• Journal of the Korea institute for structural maintenance and inspection
• /
• v.28 no.3
• /
• pp.37-46
• /
• 2024

This study investigates the evolution of concrete damage due to chloride-induced steel corrosion through Impact-echo (IE) testing. Three reinforced concrete specimens, each measuring 1500 mm in length, 400 mm in width, and 200 mm in thickness, were fabricated using three concrete mixture proportions of blended cement types: ordinary Portland cement, ground granulated blast-furnace slag and fly ash. Steel corrosion in the concrete was accelerated by impressing a 0.5 A current following a 35-day cycle of wet-and-dry saturation in a 3% NaCl solution. Initial IE data collected during the saturation phase showed no significant changes, indicating that moisture had a minimal impact on IE signals and highlighting the slow progress of corrosion under natural conditions. Post-application of current, however, there was a noticeable decline in both IE peak frequency and the P-wave velocity in the concrete as the duration of the impressed current increased. Remarkably, progressive monitoring of IE proves highly effective in capturing the critical features of steel-corrosion induced concrete deterioration, such as the onset of internal damages and the rate of damage propagation. These results demonstrate the potential of progressive IE data monitoring to enhance the reliability of diagnosing and prognosticating the evolution of concrete damage in marine environment.

• Journal of the Korea Concrete Institute
• /
• v.24 no.6
• /
• pp.715-726
• /
• 2012

Since strength and diffusion coefficient of concrete, representative concrete properties that in change with age, the time effect must be considered in the analysis of chloride penetration. In this study, an evaluation of correlation between accelerated diffusion coefficient, apparent diffusion coefficient, and compressive strength in high performance concrete with various mineral admixtures such as ground granulated blast furnace slag, fly ash, and silica fume was performed. For this work, thirty mix proportions were prepared. Accelerated diffusion coefficients at the age of 28, 91, 180, and 270 days were evaluated. For apparent diffusion coefficient, submerging test for 6 months was performed. For evaluation of compressive strength with ages, the compressive strength test was carried out at an age of 7, 28, 91, 180 days. The results of accelerated diffusion coefficient, apparent diffusion coefficient, and strength were compared, and the correlation was analyzed considering time dependency. From this study, linear relationship between accelerated diffusion and apparent diffusion coefficient were obtained regardless of concrete age. The linear relations were also observed in strength-accelerated diffusion coefficient and strength-apparent diffusion coefficient regardless of concrete age.

• Journal of the Korea Concrete Institute
• /
• v.16 no.3 s.81
• /
• pp.319-326
• /
• 2004

This paper investigates the effect of the concrete containing mineral admixtures(pozzolanic materials such as fly-ash, ground granulated blast-furnace slag, silica fume and meta kaolin) on the resistance properties to chloride ion invasion. The purposed testing procedure was applied to the concrete replaced mineral admixtures for 3${\~}$4 replacement ratios under water-binder ratios ranged from 0.40 to 0.55. For the electro-migration test, Tang and Nilsson's method was used to estimate the diffusion coefficient of chloride ion. As a results, the water-binder ratios, kinds of mineral admixtures and replacement ratios, water curing periods had a great effect on the diffusion coefficient of chloride ion, and the optimal replacement ratios had a limitation for each mineral admixtures. Also, the use of mineral admixtures by mass(replacement of OPC) enhance the resistance ability against chloride penetration compared with the plain concrete. The compressive strength was shown related to the diffusion coefficient of chloride ion, the compressive strength increases with the diffusion coefficient of chloride ion decreasing. Below the 50 MPa, the variation of diffusion coefficient of concrete replaced mineral admixtures was bigger than that of plain concrete.

• Journal of the Korea Concrete Institute
• /
• v.26 no.4
• /
• pp.507-515
• /
• 2014

Although the construction joints of a concrete structure are properly treated with some measures, leakage has frequently occurred. A series of tests on the bond characteristics between new and old concrete were carried out in this study, assuming that the leakage at the construction joints has certain relationship with the bond of concrete. To assess the bond characteristics under various conditions, a number of specimens were made that have an interface between new and old concrete and bond strength, flexural strength and splitting tensile strength were measured. Main test variables are type and amount of mineral admixtures, treatment method of the interface and type of waterstops. In addition, the effects of placing interval between the concrete and of the age of the strength tests were investigated. The test results showed a slightly increased bond strength when applying mineral admixtures, which can be attributed to the interface filled with the calcium silicate hydrate that is formed by pozzolanic reaction. On the other hand, the bond strength was higher when the interface was treated rough and dry, and the roughness of a waterstop affected the bond capacity of the waterstop. Also, an assessment is required that considers the type of strength test because the bond strength varied according to the test methods.

• Journal of the Korea Concrete Institute
• /
• v.29 no.3
• /
• pp.307-314
• /
• 2017

Concrete is a durable and cost-benefit construction material, however performance degradation occurs due to steel corrosion exposed to chloride attack. Penetration of chloride ion usually decreases due to hydrates formation and reduction of pores, and the reduced chloride behavior is considered through decreasing diffusion coefficient with time. In the work, HPC (High Performance Concrete) samples are prepared with 3 levels of W/B (water to binder) ratios of 0.37, 0.42, and 0.27 and 3 levels of replacement ratios of 0%, 30% and 50%. Several tests containing chloride diffusion coefficient, passed charge, and compressive strength are performed considering age effect of 28 days and 180 days. Chloride diffusion is more reduced in OPC concrete with lower W/B ratio and GGBFS concrete with 50% replacement ratio shows significant reduction of chloride diffusion in higher W/B ratio. At the age of 28 days, GGBFS concrete with 50% replacement ratio shows more rapid reduction of chloride diffusion than strength development, which reveals that abundant GGBFS replacement has effective resistance to chloride penetration even in the early-aged condition.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.5 no.4
• /
• pp.375-381
• /
• 2017

Recently, due to the increasing of interest about the eco-friendly concrete, it is being increased to use concretes containing by-products of industry such as fly ash, ground granulated blast furnace slag, silica fume, and etc. Especially, these are well known for improving the resistance to reinforcement corrosion in concrete and decreasing chloride ion penetration. The purpose of this experimental research is to evaluate the resistance to corrosion of reinforcement and critical chloride content of high volume fly ash concrete(HVFAC) which is replaced with fly ash for approximately 50% cement content. For this purpose, corrosion monitoring of reinforcement by half cell potential method was carried out for the cylindrical test specimens that the upper of reinforcement in concrete was exposed to detect the time of corrosion initiation for reinforcement. It was observed from the test result that the the time of corrosion initiation for reinforcement of HVFAC by the accelerated corrosion tests increased 1.2~1.3 times than plain concrete and the critical chloride contents of plain concrete and HVFAC were found to range $0.80{\sim}1.20kg/m^3$, $0.89{\sim}1.60kg/m^3$, respectively.

• Proceedings of the Korean Society for Emotion and Sensibility Conference
• /
• 2009.11a
• /
• pp.265-268
• /
• 2009

전기로 산화 슬래그 골재는 철강산업의 부산물을 재활용한다는 측면에서 친환경적일 뿐만 아니라 고갈되고 있는 골재자원을 대체할 수 있다는 측면에서 중요한 가치를 지닌다. 본 연구에서는 다량의 철성분을 함유하고 있어 높은 밀도를 나타내는 전기로 산화슬래그 골재를 사용한 친환경 콘크리트의 횡구속 성능에 관하여 검토하였다. 이 실험에서는 전기로 산화슬래그 굵은 골재 및 잔골재를 적용한 콘크리트 공시체를 제작하여 천연 굵은 골재와 잔골재를 적용한 콘크리트의 횡구속 거동을 파악하였다. 실험변수는 콘크리트 제작에 사용한 골재의 종류, 횡보강에 사용한 나선 철근의 항복강도로 하였다. 실험결과 전기로 산화슬래그 골재를 사용하였을 경우 천연골재를 사용한 실험체와 유사한 횡구속 효과를 보였다.

• Proceedings of the Korean Institute of Resources Recycling Conference
• /
• 2005.10a
• /
• pp.236-239
• /
• 2005

본 연구에서는 콘크리트 잔골재 대체 골재로써의 재활용을 위한 재강슬래그의 특성을 조사하였다. 화학조성과 중금속 용출, 재강슬래그의 soundness 및 모르타르의 압축강도를 측정하였다. 그 결과, 중금속 용출과 soundness는 한국 산업 기준(Korean Industrial Standard)과 한국 환경 기준(Korean Environmental Limit)에 적합하였다. 모르타르의 압축 강도는 재강슬래그의 대체 비율이 커질수록 증가하였다.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2014.05a
• /
• pp.100-101
• /
• 2014

The global warming because of the CO₂ emission and solution about this emerge as the international enviroment problem. Particularly, it is the absolutely it is needed for reducing the CO₂ in the cement industry and harmful material actual condition. And the construction of home and abroad and material manufacturers tries for the technology development for the carbon dioxide and harmful material reduction which the portland cement in manufacture is usually emitted along with the increase of concerns about the environment-friendly concrete and panel. Therefore, in this research, the compressive strength of the inorganic binder and flexural strength tries to be measured in order to draw the inappropriate high temperature cure time of the ternary system inorganic binder using the blast furnace slag, red mud, silica fumewhich is the industrial byproduct with the cement substitute material, and etc.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2017.05a
• /
• pp.107-108
• /
• 2017

In this search, by evaluating the field applicability of soil mixed pavement of Red mud is mixed into the soil mixed pavement field applicability, and tries to present the basic data about the site application of recycling of red mud and low carbon construction material to. As a result, the conventional soil concrete organization standards (SPS-KSCICO-001: 2003) meets the criteria for parking lot, making use of red mud, natural color as well as the natural loess is expressed.