• 대한금속재료학회지
• /
• 제50권5호
• /
• pp.345-351
• /
• 2012

A three-point bending test was performed on roll-bonded Mg/Al/STS clad-metal plates under two different testing conditions (Mg layer in tension, or STS in tension) and their mechanical response and fracture behavior were investigated. Bending strength was found to be greater under the condition of Mg layer in tension. Heat treatment at $200^{\circ}C$ increased the bending formability, suggesting the interfacial strength increased at $200^{\circ}C$. Under the condition of Mg in tension, the clad heat-treated at $300^{\circ}C$ and $400^{\circ}C$ fractured in two steps, with the first step associated with the interfacial fracture between Mg and Al, and the second the fracture of the Mg layer. STS/Al layers were found to be bent without complete fracture. Under the condition of STS in tension, the clad heat-treated at $300^{\circ}C$ and $400^{\circ}C$ exhibited a very small load drop at the displacement, which is similar to that of the first load drop associated with the interfacial fracture under the condition of Mg in tension. In this case, no interfacial cracks were found and the complete cut-through fracture of clad was observed at low temperature heat treatment conditions, suggesting excellent interfacial strength. When the heat treatment temperature was higher than $300^{\circ}C$, interfacial cracks were observed. The local stress condition and the position of the interface with respect to the surface were found to have a great influence on the fracture behaviors of clad metals.

• Steel and Composite Structures
• /
• 제24권4호
• /
• pp.399-408
• /
• 2017

Of high strength bolts, the torque shear type bolt is known to be clamped normally when pin-tails are broken. Sometimes the clamping loads on slip critical connections considerably fluctuate from the required tension due to variation of torque coefficient. This is why the viscosity of lubricant affects the torque coefficient by temperature. In this study, the clamping tests of high strength bolts were performed independently at laboratory conditions and at outdoor environment. The temperatures of outdoor environment candidates were ranged from $-11^{\circ}C$ to $34^{\circ}C$ for six years. The temperature at laboratory condition was composed from $-10^{\circ}C$ to $50^{\circ}C$ at each $10^{\circ}C$ interval. At outdoor environment conditions, the clamping load of high strength bolt was varied from 159 to 210 kN and the torque value was varied from 405 to 556 Nm. The torque coefficients at outdoor environment were calculated from 0.126 to 0.158 when tensions were measured from 179 to 192 kN by using tension meter. The torque coefficients at outdoor environment conditions were analyzed as the range from 0.118 to 0.152. From these tests, the diverse equations of torque coefficient, tension dependent to temperature can be acquired by statistic regressive analysis. The variable of torque coefficient at laboratory conditions is 0.13% per each $1^{\circ}C$ when it reaches 2.73% per each $1^{\circ}C$ at outdoor environment conditions. When the results at laboratory conditions and at outdoor environment were combined to get the revised equations, the change in torque coefficient was modified as 0.2% per each $1^{\circ}C$ and the increment of tension was adjusted as 1.89 % per each $1^{\circ}C$.

• 한국자동차공학회논문집
• /
• 제6권1호
• /
• pp.143-150
• /
• 1998

The evaluation of joint fatigue strength of light weight materials for electrical vehicle body has been performed through single lap joint tests with the design parameters such as joint style, adherend, bonding overlap length and bonding thickness. Fatigue strength was evaluated through 5-Hz, tension-tension, load controlled test with the stress ratio zero value. It is experimentally observed that fatigue strength of joint increases for the increase of overlap length. The combinations of Al-Al and Al-FRP adherends show that fatigue strength of joint is hardly changed for the increase of bonding thickness, but FRP-FRP adherend specimen shows that fatigue strength of joint increases after decreases for the increase of bonding thickness. Al-Al adherend specimen has much higher fatigue length than Al-FRP and FRP-FRP adherend specimens. Riveting at adgesive bonded joint gives little effect on fatigue strength.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 1998년도 봄 학술발표회논문집(II)
• /
• pp.665-670
• /
• 1998

This study was carried out to investigate quantitatively the relationship between the degree of rebar corrosion and the strength of reinforced concrete beams. After producing equations for the relationship between both the tensile properties of rebars and bond properties and the corrosion percentage of rebars. Finite element analysis and bending tests were conducted for RC beams damaged by corrosion of tension main rebar. As a result, it was made that the strength of RC beams damged by corrosion could be practically simulated by FEM using experimentally determined material representing the bond properties and the mechanical properties of corroded rebars.

• Computers and Concrete
• /
• 제4권3호
• /
• pp.187-206
• /
• 2007

A rational three-dimensional nonlinear finite element model is described and implemented for evaluating the behavior of high strength concrete slabs under transverse load. The concrete was idealized by using twenty-nodded isoparametric brick elements with embedded reinforcements. The concrete material modeling allows for normal (NSC) and high strength concrete (HSC), which was calibrated based on experimental data. The behavior of concrete in compression is simulated by an elastoplastic work-hardening model, and in tension a suitable post-cracking model based on tension stiffening and shear retention models are employed. The nonlinear equations have been solved using the incremental iterative technique based on the modified Newton-Raphson method. The FE formulation and material modeling is implemented into a finite element code in order to carry out the numerical study and to predict the behavior up to ultimate conditions of various slabs under transverse loads. The validity of the theoretical formulations and the program used was verified through comparison with available experimental data, and the agreement has proven to be very good. A parametric study has been also carried out to investigate the influence of different material and geometric properties on the behavior of HSC slabs. Influencing factors, such as concrete strength, steel ratio, aspect ratio, and support conditions on the load-deflection characteristics, concrete and steel stresses and strains were investigated.

• 한국안전학회지
• /
• 제21권5호
• /
• pp.17-21
• /
• 2006

In this study, SPCC cross-tension type specimens produced under various spot welding conditions were tensile and fatigue tested. Decrease of 2 kA in normal current condition of 10 kA caused a large amount of reduction in both static joining strength and fatigue life. And 2 kA increase resulted in increase of static joining strength and an increase in low cycle regime but a decrease in high cycle regime, revealing the fact that fatigue strength rather than static joining strength would be a major factor during design process in view of the body endurance. As a results of estimating the fatigue lifetimes of various types of spot weld specimens. equivalent stress intensity factor is the proper parameter for predicting the lifetimes of various types of specimens. which can be expressed as ${\Delta}K_{eq}(N/nm^{1.5})=11550N^{-0.36}_{f}$.

• 한국구조물진단유지관리공학회 논문집
• /
• 제13권6호통권58호
• /
• pp.97-105
• /
• 2009

본 연구에서는 대직경 고장력볼트 이음부의 안전성 및 경제성을 검토할 목적으로 F10T-M30 대직경 고장력볼트를 사용한 시험편을 대상으로 정적 인장시험을 실시하여 미끄러짐 특성을 평가하였다. 또한 유한요소해석을 실시하고 볼트의 강도등급 및 직경에 따른 소요볼트 개수를 산정하였다. 그 결과 M30 고장력볼트의 평균 미끄러짐 계수는 도로교설계기준의 기준인 0.4를 초과하며, M22 고장력볼트와 동등한 미끄러짐 성능을 확보하는 것으로 나타났다. 또한 고장력볼트의 강도등급 및 직경에 따른 경제성 분석을 실시한 결과, F10T-M22 고장력볼트를 기준으로 하여 F13T-M22 고장력볼트를 적용하면 소요볼트 개수가 21% 감소하며, F10T-M30 고장력볼트를 적용하면 46% 감소하는 것으로 나타나 고장력볼트의 대직 경화에 따른 경제성을 확인할 수 있었다.

• 한국자동차공학회논문집
• /
• 제6권6호
• /
• pp.166-173
• /
• 1998

The evaluation of joint fatigue strength of light weight materials for an electrical vehicle body has been performed through T-peel joint tests with the design parameters such as joint style, adherend type, adherend thickness, adhesive thickness, and various adhesives. Fatigue strength was evaluated through 5-Hz, tension-tension, load controlled test with the zero stress ratio. It was observed that the fatigue strength of the joint increases with the increase of the adherend thickness. With the increase of the adhesive thickness, however, the fatigue strength of the joint increases insignificantly. An aluminum-FRP adherend combination shows much higher fatigue strength than an aluminum-aluminum adherend combination. The results of fatigue tests were found to be consistent with those of static tests.

• 대한물리치료과학회지
• /
• 제29권2호
• /
• pp.28-37
• /
• 2022

Background: The purpose of this study was to investigate the effects of differences in the tension of Kinesio tape applied to the tibialis anterior muscle on muscle strength, joint range of motion and balance of ankle joint in young adults. Design: Randomized Controlled Trial. Methods: 41 young college students participated in this study. And the subjects were allocated randomly to two group. The experimental group had a tension difference (10%G, n=20). And there was no difference in tension in the control group (0%G, n=21). Jtech power track II, goniometer, and Biorescue were used to measure muscle strength, joint range of motion and balance. The paired t-test was performed to examine the differences within the groups before and after taping, and the independent t-test was performed to examine the differences between the groups. Result: 1) As a result of measuring muscle strength of each group, all measurements except 0%G of plantar flexion showed insignificant results. 2) Measurement of joint range of motion each group showed that neither 0%G nor 10%G was significant. 3) As a result of measuring the baladncing ability of each group there was a significant decrease in length, and average speed of the balancing capability (p<.05). 4) Comparisons between groups showed significant differences in the area among balance capability (p<.05). Conclusions: Based on these findings, the tension difference of Kinesio tape applied to the tibialis anterior muscle shows little effect on the muscle strength, range of motion, and balance of ankle joints. Given the current lack of research on the tension of kinesio tapes many studies are needed in the future to establish clear theories.

• 대한치과의사협회지
• /
• 제11권1호
• /
• pp.41-44
• /
• 1973

The experiment consisted of cementing full veneer crown of extracted teeth and a standardized cylindrical metal dies (6mm diameter, 6mm height, 1mm shoulder) and then measuring the tensile strength required to remove the cemented restoratoins by the Instron testing machine in the Korea Institude of Science and Technology. The Instron machine was operated at a rate of loading of 0.2cm per minute. From the experiments, the following results obtained. 1. The tension of zinc phosphate and alumina EBA cements were highest all of the cements. 2. The tension of Fynal and the addition of eugenol to zinc Phosphate cements were similar. The addition of eugenol to zinc phosphate cement was half stength and Fynal cement was on third strength than zinc phosphate cement. 3. The tension of zinc oxide-eugenol cement was lowest all of the cements.