• 대한기계학회논문집
• /
• 제19권4호
• /
• pp.1033-1040
• /
• 1995

To simulate strength reliability and durability of ceramic parts under gas turbine application environments, particle impact damage behaviors in silicon carbide oxidized at 1673 K and 1523 K for 200 hours in atmosphere were investigated. The long-term oxidation produced a slight increase in the static fracture strength. Particle impact caused a spalling of oxide layer. The patterns of spalling and damage induced were dependent upon the property and impact velocity of the particle. Especially, the difference in spalling behaviors induced could be explained by introducing the formation mechanism of lateral crack and elastic-plastic deformation behavior at impact sit. At the low impact velocity regions, the oxidized SiC showed a little increase in the residual strength due to the cushion effect of oxide layer, as compared with the as-received SiC without oxide layer.

• Computers and Concrete
• /
• 제13권3호
• /
• pp.389-409
• /
• 2014

Precast hollow core slabs (HCS) are technically advanced products in the precast concrete industry, widely used in the last years due to their versatility, their multipurpose potential and their low cost. Using three dimensional FEM (Finite Element Method) elements, this study focuses on the stresses induced by the prestressing of steel. In particular the investigation of the spalling crack formation that takes place during prestressing is carried out, since it is important to assure the appropriate necessary margins concerning such stresses. In fact, spalling cracks may spread rapidly towards the web, leading to the detachment of the lower part of the slab. A parametric study takes place, capable of evaluating the influence of the tendon position and of the web width on the spalling stress. Consequently, after an extensive literature review on the topic of soft computing, an optimization of the HCS is performed by means of Genetic Algorithms coupled with 3-D FEM models.

• 한국정밀공학회:학술대회논문집
• /
• 한국정밀공학회 1995년도 춘계학술대회 논문집
• /
• pp.220-226
• /
• 1995

A study on the spalling causes of work roll for cold rolling was performed in the cold rolling mill. Performance of work roll is dependent to a great extent on spalling sothat both roll manufactures and users show great interest in spalling. So this paper shows that spalling origin on the roll surface. As being well known, spalling mostlyoccurred due to developing fatigue fracture originated a crack on a roll. But such spalling can be prevented by proper roll maintenance, The spalling accidents have sharply decreased since 1981 because of the use of ultrasonic test to detect cracks on a roll.

• 전산구조공학
• /
• 제7권3호
• /
• pp.167-176
• /
• 1994

균열전파 현상은 항상 형상이 변화하는 대표적인 문제중의 하나이다. 본 연구는 준-정적 균열전파 현상을 해석하기 위하여 들로네이 특성을 이용한 국지 요소재편 알고리즘을 제시하였다. 이 알고리즘은 요소 재편성과 세분화를 모두 수행할 수 있도록 준비되었다. 적용예로 M 적분법을 사용하여 주로 혼합 모우드로 균열이 전파되는 스폴링 현상을 해석하였다.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2002년도 가을 학술발표회 논문집
• /
• pp.817-822
• /
• 2002

The problem of the crack which occures from the reinforced concrete structure could be caused by the complexed factors. When the crack happen, it caused fatal blemish to manage and maintain the structure such as structural problem, licking, spalling, viewing Even though they study and work hard to solve this kind of problem in the world, there are no countermeasure for perfect prevention of crack. After the crack checked out, a method of repair-reinforcement has been studied and operated actively, Generally, occurance of the crack in the concrete structure could be taken as granted, no need to mention the damage from the crack, domestic construction try to hide it rather than repair basically, In many cases the construction amount for repairing the crack has to be made in the construction area and the amount is very expensive. To save the repaing fee, companys repair it under the meeting of their desire. it can be expected for the effection of the construction. For this reason, we compare a new injection method to solve the demerits of the present method, to save and use the merit of the present method.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2005년도 추계 학술발표회 제17권2호
• /
• pp.535-538
• /
• 2005

The problem of the crack which occures from the reinforced concrete structure. could be caused by the complexed factors. When the crack happen, it caused fatal blemish to manage and maintain the structure such as structural problem, licking, spalling, viewing Even though they study and work hard to solve this kind of problem in the world, there are no countermeasure for perfect prevention of crack. After the crack checked out, a method of repair-reinforcement has been sutdied and operated actively. In this experiment, studied durability of repair material. Experiment wave and durability of epoxy and urethane's were shown good result, and micro cement's durability displayed result that is not good. Result of a repeat tired experiment displayed result that micro cement is bad.

• 한국철도학회:학술대회논문집
• /
• 한국철도학회 2008년도 추계학술대회 논문집
• /
• pp.928-934
• /
• 2008

Resently, Fiber Reinforced Concrete is used for not only preventing crack of concrete but also reinforcing general methods. Steel Fiber and PP(poly-propylene) Fiber are usually used as fiber reinforced materials. However, using these materials for shotcrete on Railway tunnel can cause some problems such as damage of pressure hose and shotcrete rebound. In addition, Steel fiber is an expensive material and it can cause safety problems during applying to shotcrete. PP Fiber can cause a problem in fiber balling during applying to shotcrete railway tunnel construction. A purpose of the research is applying a development of PET(Poly Etylene Terephtalate) fiber by recycling pet bottles to the shotcrete tunnel exposed to explosion spalling. To investigate the reinforcement effect of the PET fiber, some basic tests are accomplished to physical properties and explosion spalling by fire. As a result of the tests, a concrete mixing the PET fiber has stronger resistance effect in the explosion spalling by high temperature than another strong fiber concrete does, and that the former concrete is also equal or more effective on the result of the above tests to physical properties like compression and strain than the latter one is demonstrated.

• 한국정밀공학회지
• /
• 제10권3호
• /
• pp.69-80
• /
• 1993

It is important to prevent roll failure in hot rolling process for reducing maintenance coat and production loss. Roll material and rolling conditions such as the roll force and torque have been intensively investigated to overcome the roll failures. In this study, a computer roll life prediction system under working condition is developed and evaluated on IBM-PC level. The system is composed and fatigue estimation models which are stress analysis, crack propagation, wear and fatigue estimation. Roll damage can be predicted by calculating the stress anplification, crack depth propagation and fatigue level in the roll using this computer model. The developed system is applied to a work roll in actual hot rolling process for reliability evaluation. Roll failures can be diagnosed and the propriety of current working condition can be determined through roll life prediction simulation.

• 콘크리트학회논문집
• /
• 제25권1호
• /
• pp.99-106
• /
• 2013

고속 비상체에 의한 충격을 받는 콘크리트는 그 충격력에 의해 관통, 표면관입 및 배면박리뿐만 아니라 균열의 확산에 의해 나타나는 국부적인 파괴 등 정하중을 받을 때와 다른 파괴거동을 보인다. 이러한 콘크리트의 파괴거동은 비상체의 재료적 특성, 충돌속도, 질량 및 기하학적 구조뿐만 아니라 콘크리트의 재료적 특성, 시험체의 크기 및 두께, 보강재료 및 방법 등 다양한 요인에 의해 영향을 받는다. 이 연구에서는 콘크리트 재료의 압축강도에 따른 표면관입깊이 및 배면박리성상에 대하여 평가하고, 섬유보강에 의한 배면박리억제효과에 대하여 검토하고자 하였다. 그 결과 압축강도의 증가로 인하여 표면관입깊이는 감소하였으며, 이 연구 범위의 결과는 수정 NDRC식 및 US ACE식과 유사한 경향을 나타냈다. 반면, 배면박리억제에 있어 압축강도 증가에 의한 영향은 확인할 수 없었으며, 섬유보강에 의한 인성의 향상을 통하여 배면박리를 억제할 수 있었다.

• 수산해양기술연구
• /
• 제14권2호
• /
• pp.69-78
• /
• 1978

알루미나이징강에 대하여 초기마모영역에서 rolling-sliding 마모시험을 한 결과를 요약하면 다음과 같다. 1) 2차 확산재의 내마모성이 가장 우수하고 처녀재에 비하여 저응력 레벨에서 약 18%, 고응력에서 약 40%의 마모감소를 나타낸다. 2) 2차 확산재는 피복층과 합금층 경계부근의 공공생성으로 인하여 예상보다 내마모성이 낮다. 3) 알루미나이징강의 rolling-sliding 접촉에 의한 마모파양의 형태는 spalling 이며 spalling crack은 합금속의 경계부근에서 발생한다.