• Transactions of the Korean Society of Mechanical Engineers
• /
• v.19 no.4
• /
• pp.1033-1040
• /
• 1995

To simulate strength reliability and durability of ceramic parts under gas turbine application environments, particle impact damage behaviors in silicon carbide oxidized at 1673 K and 1523 K for 200 hours in atmosphere were investigated. The long-term oxidation produced a slight increase in the static fracture strength. Particle impact caused a spalling of oxide layer. The patterns of spalling and damage induced were dependent upon the property and impact velocity of the particle. Especially, the difference in spalling behaviors induced could be explained by introducing the formation mechanism of lateral crack and elastic-plastic deformation behavior at impact sit. At the low impact velocity regions, the oxidized SiC showed a little increase in the residual strength due to the cushion effect of oxide layer, as compared with the as-received SiC without oxide layer.

• Computers and Concrete
• /
• v.13 no.3
• /
• pp.389-409
• /
• 2014

Precast hollow core slabs (HCS) are technically advanced products in the precast concrete industry, widely used in the last years due to their versatility, their multipurpose potential and their low cost. Using three dimensional FEM (Finite Element Method) elements, this study focuses on the stresses induced by the prestressing of steel. In particular the investigation of the spalling crack formation that takes place during prestressing is carried out, since it is important to assure the appropriate necessary margins concerning such stresses. In fact, spalling cracks may spread rapidly towards the web, leading to the detachment of the lower part of the slab. A parametric study takes place, capable of evaluating the influence of the tendon position and of the web width on the spalling stress. Consequently, after an extensive literature review on the topic of soft computing, an optimization of the HCS is performed by means of Genetic Algorithms coupled with 3-D FEM models.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 1995.04b
• /
• pp.220-226
• /
• 1995

A study on the spalling causes of work roll for cold rolling was performed in the cold rolling mill. Performance of work roll is dependent to a great extent on spalling sothat both roll manufactures and users show great interest in spalling. So this paper shows that spalling origin on the roll surface. As being well known, spalling mostlyoccurred due to developing fatigue fracture originated a crack on a roll. But such spalling can be prevented by proper roll maintenance, The spalling accidents have sharply decreased since 1981 because of the use of ultrasonic test to detect cracks on a roll.

• Computational Structural Engineering
• /
• v.7 no.3
• /
• pp.167-176
• /
• 1994

A local remeshing algorithm using Delaunay property is developed for the analysis on the phenomenon of quasi-static crack propagation, which is a typical problem of accompanying constantly varying geometry. The algorithm performs both remeshing and refinement. The use of M-integral is demonstrated to simulate crack propagation under mixed mode with the edge spalling problem.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2002.10a
• /
• pp.817-822
• /
• 2002

The problem of the crack which occures from the reinforced concrete structure could be caused by the complexed factors. When the crack happen, it caused fatal blemish to manage and maintain the structure such as structural problem, licking, spalling, viewing Even though they study and work hard to solve this kind of problem in the world, there are no countermeasure for perfect prevention of crack. After the crack checked out, a method of repair-reinforcement has been studied and operated actively, Generally, occurance of the crack in the concrete structure could be taken as granted, no need to mention the damage from the crack, domestic construction try to hide it rather than repair basically, In many cases the construction amount for repairing the crack has to be made in the construction area and the amount is very expensive. To save the repaing fee, companys repair it under the meeting of their desire. it can be expected for the effection of the construction. For this reason, we compare a new injection method to solve the demerits of the present method, to save and use the merit of the present method.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2005.11a
• /
• pp.535-538
• /
• 2005

The problem of the crack which occures from the reinforced concrete structure. could be caused by the complexed factors. When the crack happen, it caused fatal blemish to manage and maintain the structure such as structural problem, licking, spalling, viewing Even though they study and work hard to solve this kind of problem in the world, there are no countermeasure for perfect prevention of crack. After the crack checked out, a method of repair-reinforcement has been sutdied and operated actively. In this experiment, studied durability of repair material. Experiment wave and durability of epoxy and urethane's were shown good result, and micro cement's durability displayed result that is not good. Result of a repeat tired experiment displayed result that micro cement is bad.

• Proceedings of the KSR Conference
• /
• 2008.11b
• /
• pp.928-934
• /
• 2008

Resently, Fiber Reinforced Concrete is used for not only preventing crack of concrete but also reinforcing general methods. Steel Fiber and PP(poly-propylene) Fiber are usually used as fiber reinforced materials. However, using these materials for shotcrete on Railway tunnel can cause some problems such as damage of pressure hose and shotcrete rebound. In addition, Steel fiber is an expensive material and it can cause safety problems during applying to shotcrete. PP Fiber can cause a problem in fiber balling during applying to shotcrete railway tunnel construction. A purpose of the research is applying a development of PET(Poly Etylene Terephtalate) fiber by recycling pet bottles to the shotcrete tunnel exposed to explosion spalling. To investigate the reinforcement effect of the PET fiber, some basic tests are accomplished to physical properties and explosion spalling by fire. As a result of the tests, a concrete mixing the PET fiber has stronger resistance effect in the explosion spalling by high temperature than another strong fiber concrete does, and that the former concrete is also equal or more effective on the result of the above tests to physical properties like compression and strain than the latter one is demonstrated.

• Journal of the Korean Society for Precision Engineering
• /
• v.10 no.3
• /
• pp.69-80
• /
• 1993

It is important to prevent roll failure in hot rolling process for reducing maintenance coat and production loss. Roll material and rolling conditions such as the roll force and torque have been intensively investigated to overcome the roll failures. In this study, a computer roll life prediction system under working condition is developed and evaluated on IBM-PC level. The system is composed and fatigue estimation models which are stress analysis, crack propagation, wear and fatigue estimation. Roll damage can be predicted by calculating the stress anplification, crack depth propagation and fatigue level in the roll using this computer model. The developed system is applied to a work roll in actual hot rolling process for reliability evaluation. Roll failures can be diagnosed and the propriety of current working condition can be determined through roll life prediction simulation.

• Journal of the Korea Concrete Institute
• /
• v.25 no.1
• /
• pp.99-106
• /
• 2013

Concrete materials subjected to impact by high velocity projectiles exhibit responses that differ from those when they are under static loading. Projectiles generate localized effects characterized by penetration of front, spalling of rear and perforation as well as more widespread crack propagation. The magnitude of damage depends on a variety of factors such as material properties of the projectile, impact velocity, the mass and geometry as well as the material properties of concrete specimen size and thickness, reinforcement materials type and method of the concrete target. In this study, penetration depth of front, spalling thickness of rear and effect of spalling suppression of concrete by fiber reinforcement was evaluated according to compressive strength of concrete. As a result, it was similar to results of the modified NDRC formula and US ACE formula that the more compressive strength is increased, the penetration depth of front is suppressed. On the other hand, the increase in compressive strength of concrete does not affect spalling of rear suppression. Spalling of rear is controlled by the increase of flexural, tensile strength and deformation capacity.

• Journal of the Korean Society of Fisheries and Ocean Technology
• /
• v.14 no.2
• /
• pp.69-78
• /
• 1978

It is well known that the aluminizing steel is excellent in corrosion resistance and heat resistance. Therefore it has been used as boiler parts, heat exchanger parts and guide rails which are used under comparatively simple conditions. Recently, it has been noticed that aluminizing steel has high resistance to various atmosphere, high temperature oxidation and seawater resistance. So its usage has been extended widely to the production of parts such as intake and exhaust valve of internal combustion engine, turbine blade and pipelines On ships which required such properties. It is considered that aluminium coated steel is excellent in wear resistance because of high hardness on main ingredient FezAIs of Fe-AI alloy layer existed in diffusion coating layer. And it will beused as a new material taking wear resitance with seawater resistance in marine field. However it is difficult to findout any report concering the wear behaviors or properties of alum in izing steel. In this study the experiment was carried out under the condition of rolling-sliding contact using an Amsler-type wear testing machine at 0.80, 0.91, 1. 10, 1. 25% of slip ratio and 55.43, 78.38, 110.85 kg/mm^2 of Hertz's contact stress in run-in period for the purpose of service-ability test of aluminizing steel as a wear resisting material and obtaining the available design data. The followings are the obtained results from the experimen tal study; 1) The 2nd diffusion material has most excellent wear resistance. This material has brought out about 18% decrease of wear weight in a lower friction load level and 40~G decrease in a higher level comparing to the raw material. 2) Satisfactory effect of wear resistivity cannot be much expected in 2nd diffusion specimens. This is considered due to the formation of fine void in the alloy layer near the boundary to the aluminium layer. 3) Fracture on friction surface of aluminizing steel by the rolling-sliding contact is spalling, and spalling crack occurres initially beneath the specimen surface near the boundary in diffusion coating layer.