• Polymer(Korea)
• /
• v.36 no.4
• /
• pp.531-535
• /
• 2012

Conductive polyaniline (PANI) nanofibers in UV-curable resin were used for a transparent conductive film. The emeraldine-salt PANI (ES-PANI) nanofibers were prepared by chemical oxidation polymerization of aniline, which could be changed into emeraldine-base PANI by dedoping. EB-PANI nanofibers as a precursor for conductive fillers were thereby transformed into re-dpoed PANI (rES-PANI) by dodecylbenzenesulfonic acid in the UV-curable resin solution. rES-PANI nanofibers have high conductivity and long-term stability in the solution without a defect of nanostructure. The resulting conductive resin solution was proved to be highly stable where no precipitation of rES-PANI fillers was observed over a period of 3 months. The transparent film was spin-casted on a poly(methyl methacrylate) sheet of thickness ca. $5{\mu}m$. A surface resistance of $6.5{\times}10^8{\Omega}/sq$ and transmittance at 550 nm of 91.1% were obtained for the film prepared with a concentration of 1.4 wt% rES-PANI nanofibers in the solution. This transformation process of rES-PANI from ES-PANI by dedoping-redoping can be an alternative method for the preparation of an antistatic protection film with controllable surface resistance and optical transparencies with the PANI concentration in UV-curable solution.

• Polymer(Korea)
• /
• v.34 no.2
• /
• pp.126-132
• /
• 2010

A cation-exchange nanofiber poly(vinylidene fluoride) (PVdF) membrane was prepared by a radiation-induced graft polymerization (RIGP) of sodium styrene sulfonate (NaSS) in the presence of the polymerizable access agents in methanol solution. The used polymerizable access agents include styrene, acrylic acid, and vinyl pyrrolidone. The anion-exchange nanofiber PVdF membrane was also prepared by RIGP of glycidyl methacrylate (GMA) and its subsequent chemical modification. The successful preparations of cation- and anion-exchange PVdF membranes were confirmed via SEM, XPS and thermal analysis. The content of the grafting yield, ion-exchange group, and water uptake was in the range of 30.0~32.3%, 2.81~3.01 mmol/g and 66.6~147%, respectively. The proton conductivity at 20$^{\circ}C$ was in the range of 0.020~0.053 S/cm. From the result, the prepared ionexchange PVdF membrane can be used as a separator in battery cells.

• Applied Chemistry for Engineering
• /
• v.10 no.4
• /
• pp.502-508
• /
• 1999

We prepared non-porous membrane on the $Al_2O_3$ substrate with the different pore by the size by the plasma polymerization of $CHF_3$. We studied the permeability characteristics of membrane by Ar treatment and the effect of substrate pore size on gas permeation mechanism. The selectivity was increased with Ar plasma treatment time and rf-power near the substrate to the cathode while the permeability was decreased. It was observed that the solution-diffusion model would be applied to non-porous layers while it is applied Knudsen diffusion model to the substrate. From the experimental observation, it could be concluded that the pore size of $Al_2O_3$ membrane influenced on the permeability and the selectivity.

• Polymer(Korea)
• /
• v.36 no.5
• /
• pp.599-605
• /
• 2012

The physicochemical properties such as surface hardness, solvent mechanical wear resistance, and resistance to scratch properties of poly(3,4-ethylenedioxythiophene) (PEDOT) thin film prepared by vapor phase polymerization (VPP) was effectively improved by post-treatment of various metal alkoxide sol solutions. Metal oxide layer derived from sol-gel process of metal alkoxide was generated on the PEDOT thin film layer by VPP, resulting in improving mechanical properties of the conductive thin films without any deterioration of their original surface resistance. Several kinds of silicone and titanium alkoxide derivatives with various functional groups were used as metal alkoxide sol sources. Among them, PEDOT-metal oxide composite thin film derived tetraethyl orthosilicate showed the best performance in the terms of surface resistance, transmittance, and various physicochemical properties. The effect of metal alkoxide content in washing solution, oxidant content and drying temperature have been investigated in order to optimize the various properties of PEDOT-metal oxide composite thin film.

• Korean Journal of Fisheries and Aquatic Sciences
• /
• v.32 no.5
• /
• pp.664-668
• /
• 1999

The extracting conditions of alginates from sea tangle were evaluated by measuring water vapor permeability (WVP) and tensile properties of alginate film to obtain basic data of making an edible and biodegradable film. The alginates were extracted with $1\%,\;3\%$ and $5\%$ sodium carbonate ($Na_2CO_3$) for 1, 3, 5 and 10 hours, and the alginate film was made with various plasticizers. The higher concentration of $Na_2CO_3$ solution showed the lower viscosity and polymerization degree of alginate and the film prepared with alginates having low viscosity showed the higher WVP. The extracting hours had little effect on the WVP and the elongation of alginate film, but the polymerization degree of alginates directly affected the tensile strength of the film. The addition of sorbitol and polyethylene glycol as a plasticizer lowered the WVPs and the elongation of alginate film.

• Proceedings of the Korean Fiber Society Conference
• /
• 2003.10a
• /
• pp.23-24
• /
• 2003

We synthesized a poly[2-(2'-hydroxyphenyl) benzoxazole] under the two step procedures of Suzuki coupling polymerization with corresponding monomers followed by the deprotection of benzyl group. The polymer in DMF solution is applicable to colorimetric sensing fluoride anion, which shows a color change from colorless to yellow. High sensitivity to fluoride anion compared to other anions such as phosphate, chloride, and sulfate is ascribed to the high coordination ability of the 2-(2'-hydroxy phenyl)benzoxazole moiety in the polymer chain. Emission shift by metal cations, which can be applied to fluorescent sensing w as also observed in the polymer solution.

• Journal of the Korean Applied Science and Technology
• /
• v.17 no.2
• /
• pp.76-82
• /
• 2000

The relative reactivities of branched and linear polycarbonates were investigated by measuring unreacted chloroformate concentration. It was found that the polymerization for the branched polymer proceeded ca. 10 times faster than that for the linear polymers. The effect of catalyst on a condensation step was studied by changing the amount of TEA (triethylamine) at $t_{0}$ and $t_{60}$ with keeping constant amount of TEA. The viscosity average molecular weight for the obtained branched polycarbonates were measured and compared with those of linear polycarbonates. It was found that the viscosity molecular weights of the obtained polymers decreased nonlinearly as wt % of added oligomer increased. The solution viscosities in methylenechloride for linear and branched polycarbonate increased nonlinearly as the content of polymer increased.

• Journal of the Korean Applied Science and Technology
• /
• v.19 no.4
• /
• pp.335-338
• /
• 2002

A new process for polymeric gate insulator in field-effect transistors was proposed. Fourier transform infrared absorption spectra were measured in order to identify ODPA-ODA polyimide. Its breakdown field and electrical conductivity were measured. All-organic thin-film transistors with a stacked-inverted top-contact structure were fabricated to demonstrate that thermally evaporated polyimide films could be used as a gate insulator. As a result, the transistor performances with evaporated polyimide was similar with spin-coated polyimide. It seems that the mass-productive in-situ solution-free processes for all-organic thin-film transistors are possible by using the proposed method without vacuum breaking.

• Journal of the Korean Chemical Society
• /
• v.16 no.1
• /
• pp.50-55
• /
• 1972

The mechanical degradation of $poly(\alpha-methyl$ styrene) in several mixed solvents (chlorobenzene-n-butyl alcohol, chlorobenzene-sec-butyl alcohol, chlorobenzene-Kerosene, chlorobenzene-methylketone) was studied using the capillary flow method. The velocity constant of scission reaction (K) and the limited degree of polymerization (g) were compared at the same value of [${\eta}$], which is considered as the parameter of molecular dimension of polymers in solution. As results, (K) did not change much, even if the species and the volume fraction of poor(non-) solvents changed, while the value of (g) changed according to the species of poor (non-) solvents and the value of [${\eta}$] these results were discussed.

• The Korean Journal of Ceramics
• /
• v.5 no.3
• /
• pp.265-269
• /
• 1999

Polyethylene was modified with silanol groups on its surface by photografting of vinyltrimethoxysilane in vapor phase by using benzophenon as a polymerization initiator and by hydrolyzing the methoxysilane groups into the silanol groups with HCI solution. The modified polyethylene formed a dense and homogeneous apatite layer on its surface in a solution with ion concentrations 1.5 times those of human blood plasma within 21 days. This kind of biomimetic process could provide techniques for fabricating apatite-polymer composites with three dimensional structure analogous to the natural bone.