• Korean Chemical Engineering Research
• /
• v.49 no.6
• /
• pp.804-809
• /
• 2011

Tubular $Ba_{0.5}Sr_{0.5}Co_{0.8}Fe_{0.2}O_{3-${\delta}$}$ membranes were prepared by extrusion. TGA results of green body membrane after extrusion showed three successive weight losses due to decomposition of organic additives and carbonate. Drying shrinkage rate of tubular $Ba_{0.5}Sr_{0.5}Co_{0.8}Fe_{0.2}O_{3-${\delta}$}$ membranes was no change after 68 h and higher in the membrane with large outer diameter. XRD and SEM results showed the sintered membranes were the single phase structure and dense. The stoichiometric molar ratio agreed well with composition ratio calculated by EDS results for $Ba_{0.5}Sr_{0.5}Co_{0.8}Fe_{0.2}O_{3-${\delta}$}$ membrane. Radial crushing strength of tubular $Ba_{0.5}Sr_{0.5}Co_{0.8}Fe_{0.2}O_{3-${\delta}$}$ membrane with 0.95 mm thickness was 5.7 kgf/$mm^2$ and the oxygen permeation rate of same membrane was 146.85 mL/min ($Jo_2$=2.33 mL/$min{\cdot}cm^2$) at $950^{\circ}C$. Therefore, it was known that use of vacuum pump was more effective than that of sweep gas to obtain higher oxygen permeation flux.

• Journal of the Korean Geotechnical Society
• /
• v.18 no.2
• /
• pp.23-37
• /
• 2002

Failure of the cut slope is triggered by combination of internal and extemal failure factors. Internal failure factors are related to geological and geometrical conditions of slope itself, and natural and/or artificial loadings on slope can be the external failure factors. Influences of these failure factors show different intensity according to the ground condition and are controlled by behavior characters of the slope. In this study, the soil depth ratio(SR), block size ratio(BR) and rock strength are used as the criteria to divide ground condition based on behavior characteristics. Ground condition of the slope is divided into discontinuous jointed rock mass and continuos soil-like mass, highly fractured rock mass and massive rock mass by the criteria(SR and BR). The SFi-system is a rating system to determine the slope failure index(SFi) by analyzing internal and external factors based on classification of the ground condition. The results of the SFi-system application to the real cut slopes show close relationship between the SFi value and potential or dimension of the failure. Therefore, the SFi-system can be used as a useful tool to predict and analyze the characteristic of the slope failure.

• Journal of the Korean Society of Tobacco Science
• /
• v.11 no.2
• /
• pp.211-224
• /
• 1989

10. Three major factors, freeness, filler and blend ratio that exercised considerable influence on physical properties of cigarette papers were chosen for the sake of their optimization at this experiment. An optimization of those above factors in paper manufacturing was investigated using response surface analysis. Optimum beating degree for Kenaf, Flax and NBKP showed around 72。SR, 68。SR and 85 SR, respectively, in considering of five quality index such as porosity, tensile strength, stretch, whiteness and opacity. The best blending ration of reciprocal pulps treated under optimum beating degree were diversified and combination scope of the bast fiber (Kenaf, Flax) to the NBKP was range from 30% to 65% in case of the Kenaf, from 25 to 40% in Flax at the same receipe. The optimum range of calcium carbonate content revealed 25%~30% in Kenaf mixed NBKP and 24%~31% in Flax mixed NBKP.

• Laser Solutions
• /
• v.1 no.1
• /
• pp.30-38
• /
• 1998

This study includes the efface of shielding gas types on $CO_2$ laser weldability of low carbon automotive galvanized steel. The types of shielding gas evaluated are He, $CO_2$, Ar, $N_2$, 50%Ar＋50%$N_2$. The weld penetration, strength, formability(Erichsen test) of Laser weld are found to be strongly dependent upon the types of shielding gas used. Further, the maximum travel speed and flow rate to form a keyhole weld is also dependent upon types of shielding gas. The ability of shielding gas in removing plasma plume and thus increasing weld penetration is believed to be closely related with ionization/dissociation potential, which determine the period of plasma formation and disappearance. Further, thermal conductivity and reactivity of gas with molten pool also give strong effect on penetration and porosity formation which in turn affect on the formability and strength.

• Progress in Superconductivity and Cryogenics
• /
• v.5 no.1
• /
• pp.13-16
• /
• 2003

Adhesion of $SrZrO_3$ resistive oxide barrier on Ag sheathed Bi(2223) tapes prepared by the sol-gel and dip-coating method was evaluated with an aid of Taguchi method and Lie($2^1{\times}3^7$) orthogonal arrays to determine the optimal process combination of levels of factors that best satisfy the bigger is better quality characteristic (QC=B). For analyses of results statistical calculations such as average and analysis of variance (ANOVA) were employed to analyze the results for improving the performance qualities of the dip-coated $SrZrO_3$ film. Experimentally, the performance of the films was evaluated in terms of bond strength by varying Sr/Zr moi ratio (A), amount of organic vehicle additives (B), drying temperature (C) and time (D), heat treatment temperature (E) and time (F), respectively. The optimal combination of levels of factors was determined to be $A_3B_2C_3D_2E_1F_3$ having a 90% confidence level.

• Transactions of the Korean Society of Mechanical Engineers B
• /
• v.41 no.6
• /
• pp.423-427
• /
• 2017

In this paper, an anchor design that improves bonding strength uniformity in the silicon-on-glass (SOG) process is presented. The SOG process is widely used in conjunction with electrode-patterned glass substrates as a standard fabrication process for forming high-aspect-ratio movable silicon microstructures in various types of sensors, including inertial and resonant sensors. In the proposed anchor design, a trench separates the silicon-bonded area and the electrode contact area to prevent irregular bonding caused by the protrusion of the electrode layer beyond the glass surface. This technique can be conveniently adopted to almost all devices fabricated by the SOG process without the necessity of additional processes.

• Korean Chemical Engineering Research
• /
• v.44 no.3
• /
• pp.284-288
• /
• 2006

$(Ca,Sr)_{2-y}MgSi_2O_7:Eu^{2+}{_y}$ (CMS) phosphor particles were prepared by using a spray pyrolysis process. The luminescent property was optimized by changing the content of Eu and the post-treatment temperature. The luminescence characteristics were also monitored with changing the ratio of Ca to Sr. The pure tetragonal $Ca_2MgSi_2O_7$ or $Sr_2MgSi_2O_7$ particles were obtained when the post-treatment temperature was over $1,000^{\circ}C$. The highest emission intensity of CMS particles were achieved when the concentration (y) of Eu and the treatment temperature were 0.05 and $1,250^{\circ}C$,respectively. The emission wavelength $({\lambda}_{max})$ of ${(Ca_{1-x},Sr_x)}_{1.95}MgSi_2O_7:{Eu^{2+}}_{0.05}$ was gradually shifted from 524 nm to 456 nm with increasing the content of Sr due to the reduction of crystal field strength. The emission intensity and its width of $Sr_2MgSi_2O_7:Eu$ was greatly enhanced by substituting Ca of less than 10 mol％ for Sr without any significant peak shift. The morphology of as-prepared particles was spherical, but changed to irregular-shaped one after the post treatment at the temperature range from 900 at $1,300^{\circ}C$.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2002.05c
• /
• pp.79-82
• /
• 2002

$(Ba_{0.6-x}Sr_{0.4}Ca_x)TiO_3$ + ywt% MgO (x=0.10, 0.15, 0.20, y=0.0~3.0) ceramics were fabricated by the conventional solid-state reaction, and their structural and dielectric properties were investigated with variation of composition ratio and MgO doping content. A second phase, representative of MgO, appears in 3wt% MgO-doped BSCT specimens. Average grain sizes decreased with increasing amounts of MgO, and the BSCT(40/40/20) specimens doped with 3wt% MgO showed a value of $9.3{\mu}m$. The Curie temperature and relative dielectric constant at room temperature were decreased with increasing MgO doping content and Ca composition ratio. The relative dielectric constant was non-linearly decreased as the field strength is increased. The tunability was increased with decreasing a Ca content and the BSCT(50/40/10) specimen doped with 1.0wt% MgO content showed the highest value of 6.4% at 5kV/cm.

• Proceedings of the Korea Concrete Institute Conference
• /
• 1997.04a
• /
• pp.278-284
• /
• 1997

This study dealt with the flowing properties of the super flowing concrete for class F fly ash producted thermal power plant and the application for concrete industry. For this purpose, fly ash is analyzed for confined water ratio($\beta_p$)and the super flowing concrete is tested the flowing properties including flowing velocity, funneling time, height difference of box test and compressive strength. As the result, in order to satisfy the flowing properties of the super flowing concrete using class F fly ash, the optimum mixing conditions are determined water-bindrer ratio 37$\pm$2%, volume ratio of fine aggregates(Sr) 47$\pm$2% and coarse aggregates(Gv) 51$\pm$1%.

• Korean Journal of Food Science and Technology
• /
• v.29 no.6
• /
• pp.1184-1190
• /
• 1997

Corn zein coated carrageenan films were manufactured by immersing preformed ${\kappa}-carrageenan$ films into solution of different concentrations of corn zein (CZ) solids (10, 20, and 30% in 95% ethyl alcohol) with polyethylene glycol (20% w/w of CZ), glycerol (24% w/w of CZ). For all types of films, water vapor permeability (WVP), water solubility (WS), swelling ratio (SR), tensile strength (TS), percent elongation at break (E), heat sealing strength (HS), and Hunter color values (L, a, and b) were determined. WVP of corn zein coated ${\kappa}-carrageenan$ films decreased significantly (p<0.05) as the concentration of com zein increase. Coating with corn zein also decreased film WS and SR linearly with the concentration of corn zein. TS of corn zein coated carrageenan films decreased linearly with corn zein concentration. All the com rein coated carrageenan films showed heat sealing properties even though their sealing strength was less than half of corn zein film. Obviously corn zein coating affected color of ${\kappa}-carrageenan$ films, which was mainly caused by increase in yellowness (Hunter b-value).