• Journal of Adhesion and Interface
• /
• v.3 no.2
• /
• pp.30-39
• /
• 2002

The effect of cure accelerator content on the change in crosslink density by thermal aging was studied for silica-filled natural rubber (NR) vulcanizates. Influence of silane coupling agent was also investigated. N-tert-Butyl-2-benzothiazole sulfenamide (TBBS) and bis-(3-(triethoxysilyl)-propyl)-tetrasulfide (TESPT) were used as a cure accelerator and a silane coupling agent, respectively. The crosslink density increased by thermal aging and the increasing level became larger as the aging temperature increased. The degree of crosslink density change of the vulcanizates without the silane coupling agent was larger than that of the vulcanizates containing the silane coupling agent. For the vulcanizates silane coupling agent, the activation energy for the crosslink density change decreased with increase of the cure accelerator content in the vulvanizate.

• Journal of Adhesion and Interface
• /
• v.16 no.2
• /
• pp.55-62
• /
• 2015

It was investigated that the effect of surface modification and concentration of fumed silica on the adhesion properties and thermal stability of 2-EHA/AA pressure sensitive adhesive (PSAs) prepared by UV irradiation. The influence of repeating units of crosslinking agent on PSAs were also studied. From SEM analysis, PSAs synthesized with surface modified silica had finer dispersion of silica particles in polymer matrix due to the interfacial interaction. Results of the study showed that increase in tack and peel strength when under 0.3 wt% of silane treated silica were added in the reaction mixture. The addition of PEGDMA for crosslinking agent offers positive effect on adhesion properties in comparison with PSAs using EGDMA for crosslinker, which may be attributed to high mobility of ethylene oxide repeating units in PEGDMA. From the thermal degradation residue of PSAs, it was revealed that thermal stability was improved with silica addition due to the strong interfacial bonding between silane modified silica and polymer matrix, which may act as a thermal barriers into 2-EHA/AA PSAs.

• Bulletin of the Korean Chemical Society
• /
• v.34 no.1
• /
• pp.143-148
• /
• 2013

Novel titanium containing solid core mesoporous shell silica has been synthesized by using octadecyltrichloro silane and triethylamine. The synthesized material was characterized by various physicochemical techniques. The mesoporous character of the material has been revealed from PXRD studies. The presence of octadecyltrichloro silane and triethylamine in the sample has been confirmed from EDAX studies. TG/DTA analysis reveals the thermal characteristics of the synthesized material. The presence of titanium in the frame work and its coordination state has been studies by UV-vis DR studies and XPS analysis. Chemical environment of Si in the framework of the material has been studied by $^{29}SiMASNMR$ studies. The surface area of the material is found to be around $550\;m^2g^{-1}$ and pore radius is of nano range from BET analysis. The spherical morphology and particle size of the core as well as shell has been found to be 300 nm and 50 nm respectively from TEM analysis. The catalytic application of this material towards the synthesis of caprolactam from cyclohexanone in presence of hydrogen peroxide through ammoxidation reaction has been investigated. The optimum conditions for the reaction have been established. The plausible mechanism for the formation of core silica and conversion of cyclohexanone has been proposed.

• The Journal of Korean Academy of Prosthodontics
• /
• v.45 no.2
• /
• pp.159-168
• /
• 2007

Statement of problem: Literature showed different results on the durability of bonded ceramic restoration. Purpose: The purpose of this article is to review the effect of surface treatment of ceramics in resin-ceramic bond to get predictable results. Material and method: PubMed data base was utilized to search the articles which were written in English and published in 1986 and 2006. Some electronic published articles which are forthcoming to publish in paper were also included for this review. This review article focused on the effect of acid etching and silane application on the silica based ceramics. The durability of resin-ceramic bonding, the methodology for bond strength test and resin bonding to alumina or zirconia based ceramics were compared in brief at the end of the review. Results and Conclusion: the effect of silane application can be influenced by the contaminations of saliva or solutions. Micromechanical retention by acid etching as well as silane application plays an important role in initial and durable bond strength between resin and ceramic. The use of phosphate modified resin cement following tribochemical silica coating and silane application produced best bond strength for alumina or zirconia based ceramics.

• Applied Chemistry for Engineering
• /
• v.1 no.2
• /
• pp.133-139
• /
• 1990

Methacrylate functional silanes with different methylene spacer groups have been synthesized and the orientation effect and absorption behavior of these silane coupling agent were investigated by Fourier transform infrared spectroscopy(FT-IR). The mechanical properties of glass bead/polyester composites are found to be dependent on the spacer group of treated silane coupling agent. The absorption rate of the silane coupling agent onto the fumed silica surface decreases with increasing the number of the methylene spacer in methacrylate functional silanes. Silane molecules containing long spacer groups are adsorbed onto silica slightly bowed with respect to the substrate surface. The relationship between silane molecular structure and mechanical properties of polymer composites is also investigated in order to improve hot/wet properties of glass fiber/polyester composites.

• Elastomers and Composites
• /
• v.57 no.4
• /
• pp.129-137
• /
• 2022

Low molecular weight liquid butadiene rubber (LqBR) is a processing aid that can resolve the migration problem of tire tread compounds. Various studies are being conducted to replace the petroleum-based processing oil with LqBR. However, the effect of the loading time of LqBR in the compounding process on silica dispersion and vulcanizate properties is not well known. In this study, we analyzed silica dispersion, vulcanizate properties, and viscoelastic properties of silica-filled tire tread compound according to the processing aid type (TDAE oil, non-functional LqBR) and, silane terminated LqBR) and input timing. In the non-functional LqBR compounds, the 'with TESPT' mixing procedure showed excellent dynamic viscoelastic properties while silane-terminated LqBR compounds showed that the 'after TESPT' mixing procedure was good for 300% modulus and abrasion resistance.

• Elastomers and Composites
• /
• v.46 no.3
• /
• pp.237-244
• /
• 2011

Five natural rubber (NR) composites with different reinforcing systems of unfilled, carbon black, carbon black with silane coupling agent, silica, and silica with silane coupling agent were thermally aged and change of the crosslink densities by the accelerated thermal aging was investigated. The crosslink densities on the whole increased as the aging time elapsed irrespective of the reinforcing systems. The crosslink density changes became noticeable by increasing the aging temperature. For carbon black-filled composites, the silane coupling agent made the crosslink density change to be increased. For silica-filled composites, however, the silane coupling agent made the crosslink density increment reduced at 60 and $70^{\circ}C$ and it hardly affect the degree of the crosslink density change at 80 and $90^{\circ}C$. The activation energies for the crosslink density changes of the carbon black-filled samples increased continuously in a logarithmic fashion, whereas that of the silica-filled one showed a quasi-steady state ranges at aging times of 30-150 days. The activation energy of the unfilled sample increased exponentially with the aging time. The experimental results were explained with sulfur donation from the silane coupling agent, surface modification of the filler by the silane coupling agent, adsorption of curative residues on the silica surface, and release of the adsorbed curative residues.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.22 no.2
• /
• pp.789-793
• /
• 2021

A lithium secondary battery is the most promising candidate for future energy storage devices. On the other hand, the battery capacity decreases gradually due to the small amount of water and decomposition of the salts during the charging and discharging process, which deteriorates at high temperatures. Many researchers focused on increasing the cycling performance, but there have been few studies on the fundamental problem that removes water and HF molecules. In this study, silane molecules that are capable of absorbing water and HF molecules are introduced to the separator. Firstly, silica-coated amino-silane (APTES, 3-aminopropyltriethoxysilane) was synthesized, then the silica reacted with epoxy-silane, GPTMS ((3-glycidyloxypropyl)trimethoxysilane). A ceramic-coated separator was fabricated using the silane-coated silica, which is coated on porous polyethylene substrates. FT-IR spectroscopy and TEM analysis were performed to examine the chemical composition and the shape of the silane-coated silica. SEM was performed to confirm the ceramic layers. LMO half cells were fabricated to evaluate the cycling performance at 60 ℃. The cells equipped with a GPTMS-silica separator showed stable cycling performance, suggesting that it would be a solution for improving the cycling performance of the Li-ion batteries at high temperatures.

• Journal of Adhesion and Interface
• /
• v.10 no.2
• /
• pp.98-105
• /
• 2009

Poly(amic acid) was synthesized from the reaction of p-PDA/ODA and PMDA/BPDA and silane oligomer containing epoxy group was also synthesized from the reaction of tetramethylorthosilicate (TMOS) and glycidol. After hybridizing poly (amic acid) and silane oligomer, they were effectively converted into polyimide/silica hybrid films by thermal imidization process. As the silica contents in hybrid films increased, CTE values decreased from 17 ppm/K to 10 ppm/K and the tensile modulus increased, in spite of decreasing tensile strength. In addition, the peel test showed that the adhesion strength of hybrid film was enhanced from $0.43kg_f/cm$ to $1.02kg_f/cm$. Therefore, it could be concluded that the polyimide/silica hybrid film is effective to enhance adhesion strength for FCCL films.

• Elastomers and Composites
• /
• v.49 no.3
• /
• pp.239-244
• /
• 2014

Reaction between silica and silane coupling agent without solvent was investigated using transmission mode Fourier transform infrared spectroscopy (FTIR) and thermogravimetric analysis (TGA). Bis[3-(triethoxysilylpropyl) tetrasulfide] (TESPT) was used as a silane coupling agent. After removing the unreacted TESPT, formation of chemical bonds was analyzed using FTIR and content of reacted TESPT was determined using TGA. Content of the coupling agent bonded to silica increased with increase in the coupling agent content, but the oligomers were formed by condensation reaction between coupling agents when the coupling agent was used to excess. In order to identify bonds formed among silica, coupling agent, and rubber, a silica-coupling agent-BR model composite was prepared by reaction of the modified silica with liquid BR of low molecular weight and chemical bond formation of silica-coupling agent-BR was investigated. Unreacted rubber was removed with solvent and analysis was performed using FTIR and TGA. BR was reacted with the coupling agent of the modified silica to form chemical bonds. Polarity of silica surface was strikingly reduced and particle size of silica was increased by chemical bond formation of silica-coupling agent-BR.