• Corrosion Science and Technology
• /
• v.19 no.1
• /
• pp.43-50
• /
• 2020

In this study, the effects of KCl(s) and K₂SO₄(s) on the oxidation characteristics of 2.25Cr-1Mo steel were investigated for 500 h in 10O₂ + 10CO₂ (vol%) gas environmen at 650 ℃. Oxidation kinetics were characterized by weight gain, oxide layer thickness, and fitted models for the experiment data were proposed. The fitted models presented considerable agreement with the experimental data. The oxide layer was analyzed using the scanning electron microscope, optical microscope, and energy dispersive X-ray spectroscopy. The oxidation kinetics of 2.25Cr-1Mo steel with KCl and K₂SO₄ coatings showed significantly different oxidation kinetics. KCl accelerated the oxidation rate very much and had linear oxidation behavior. In contrast, K₂SO₄ had no significant effect, which had parabolic kinetics. The oxide layer was commonly composed of Fe₂O₃, Fe₃O₄, and FeCr₂O₄ spinel. KCl strongly accelerated the oxidation rates of 2.25Cr-1Mo steel in the high-temperature oxidation environment. Conversely, K₂SO₄ had little effect on the oxidation rates.

• Journal of the Korean Magnetics Society
• /
• v.17 no.6
• /
• pp.238-241
• /
• 2007

Ni-Cu-Zn ferrites were prepared by the co-precipitation. Physical properties and Microwave absorbing properties were investigated in Ni-Cu-Zn ferrite for the aim of microwave absorbers. From the analysis of X-ray diffraction patterns, we can see that all the particles have only a single phase spinel structure. The loss factor was maximum at sintering temperature $1100^{\circ}C$. The initial permeability of sintered ferrite obtained was an average of 50. We found that the $(Ni_{0.7}Cu_{0.2}Zn_{0.1}O)_{1.02}(Fe_2O_3)_{0.98}$ can be used in ferrite rubber composite microwave absorber when sintering temperature at $1100^{\circ}C$.

• Korean Journal of Materials Research
• /
• v.24 no.1
• /
• pp.53-59
• /
• 2014

The corrosion resistance of submerged entry nozzle (SEN) materials were investigated for high-class steel manufacturing. Composite samples were fabricated by mixing $ZrO_2$, $Al_2O_3$, MgO, mullite, spinel, and carbon. The raw materials were mixed with attrition milling, compacted in a uniaxial pressure of 200MPa and calcined at $1000^{\circ}C$ for 3 h in $N_2$ atmosphere. The bulk density and apparent porosity of the calcined samples were measured by the liquid displacement method in water using Archimedes's principle. The corrosion resistance of the samples were measured by cup test with mold powder at $1550^{\circ}C$ for 2 h. The microstructure and elemental analysis of samples were observed by scanning electron microscopy (SEM), energy dispersive spectrum (EDS), and X-ray diffraction pattern (XRD). The XRD result shows that the starting raw materials were crystalline phase. The microstructure of fabricated specimen was investigated before and after corrosion tests at $1000^{\circ}C$ and $1550^{\circ}C$ for 2h. $ZrO_2$-C composite showed good resistance in the slag corrosion test. Among the composite oxide materials, $ZrO_2-Al_2O_3$-C and $ZrO_2$-MgO-C showed better resistance than $ZrO_2$-C in the slag corrosion test. The diameter variation index of $ZrO_2$-C refractory was 16.1 at $1000^{\circ}C$ for 2 h. The diameter variation index of the $ZrO_2-Al_2O_3$-C refractory was larger than that of the $ZrO_2$-C refractory at $1550^{\circ}C$ for 2 h.

• Korean Journal of Materials Research
• /
• v.24 no.7
• /
• pp.370-374
• /
• 2014

Inorganic pigments have high thermal stability and chemical resistance at high temperature. For these reasons, they are used in clay, paints, plastic, polymers, colored glass and ceramics. $CoAl_2O_4$ nano-powder was synthesized by reverse-micelle processing the mixed precursor(consisting of $Co(NO_3)_2$ and $Al(NO_3)_3$). The $CoAl_2O_4$ was prepared by mixing an aqueous solution at a Co:Al molar ratio of 1:2. The average particle size, and the particle-size distribution, of the powders synthesized by heat treatment (at 900; 1,000; 1,100; and $1,200^{\circ}C$ for 2h) were in the range of 10-20 nm and narrow, respectively. The average size of the synthesized nano-particles increased with increasing water-to-surfactant molar ratio. The synthesized $CoAl_2O_4$ powders were characterized by X-ray diffraction analysis(XRD), field-emission scanning electron microscopy(FE-SEM) and color spectrophotometry. The intensity of X-ray diffraction of the synthesized $CoAl_2O_4$ powder, increased with increasing heating temperature. As the heating temperature increased, crystal-size of the synthesized powder particles increased. As the R-value(water/surfactant) and heating temperature increased, the color of the inorganic pigments changed from dark blue-green to cerulean blue.

• The Journal of the Petrological Society of Korea
• /
• v.20 no.1
• /
• pp.61-75
• /
• 2011

Mantle-derived xenoliths, corresponding to spinel harzburgite and lherzolite in alkali basalts from Jeju Island, are metasomatized to various extents. They contain distinctive secondary orthopyroxene, forming corona or poikilitic textures. It clearly indicate that this secondary orthopyroxene has been produced at the expense of olivine along the grain boundaries and margins, suggesting silica-enriched metasomatic melt infiltrated through grain boundaries. Based on the geotectonic characteristics of Jeju Island and textural characteristics and major elements composition of mantle xenoliths, it is suggested that the silica-enriched melt/fluid could have derived from the ancient subducted slab, possibly in the mantle wedge, implying that the high $SiO_2$ activity in the lithospheric upper mantle beneath Jeju Island at that time.

• Journal of Magnetics
• /
• v.7 no.2
• /
• pp.25-28
• /
• 2002

Slowly cooled $Cu_xFe_{3-x}O_4$ ($\chi$=0.1, 0.2) have been investigated over a temperature range from 82 to 700 K using the M$\ddot{o}$ssbauer technique. X-ray diffraction shows that these have a single-phase cubic spinel structure of lattice parameters $\alpha$=8.396 and 8.398${\AA}$, respectively. Since Cu ions prefer B (octahedral) sites to A (tetrahedral) sites, the ionic distribution is $(Fe)_A[Fe_{2-x}Cu_x]_BO_4$. M$\ddot{o}$ssbauer spectra consisted of two sets of 6-line pattern from. A site in ferric state and B site in ferrous-ferric state. Intensity ratio of B to A subspectra is 1.0 at 82 K and increases to 2.0 at 700 K with increasing temperature. After annealing the samples under vacuum at $450^circ{C}$ for a half hour, x-ray diffraction patterns have the peaks of magnetite- and hematite-phase. Lattice constants of magnetite-phase are 8.395 and 8.392 ${\AA}$ smaller than 8.396 and 8.398 ${\AA}$ before annealing, respectively. M$\ddot{o}$ssbauer spectra reveal the conventional magnetite pattern with the additional hematite pattern. Intensity ratios of B to A subspectra fur magnetite-phase become 1.9-2.0 over all temperature ranges and Cu ions are distributed over A and B sites randomly. Ratios of hematite to total intensity in M$\ddot{o}$ssbauer spectra for $\chi$= 0.1 and $\chi$= 0.2 are 10 and 21%, respectively. These hematite ratios may be due to annealing under vacuum at $450^circ{C}$, which transforms $Cu^{2+}$ ionic states into $Cu^{1+}$. Verwey temperatures far $\chi$= 0.1 and $\chi$= 0.2 are $123\pm2$ K and $128\pm2$ K.

• Journal of the Korean Electrochemical Society
• /
• v.7 no.1
• /
• pp.1-8
• /
• 2004

This paper deals with the recent development of high-voltage cathode materials of mono- and di- metal ions substituted spinel $LiMn_2O_4$ for lithium batteries. $LiCu_xMn_{2-x}O_4(0{\leq}x{\leq}0.5)$ shows reversible intercalation/deintercalation in two potential regions, $3.9\~43\;and\;4.8-5.0V$ and stable electrochemical cycling behavior but with low capacity. $LiNi_{0.5}Mn_{1.5}O_4$ obtained by a sol-gel process delivers a capacity of 127mAh $g^{-1}$ on the first cycle and sustains a value of 124 mAh $g^{-1}$ even after the 60th cycle. The $Li_xCr_yMn_{2-y}O_4(0{\leq}x{\leq}0.5)$ solid-solutions exhibit enhanced specific capacity, larger average voltage, and improved cycling behaviors for low Cr content. $LiCr_yMn_{2-y}O_4$ presents a reversible Li deintercalation process at 4.9V, whose capacity is proportional to the Cr content in the range of $0.25{\leq}x{\leq}0.5$ and delivers higher capacities. $LiM_yCr_{0.5-y}Mn_{1.5}O_4(M=Fe\;or\;Al)$ shows that the capacity retention is lowered compared with lithium manganate. The cumulative capacities obtainable with Al-substitutted materials are less than those with Fe-substituted materials. $LiCr_xNi_{0.5-x}Mn_{1.5}O_4(x=0.1)$ delivers a high initial capacity of 1$152mAh\;g^{-1}$ with excellent cycleability.

• The Korean Journal of Ceramics
• /
• v.2 no.2
• /
• pp.102-110
• /
• 1996

The Mg-PSZ/$Al_2O_3$ fibers were fabricated by the sol-gel method. The added $Al_2O_3$ amounts were varied from 5 to 20 mol%. The phase transformation studies of a drawn Mg-PSZ/$Al_2O_3$ fibers were investigated by use of X-ray diffraction, IR and Raman spectroscopy. Microstructure and tensile strength of fibers were subjected to scanning electron microscopy and tensile strength tester. When $Al_2O_3$ was added to the Mg-PSZ fibers, it was found out from the analysis of XRD patterns and Raman spectra that a small amount of crystalline spinel($MgAl_2O_4$) started to form due to the reaction between $Al_2O_3$ and MgO, at $1000^{\circ}C$, and the phase transformation temperature of $ZrO_2$ crystal phase at different sintering temperatures increased. Also, the rapid grain growth with average size of 2.0 ${\mu}m$ shown in Mg-PSZ fiber at $1500^{\circ}C$ was considerably suppressed to 0.39 ${\mu}m$ by adding $Al_2O_3$ at the same temperature. When the Mg-PSZ/$Al_2O_3$ fibers containing 5 mol% $Al_2O_3$ were sintered $800^{\circ}C$ for 1 hr, average tensile strength of fibers was 0.9 GPs at diameters of 20 to 30 ${\mu}m$, but as the sintering temperatures was increased to $1000^{\circ}C$ for 1 hr, average tensile strength of fibers increased to 1.2 GPa in the same diameter range.

• Journal of the Korean Ceramic Society
• /
• v.20 no.1
• /
• pp.37-42
• /
• 1983

An attempt was made to derive a possible synthetic mechanism of Fluoro-phlogopite (Mica, 4Mg.$Al_2O_3$.$6SiO_2$.$K_2O$.$2MgF_2$) The pevention of fluorine vaporization turned out to be the key in the synthesis of Mica in question.l Consequently the quinary system of Mica was seperately synthesized ; frist 4MgO.$Al_2O_3-6SiO_2$(ternary system) was sintered at 135$0^{\circ}C$ and $K_2O$ and $MgF_2$ were added and second 4MgO.$Al_2O_3-6SiO_2$.$K_2O$ (quarternary system) was heat-treated at 135$0^{\circ}C$ and $MgF_2$ was added. The ternary system resulted in Proto-enstatite Cordierite and Spinel phases while Forsterite and Leucite were shown in the quarternay system . In both methods Fluoro-phlogopite was systhesized but the solid state reactions to form Mica from the ternary system and the quarternary system were different. High temperature reactions in the formation of Mica were investigated employing XRD, DTA and SEM The study of the synthesis of Mica indirectly suggested a method of phase analysis of quinary system(MgO-$Al_2O_3-SiO_2-K_2O-MgF_2$) and quarternary system(MgO-$Al_2O_3-SiO_2-K_2O-MgF_2$) at various temperatures.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.29 no.6
• /
• pp.337-341
• /
• 2016

In this study, $ Ni_{0.79}(Mn_{2.21-x}Cu_x)O_4$ (x=0~0.25) specimens were prepared by using a conventional mixed oxide method. All specimens were sintered in air at $1,200^{\circ}C$ for 12 h and cooled at a rate of $2^{\circ}C/min$ to $800^{\circ}C$, subsequently quenching to room temperature. We investigated the structural and electrical properties of $ Ni_{0.79}(Mn_{2.21-x}Cu_x)O_4$ specimens with variation of CuO amount for the application of NTC thermistors. As results of X-ray diffraction patterns, all specimens showed the formation of a complete solid solution with cubic spinel phase. The relationship between ln ${\rho}$ and the reciprocal of absolute temperature(1/T) for the NTC thermistors was shown linearity, which exhibited the typical NTC thermistor properties. With increasing the amount of CuO, resistivity at room temperature, B-value, and temperature coefficient resistance decreased.