• 한국표면공학회지
• /
• 제27권1호
• /
• pp.29-35
• /
• 1994

The effects of coating of 3$\mu\textrm{m}$ thickness on the mechanical property of alumina after heat treatment at 100$0^{\circ}C$ for 30minutes under $10^{-6}$torr vacuum was quantified in terms of modulus of rupture(MOR) using Weibull plot. While the copper coating did not change MOR of alumina due to the nonwetting behavior of Cu on $Al_2O_3$, the reactive titanium metal coating caused a noticeable 29% reduction in averaged MOr strength. This was related with the combined effects of microcracks in coating formed during heat treatment and good bonding character between Ti and $Al_2O_3$. The effect of cosputtering of Ti and Cu, bilayer coatings of Cu/Ti and Ti/Cu were also investigated. It was found that Ti, cosputtered, Cu/ti and Ti/Cu coatings reduced MOR strength of alumina in the order listed. This was correlated with the amount of Ti at coating/alumina inter-face associated with a coated layer or segregation of Ti during heat treatment.

• Journal of the Korean Wood Science and Technology
• /
• 제25권3호
• /
• pp.96-104
• /
• 1997

The objective of this research project was to develop the wooden footpath block to reuse of wood waste. Some physical and mechanical properties of the wooden block such as water absorption, thickness swelling, modulus of rupture, internal bond, density profile and impact resistance were studied. Water absorption and thickness swelling of the wooden block were greatly reduced when the wooden block was pressed inside the forming device than by conventional hot pressing. Also, Modulus of rupture and internal bond of the wooden block were increased greatly when the pressing was completed inside the forming device. The density profile of the wooden block was improved up to 93.5%, minimum to average density ratio. The wooden block manufactured in this study have excellent physical and mechanical prperties in comparison with existing wood based materials. So, these wooden blocks are applicable to footpth block or other exterior members.

• Journal of the Korean Wood Science and Technology
• /
• 제41권5호
• /
• pp.392-398
• /
• 2013

This study investigated the effect of test zone selection for evaluating bending strength of visually graded lumber. This will contribute to the understanding of two different methods under different standards. In method I, the major defect was randomly placed in the test specimen. In method II, the major defect was randomly placed in the maximum moment zone (MMZ). The results showed that the method II is more accurate for reflecting the effect of defects governing the grade of lumber. Unless the maximum strength-reducing defect (MSRD) is placed in MMZ, the evaluated value would be higher than that of MSRD. For evaluating the modulus of rupture (MOR) of visually graded lumber in test set-up of Method I, the Eq. (5) needs to be considered.

• 한국재료학회:학술대회논문집
• /
• 한국재료학회 1993년도 추계 학술발표 강연 및 논문 개요집
• /
• pp.48-48
• /
• 1993

• 대한기계학회논문집A
• /
• 제20권3호
• /
• pp.882-890
• /
• 1996

Mechanical properties, including Young's modulus, residual stress and rupture strength, of a thermally evaporated gold film have been measured form a blister test. In a theoretical study, the priniple of minimum potential energy and that of virtual work have been applied to the pressurized circular membrane problem, and load-deflection relations have been derived for typical membrane deflection mode of spheroidal shape. In an experimental study, circular gold membranes of 4800 A-thickness and 3.5mm diameter were fabricated by the silicon electropolishing technique. Mecahnical properties of the thin gold films were deduced from the load-deflection curves obtained by the blister test, Young's moduli, obtianed from blister test, have been in the range of 45-70 GPa, while those of bulk gold have been in the range of 78-80 GPa. Residual stresses in the evaporated gold films have been measured as 28-110MPa in tension, The rupture strength of the gold film has turned out to be almost equal to that of dental gold alloy (310-380MPa). It has been demonstrated that the present specimen fabrication method and blister test apparatus have been effective for simultaneous measurement of Young's modulus, residual stress and repture strength of thin solid films. Especially, the electropolishing technique employed here has provided a simple and practical way to fabricate thin membranes in a circular or an arbitrary shape, which could not be obtained by the conventional anisotropic silicon mecromachining technique.

• 대한토목학회논문집
• /
• 제30권2A호
• /
• pp.185-191
• /
• 2010

콘크리트 구조물의 사용성과 내구성 저하의 원인이 되는 균열은 응력의 크기, 응력구배 및 기타 구조적 재료적 원인 등에 의하여 발생하기 때문에 콘크리트의 균열강도를 정확히 예측하기는 매우 어렵다. 특히 판구조의 경우 기존의 일축휨강도에 의한 균열평가가 실제 구조물의 균열강도와 상이할 수 있다. 본 연구에서는 이축휨인장강도 평가에 적합한 시험체 제원을 적용하여 일축과 이축휨강도 특성을 비교, 평가하였다. 실험결과 골재의 크기 및 실험체 크기의 증가에 따라 일축 및 이축휨강도 모두 강도가 저하되는 것으로 나타났다. 일축휨강도에 비하여 이축휨강도가 일축휨강도의 39.5~99.2%로서 전반적으로 낮은 강도를 갖는 것으로 평가되었으며, 특히 20 mm 골재를 사용한 경우에는 76%정도로 고찰되었다.

• Journal of the Korean Wood Science and Technology
• /
• 제44권3호
• /
• pp.315-322
• /
• 2016

2개 이상의 보부재 집성재 요소들의 측면접착으로 제작된 "블록접착집성재"는 대단면 목조건축물의 건축부재로 활용 가능한 구조용재다. 블록접착집성재의 측면은 접착제의 종류와 도포량 및 압체압력을 각기 다른 조합으로 접착하여 박리시험과 전단블록시험으로 접착성능을 검토하였다. 실험결과 레조시놀접착제 $500g/m^2$을 도포하고 압체압력 1.5 MPa의 조건으로 제작된 블록접착집성재의 측면접착성능이 가장 양호하였다. 양호한 측면접착조건으로 제작된 블록접착집성재는 동일단면계수의 대조군 집성재와 휨 강도 성능을 비교 검토하였다. 블록접착집성재의 휨 탄성계수는 대조군 집성재와 유사하였으며, 파괴계수는 대조군집성재 보다 27% 향상되었다. 할렬은 대조군집성재 보다 블록접착집성재에서 다량 발생하였으며, 블록접착집성재의 측면접착층에서 계면파괴나 응집파괴는 관찰되지 않았다.

• 임산에너지
• /
• 제22권2호
• /
• pp.60-68
• /
• 2003

목재의 기계적 특성을 평가하기 위하여 여러 가지 비파괴 측정 기술이 도입되고 있다. 본 실험은 낙엽송(Larix kaempferi Carr.) 소경재 원목을 초음파의 통과 속도와 종진동의 고유진동수를 이용한 비파괴 측정 기술로 영계수를 측정하여 휨강도 실험을 통해 얻은 실측 영계수와 휨파괴계수의 상관관계를 검토하였다. 실험에는 50본의 소경재 원목이 사용되었다. 종진동의 고유진동수를 이용한 영계수와 실측 영계수는 비교적 높은 상관관계를 나타내었다. 초음파를 이용한 비파괴 영계수 측정은 옹이의 출현빈도가 높은 원목의 선별에 효과적이었으며 종진동의 고유진동수를 이용한 측정은 할렬의 출현빈도가 높은 원목의 선별에 효과적임을 확인하였다.

• 한국건설순환자원학회논문집
• /
• 제4권4호
• /
• pp.446-453
• /
• 2016

이 연구에서는 고로슬래그를 혼입한 콘크리트를 사용하여 제작한 콘크리트 수로관의 구조성능을 파악하였다. 고로슬래그 혼입 콘크리트의 재료특성 실험과 고로슬래그 혼입 콘크리트 수로관의 구조거동실험을 수행하였다. 보통 포틀랜드 시멘트(OPC)를 기본 바인더로 하여 고로슬래그 혼입량에 따른 콘크리트의 물성을 파악하였다. 콘크리트의 역학적 특성으로써 압축강도, 탄성계수 및 파괴계수를 측정하였다. 고로슬래그 혼입 콘크리트의 역학적 특성은 OPC 콘크리트의 역학적 특성과 거의 대등한 수준으로 나타난다. 또한 고로슬래그를 45%까지 혼입한 콘크리트의 구조 강도는 KS 기준의 강도 하한값보다 크게 나타난다. 연구결과는 고로슬래그 혼입 콘크리트를 사용한 수로관의 구조성능 평가의 유용한 연구자료로 활용될 수 있다.

• 비파괴검사학회지
• /
• 제9권2호
• /
• pp.18-24
• /
• 1989

Computer-aided high frequency ultrasonic is applied to aluminum oxide(85w%, 94w%, 96w%, and 99w%) MOR(modulus of rupture) samples to evaluate mechanical properties such as density variation, pore content, elastic modulus, shear modulus, and poisson's ratio. Ultrasonic wave velocity and attenuation measurement techniques were used as an evaluator of such properties. Pulse-echo C-Scan images with different fate setting method using 50MHz center frequency 1 inch focal length transducer allows evaluation of density variation and pore content. Elastic modulus calculated with the relation of density and ultrasonic velocity. It shows good reliability as compared with resonance method. Sintered density variation of $0.025g/cm^{3}$, that is 0.6% of theoretical density in $Al_{2}O_{3}$ samples can be observed by ultrasonic velocity measurement. Attenuation measurement method qualitatively agree with 4-point fracture testing result concerning of porosity content.