• Korean Journal of Crystallography
• /
• v.11 no.4
• /
• pp.212-223
• /
• 2000

A stochiometric mix of CuInTe₂ polycrystal was prepared in a honizonatal furnace. To obtain the single crystal thin films, CuInTe₂ mixed crystal was deposited on throughly etched GaAs(100) by the HWE system. The source and substrate temperatures were 610℃ and 450℃ respectively, and the thickness of the deposited single crystal thin film was 2.4㎛. CuInTe₂ single crystal thin film was proved to be the optimal growth condition when the excition emission spectrum was the strongest at 1085.3 nm(1.1424 eV) of photoluminescence spectrum at 10 K, and also FWHM of Double Crystal X-ray Rocking Curve (DCRC) was the smallest, 129 arcsec. The Hall effect on this sample was measured by the method of Van der Pauw, and the carrier density and mobility dependent on temperature were 9.57x10/sup 22/ electron/㎥, 1.31x10/sup -2/㎡/V·s at 293 K, respectively. The ΔCr(Crystal field splitting) and the ΔSo (spin orbit coupling splitting( measured at f10K from the photocurrent peaks in the short wavelength of the CuInTe₂ single crystal thin film were about 0.1200 eV, 0.2833 eV respectively. From the PL spectra of CuInTe₂ single crystal thin film at 10 K, the free exciton (E/sub x/) was determined to be 1064.5 nm(1.1647 eV) and the donor-bound exciton(D/sup 0/, X) and acceptor-bound exciton (A/sup 0/, X) were determined to be 1085.3 nm(1.1424 eV) and 1096.8 nm(1.1304 eV0 respectively. And also, the donor-acciptor pair (DAP)P/sub 0/, DAP-replica P₁, DAP-replica P₂ and self-activated (SA) were determined to be 1131 nm (1.0962 eV), 1164 nm(1.0651 eV), 1191.1 nm(1.0340 eV) and 1618.1 nm (0.7662 eV), respectively.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.12 no.4
• /
• pp.202-209
• /
• 2002

The stochiometric mix of evaporating materials for the $CuInSe_2$single crystal thin films was prepared from horizontal furnace. To obtain the single crystal thin films, $CuInSe_2$compound crystal was deposited on thoroughly etched semi-insulating GaAs(100) substrate by the Hot Wall Epitaxy (HWE) system. The source and substrate temperature were $620^{\circ}C$ and $410^{\circ}C$, respectively. The crystalline structure of single crystal thin films was investigated by the photoluminescence and double crystal X-ray diffraction (DCXD). The carrier density and mobility of $CuInSe_2$single crystal thin films measured from Hall effect by van der Pauw method. From the photocurrent spectrum by illumination of perpendicular light on the c-axis of the $CuInSe_2$single crystal thin film, we have found that the values of spin orbit splitting $\Delta$So and the crystal field splitting $\Delta$Cr. From the photoluminescence measurement on $CuInSe_2$single crystal thin film, we observed free exciton ($E_x$) existing only high quality crystal and neutral bound exciton ($A^{\circ}$, X) having very strong peak intensity. Then, the full-width-at-half-maximum (FWHM) and binding energy of neutral donor bound exciton were 7 meV and 5.9 meV, respectivity. By haynes rule, an activation energy of impurity was 59 meV.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2004.11a
• /
• pp.175-178
• /
• 2004

The stochiometric mixture of evaporating materials for the $ZnIn_2S_4$ single crystal thin film was prepared from horizontal furnace. To obtain the $ZnIn_2S_4$ single crystal thin film, $ZnIn_2S_4$ mixed crystal was deposited on throughly etched semi-insulating GaAs(100) in the Hot Wall Epitaxy(HWE) system. The source and substrate temperature were $610^{\circ}C$ and $450^{\circ}C$, respectively and the growth rate of the $ZnIn_2S_4$ sing1e crystal thin film was about $0.5\;{\mu}m/hr$. The crystalline structure of $ZnIn_2S_4$ single crystal thin film was investigated by photoluminescence and double crystal X-ray diffraction(DCXD) measurement. The carrier density and mobility of $ZnIn_2S_4$ single crystal thin film measured from Hall effect by van der Pauw method are $8.51{\times}10^{17}\;cm^{-3}$, $291\;cm^2/V{\cdot}s$ at $293_{\circ}\;K$, respectively. From the photocurrent spectrum by illumination of perpendicular light on the c - axis of the $ZnIn_2S_4$ single crystal thin film, we have found that the values of spin orbit splitting ${\Delta}S_O$ and the crystal field splitting ${\Delta}Cr$ were 0.0148 eV and 0.1678 eV at $10_{\circ}\; K$, respectively. From the photoluminescence measurement of $ZnIn_2S_4$ single crystal thin film, we observed free excition $(E_X)$ typically observed only in high quality crystal and neutral donor bound exciton $(D^{o},X)$ having very strong peak intensity The full width at half maximum and binding energy of neutral donor bound excition were 9 meV and 26 meV, respectively, The activation energy of impurity measured by Haynes rule was 130 meV.

• Journal of the Korean Vacuum Society
• /
• v.20 no.6
• /
• pp.449-455
• /
• 2011

The luminescence properties of $In_{0.5}Ga_{0.5}As/In_{0.5}Al_{0.5}As$ multiple quantum wells (MQWs) grown on $In_{0.4}Al_{0.6}As$ buffer layer have been investigated by using photoluminescence (PL) and time-resolved PL measurements. A 1-${\mu}m$-thick $In_{0.4}Al_{0.6}As$ buffer layers were deposited at various temperatures from $320^{\circ}C$ to $580^{\circ}C$ on a 500-nm-thick GaAs layer, and then 1-${\mu}m$-thick $In_{0.5}Al_{0.5}As$ layers were deposited at $480^{\circ}C$, followed by the deposition of the InGaAs/InAlAs MQWs. In order to study the effects of $In_{0.4}Al_{0.6}As$ layer on the optical properties of the MQWs, four different temperature sequences are used for the growth of $In_{0.4}Al_{0.6}As$ buffer layer. The MQWs consist of three $In_{0.5}Al_{0.5}As$ wells with different well thicknesses (2.5-nm, 4.0-nm, and 6.0-nm-thick) and 10-nm-thick $In_{0.5}Al_{0.5}As$ barriers. The PL peaks from 4-nm QW and 6-nm QW were observed. However, for the MQWs on the $In_{0.4}Al_{0.6}As$ layer grown by using the largest growth temperature variation (320-$580^{\circ}C$), the PL spectrum only showed a PL peak from 6-nm QW. The carrier decay times in the 4-nm QW and 6-nm QW were measured from the emission wavelength dependence of PL decay. These results indicated that the growth temperatures of $In_{0.4}Al_{0.6}As$ layer affect the optical properties of the MQWs.

• Proceedings of the KIEE Conference
• /
• 1988.11a
• /
• pp.372-375
• /
• 1988

The III-V ternary alloy semiconductor $In_{l-x}Ga_{x}As$ were grown by the temperature Gradient of $0.60{\leq}x{\leq}0.98$. The electrical properties were investigated by the Hall effect measurement with the Van der Pauw method in the temperature range of $90{\sim}300K$. $In_{l-x}Ga_{x}As$ were revealed n-type and the carrier concentration at 300K were in the range of $9.69{\times}10^{16}cm^{-3}{\sim}7.49{\times}10^{17}cm^{-3}$. The resistivity was increased and the carrier mobility was decreased with increasing the composition ratio. The optical energy gap determined by optical transmission were $20{\sim}30meV$ lower than theoretical valves on the basis of absorption in the conduction band tail and it was decreased with increasing the temperature by the Varshni rule. In the photoluminescence of undoped $In_{l-x}Ga_{x}As$ at 20K, the main emission was revealed by the radiative recombination of shallow donor(Si) to acceptor(Zn) and the peak energy was increased with increasing the composition, X. The diffusion depth of Zn increases proportionally with the square root of diffusion time, and the activation energy for the Zn diffusion into $In_{0.10}Ga_{0.90}As$ was 2.174eV and temperatures dependence of diffusion coefficient was D = 87.29 exp(-2.174/$K_{B}T$). The Zn diffusion p-n $In_{x}Ga_{x}As$ diode revealed the good rectfying characteristics and the diode factor $\beta{\approx}2$. The electroluminescence spectrum for the Zn-diffusion p-n $In_{0.10}Ga_{0.90}As$ diode was due to radiative recombation between the selectron trap level(${\sim}140meV$) and Zn acceptor level(${\sim}30meV$). The peak energy and FWHM of electroluminescence spectrum at 77K were 1.262eV and 81.0meV, respectively.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.31 no.5
• /
• pp.324-329
• /
• 2018

Red phosphor in glasses (PiGs) for automotive light-emitting diode (LED) applications were fabricated with 620-nm $CaAlSiN_3:Eu^{2+}$ phosphor and Pb-free silicate glass. PiGs were synthesized and mounted on high-power blue LED to make a monochromatic red LED. PiGs were simple mixtures of red phosphor and transparent glass powder. After being fabricated with uniaxial press and CIP at 300 MPa for 20 min, the green bodies were thermally treated at $550^{\circ}C$ for 30 min to produce high dense PiGs. As the phosphor content increased, the density of the sintered body decreased and PiGs containing 30% phosphor had a full sintered density. Changes in photoluminescence spectra and color coordination were studied by varying the thickness of plates that were mounted after optical polishing. As a result of the optical spectrum and color coordinates, PiG plate with $210{\mu}m$ thickness showed a color purity of 99.7%. In order to evaluate the thermal stability, the thermal quenching characteristics were measured at temperatures of $30{\sim}150^{\circ}C$. The results showed that the red PIG plates were 30% more thermally stable compared to the AlGaInP red chip.

• The Transactions of the Korean Institute of Electrical Engineers C
• /
• v.48 no.1
• /
• pp.12-17
• /
• 1999

$MgIn_2Se_4 and MgIn_2Se_4 : Ni^{2+}$ single crystals were grown in the rhombohedral structure by the chemical transport reaction (C.T.R.) method using iodine as a transport agent. The optical absorption measured near the fundamental band edge showed that the optical energy band structure of these compounds had a direct band gap. The fundamental absorption band edge of these single crystals shift to a shorter wavelength region by decreasing temperature and the temperature dependence of the optical energy gaps in these compounds satisfy Varshni equation. The impurity optical absorption peaks due to nickel are observed in $MgIn_2Se_4 and MgIn_2Se_4 : Ni^{2+}$ single crystal. These impurity optical absorption peaks can be attributed to the electronic transitions between the split energy levels of $Ni_{2+}$ ions located at $T_d$ symmetry site of $MgIn_2Se_4$ host lattice. In the hotoluminescence spectrum of the single crystal at 10 K, a blue emission with a peak at 687nm and a green emission with a peak at 815nm for the $MgIn_2Se_4$ single crystal were observed.

• Journal of the Korean Vacuum Society
• /
• v.1 no.1
• /
• pp.126-133
• /
• 1992

This study deals with the crystal growth and the optical characteristics of CdS thin films activatedby silver. CdS:Ag thin films were deposited by using an electron beam evaporation(EBE) technique in vacuumof 1.5X 10-'torr, voltage of 4 kV, current of 2.5 mA and substrate temperature of 250$^{\circ}$C CdS:Ag photoconductivefilms prepared by EBE method show high photoconductivity after annealing at about 550"c for 0.5 h in air andAr gas.The grain size of CdS:Ag thin films annealed in Ar atmosphere (1 atm) was grown over 1 ym and the thicknessof the films is 4-5 pm. The analysis of X-ray diffraction patterns shows that the crystal structures are hexagonal.The diffraction line by (00.2) plane can only be observed, indicating that c-axis of hexagonal grows preferentiallyperpendicular to the substrate. The profiles of photoluminescence spectra of CdS:Ag films show Gaussian typecurves at room temperature, the maximum peak spectral sensitivity of CdS:Ag is located at the wavelength of520 nm.We annealed CdS:Ag thin films in air and Ar vapor in order to make the CdS photoconductors having theintensive photocurrent, the broad distribution of the photocurrent spectrum and the large value of the ratioof the photocurrent (pc) to the dark current(dc). We found that CdS:Ag thin films annealed in air atmospherewas the best one.air atmosphere was the best one.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2007.06a
• /
• pp.179-180
• /
• 2007

Single crystal $AgGaSe_2$ layers were grown on thoroughly etched semi-insulating GaAs(100) substrate at $420^{\circ}C$ with hot wall epitaxy (HWE) system by evaporating $AgGaSe_2$ source at $630^{\circ}C$. The crystalline structure of the single crystal thin films was investigated by the photoluminescence and double crystal X-ray diffraction (DCXD). The carrier density and mobility of single crystal $AgGaSe_2$ thin films measured with Hall effect by van der Pauw method are $4.05{\times}\;10^{16}/cm^3$, $139\;cm^2/V{\cdot}s$ at 293 K. respectively. The temperature dependence of the energy band gap of the $AgGaSe_2$ obtained from the absorption spectra was well described by the Varshni's relation, $E_g(T)=1.9501\;eV\;-\;(8.79{\times}10^{-4}\;eV/K)T^2$/(T + 250 K). The crystal field and the spin-orbit splitting energies for the valence band of the $AgGaSe_2$ have been estimated to be 0.3132 eV and 0.3725 eV at 10 K, respectively, by means of the phcitocurrent spectra and the Hopfield quasicubic model. These results indicate that the splitting of the ${\Delta}So$ definitely exists in the $\Gamma_5$ states of the valence band of the $AgGaSe_2$. The three photocurrent peaks observed at 10 K are ascribed to the $A_1$-, $B_1$-, and $C_1$-exciton peaks for n = 1.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.15 no.1
• /
• pp.1-9
• /
• 2005

A stoichiometric mixture of evaporating materials for AgGaS₂ single crystal thin films was prepared from horizontal electric furnace. To obtain the single crystal thin films, AgGaS₂ mixed crystal was deposited on thoroughly etched semi-insulating GaAs(100) substrate by the hot wall epitaxy (HWE) system. The source and substrate temperatures were 590℃ and 440℃, respectively. The temperature dependence of the energy band gap of the AgGaS₂ obtained from the absorption spectra was well described by the Varshni's relation, E/sub g/(T) = 2.7284 eV - (8.695×10/sup -4/ eV/K)T²/(T + 332 K). After the as-grown AgGaS₂ single crystal thin films was annealed in Ag-, S-, and Ga-atmospheres, the origin of point defects of AgGaS₂ single crystal thin films has been investigated by the photoluminescence (PL) at 10 K. The native defects of V/sub Ag/, V/sub s/, Ag/sub int/, and S/sub int/ obtained by PL measurements were classified as a donors or accepters type. And we concluded that the heat-treatment in the Ag-atmosphere converted AgGaS₂ single crystal thin films to an optical n-type. Also, we confirmed that Ga in AgGaS₂/GaAs crystal thin films did not form the native defects because Ga in AgGaS₂ single crystal thin films existed in the form of stable bonds.