• Design & Manufacturing
• /
• v.15 no.3
• /
• pp.39-44
• /
• 2021

In molding of continuous fiber-reinforced thermoplastic composites, it is very difficult to impregnate between the reinforcements and the matrix since the matrix has a high melting temperature and high viscosity. Therefore, most of composite molding processes are divided in the manufacturing processes of intermediate materials called prepreg and the forming of products from intermediate materials. The divided process requires additional facilities and thermoforming, and they increase the cycle time and cost of composite products. These problems can be resolved by combining the continuous fiber-reinforced composite molding process with injection molding. However, when a composite material is manufactured by inserting woven fabric into the injection mold, poor impregnation occurs on the surface of the molded product. It affects the properties of the composites. In this paper, through an impregnation experiment using cores with different heat transfer rates and pore densities, the reason for the poor impregnation was confirmed, and molding experiments were conducted to produce composite with improved surface impregnation by inserting the mesh. And also, the surface impregnation and deformation of composites molded using different types of mesh were compared with each other.

• Journal of the Korean Wood Science and Technology
• /
• v.40 no.5
• /
• pp.343-351
• /
• 2012

A large diameter roundwood is an important element of Korean traditional buildings, Hanok, and is hard to be dried without surface cracks. Four different pretreatments, such as pre-cracking, oil heating, kerfing-oil heating and PEG impregnation, were investigated for reducing the surface cracks of large-diameter roundwood specimens during heat treatment. The roundwood specimens of pre-cracking, oil heating and kerfing-oil heating showed surface cracks during pretreatment, but that of PEG impregnation did not. It was confirmed that kerfing reduced the total crack width. Among the four pretreatments and control only the PEG impregnation roundwood specimen had no crack on both outer and inner surfaces after heat treatment. The PEG impregnation specimen shrank only 1.6% in the tangential direction while the pre-cracking did 8.0%.

• Journal of the Korean institute of surface engineering
• /
• v.53 no.6
• /
• pp.300-305
• /
• 2020

Corrosion of reinforcement steel rebar is a serious problem in a wide range of concrete application for buildings and infrastructures. Hydrophobizing surface treatments, such as self-assembled monolayer coating, edible oil-impregnation and silicone oil-impregnation were applied to solidified concrete. The hydrophobizing of concrete significantly reduces an absorption and transportation of water toward a steel rebar in concrete, so that the corrosion resistance of the steel rebar. In particular, the silicone oil-impregnation not only forms the hydrophobic monolayer on the concrete but also fills the inter-connected pores of concrete, thus the corrosion of steel rebar is significantly inhibited compared to the self-assembled monolayer coating and edible oil-impregnation. Therefore, the silicone oil-impregnation can be a promising candidate for preventing corrosion of steel rebar in concrete for durable performance and safety.

• Journal of the Korean Ceramic Society
• /
• v.40 no.10
• /
• pp.1021-1026
• /
• 2003

Resin impregnation of carbon materials was affected by surface of carbon materials. The surface of carbon materials with coupling treatment improved comparability and wettability with resin, and that increased impregnation efficiency and properties of carbon materials. As a results of FT-IR, The silanol was coated on carbon surface with one layer. Coupling treatment of carbon materials increased impregnation efficiency, which improved porosity, mechanical strength, density and friction behavior.

• Journal of Korea Foresty Energy
• /
• v.22 no.1
• /
• pp.24-29
• /
• 2003

Using woodceramics made from sawdust board of Larix leptolepis thinning logs, change in surface temperature were investigated, by the rate of resin impregnation and burning temperature. As the surface temperature of silicon rubber heater was going up, that of woodceramics also increase rapidly. Woodceramics made from under the condition of the rate of resin impregnation 70-80% and burning temperature 800-$1000^{\circ}C$, were higher than that of surface temperature. Also, it was found that woodceramics maintained heat for a long time because the descending velocity of their surface temperature was lower than that of the heater.

• Journal of the Korean institute of surface engineering
• /
• v.53 no.2
• /
• pp.80-86
• /
• 2020

This paper is concerned with type of imperfections present within the anodic oxide films on AA2024 and surface hardness of the anodic film measured after ink-impregnation. The anodic oxide films were formed for 25 min at 40 mA/㎠ and 15±0.5℃ and 300 rpm of magnet stirring rate in 20% sulfuric acid solution. The ink-impregnation allows clear observations of not only the imperfections within the anodic oxide films but also an indentation mark on the oxide film surface made by a pyramidal-diamond penetrator for the hardness measurement. There were observed four different regions in the anodic oxide films on AA2024 and the surface hardness of the anodic oxide films appeared to be crucially dependent on the type of defects, showing 60~100 H_v on the oxide surface region I with large size black defect, 100~140 H_v on the oxide surface region II with large size grey defect, 140~170 H_v on the oxide surface region III with mall size black and/or grey defects and 170~190 H_v on the oxide surface region IV without defects. The pyramidal indentation marks were observed to be distorted in the regions with a large size black and grey defects, while no distortion of the indentation mark was observed in the regions with small size defects and without visible defects.

• Journal of the Korean institute of surface engineering
• /
• v.32 no.3
• /
• pp.363-365
• /
• 1999

The improved method comprises electrochemically deposition of nickel hydroxide into the sintered nickel plaque cathode from nickel aqueous electrolyte at acid pH in a treating zone containing an anode. The electrochemical impregnation was examined under various conditions. Deposition condition of fine active material was obtained from the impregnation of a high temperature and also high current density. This method also could be decreased swelling and buckling of the plaque. A nickel electrode prepared by electrochemical impregnation is useful as the positive in nickel-cadmium cells. The utilization of the active material indicated almost 100% based on a one electron charge.

• Design & Manufacturing
• /
• v.14 no.4
• /
• pp.11-16
• /
• 2020

In this study, forming of carbon composite parts was performed using an injection/compression molding process. An impregnation of matrix is determined by ability of wet and flow rate between the matrix and reinforcement. The flow rate of matrix passing through the reinforcements is a function of permeability of reinforcement, a viscosity of matrix and pressure gradient on molding, and the viscosity of the matrix depends on the mold temperature, molding pressure and shear strain of matrix. Therefore, compression molding experiment was conducted using a heating mold in order to confirm the possibility of matrix impregnation. The impregnation of the matrix through the porosities between the woven yarns was confirmed by the cross-sectional SEM image of compression molded parts. An injection molding process was also performed at a short cycle time, high molding pressure and low mold temperature than those of compression experiment conditions. Deterioration of impregnation on the surface of molded parts were caused by these injection conditions and it could be the reason of decreasing the maximum tensile strength. In order to improve impregnation of matrix on the surface, injection/compression molding and insert-over molding were applied. As a result of applying injection/compression molding and insert-over molding, it was shown that the improvement of impregnation on the surface and the maximum tensile strength was increased about 2.8 times than the virgin matrix.

• Journal of Korean Society of Water and Wastewater
• /
• v.34 no.6
• /
• pp.425-435
• /
• 2020

Numerous chemical modifications on activated carbon such as acidic conditioning, thermal treatment and metal impregnation have been investigated to enhance adsorption capacities of micropollutants in water treatment plants. In this study, chemical modification including acidic, alkaline treatment, and iron-impregnation was evaluated for adsorption of 2,4-dichlorophenol (2,4-DCP). For Fe-impregnation, three concentrations of ferric chloride solutions, i.e., 0.2 M, 0.4 M, and 0.8 M, were used and ion-exchange (MIX) of iron and subsequent thermal treatment (MTH) were also applied. Surface properties of the modified carbons were analyzed by active surface area, pore volume, three-dimensional images, and chemical characteristics. The acidic and alkaline treatment changed the pore structures but yielded little improvement of adsorption capacities. As Fe concentrations were increased during impregnation, the active adsorption areas were decreased and the compositional ratios of Fe were increased. Adsorption capacities of modified ACs were evaluated using Langmuir isotherm. The MIX modification was not efficient to enhance 2,4-DCP adsorption and the MES treatment showed increases in adsorption capacities of 2,4-DCP, compared to the original activated carbon. These results implied a possibility of chemical impregnation modification for improvement of adsorption of 2,4-DCP, if a proper modification procedure is sought.

• Journal of the Korean institute of surface engineering
• /
• v.54 no.2
• /
• pp.90-95
• /
• 2021

Surface modification technique enabling the control of condensation provides various benefit in various engineering systems, such as heat transfer, desalination, power plants, and so on. In this study, lubricant oil-impregnation into Teflon-coated nanoporous anodic oxide layer of aluminum to enhance a de-wetting and mobility of water droplet on surface. Due to the surface treatment improving water-repellency, the condensation mode is changed to dropwise, thus the frequency of sliding condensed water droplet on surface is increased. For these reasons, the surface of oil-impregnated Teflon-coated nanoporous anodic aluminum oxide shows significantly enhanced condensation heat transfer compared to bare aluminum surface. In addition, the porosity of anodic aluminum oxide affected the mobility of water droplet even with oil-impregnation and Teflon-coating, indicating that the optimization of porous structure of anodic oxide is required for maximizing the condensation heat transfer.