• E2M - 전기 전자와 첨단 소재
• /
• 제1권1호
• /
• pp.44-53
• /
• 1988

In this study, PZT/PVDF composites with O-3 phase connectivity were prepared by hot pressing method, and the dielectric and piezoelectric properties as a function of PZT volume fraction were investigated. A modified cubic model was introduced to explain the influence of the PZT volume fraction on the experimentally determined dielectric constant. As A n=0.125, the measured dielectric constant values agreed with the calculated values. It was found that dielectric constant .xi.$_{33}$ and piezoelectric coefficient d$_{33}$ increased with indreasing PZT volume fraction, and hydrostatic piezoelectric figure of merit d/aub h/.g$_{h}$ was improved relative to that of the PZT single phase material.l.l.l.

• Journal of Advanced Marine Engineering and Technology
• /
• 제19권2호
• /
• pp.81-91
• /
• 1995

A miniature size electrostatic induction motor has been fabricated and studied with emphasis on the role of the surface resistivity, the relative dielectric constant of the rotor surface materials and the rotor liner materials, which control the charge induction and relaxation on the rotor surface and the field intensity between the rotor and the stator. It is found that the higher resitivity and/or the higher relative dielectric constant, concurrently the longer relaxation time constant of the rotor surface materials make the motor speed get higher speed. In case of discrete coated rotor surface it is found that the motor speed was increased logarithmically as narrow as width of the discrete coated Ti. And the degree of width of discrete coated Ti to the axial direction of the rotor was $60^{\circ}$ and $150^{\circ}$, the motor has got a 125% higher than that at the degree of $0^{\circ}$.

• 한국재료학회지
• /
• 제21권4호
• /
• pp.196-201
• /
• 2011

It is known that the relative dielectric constant of insulating polyethylene matrix composites with conducting materials (such as carbon black and metal powder) increases as the conducting material content increases below the percolation threshold. Below the percolation threshold, dielectric properties show an ohmic behavior and their value is almost the same as that of the matrix. The change is very small, but its origin is not clear. In this paper, the dielectric properties of carbon black-filled polyethylene matrix composites are studied based on the effect medium approximation theory. Although there is a significant amount of literature on the calculation based on the theory of changing the parameters, an overall discussion taking into account the theory is required in order to explain the dielectric properties of the composites. Changes of dielectric properties and the temperature dependence of dielectric properties of the composites made of carbon particle and polyethylene below the percolation threshold for the volume fraction of carbon black have been discussed based on the theory. Above the percolation threshold, the composites are satisfied with the universal law of conductivity, whereas below the percolation threshold, they give the critical exponent of s = 1 for dielectric constant. The rate at which the percentages of both the dielectric constant and the dielectric loss factor for temperature increases with more volume fraction below the percolation threshold.

• 한국전기전자재료학회논문지
• /
• 제11권3호
• /
• pp.221-228
• /
• 1998

In this study, the $\beta$-Polyvinylidene fluoride(PVDF) thin films were fabricated by physical vapor deposition method. Also, the properties of dielectric relaxation were studied to understand carrier's behavior of PVDF thin films, to be regarded as the excellent piezo and pyroelectricity. In the process of vapor deposition, the $\beta$-PVDF thin films have been fabricated under the condition of the substrate temperature at 3$0^{\circ}C$, the applied electric field at 142.8kV/cm and the pressure at 2.0${\times}10^{-5}$torr. The dielectric properties of PVDF have been studied in the frequency range 10Hz to 1MHz at temperature from 30 to $100^{\circ}C$. The relative dielectric constant of $\alpha$ and $\beta$-PVDF were 6.8 and 9.8, respectively, under a frequency of 1kHz. Such a phenomenon was caused by the decrease in intermolecular forces originated by the phase-transition from the TGTG' molecular conformation to the TT planar zig-zag conformation. And the relative dielectric constant is increased as a measuring temperature increases, because of the reduction of relaxation time caused by the decrease of intermolecular force.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 1999년도 춘계학술대회 논문집
• /
• pp.325-328
• /
• 1999

The physical and electrical properties of $\textrm{Ba}_1$ $_{x}\textrm{Sr}_{x}$($\textrm{Mg_{1/3}Nb_{2/3}}$)$\textrm{O}_3$ (x =0, 0.2, 0.4, 0.6, 0.8, 1.0) ceramics were investigated. The Bal $_{x}\textrm{Sr}_{x}$($\textrm{Mg_{1/3}Nb_{2/3}}$)$\textrm{O}_3$ systems were shown that the hexagonally ordered superlattices were increased with increasing x values. The relative densities of all samples were over 97% theoretical densities. The dc resistivities of samples were $10^{13}$ - $10^{14}$$\Omega\textrm{cm}$at room temperature, these values were nearly constant at 130(x=0)-$230^{\circ}C$ (x=l). However, the resistivities of samples decreased rapidly above those temperature and their activation energies were from 1.0 to 1.52 eV. The relative dielectric constant was 33(BMN) and 30.6(SMN) respectively. And the highest value was shown at x=0.4 and the value was 34.3. The temperature coefficient of dielectric constant was -61 ppm/$^{\circ}C$(BMN) and 79 ppm/$^{\circ}C$ (SMN) respectively.

• Transactions on Electrical and Electronic Materials
• /
• 제10권2호
• /
• pp.49-52
• /
• 2009

Barium strontium calcium titanate powders were prepared with the sol-gel method. Ferroelectric $(Ba_{0.54}Sr_{0.36}Ca_{0.1})TiO_3$(BSCT) thick films were fabricated by the screen-printing method on alumina substrate. Then we investigated the structural and dielectric properties of the BSCT thick films at different sintering temperatures. The thermal analysis showed that the BSCT polycrystalline perovskite phase formed at around $660^{\circ}C$. The X-ray diffraction analysis showed a cubic perovskite structure with no second phase present in all of the BSCT thick films. The average grain size and the thickness of the specimens sintered at $1450^{\circ}C$ were about $1.6{\mu}m$ and $45{\mu}m$, respectively. The relative dielectric constant increased and the dielectric loss decreased as the sintering temperature was increased; for BSCT thick films sintered at $1450^{\circ}C$ the values of the dielectric constant and the dielectric loss were 5641 and 0.4%, respectively, at 1 kHz.

• 한국세라믹학회지
• /
• 제45권4호
• /
• pp.208-213
• /
• 2008

In this study, helical antenna with microwave ZST ceramics was designed using finite element method and developed. Studied parameters are relative dielectric constant of the dielectric core and the width of the conduction metal band of the antenna. As shown in the results, the center frequency of the antenna was decreased as the dielectric constant increased. Also beam width of the antenna increased as both the dielectric constant and the conduction band width increased. Based on the designed optimal shape, the manufactured antenna has the good beam width at center frequency 1.58 GHz.

• Transactions on Electrical and Electronic Materials
• /
• 제4권2호
• /
• pp.24-28
• /
• 2003

(Ba,Sr,Ca)TiO$_3$ powders, prepared by the sol-gel method, were mixed with organic binder and the BSCT thick films were fabricated by the screen printing techniques on alumina substrates. All the BSCT thick films, sintered at 1420$^{\circ}C$, showed the typical XRD patterns of a perovskite polycrystalline structure. The average grain sizes decreased with increasing amounts of ZrO$_2$, and the BSCT(40/40/20) thick films doped with 2wt% MnO$_2$ showed a value of 8$\mu\textrm{m}$. The thickness of thick films by four-cycle on printing/drying was approximately 951$\mu\textrm{m}$. The relative dielectric constant decreased with increasing Ca content and MnO$_2$ doping amount. The relative dielectric constant, dielectric loss and tunability of the BSCT(50/40/10) thick films doped with 2.0wt% ZrO$_2$ were 772, 0.184％ and 15.62%, respectively.

• 한국안전학회지
• /
• 제9권4호
• /
• pp.58-68
• /
• 1994

A miniature size electrostatic induction motor has been fabricated and studied parameters Influencing dominantly to the motor speed, such as a voltage and frequency of the 3 phase ac power source supplied to the stator of fabricated motor, the surface resistivity and relative dielectric constant of the rotor surface materials and the concurrently calculated relaxation time constants. It is found that the higher resitivity and/or the higher relative dielectric constant, concurrently the longer relaxation time constant of the rotor surface materials make the motor speed get higher speed. In case of discrete coated rotor surface it is found that the motor speed was increased logarithmically as narrow as width of the discrete coated Ti. And the degree of width of discrete coated Ti to the axial direction of the rotor was 60$^{\circ}$ and 150$^{\circ}$, the motor has got a 125% higher than that at the degree of 0$^{\circ}$.

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 1999년도 추계학술대회 논문집 학회본부 C
• /
• pp.845-847
• /
• 1999

(Ba, Sr)$TiO_3$[BST] thin films were fabricated on Pt/$TiO_2/SiO_2$/Si substrate by RF sputtering. The structural and dielectric properties of the BST thin films were investigated with the deposition time. Increasing the deposition time from 20 min. to 60 min., second phases were decreased, and EST (111), (100), (200) peaks were increased. The relative dielectric constant and dielectric loss of the EST thin films with the thickness of 3000$\AA$ were 300 and 0.018, respectively at 1[kHz]. The relative dielectric constants was decreased and dielectric losses was increased as increasing the frequency.