• Korean Chemical Engineering Research
• /
• v.46 no.2
• /
• pp.402-407
• /
• 2008

Recent popularity in mobile electronics requires higher standard on the mechanical strength of electronic packaging. Thus, the method of soldering between chip and substrate in electronic packaging process is changing from conventional method using intermetallic compound to a new method using organic solderability preservative (OSP) in order to improve the stability and the reliability of final product. Since current organic solder preservatives have several serious problems like thermo-stability during packaging process, however, it is necessary to develop new OSPs having thermo-stability. The main purpose of this study is to investigate the effect of MeOH/IPA (Isopropyl alcohol) ratio on the fluxing of a new OSP, developed in previous research, andto find out an optimum formulation of flux components for the application of the OSP in current packaging process. As a result of this study, it was revealed that higher MeOH/IPA ratio in flux showed better performance of fluxing a new OSP.

• Korean Chemical Engineering Research
• /
• v.49 no.2
• /
• pp.161-167
• /
• 2011

Recent popularity in mobile electronics requires higher standard on the mechanical strength of electronic packaging. Thus, the method of soldering between chip and substrate in electronic packaging process is changing from conventional method using intermetallic compound to a new method using organic solderability preservatives (OSP) in order to improve the stability and the reliability of final product. Since current OSPs have several serious problems like thermo-stability during packaging process, however, it is necessary to develop new OSPs having thermo-stability. The main purpose of this study is to develop various thermo-stable OSPs based upon poly(vinyl pyridine-co- methylmethacrylate) and to evaluate their anti-oxidation property protecting Cu pad, thermo-stability and solubility to acid- or alcohol-containing aqueous solution during pos-fluxing. All OSPs showed not only good anti-oxidation property, thermo-stability and solubility but also more advantages like low cost, less odor, and less hygroscopic.

• Conservation Science in Museum
• /
• v.27
• /
• pp.147-164
• /
• 2022

Over 200,000 Korean cultural heritage items are currently located abroad. They have made their way to 22 countries under different circumstances and with unique backgrounds. While some of them continue to contribute to promoting Korean culture around the world, others cannot be exhibited due to damage or poor condition. In view of these circumstances, the Overseas Korean Cultural Heritage Foundation (OKCHF) has since 2013 provided museums and art galleries abroad with support for the conservation, restoration, and utilization of the Korean cultural heritage items that they house. As a part of these efforts and on the occasion of the 120th anniversary of the diplomatic relationship between the Republic of Korea and the Kingdom of Belgium in 2021, a gilt-bronze case for acupuncture needles dating to the Goryeo period (918-1392) from the collection of the Royal Museums of Art and History (RMAH), Belgium was brought to Korea for conservation treatment. The primary purpose of this conservation treatment was to restore the original form of the relic and slow to the degree possible the progress of corrosion. The conservation treatment of the gilt-bronze case followed the fundamental order of conservation treatment: removal of corrosive substances, stabilization, and reinforcement. Since this was the first case of restoring metallic cultural properties under the abovementioned support program by the OKCHF, special methodologies distinct from those available in overseas institutions were required. Diverse scientific methods (e.g., X-ray inspection, CT scanning, 3D microscopy) were applied to identify the metalcraft techniques used in the Goryeo period. The analysis found that several designs, including lotus and scrollwork, were exquisitely engraved on the surface of the case by making dots using a round-edged chisel. A bronze plate engraved with designs was rolled into a cylindrical form. The ends were overlapped by 2 to 3 centimeters and then attached to each other by silver soldering. The overlapping ends were welded flat with nearly no gaps. As the final process in the production, the case was lavishly gilt with gold powder using amalgam gilding. The conservation treatment of the gilt-bronze case for acupunctural needles in the RMAH collection restored the original form of the relic and arrested further corrosion. Above all, it revived the historic and academic value of the overseas Korean cultural heritage through scientific analysis.

• Journal of Welding and Joining
• /
• v.30 no.5
• /
• pp.64-69
• /
• 2012

Sn-Bi eutectic alloy has been widely used as one of the key solder materials for step soldering at low temperature. The Sn-58Bi solder paste containing chloride flux was adopted to compare with that using the chloride-free flux. The paste was applied on the electroless nickel-immersion gold (ENIG) surface finish by stencil printing, and the reflow process was then performed at $170^{\circ}C$ for 10 min. After reflow, the solder joints were aged at $125^{\circ}C$ for 100, 200, 300, 500 and 1000 h in an oven. The interfacial microstructures were obtained by using scanning electron microscopy (SEM), and the composition of intermetallic compounds (IMCs) was analyzed using energy dispersive spectrometer (EDS). Two different IMC layers, consisting of $Ni_3Sn_4$ and relatively very thin Sn-Bi-Ni-Au were formed at the solder/surface finish interface, and their thickness increased with increasing aging time. The wettability of solder joints was investigated by wetting balance test. The mechanical property of each aging solder joint was evaluated by the ball shear test in accordance with JEDEC standard (JESD22-B117A). The results show that the highest shear force was measured when the aging time was 100 h, and the fracture mode changed from ductile fracture to brittle fracture with increasing aging time. On the other hand, the chloride flux in the solder paste did not affect the shear force and fracture mode of the solder joints.