• Journal of the Korean Graphic Arts Communication Society
• /
• v.27 no.1
• /
• pp.49-58
• /
• 2009

Computer to plate technology(CTP) have become fully commercial. The current wide range of computer to plate system and plate makes many potential customers insecure. This process which began around 1995 has now been successfully completed, so that a wide variety of high performance systems is available. The computer to plate method of producing printing plates eliminates films from the production process, thus reducing costs and shortening production times. To discover the optimization formulation of sensitized materials we were changed formulation of resin and violet solution in thermal sensitizers. Also we were analyzed the CTP plate's surface and the result of coating and development at each sample. we were analyzed the effects of development condition as temperature and speed, the plate wear of printing test in C, M, Y, Bk ink. This paper aims to find out suitable ways that we can develop a domestic CTP plate.

• Corrosion Science and Technology
• /
• v.6 no.3
• /
• pp.133-139
• /
• 2007

Nickel powder was coated with aluminum nitrate solution to increase the thermal stability of a porous nickel support and control the nickel content in the Pd-Cu-Ni ternary alloyed membrane. Raw nickel powder and alumina coated nickel powder were uniaxialy pressed by home made press with metal cylindrical mold. Though the used nickel powder prepared by pulsed wire evaporation (PWE) method has a good thermal stability, the porous nickel support was too much sintered and the pores of porous nickel support was plugged at high temperature (over $800^{\circ}C$) making it not suitable for the porous support of a palladium based composite membrane. In order to overcome this problem, the nickel powder was coated by alumina and alumina modified porous nickel support resists up to $1000^{\circ}C$ without pore destruction. Furthermore, the compositions of Pd-Cu-Ni ternary alloy membrane prepared by magnetron sputtering and Cu-reflow could be controlled by not only Cu-reflow temperature but also alumina coating amount. SEM analysis and mercury porosimeter analysis evidenced that the alumina coated on the surface of nickel powder interrupted nickel sintering.

• Corrosion Science and Technology
• /
• v.10 no.1
• /
• pp.24-29
• /
• 2011

The greatest purpose of chromate treatment is to improve anti-corrosion by stabilizing a metal surface. Because metal surface forms a compound by absorbing oxygen or water in the air by being generally unstable, it is necessary to improve anti-corrosion of the metal by forming the metal surface with a stable film. When considering the economical efficiency and requirements together because the film of the metal surface treated with chromate has good anti-corrosion and the stability also in the air by being compact and strong, Chromate treatment has been used most up to the electronics industry from the auto industry. However, these days, because hexavalent chromium is both a toxic agent to be able to cause cancers and deadly poisonous environmental pollutant, the strong legal controls on its use is being imposed all over the world. Because of this reason, a new anti-corrosion method is being required. Also, by users' various demands, the passivations that have recently been developed require various characteristics such as conductivity, chemical resistance, alkali cleaning resistance as well as anti-corrosion. We could confirm the results such as excellent anti-corrosion compared to chromate, conductivity, chemical resistance and detergent resistance as the result of analysis of various characteristics of the galvannealed sheet steels coated with Cr-Free solution developed in this research.

• 한국정보디스플레이학회:학술대회논문집
• /
• 2008.10a
• /
• pp.1638-1641
• /
• 2008

We have investigated the effectiveness of a gravure printing method for the fabrication of organic light-emitting diode (OLED) and Organic Thin Film Transistor (OTFT). Printing of the organic layers was performed with a small-scale gravure coating machine, while the metallic layers were vacuum-evaporated. Devices with gravure-printed layers are at least comparable with the spin-coated devices. Effects of the solvent formulation and surface energy mismatch between the organic layer materials on the printed patterns and device performance were discussed. We will present the initial design and experimental data of OTFT fabricated by roll-type soft contact transfer process.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2004.11a
• /
• pp.37-40
• /
• 2004

CdTe nanoparticles were synthesized in aqueous solution by colloidal method. The absorption and photoluminescence(PL) spectrum of the synthesized CdTe nanoparticles revealed the strong exitonic peak in the visible region. Photocurrent of CdTe nanoparticles were observed in the structure of Al/CdTe/ITO that was fabricated by spin coating of CdTe nanoparticles. The wavelength dependence of photocurrent was very similar to the absorption spectrum, indicating the charges generated by the absorption of photons give direct contribution to photocurrent. This study suggests that CdTe nanoparticles are very prospective materials for optoelectronics.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2000.05b
• /
• pp.34-38
• /
• 2000

Recently, the ceramics of high permittivity are applied to DRAM and FRAM. In this study, (Ba, Sr)$TiO_3$ (BST) ceramics thin films were prepared by Sol-Gel method. BST solution was made and spin-coated on Pt/$SiO_2$/Si substrate at 4000 [rpm] for 10 seconds. Coated specimens were dried at $150[^{\circ}C]$ for 5 minutes. Coating process was repeated 3 times and then sintered at $750[^{\circ}C]$ for 30 minutes. Each specimen was analyzed structure and electrical characteristics by Fractal Process. Thickness of BST ceramics thin films are about $2000{\AA}$. Dielectric constant and loss of thin films was little decreased at 1[KHz] - 1[MHz]. Dielectric constant and loss to frequency were 250 and 0.02 in BST3. The property of leakage current as the realation between the current and the voltage was that change of the leakage current was stable when the applied voltage was 0~3[V].

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2010.06a
• /
• pp.181-181
• /
• 2010

Few-walled carbon nanotubes (FWNTs)-based field emitters with long term stability are fabricated by using a spray method. Tetraethylorthosilicate (TEOS) sol as a binder was mixed with dispersed solution of FWNTs to enhance the adhesion of FWNTs on the cathode substrate. Due to the strong intermolecular interaction of TEOS to the functional groups attached on CNTs and substrate, CNTs are tightly adhered to the cathode electrode when heat treatment is performed at $150^{\circ}C$ for 1 hour, resulting in a stable electron emission of CNT emitters for long time. Excellent field emission characteristics were exhibited, with a large field enhancement factor and low turn-on voltage, comparable to those of CNT emitters fabricated by a screen printing of CNT paste. Therefore, FWNTs / TEOS hybrid films could be utilized as an alternative for the efficient and reliable field emitters.

• Clean Technology
• /
• v.23 no.3
• /
• pp.314-324
• /
• 2017

To verify the viability of Co, Ru and Zr-based catalyst for $CO_2$ (dry) reforming reaction, catalysts were fabricated using cordierite, silicon carbide and rota monolithic substrates, and they were compared with the conventional $Co-Ru-Zr/SiO_2$ catalyst in terms of performance and durability. Cordierite monolith was showed high activity with the least amount of active component. In addition, when Cordierite monolith was coated with Co-Ru-Zr in various ways, most excellent performance was showed at a precursor solution coating method. In particular, when 0.9 wt% Co-Ru-Zr/Cordierite was used for reaction, it was observed that 95% $CO_2$ conversion was maintained for 300 h at $900^{\circ}C$.

• Proceedings of the KIEE Conference
• /
• 1995.11a
• /
• pp.335-337
• /
• 1995

In this study, $Pb(Zr_{0.52}Ti_{0.48})O_3$ ceramic thin films were fabricated from an alkoxide-based by Sol-Gel method. $Pb(Zr_{0.52}Ti_{0.48})O_3$ stock solution was made and spin-coated on the $Pt/SiO_2/Si$ substrate at 4000[rpm] for 30[sec]. Coated specimens were dried at 400[$^{\circ}C$] for 10 [min]. The coating process was repeated 4 times and then heat-treated at 500$\sim$800[$^{\circ}C$], 1 hour. The final thickness of the thin films were about 3000[A]. The crystallinity and microstructure of the thin films were investigated for varing the sintering condition. The ferroelectric perovskite' phases precipitated under the sintering of 700[$^{\circ}C$] for 1 hours. In the $Pb(Zr_{0.52}Ti_{0.48})O_3$ thin films sintered at 700[$^{\circ}C$] for 1 hour, dielectric constant and dielectric loss were 2133, 2.2[%] at room temperature, respectively. $Pb(Zr_{0.52}Ti_{0.48})O_3$ thin film capacitors having good dielectric and electrical properties are expected for the application to the dielectric material of DRAM.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2010.05a
• /
• pp.24.1-24.1
• /
• 2010

In practical operation, the exposed surfaces may get dirty thus degrade the performance of devices. So the combination of self cleaning and antireflection is very desirable for use in outdoor photovoltaic and displaying devices, self cleaning windows and car windshields. For the purpose of self cleaning, the surface needs to be either superhydrophobic or superhydrophilic. However, in practice AR in the visible region and self cleaning are a pair of competitive properties. To satisfy the requirements for superhydrophobic or superhydrophilic surfaces, high surface roughness is required. But it usually cause severely light scattering. Photo-responsive coatings (TiO2, ZnO etc.) can lead to superhydrophilic. However, the refractive indices are high. Thus for porous structure, controlling pore size in the underwavelength scale to reduce the light scattering is very crucial for highly transparent and self cleaning antireflection coating. Herein, we demonstrate a simple method to make high performance broadband antireflection layer on the glass surface, by "carving" the surface by hot alkali solution. Etched glass has superhydrophilic surface. By chemical modification, it turns to superhydrophobic. Enhanced transparency (up to 97%) in a broad wavelength range was obtained by short time etching. Also antifogging effect has been demonstrated, which may offer advantage for devices working at high humidity environment or underwater. Compositional dependence of the properties was observed by comparing three different commercially available glasses.