• Journal of Ceramic Processing Research
• /
• v.13 no.spc1
• /
• pp.37-41
• /
• 2012

A lithium ion conducting borosilicate glass was fabricated by a conventional melt quenching technique from a mixture of Li2CO3, B2O3 and SiO2 powders. The Li ion conductivity of the lithium borosilicate glasses was evaluated in terms of the SiO2/B2O3 ratio. In the Li2O-B2O3-SiO2 ternary glass, the glass forming region decreases with an increasing Li2O content. At the same Li2O, the crystallization tendency of the glass samples increases with the SiO2/B2O3 ratio, resulting in a reduced glass forming region in the Li2O-B2O3-SiO2 ternary glass. The electrical conductivity moderately depends on the SiO2/B2O3 ratio in the Li2O-B2O3-SiO2 ternary glass. The conductivity of the glasses slightly increases with the SiO2/B2O3 ratio. The observed phenomenon can be explained by the modification of the glass structure as a function of the SiO2 content.

• Journal of the Korean Ceramic Society
• /
• v.56 no.2
• /
• pp.173-177
• /
• 2019

Thermal properties of a SiO₂-B₂O₃-BaO ternary glass system depending on compositional change of BaO have been examined to find a proper sealing material for reversible oxide cells. Glass transition temperature and thermal expansion coefficients increased simultaneously up to 55 mol% of BaO content. The structural role of BaO with regard to the thermal properties has been discussed on the basis of Raman spectroscopy results. Flowability of the glass at sealing temperature has been examined with packed glass powders of 12 mm diameter along with a high temperature optical microscope. The practical sealing property of the glass was also examined with YSZ coated with NiO-yittria stabilized zirconia (NiO-YSZ) and it showed good adhesion without noticeable reaction with NiO-YSZ layer.

• Advances in concrete construction
• /
• v.12 no.5
• /
• pp.429-437
• /
• 2021

In the era of building engineering the intensification of Self Compacting Concrete (SCC) is world-shattering magnetism. It has lot of rewards over ordinary concrete i.e., enrichment in production, cutback in manpower, brilliant retort to load and vibration along with improved durability. In the present study, the mechanical strength of CM-2 (SCC containing 10% of rice husk ash (RHA) as cement replacement and 600 grams of glass fibers per cubic meter) was investigated at various dosages of cement replacement by fly ash (FA) and GGBS. A total of 17 SCC mixtures including two control SCC mixtures (CM-1 and CM-2) were developed for investigating fresh and hardened properties in which, ten ternary cementitious blends of SCC by blending OPC+RHA+FA, OPC+RHA+GGBS and five quaternary cementitious blends (OPC+RHA+FA+GGBS) at different replacement dosages of FA and GGBS were developed with reference to CM-2. For constant water-cement ratio (0.42) and dosage of SP (2.5%), the addition of glass fibers (600 grams/m³) in CM-1 i.e., CM-2 shows lower workability but higher mechanical strength. While fly ash based ternary blends (OPC+RHA+FA) show better workability but lower mechanical strength as FA content increases in comparison to GGBS based ternary blends (OPC+RHA+GGBS) on increasing GGBS content. The pattern for mixtures appeared to exhibit higher workablity as that of the concentration of FA+GGBS rises in quaternary blends (OPC+RHA+FA+GGBS). A decrease in compressive strength at 7-days was noticed with an increase in the percentage of FA and GGBS as cement replacement in ternary and quaternary blended mixtures with respect to CM-2. The highest 28-days compressive strength (41.92 MPa) was observed for mix QM-3 and the lowest (33.18 MPa) for mix QM-5.

• Polymer(Korea)
• /
• v.25 no.2
• /
• pp.226-232
• /
• 2001

The properties of poly(ethylene terephthalate) (PET)/maleic anhydride-grafted polypropylene (MAgPP)/poly(styrene-co-maleic anhydride)(PScMA) ternary blend were investigated. The ternary blend was immiscible based on the glass transition temperatures measured by dynamic mechanical analyzer (DMA). The degradation of MAgPP during melt mixing for 30 min at 280$^{\circ}C$ did not affect the properties of the ternary blend. The interaction among the components was confirmed from the rheological properties, which was increased with the PSCMA contents. In terms of the mechanical properties, it was observed to satisfy the mixture rule for a multiple system.

• Journal of the Korean Magnetic Resonance Society
• /
• v.9 no.1
• /
• pp.61-66
• /
• 2005

$^{11}B MAS NMR$ spectra of binary glass system $xV_2O5-B_2O_3$ and ternary glass system $xV_2O5-B_2O_3-yNa_2O$ (x = $V_2O_5 mol%/$B_2O_3$ mol%, y = $Na_2O$ mol$/$B_2O_3$ mol%) were acquired. $BO_3$ units are dominant components in the spectra of $xV_2O_5-B_2O_3$glass systems while both $BO_3$ and $BO_4$ unit appear in comparable amounts in the spectra of $xV_2O_5-B_2O_3-yNa_2O$ glass systems. More $BO_3$ units were monitored for higher $V_2O_5$ contents while more $BO_4$ unit for higher $Na_2O$ contents. Quadrupole parameters such as $e^2qQ$ and $\eta$ obtained form spectral simulation indicate that $e^2qQ$ has a maximum value at x = y 1 and $\eta$ decreases and increases as x or y grows, respectively. Our results suggest that $V_2O_5$ and $Na_2O$ play opposite roles in the ternary glasses.

• Advances in nano research
• /
• v.13 no.1
• /
• pp.97-111
• /
• 2022

In the present article, silica nanoparticles (SNPs) were exploited to improve the tribological and mechanical properties of vinyl ester/glass fiber composites. To the best of our knowledge, there hasn't been any prior study on the wear properties of glass fiber reinforced vinyl ester SiO₂ nanocomposites. The wear resistance is a critical concern in many industries which needs to be managed effectively to reduce high costs. To examine the influence of SNPs on the mechanical properties, seven different weight percentages of vinyl ester/nano-silica composites were initially fabricated. Afterward, based on the tensile testing results of the silica nanocomposites, four wt% of SNPs were selected to fabricate a ternary composite composed of vinyl ester/glass fiber/nano-silica using vacuum-assisted resin transfer molding. At the next stage, the tensile, three-point flexural, Charpy impact, and pin-on-disk wear tests were performed on the ternary composites. The fractured surfaces were analyzed by scanning electron microscopy (SEM) images after conducting previous tests. The most important and interesting result of this study was the development of a nanocomposite that exhibited a 52.2% decrease in the mean coefficient of friction (COF) by augmenting the SNPs, which is beneficial for the fabrication/repair of composite/steel energy pipelines as well as hydraulic and pneumatic pipe systems conveying abrasive materials. Moreover, the weight loss due to wearing the ternary composite containing one wt% of SNPs was significantly reduced by 70%. Such enhanced property of the fabricated nanocomposite may also be an important design factor for marine structures, bridges, and transportation of wind turbine blades.

• Proceedings of the Korean Nuclear Society Conference
• /
• 1997.05b
• /
• pp.341-344
• /
• 1997

A vitrification process is under development in KEPRI for the treatment of low-and medium-level radioactive waste. Although the project is for developing and building Vitrification Pilot Plant in Korea, one of KEPRI's concerns is the quality control of the vitrified glass. This paper discusses a methodology for the estimation of glass composition by on-line measurement of molten glass properties, which could be applied to the plant for real-time quality control of the glass product. By remotely measuring viscosity and density of the molten glass, the glass characteristics such as composition can be estimated and eventually controlled. For this purpose, using the database of glass composition vs. physical properties in isothermal three-component system of SiO$_2$-Na$_2$O-B$_2$O$_3$, a software TERNARY has been developed which determines the glass composition by using two known physical properties(e.g. density and viscosity).

• Journal of the Korean Ceramic Society
• /
• v.32 no.10
• /
• pp.1093-1102
• /
• 1995

Water-soluble phosphate glasses containing Ag or Cu ion were prepared through melting process. Then the powdered glass samples were dissolved in D.I. water at room temperature with changing the dissolution time. In terms with the glass composition, dissolution characteristics, bactericidal effects and cytotoxicities were investigated. Dissolved amounts increased uniformly with dissolution time, and the dissolution rate was higher for ternary glass than for binary glass and with less metal oxide amount. And the dissolution rate of the glass with Ag ion was higher than that with Cu ion, and the bactericidal effect of the glass with Ag ion was also greater. Solution with more than 25 ppm of Ag was observed to have strong cytotoxicity to L929, and solutions of lower Ag concentration or with Cu seemed to have little cytotoxicity.

• Journal of the Korean Ceramic Society
• /
• v.29 no.3
• /
• pp.223-231
• /
• 1992

CaO and ZnO were added to Al2O3-SiO2 binary system respectively as flux, then ZrO2 and TiO2 were applied as nucleating agent to these CaO-Al2O3-SiO2 and ZnO-Al2O3-SiO2 ternary system glass. The transparency could not be kept in CaO-Al2O3-SiO2 system glass, whereas the transparent glass-ceramics were prepared in ZnO-Al2O3-SiO2 system glass containing ZrO2 as the nucleating agent. At this time the optimum heating temperatures for the nucleation and the crystal growth were 78$0^{\circ}C$ and 97$0^{\circ}C$. The sizes of the precipitated crystals in the transparent glass-ceramics were below 0.1 ${\mu}{\textrm}{m}$, and their light transmissibilities were more than 80%.

• Fibers and Polymers
• /
• v.1 no.2
• /
• pp.83-91
• /
• 2000

Thermotropic liquid crystalline polymer made up of poly(p-hydroxybenzoate) (PHB)-poly(ethylene terephthalate)(PET) 8/2 copolyester, poly(ethylene 2,6-naphthalate) (PEN) and PET were mechanically blended to pursue the liquid crystalline phase of ternary blends. Complex viscosities of blends decreased with increasing temperature and PHB content. DSC thermal analysis indicated that glass transition temperature (Tg) and melting temperature (Tm) of blends increased with increasing PHB content. Both tensile strength and initial modulus increased with raising PHB content and take-up speed of monofilaments. In the WAXS diagram, only PEN crystal reflection at 2Θ=$15.5^{\circ}C$ appeared but PET crystal reflection was not shown in all compositions. The degree of transesterification and randomness of blends increased with blending time but sequential length of both PEN and PET segment decreased.