• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.07a
• /
• pp.377-380
• /
• 2001

The BST thin films to composite (Ba$\sub$x/Sr$\sub$l-x/)TiO$_3$ using sol-gel method were fabricated on Pt/Ti/SiO$_2$/Si substrate. The thin film capacitor to be ferroelectric materials was investigated by structural and electrical properties. BST solution was composited by moi ratio, and then spin-coated (from 3 times to 5 times coating on Pt/SiO$_2$/Si substrate. Thickness of BST ceramics thin films are about 2600∼2800[${\AA}$] in 3 times deposition. The property of leakage current was stable when the applied voltage was 3[V]. Leakage current of 3 times coated BST thin film was 10$\^$-9/∼10$\^$-11/[A] at 0∼3[V].

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2002.07b
• /
• pp.988-991
• /
• 2002

ITO (Indium Tin Oxide) powder was synthesized by precipitation method. ITO colloidal solutions for coating on glass were fabricated by ball milling method. ITO colloidal solution with variation of concentration from 2% to 15% were fabricated ITO thin film measured sheet resistance and transmittance. In the result, 15% sol showed the lowest value of sheet resistance, 2% sol showed the highest value of transmittance. In addition, effect of annealing temperature and $SiO_2$ film were investigated.

• Proceedings of the KIEE Conference
• /
• 2006.07d
• /
• pp.2209-2210
• /
• 2006

In this paper, PZT(20/80) thick films were fabricated by the screen-printing method. And the PZT(80/20) coating solution was synthesized by the sol-gel method. PZT(20/80) thick films were screen-printed on the alumina substrates. PZT(80/20) thin film was spin-coaled on the PZT(20/80) thick films to obtain densification. And the structural and electrical properties of PZT thick films were investigated with variation of sintering temperature. The PZT specimen sintered at $650^{\circ}C$ showed good relative dielectric constant of 219 and dielectric loss of 2.45%. Also the remanent polarization and the coercive field wore 16.48 ${\mu}C/cm^2$ and 35.48kV/cm, respectively.

• Proceedings of the KIEE Conference
• /
• 2006.07d
• /
• pp.2211-2212
• /
• 2006

Ferroelectric PZT (70/30) thick films were fabricated by the screen printing method. And the PZT (30/70) precusor solution were infiltrated by the spin-coating method on the PZT thick films to obtain a densification. All PZT thick films were sintered at $1050^{\circ}C$ for 10 min. Structural properties, such as crystalline structure, microstructures and compositional ratio, of PZT thick films were investigated with the variation of the number of sol coatings using XRD, SEM and EDS, respectively. All PZT thick films exhibited a perovskite polycrystalline structure without a pyrochloer phase. The thickness of PZT thick films, 4-times screen-printed, was approximately $60{\mu}m$. And the densification of the PZT thick films increased with increasing the number of sol coatings.

• Proceedings of the KIEE Conference
• /
• 2006.07a
• /
• pp.577-578
• /
• 2006

In this paper, PZT(20/80) thick films were fabricated by the screen-printing method. And the PZT(80/20) coating solution was synthesized by the sol-gel method. PZT(20/80) thick films were screen-printed on the alumina substrates. PZT(80/20) thin film was spin-coated on the PZT(20/80) thick films to obtain densification. And the structural and electrical properties of PZT thick films were investigated with variation of sintering temperature. The PZT specimen sintered at 650f showed good relative dielectric constant of 219 and dielectric loss of 2.45%. Also the remanent polarization and the coercive field were 16.48${\mu}C/cm^2$ and 35.48kV/cm, respectively.

• Proceedings of the KIEE Conference
• /
• 2006.07a
• /
• pp.579-580
• /
• 2006

Ferroelectric PZT (70/30) thick films were fabricated by the screen printing method. And the PZT (30/70) Precusor solution were infiltrated by the spin-coating method on the PZT thick films to obtain a densification. All PZT thick films were sintered at $1050^{\circ}C$ for 10min. Structural properties, such as crystalline structure, microstructures and compositional ratio, of PZT thick films were investigated with the variation of the number of sol coatings using XRD, SEM and EDS, respectively. All PZT thick films exhibited a perovskite polycrystalline structure without a pyrochloer phase. The thickness of PZT thick films, 4-times screen-printed, was approximately 60fm. And the densification of the PZT thick films increased with increasing the number of sol coatings.

• 한국전산유체공학회:학술대회논문집
• /
• 2007.10a
• /
• pp.39-44
• /
• 2007

A similarity solution of the Navier-Stokes equation for the axisymmetric stagnation flow near a plane wall coated with a magnetic fluid of uniform thickness is constructed. The shape functions representing the flow in two (magnetic and normal) fluid layer are determined from a third order boundary value problem, which is solved by the Runge-Kutta method with two shooting parameters. Features of the flow including streamline pattern and interface velocity are investigated for the varying values of density ratio, viscosity ratio, and Reynolds number. The results for the interface and wall shear stress, boundary layer and displacement thickness are also presented.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1996.11a
• /
• pp.175-179
• /
• 1996

Ferroelectric SrBi$_2$Ta$_2$$O_{9}$ thin films were fabricated by tole Sol-Gel method using a spin-on coating with MOD(Metal Organic Dccomposition) solution on Pt/Ti/SiO$_2$/Si(100) substratcs. The films were anncalcd at 80$0^{\circ}C$ for one hour in oxygen atmosphere. The effects of Bi/Ti mole ratios on crystalline orientations, surface morphologies, and subface composition SBT thin films with a Bi/Ta mole ratios from 1.1 to 1.3 were investigated using X-ray Diffractometry (XRD). Atomic Force (AFM), X-Ray Photoelectron Spectroscopy(XPS). Ferroelectric properties of these films were also measured.d.

• Proceedings of the KIEE Conference
• /
• 2006.07b
• /
• pp.1243-1244
• /
• 2006

In this paper, PZT(20/80) thick films were fabricated by the screen-printing method. And the PZT(80/20) coating solution was synthesized by the sol-gel method. PZT(20/80) thick films were screen-printed on the alumina substrates. PZT(80/20) thin film was spin-coated on the PZT(20/80) thick films to obtain densification. And the structural and electrical properties of PZT thick films were investigated with variation of sintering temperature. The PZT specimen sintered at $650^{\circ}C$ showed good relative dielectric constant of 219 and dielectric loss of 2.45%. Also the remanent polarization and the coercive field were $16.48{\mu}C/cm^2$ and 35.48kV/cm, respectively.

• Proceedings of the KIEE Conference
• /
• 2006.07b
• /
• pp.1245-1246
• /
• 2006

Ferroelectric PZT (70/30) thick films were fabricated by the screen printing method. And the PZT (30/70) precusor solution were infiltrated by the spin-coating method on the PZT thick films to obtain a densification. All PZT thick films were sintered at $1050^{\circ}C$ for 10 min. Structural properties, such as crystalline structure, microstructures and compositional ratio, of PZT thick films were investigated with the variation of the number of sol coatings using XRD, SEM and EDS, respectively. All PZT thick films exhibited a perovskite polycrystalline structure without a pyrochloer phase. The thickness of PZT thick films, 4-times screen-printed, was approximately $60{\mu}m$. And the densification of the PZT thick films increased with increasing the number of sol coatings.