• 한국기계가공학회지
• /
• 제19권11호
• /
• pp.102-108
• /
• 2020

The demand for lightweight materials and high-strength steel has rapidly increased to help reduce the weight of a vehicle body; it improves the fuel efficiency of automobiles and provides passenger safety. Additionally, as the material becomes thinner, the demand for its resistance against corrosion becomes higher. Hence, the application of the surface-treated steel sheet has surged rapidly. In this study, a weld bonding experiment using a delta spot welding machine is performed on a thin sheet of a different material (Al6061-T6/GA440). The thickness of the material was kept at 1 mm to reduce the weight of the automobile body parts. Additionally, the purpose of this study is to control the heat input by applying the welding conditions of a multi-stage pressure pattern to improve corrosion resistance shear strength. The analysis of nugget diameter measurement, shear tensile test, and salt spray test was performed to achieve the aim.

• 대한안전경영과학회지
• /
• 제2권4호
• /
• pp.197-208
• /
• 2000

ABS sensor ring has been manufactured by powder metallurgy (P/M) method using 400 series ferrite stainless steel. The results are following. It is supposedly sufficient to use for control computer due to good experimental results of magnetic characteristics. Compared with sensor ring made by iron, 400 series ferrite stainless steel has shown a good corrosion resistance without an addition surface treatment. Thus the decreasing production process has been obtained. As a result mechanical characteristics of hardness and tensile test, 400 series ferrite stainless steel shown a good endurance when it is combined to constant velocity joint(C/V), and has a good hardness properties endurable to sand and pebble impact. The products before sintering are much more corrodible in the condition of spray test of salt water and ammonia than humidity and nitrogen condition.

• 청정기술
• /
• 제11권3호
• /
• pp.153-164
• /
• 2005

This study found a reliable evaluation for four kinds of pb-Free plating solutions and it's layers, through pure Sn, SnAg, SnBi and SnCu. These four kind of solutions are widely used to pb-Free plating. Hull-cell, Harring-blum, coverage, throwing power, current efficiency, stability, life-time, composition, hardness, roughness, abrasion, scratch, solderability, corrosion, contact angle, morphology, SIR(Surface insulation resistance) and Whisker test were experimented. Also, Using ICP, XRF, FE-SEM, EDS, temperature/humidity chamber, solderability tester, hardness tester, roughness tester, abrasion tester, salt spray tester, contact angle tester, SIR tester, and microscope. In this paper could be shown the systematic and various analysis for reliability about four kinds of pb-Free plating solutions, processes and it's deposit surface.

• Corrosion Science and Technology
• /
• 제12권1호
• /
• pp.27-33
• /
• 2013

According to its merits about high curing speed and low emission of volatile organic compounds, UV curable inorganic-organic coating technology has been developed as an alternative for toxic and carcinogenic chromate-based treatments for years. It is consistently observed that ultra-thin films offer excellent corrosion protection as well as paint adhesion to metals. Based on the tetra-ethylorthosilicate(TEOS) and methacryloxypropyl trimethoxysilane(MPTMS), inorganic sol was synthesized and formed hybrid networks with UV curable acrylic monomer, 6-hexanediol diacrylate(HDDA), trimethylolpropane triacrylate(TMPTA), pentaerylthritol triacrylate(PETA). Several methods were used to test their properties such as salt spray test, potentiodynamic measurement, tape peel test, etc. It was shown that anti-corrosive property and stability of storage were affected by the molecular ratios of inorganic and organic compounds. It was not only the stability of storage, but had a excellent anti-corrosive, paint adhesive, and anti-solvent properties in a final molar ratios of 0.6/0.04/0.86/0.005 (TEOS/MPTMS/Acetone/HNO3) and 0.08/0.106/0.081/0.02 (TMPTA/HDDA/PETA/photo initiator).

• Journal of Welding and Joining
• /
• 제33권4호
• /
• pp.37-43
• /
• 2015

Characteristics of dissimilar metal welds between STS 316L and carbon steel ASTM A516 Gr.70 made with GTAW have been evaluated in terms of microstructure, ferrite content, chemical analysis, hardness and corrosion resistance. Three heat inputs of 9.00, 11.25, 13.00kJ/cm were employed to make joints of dissimilar metals with ER309 wire. Based on microstructural examination, the amount of vermicular type of ${\delta}$-ferrite was increased with increasing heat input due to the increase of Creq/Nieq in the second layer of welds. Based on the EDX analysis of weld metals, Cr and Ni content in the 2nd layer increased while those content in the first layer of welds decreased with heat inputs. Cellular solidification mode in the 1st layer and dendritic solidification mode in the 2nd layer due to different cooling rates were prevailed, respectively. Heat affected zone which formed hard microstructure showed higher hardness than the weld metal. The salt spray test of dissimilar metals weld joints showed that the carbon steel surfaces only corroded. The weight loss rate due to corrosion increased up to 100hours but it decreased above 100 hours. There was little difference in the weight loss caused by corrosion regardless of heat inputs.

• 폴리머
• /
• 제34권5호
• /
• pp.405-409
• /
• 2010

내부식성이 우수한 기능기를 함유하는 새로운 졸-젤 전구체를 합성하고 이를 함유하는 유무기 하이브리드 코팅 조성물을 제조하였다. 코팅 조성물에는 통상의 졸-젤 전구체로 tetraethoxysilane을 사용하였고 비스페놀 A 타입의 에폭시를 실란화합물로 개질하였으며, 졸-젤 반응을 위하여 물과 HCl을 촉매로 사용하였다. 각 조성물은 졸-젤 전구체의 종류, 함량 등을 변화하여 다양한 코팅 조성물을 제조하였고 iron 기판위에 딥코팅하여 열경화하였다. 코팅된 iron 기판의 내부식성을 평가하기 위하여 염수분무시험과 전기화학적 임피던스 분광법을 사용하였는데, 내부식성 기능기를 함유한 유무기 하이브리드 코팅재가 일반적인 하이브리드 코팅재에 비해 매우 향상된 내부식성을 나타냄을 확인할 수 있었다. 내부식성 기능기를 함유한 코팅재의 경우, 0.1 M NaCl에서 500시간 이상 초기의 임피던스를 유지하는 반면, 일반적인 코팅재는 24시간 이후에 임피던스가 감소하는 것을 관찰할 수 있었다.

• 한국표면공학회지
• /
• 제49권5호
• /
• pp.454-460
• /
• 2016

Double-layered Al-Mg films have been deposited by using an e-beam deposition method on a cold-rolled steel sheet(CR), which the structure of the film was Al/Mg/CR. The micro-structure, alloy phase, and corrosion resistance of the Al-Mg coated CR were investigated before and after heat treatment at $400^{\circ}C$ for 2, 3, and 10 min in a nitrogen atmosphere. Total thickness of Al-Mg films was fixed at $3{\mu}m$ and the thickness ratio of Al and Mg layers(Al:Mg) has been changed from 5:1 to 1:5. The cross-sectional morphology of the films, which had the thickness ratio of 2:1(Al:Mg), 1:1, and 1:2, was changed after heat treatment from columnar to featureless structure. The x-ray diffraction data for as-deposited films showed only pure Al and Mg peaks. Al-Mg alloy peaks such as $Al_3Mg_2$ and $Al_{12}Mg_{17}$ phase appeared after the heat treatment. The Al-Mg coating with the thickness ratio of 1:1(Al:Mg) showed the best corrosion resistance of up to 500 hours by salt spray test.

• 한국표면공학회:학술대회논문집
• /
• 한국표면공학회 2015년도 춘계학술대회 논문집
• /
• pp.32-32
• /
• 2015

Electrophoretic paint (E-paint) was investigated on four different magnesium substrates: as-extruded AZ61 (AZ61), heat-treated AZ61 (AZ61-H), as-extruded TZ61 (TZ61) and heat-treated TZ61 (TZ61-H), to elucidate the effect of heat treatment and alloying elements on the deposition and corrosion resistance of E-paint. It was found that, a rapid increase of voltage, indicating that the deposition of E-paint had started, was observed after an induction time of 0.39 min for AZ61-H, 0.43 min for AZ61, 0.51 min for TZ61-H and 0.58 min for TZ61. The amount of E-paint deposited on the four samples was approximately similar, but the electrical charge used for the deposition process on the heat-treated samples was smaller than that on the as-extruded samples. The current efficiencies of E-paint on AZ samples (AZ61 and AZ61-H) were higher than those of TZ samples (TZ61 and TZ61-H), and on the heat-treated samples were higher than on as-extruded samples. All E-paintings on the four magnesium substrates had an excellent adhesion without any paint detached by tape peel-test. However, many large blisters were formed on the surface of AZ samples, and none, or very small blisters were observed on TZ samples after immersion test in DI-water for 500 h at $40^{\circ}C$. Under salt spray test (SST) conditions, E-paint on AZ samples showed blistering adjacent to scribes, while blistering of E-paint occurred on intact areas of TZ samples. The E-paint on heat-treated samples showed much better corrosion resistance than that on as-extruded samples. The ranking of greater to lesser corrosion resistance of the E-paint on these four different magnesium substrates is indicated by the order: AZ61-H > AZ61 > TZ61-H > TZ61.

• 방사성폐기물학회지
• /
• 제8권1호
• /
• pp.33-39
• /
• 2010

산화물 사용 후 핵연료를 처리하는 전해환원공정에서는 LiCl 용융염계에서 산소가 생성되는 반응을 수반하게 되며, 생성된 산소로 인해 반응기의 구조재료를 상당히 부식시킬 수 있는, 화학적으로 심각한 반응환경을 조성한다. 따라서, 고온 용융염을 다루는 전해환원 공정장치를 위해서는 최적의 재료를 선택하는 것이 필수적이다. 본 연구에 서는 리튬용융염, $675^{\circ}C$, 216시간동안 산화분위기에서 코팅이 안 된 초합금과 코팅된 초합금 시편의 고온 부식연구를 수행하였다. IN713LC 초합금 시편에 aluminized NiCrAlY bond 코팅 후 $Y_2O_3$ top 코팅을 하였다. 코팅이 안 된 초합금은 부식층의 빠른 성장응력과 열적응력에 의한 부식층의 박리로 명확한 무게손실을 보인다. 탑 코팅의 화학적 및 열적 안정성으로 인해 고온 리튬용융염을 다루는 구조재료의 부식 저항성이 증가함을 확인할 수 있었다.

• 공업화학
• /
• 제18권3호
• /
• pp.296-302
• /
• 2007

6가 크롬의 크로메이트 코팅제의 대체를 위한 3가 크롬의 크로메이트 코팅용액의 제조에 관한 것이다. 본 연구에서 제안된 코팅제는 3가 크롬원으로서 $KCr(SO_4)_2$를 35~45 g/L, 인산계 화합물로서 $NaH_2PO_4$를 20~30 g/L을 주성분으로 하고 여기에 금속계 황산화물로서 $CoSO_4$ 10~20 g/L, $ZnSO_4$ 10~20 g/L의 조성으로 구성된 것이다. 이 제안된 3가 크롬 코팅용액을 사용하여 pH 2.0~2.2, 상온에서 담지시간 20~25 s의 조건하에 시안아연도금체에 코팅된 피막은 염수분무시험결과 5% 백청발생까지 120 h 이상 견디는 우수한 내식성을 발현하였다.