• Nuclear Engineering and Technology
• /
• v.40 no.3
• /
• pp.191-198
• /
• 2008

The influence of fission products' contents on the DUPIC fuel powder and pellet properties was experimentally evaluated using SIMFUEL as a surrogate for actual spent PWR fuel due to the high radioactivity of spent fuel. Pure $UO_2$ and SIMFUEL pellets with fission products equivalent to a burn-up of 35,000 MWd/tU and 60,000 MWd/tU were used as impurities in this study. The specific surface area of the powder milled after the OREOX treatment increased and resulted in sintered pellets with a theoretical density (TD) higher than 95%, regardless of the impurity contents. However, the grain size of the sintered pellets decreased with the increasing impurity contents. As a result of the dissolved oxides in $UO_2$ from the impurity groups, the specific surface area of the OREOX powder increased with an increase of the impurities. The grain size of the sintered pellets was significantly decreased by the metallic and oxide precipitates.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.11a
• /
• pp.284-287
• /
• 2001

Multi-pole anisotropic Sr-fertile sintered magnets has been studied by powder injection molding under applied magnetic field. The orientation of anisotropic Sr-ferrite powders higher than 80% during injection molding is achieved at the following conditions; apparent viscosity lower then 2500 poise in 1000 sec$\^$-1/ shear rate and applied magnetic field higher then 4 kOe. For the high fluidity and strength of injection molded compact, and the effective binder removal without defects during solvent extraction and thermal debinding, the optimum multi-binder composition is paraffin wax(PW)/carnauba wax(CW)/HDPE = 50/25/25 wt%. The rate of binder removal is proportional to the mean particle size of Sr-ferrite powders whereas it is inversely proportional to the content of Sr-ferrite powders and the sample thickness. The high magnetic properties of Sr-ferrite sintered magnets are; 3.8 kG of remanent flux density, 3.4 kOe of intrinsic coercivity, and 1.2 kG of surface flux density (1-mm-thick) in the direction of applied magnetic field.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09a
• /
• pp.533-534
• /
• 2006

1mm-thick BLT ceramics were sintered in accordance with a bulk ceramic fabrication process. All XRD peaks detected in the sintered ceramics were indexed as the Bi-layered perovskite structure without secondary phases. Density was increased with increasing the sintering temperature up to $1050\;^{\circ}C$ and the maximum value was about 98% of the theoretical density. The remanent polarization (2Pr) value of BLT ceramic sintered at $1050\;^{\circ}C$ was approximately $6.5\;{\mu}C/cm^2$ at the applied voltage of 4.5kV. From these results, a BLT ceramic target for plused laser deposition (PLD) system was successfully fabricated.

• Journal of Powder Materials
• /
• v.19 no.1
• /
• pp.13-18
• /
• 2012

This study has been performed on the full density sintering of Fe nanopowder and the surface hardening by plasma ion nitriding. The Fe sintered part was fabricated by pressureless sintering of the Fe nanopowder at $700^{\circ}C$ in which the nanopowder agglomerates were controlled to have 0.5-5 ${\mu}m$ sized agglomerates with 150 nm Fe nanopowders. The green compact with 46% theoretical density(T.D.) showed a homogeneous microstructure with fine pores below 1 ${\mu}m$. After sintering, the powder compact underwent full densification process with above 98%T.D. and uniform nanoscale microstructure. This enhanced sintering is thought to be basically due to the homogeneous microstructure in the green compact in which the large pores are removed by wet-milling. Plasma ion nitriding of the sintered part resulted in the formation of ${\gamma}$'-$Fe_4N$ equilibrium phase with about 12 ${\mu}m$ thickness, leading to the surface hardening of the sintered Fe part. The surface hardness was remarkably increased from 176 $H_v$ for the matrix to 365 $H_v$.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2006.06a
• /
• pp.276-277
• /
• 2006

1mm-thick BLT ceramics were sintered in accordance with a bulk ceramic fabrication process. AII XRD peaks detected in the sintered ceramics were indexed as the Bi-layered perovskite structure without secondary phases. Density was increased with increasing the sintering temperature up to $1050^{\circ}C$ and the maximum value was about 98% of the theoretical density. The remanent polarization (2Pr) value of BLT ceramic sintered at $1050^{\circ}C$ was approximately $6.5\;{\mu}C/cm^2$ at the applied voltage of 4.5 kV. The calculated electromechanical coupling factor ($k_t$) of it was about 5% and the mechanical quality factor (Qm) was about 2200. From these results, a BLT ceramic target for pulsed laser deposition (PLD) system was successfully fabricated.

• The Magazine of the Society of Air-Conditioning and Refrigerating Engineers of Korea
• /
• v.5 no.3
• /
• pp.169-177
• /
• 1976

The importance of surface conditions of nucleate boiling is well recognized and it has been known that the heat transfer to boiling liquid is closely related to the bubble population density. The bubble population density should depend on various factors such as heat flux, surface roughness, surface contamination, properties of liquid, etc. In this paper the effect of surface conditions on heat transfer in nucleate boiling is treated. The experiments were carried out with distilled water boiler, on the horizontal heating surfaces, sintered with various bronze particle, under atmospheric pressure. In addition, experimental investigation for the polished bronze surface was performed. By studing a coefficient Xb defined by eq. (9), which represents the bubble foaming ability of heating surface, generalized fomula on the heat transfer in the nucleate toiling were expressed. The coefficient $X_b$, determined empirically, is not constant and indicates a major influence of the sintered metal surfaces on the $\Delta$, necessary to sustain nucleate boiling at any given heat flux. In this study, the main results are obtained as follows; (1) At low temperature difference, the coefficient $X_b$ of sintered metal surface was found to he higher than the polished surface throughout the full range of experiments. (2) The optimum sintered structure showing the maximum coefficient $X_b$ has been confirmed to exist and it is encountered when particle diameter is $256{\mu}$.

• Proceedings of the KIEE Conference
• /
• 2001.07c
• /
• pp.1405-1407
• /
• 2001

It was studied to prepare high temperature heating elements using molybdenum disilicide($MoSi_2$). Molybdenum disilicide is widely used as material for manufacturing high temperature heating elements. $MoSi_2$ heating elements could be used at 1700-1900$^{\circ}C$. However, it is relatively expensive, and its demand depends on import. $MoSi_2$ powders was mixed with 4-5wt% of montmorillonites type bentonite as plasticizer and a small amount of $Si_3N_4$, $ThO_2$, and B as additives to prepare specimen of heating elements. Then, it was extruded, dried, sintered and machined followed by heating test. Effects of sintering conditions and amount of additives were investigated, It was sintered effectively at 1,350$^{\circ}C$ for five hours. Electrical resistivity was decreased with increasing of sintering temperature and time, and related with apparent density of the specimens. It was linealy decreased with increasing of sintered density. The heating elements thus prepared was stable at 1700$^{\circ}C$ and the physical properties such as specific electrical resistivity, hardness, apparent density, thermal expansion coefficient, and bending strength were almost identical with those of commercial heating elements.

• Journal of Powder Materials
• /
• v.3 no.1
• /
• pp.49-56
• /
• 1996

The effect of$H_{2}/N_{2}$gas sintering atmosphere on the carbon content and mechanical properties during the metal injection molding process of carbonyl iron-nickel powder was studied. The carbon content of the specimen after debinding in the pure$N_{2}$atmosphere appeared 0.78 wt%. After showing the maximum value of 1.48 wt.% in the debinding atmosphere of 10%$H_{2}/N_{2}$gas mixture, the carbon content of the debinded specimen decreased gradually with increasing the$H_2$content in the$H_{2}/N_{2}$gas mixture. The carbon contents of the sintered specimen were 0.46~0.63wt% in Na gas atmosphere, while they appeared extremely low above 40%$H_{2}/N_{2}$gas atmosphere. The relative sintered density increased abruptly from 88~90% to 93~96% with the addition of Ni, while the density nearly unchanged above 2% Ni addition. The sintered density increased with increasing the fraction of$H_{2} in H_{2}/N_{2}$gas mixture. Tensile strength and hardness increased, and elongation decreased with increasing carbon and Ni content. In spite of high carbon content of 0.63 wt%, the superior elongation value of 10% was shown.

• Journal of Powder Materials
• /
• v.5 no.4
• /
• pp.299-302
• /
• 1998

Dimensional accuracy is one of the most important issues in the production of sintered parts. The iron-copper-carbon system is commonly used alloys in sintered structural parts production. The dimensional control of these alloys, however, is not easy because of their complex sintering behavior. This study is an effort to clarify the influence of common factors on dimensional change of Fe-Cu-C sintered structural parts. We determined the effect of such various parameters as chemical composition, particle diameter, compact density, sintering temperature and sintering time on dimensional changes. Consequently, we obtained a useful formula to predict the final dimension in function of these parameters. The effect of typical impurities in copper powder on the dimensional change of sintered parts has also been described.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2002.07a
• /
• pp.82-85
• /
• 2002

High-quality Sr-ferrite sintered magnets have been studied by using mill scale added SrCO$_3$ and oxidents before oxidation process. The pre-added SrCO$_3$ powders were improved the degree of oxidation and crush of mill scale and the magnetic properties of Sr-ferrite sintered magnets. The small added NaNO$_3$ oxidant was also highly improved the degree of oxidation and crush of mill scale and the magnetic properties of Sr-ferrite sintered magnets; 3805 G of remanent flux density, 3240 Oe of intrinsic coercivity, and 3.45 MGOe of maximum energy product.