• Journal of the Korea institute for structural maintenance and inspection
• /
• v.19 no.1
• /
• pp.45-52
• /
• 2015

Fiber-reinforced polymer (FRP) has been generally accepted by civil engineers as an alternative for steel reinforcing bars (rebar) due to its advantageous specific tensile strength and non-corrosiveness. Even though some glass fiber reinforced polymer (GFRP) rebars are available on a market, GFRP is still somewhat uncompetitive over steel rebar due to their high cost and relatively low elastic modulus, and brittle failure characteristic. If the price of component materials of GFRP rebar is not reduced, it would be another solution to increase the performance of each material to the highest degree. The tensile strength generally decreases with increasing diameter of FRP rebar. One of the reasons is that only fibers except for fibers in center resist the external force due to the lack of force transfer and the deformation of only outer fibers by gripping system. Eliminating fibers in the center, which do not play an aimed role fully, are helpful to reduce the price and finally FRP rebar would be optimized over the price. In this study, the effect of the hollow section in a cross-section of a GFRP rebar was investigated. A GFRP rebar with 19 mm diameter was selected and an analysis was performed for the tensile test results. Parameter was the ratio of hollow section over solid cross-section. Four kinds of hollow sections were planned. A total of 27 specimens, six specimens for each hollow section and three specimens with a solid cross-section were manufactured and tested. The change by the ratio of hollow section over solid cross-section was analyzed and an optimized cross-section design was proposed.

• Proceedings of the Korea Concrete Institute Conference
• /
• 1993.04a
• /
• pp.130-135
• /
• 1993

Twelve 1/2 scale modeled wall specimens were tested statically up to failure to investigate she shear behavior of concrete walls reinforced with welded wire fabric. major variables were spacing of reinforcing bars, type of reinforcing bar(rebar, welded sire fabric, knurling wire) and the existence of tied column type reinforcement

• Proceedings of the Korea Concrete Institute Conference
• /
• 2004.05a
• /
• pp.834-837
• /
• 2004

In this study, the electric accelerated reinforcing bar corrosion test was carried out to estimate the coefficient of electrolytic corrosion based on the concept of Faraday's law according to rebar corrosion rate and concrete compressive strength which had an effect on the actual corrosion mass loss. The results of this paper allow the prediction of corrosion amount in the electric accelerated reinforcing bar corrosion test method.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.20 no.4
• /
• pp.120-127
• /
• 2016

Due to the enlargement and high-rise of reinforced concrete structure, the application of high functional material is required. However, high-strength bar is recently introduced to the country and the material is insufficient to measure the variation of quantity of rebar quantitatively when using high-strength bar. For these reasons, this study is to provide useful data in cost decision making when applying high-strength bar at a stage of architectural project planning. For residence-commerce complex buildings, we set up six types of conditions such as in case of using only rebar, in case of using only high-strength bar, in case of using rebar mixed with high-strength bar and so on. With the standard of study model 1 that applies only SD400 regardless of rebar diameter, the analyzed result of rebar variation and the cost change of construction in other study model is as follows. When the rebar amount and cost in study model I was 100%, each ratio was 88.3% and 90.5% in study model II, 80.2% and 83.4% in study model III, 91.9% and 93.5% in study model IV, 88.9% and 87.7% in study model V and 82.4% and 85.5% in study model VI. Therefore, in case of rebar amount and construction cost, study model III was evaluated as the best that was applied only SD600.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2001.05a
• /
• pp.345-350
• /
• 2001

Reinforced concrete is, in general, known as a high durability material due to a strong alkalinity of cement. Probable concrete cracks could incur steel corrosion of RC structures and then could easily deteriorate the concrete durability, which can be fully secured by a systematic quality control for the construction of concrete structures. For the corrosion protection of reinforcing steels in concrete, however, current design specifications of concrete cover depth do not in-depth consider the effect of the cracks as well as the chloride content of RC structures. Therefore, appropriate provisions for concrete cover depth should be coded by considering the influence of concrete cracks on the corrosion of reinforcing steels. The objective of this research is to investigate pertinent cover depth, which can prohibit rebar corrosion, on the basis of experimental corrosion measurements of reinforcing steels on crack characteristics such as the width, depth and frequency of concrete cracks.

• Structural Engineering and Mechanics
• /
• v.63 no.6
• /
• pp.725-734
• /
• 2017

This paper investigated the effects of rebar corrosion on bond performance between rebar and two different concrete mixes (compressive strengths of 20.7 MPa and 44.4 MPa). The specimen was designed as a rebar centrally embedded in a 200 mm concrete cube, with two stirrups around the rebar to supply confinement. An electrochemical accelerated corrosion technique was applied to corrode the rebar. 120 specimens of two different concrete mixes with various reinforcing steel corrosion levels were manufactured. The corrosion crack opening width and length were recorded in detail during and after the corrosion process. Three different loading schemes: monotonic pull-out load, 10 cycles of constant slip loading followed by pull-out and varied slip loading followed by pull-out, were carried out on the specimens. The effects of rebar corrosion with two different concrete mixes on corrosion crack opening, bond strength and corresponding slip value, initial slope of bond-slip curve, residual bond stress, mechanical interaction stress, and energy dissipation, were discussed in detail. The mean value and coefficient of variation of these parameters were also derived. It was found that the coefficient of variation of the parameters of the corroded specimens was larger than those with intact rebar. There is also obvious difference in the two different concrete mixes for the effects of rebar corrosion on bond-slip parameters.

• Journal of the Earthquake Engineering Society of Korea
• /
• v.13 no.1
• /
• pp.9-16
• /
• 2009

For reinforced concrete members, bond strength is one of the important factors between the two materials: the concrete and the reinforcing element. The bond strength of Aramid Fiber Reinforced Polymer (AFRP) rebar was tested using the pull-out method. Presented were comparison results of the bond strength between AFRP rebar and deformed steel bars from the test. Embedded lengths and diameters of the rebar were taken into account as parameters. The bond stress-slip responses and failure modes of AFRP rebar were evaluated. It was found that the bond stress-slip responses of AFRP rebar were similar to those of deformed steel bars. As the diameter of rebar increased, the pull-out load increased. In addition, it was shown that the bond strength of an AFRP rebar was approximately 54% compared with that of a deformed steel bar.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.25 no.3
• /
• pp.157-162
• /
• 2005

In order to evaluate the corrosion of reinforcing steel-bars (rebar) in concrete, a nondestructive evaluation by the half-cell potential method is currently applied. In this study, potentials measured on a concrete surface are compensated into those on the concrete-rebar interface by the inverse boundary element method (IBEM). Because these potentials are obtained three-dimensionally (3-D), 3-D visualization is desirable. To this end, a visualization system has been developed by using VRML (Virtual Reality Modeling Language). As an application, results of a reinforced concrete (RC) slab with corroded rebars are visualized and discussed.

• Journal of the Korea Concrete Institute
• /
• v.25 no.2
• /
• pp.137-144
• /
• 2013

The use of fiber-reinforced polymer (FRP) reinforcing bars in concrete structures has been increased as an alternative of steel reinforcement which has shown greater vulnerability to corrosion problem. However, the long-term performance of concrete members with FRP reinforcement is still questioned in comparison to the used of steel reinforcement. This study presents the results of an experimental study on the long-term behaviors of GFRP (glass fiber reinforced polymer) bar reinforced concrete beams after exposed to accelerated aging in an environmental chamber with temperature of $46^{\circ}C$ ($115^{\circ}F$) and 80% of relative humidity up to 300 days. The objectives of this research was to compare strength degradation and change of ductility between GFRP reinforced concrete beams and steel reinforcement beams after accelerated aging. Two types (wrapped and sand-coated surface) of GFRP bars and steel were reinforced. in concrete beams. Test results show that the failure modes of GFRP bar reinforced concrete beams are very similar with traditional RC beams, and the change of load-carrying capacity of steel reinforcing concrete beam is greater than that of GFRP bar reinforcing concrete beam under the accelerated aging. Test result also shows that the use of GFRP reinforcing in concrete could be introduced more brittle failure than that of steel reinforcing for practical application. The deformability factor up to compression failures indicates no significant variation before and after exposure of accelerated aging.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2019.05a
• /
• pp.252-253
• /
• 2019

Corrosion of rebars in reinforced concrete structures is a major factor that shortens the life of the structure. As corrosion progresses, the adhesion between the concrete tissues and the rebar decreases and the cracks in the concrete due to the expansion of the oxide intensify. Although it is necessary to measure corrosion behavior of rebars inside the concrete to measure degradation of structures due to rebar corrosion, no studies have been conducted to measure corrosion of rebars in In-situ state. In this study, corrosion of rebars in reinforced concrete specimens was attempted to be quantified using micro-computer tomography. Since corrosion of concrete takes several months per 10mm of cover, accelerated corrosion techniques were applied. Accelerated corrosion on the specimen was conducted by applying a 10 V magnetic field to the buried rebar and external electrodes with the specimen submerged in a 10% calcium chloride solution. The experiment found that within two weeks, more than 40% of rebar reduction occurred, and the cracks in the radial cracks occurred through the concrete structure, leading to the transfer of the oxide produced through the cracks to the surface of the specimen.