the bulk layers were deposited under pure Ar. As the oxygen pressure during the deposition of the seed layer increased, the crystallinity and degree of (002) texturing increased. The resistivity gradually decreased with increasing crystallinity from $4.7\times10^4\Omega{\cdot}cm$ (no seed) to $3.7\times10^4\Omega{\cdot}cm$ (Ar/$O_2$ = 9/1). The etched surface showed a crater-like structure and an abrupt morphology change appeared as the crystallinity was increased. The sample deposited at an Ar/$O_2$ flow ratio of 9/1 showed a very high haze value of 88% at 500 nm, which was explained by the large feature size of the craters, as shown in the AFM image.

• Korean Journal of Metals and Materials
• /
• v.48 no.5
• /
• pp.456-461
• /
• 2010

We investigated the In-based ohmic contacts on Nitrogen-face (N-face) n-type GaN, as well as Ga-face n-type GaN, for InGaN-based vertical Light Emitting Diodes (LEDs). For this purpose, we fabricated Circular Transfer Length Method (CTLM) patterns on the N-face n-GaN that were prepared by using a laser-lift off method, as well as on the Ga-face n-GaN that were prepared by using a dry etching method. Then, In/transparent conducting oxide (TCO) and In/TiW schemes were deposited on the CTLM in order for low resistance ohmic contacts to form. The In/TCO scheme on the Ga-face n-GaN showed high specific contact resistance, while the minimum specific contact resistance was only 3${\times}$10$^{-2}$ $\Omega$-cm$^{2}$ after annealing at 300${^{\circ}C}$, which can be attributed to the high sheet resistance of the TCO layer. In contrast, the In/TiW scheme on the Ga-face n-GaN produced low specific contact resistance of 2.1${\times}$10$^{5}$ $\Omega$-cm$^{2}$ after annealing at 500${^{\circ}C}$ for 1 min. In addition, the In/TiW scheme on the N-face n-GaN also resulted in a low specific contact resistance of 2.2${\times}$10$^{-4}$ $\Omega$-cm$^{2}$ after annealing at 300${^{\circ}C}$. These results suggest that both the Ga-face n-GaN and N-face n-GaN.

• Journal of the Korean Chemical Society
• /
• v.66 no.3
• /
• pp.209-217
• /
• 2022

We have developed photosensitive electrochromic smart windows that does not require any transparent conducting oxide (TCO) substrate. In our previous study, we demonstrated that a flexible film-type device made with a low temperature curing WO₃ sol and TiO₂ sol could show a reversible and rapid switching between colored and bleached state via incorporation of platinum catalysts on the surface of WO₃ layer. However, when these devices were exposed to sunlight over 4 hour, it was confirmed that they did not return to fully bleached state in the darkened state due to their overcoloring process. In this study, we added 4-hydroxy-(2,2,6,6-tetramethylpiperidin-1-yl)oxyl (TEMPOL) as an additive to the electrolyte of photosensitive electrochromic device to effectively prevent the undesired overcoloring process. The resulting device with TEMPOL indeed did not undergo excessive coloration and showed great reversibility even after being exposed to sunlight for over 4 hours. Various concentrations of TEMPOL were applied to compare changes in the visible transmittance and coloring/bleaching kinetics of devices. In terms of energetic point of view, we proposed a plausible mechanism of TEMPOL to prevent excessive coloration.

• Journal of Conservation Science
• /
• v.37 no.2
• /
• pp.77-89
• /
• 2021

In this study, materials and color formation techniques were assessed for black potteries excavated from the Janghyeon-dong, Jungsan-dong and Gyodong-ri sites during the Proto-Three Kingdoms period in Ulsan, Korea. Although the black potteries were black superficially, the inner cores were either black or reddish yellow. Microscopy analysis identified that body clay was used for reddish iron oxide rich soils with quartz, alkali feldspar and mica, along with grains of myrmechite texture. Additionally, as marginal differences exist in the contents of SiO₂, Fe₂O₃ and CaO, the composition of the host rock and clay distributed around the sites was affected. Thus, we can deduce that pottery was made by soiling at a short distance. Raman spectroscopy results revealed that the black layer of the black pottery was used as amorphous combustion carbon. In addition, as a transparent layer of brown lacquer was observed on the substrate that was in contact with the surface layer, the black layer of the pottery induced black color development by a combination of combustion carbon and lacquer. Based on the mineral composition and microtexture of the body clay, the firing temperature of the potteries seemed to range from 750 to 850℃, whereas the lacquer layer was pyrolyzed at 468℃ by thermal analysis. Therefore, a combined layer of combustion carbon and lacquer, which formed the black color, was painted after the body clay was fired.