• International Journal of Highway Engineering
• /
• v.18 no.1
• /
• pp.57-62
• /
• 2016

PURPOSES : Reflection cracking has been one of the major causes of distress when asphalt pavement is laid on top of concrete pavement. This study evaluated the reflection cracking resistance of asphalt mixtures reinforced with asphalt embedded glass fiber and carbon fiber using a Texas Transportation Institute (TTI) overlay tester. METHODS : Different asphalt mixtures such as polymer-modified mastic asphalt (PSMA) and a dense graded asphalt mixture were reinforced with asphalt-embedded carbon fiber and glass fiber. For comparison purposes, two PSMA asphalt mixtures and one dense graded asphalt mixture were evaluated without fiber reinforcement. Two different overlay test modes, the repeated overlay test (R-OT) and monotonic overlay test (M-OT), were used to evaluate the reflection cracking resistance of asphalt mixtures at $0^{\circ}C$. In the R-OT test, the number of repeated load when the specimen failed was obtained. In the M-OT test, the tensile strength at the peak load and tensile strain were obtained. RESULTS : As expected, the fiber-reinforced asphalt mixture showed a higher reflection cracking resistance than the conventional nonreinforced asphalt mixtures based on the R-OT test and M-OT test. The dense graded asphalt mixture showed the least reflection cracking resistance and less resistance than the PSMA. CONCLUSIONS : The TTI overlay tester could be used to differentiate the reflection cracking resistance values of asphalt mixtures. Based on the R-OT and M-OT results, the carbon-fiber-reinforced asphalt mixture showed the highest reflection cracking resistance among the nonreinforced asphalt mixtures and glass-fiber-reinforced asphalt mixture.

• International Journal of Highway Engineering
• /
• v.7 no.2 s.24
• /
• pp.1-12
• /
• 2005

This study was conducted to evaluate effect of geogrid and fabric, which are used underneath the overlaid asphalt pavement for retarding reflection cracking by simulated laboratory test. In this study, an interlayer at the interface between old concrete pavement surface and overlaid asphalt mixture, and polymer-modifier were used as an effort of retarding reflection crack initiation and for strengthening mixture. Five products were used in preparation of asphalt concrete beam specimen which was tack coated on top of jointed concrete block. Simulated Mode I and II fracture test were conducted under wheel loading and results were compared among those products. From the test results, several material and reinforcement combinations were observed to have a significant retardation effect against reflection cracking. The most effectively strengthened pavement against reflection cracking was found to be the LDPE-modifier asphalt mixture with a grid reinforcement at the bottom.

• International Journal of Highway Engineering
• /
• v.5 no.3 s.17
• /
• pp.1-9
• /
• 2003

This study was performed to evaluate the effect of various joint sealant on reducing the reflection cracking of asphalt concrete overlay on cement concrete pavement. The test method used was an accelerated reflection cracking test in shear mode, which was developed for evaluation of reflection cracking resistance of overlaid asphalt concrete in laboratory. The test results showed that use of joint sealants resulted in a significant reduction of reflection cracking. When sealant E was used, the fatigue life was the highest, with relatively larger horizontal deformation. When Sealant B was used, the dynamic stability was the highest with the smallest horizontal deformation. In general, the greater the tensile strength of sealant, the better the crack resistance of the mixture.

• International Journal of Highway Engineering
• /
• v.2 no.4 s.6
• /
• pp.101-109
• /
• 2000

This study was performed to estimate fatigue life of polymer-modified and reinforced overlay asphalt mixtures with respect to reflection cracking in asphalt overlay pavement. In order to achieve the goal, the expedited reflection cracking test method was developed and applied to various mixtures and the results were compared one another with respect to the resistant characteristics of reflection cracking. The theoretical prediction equation of fatigue life for each mixture was suggested based on statistical analysis of experimental test results in the flexural failure mode. Since coefficients of correlation between estimated values and measured values were very high ($r^2=0.95$ or higher), the prediction model can be used for relative comparison of various pavement overlay choices to be used in the field.

• International Journal of Highway Engineering
• /
• v.7 no.4 s.26
• /
• pp.9-20
• /
• 2005

This study was carried out to select most efficient bonding methods of geogrid at the interface of old concrete pavement before placing asphalt overlay layer for reflection cracking retardation. Three bonding methods, a RSC-4 emulsified asphalt, a compound and an unsaturated polyester resin (UPR) were compared in this study. Three types of asphalt mixture (AC 60-80, RLDPE 8%, PG 76-22) and a dense-graded aggregate were used for overlay asphalt pavement. A reinforcing material which consists of a woven fabric underneath a glass fiber grid was used. An expedite test method which is for simulating mixed mode (mode I and II) fracture test was performed using a wheel tracker in laboratory. Cracking development by load repetition was measured as fatigue life (number of load cycle) and expansion of specimen body were measured for each test specimen. The results showed that UPR was the best and RSC-4 the next. But considering field applicability, RSC-4 was considered as an appropriate choice for bonding reinforcing material.

• International Journal of Highway Engineering
• /
• v.1 no.1
• /
• pp.97-106
• /
• 1999

This study was conducted to develop a test system for evaluating resistance against reflection cracking in shear mode caused by wheel load in asphalt concrete overlaid on the deteriorated cement concrete pavement. Reflection cracking resistance of selected polymer modified asphalt(PMA) mixtures with and without reinforcement was evaluated using this test system. It was shown that the test results accounted for the effectiveness of materials and reinforcement characteristics in terms of the difference in the resistance against reflection cracking. A shear failure life of a certain mixture was estimated with a high coefficient of determination. when the test results were used in a well known prediction model. Therefore, it seemed to be possible to use this technique for predicting a relative service life of on overlay.

• International Journal of Highway Engineering
• /
• v.1 no.1
• /
• pp.85-96
• /
• 1999

This study was performed to evaluate performance of polymer-modified asphalt mixtures and specially designed reinforcement techniques against reflection cracking of the asphalt pavement overlay. Selected polymers were used for asphalt modification and polyester fiber, a polypropylene film (vinyl) and a grid were used for mixture reinforcement. Using the asphalt mixture with optimum asphalt content, a slab was made and cut into two pieces of specimen. A layer of grid or vinyl was placed at the bottom of specimen to strengthen the pavement layer against crack. A repeated loading was applied to the asphalt mixture specimen which is Placed on a cement concrete with a pseudo-crack. Crack propagation under repeated loading was monitored and effectiveness of the devised crack retarding techniques was evaluated. From the test results. a significant retardation of mode I crack progress was monitored from some of the modified and reinforced asphalt mixtures.

• Journal of the Korean Geosynthetics Society
• /
• v.2 no.3
• /
• pp.39-46
• /
• 2003

The major pavement distress types found in the domestic roadways include rutting, fatigue cracking, and reflection cracking which are results of the environment and repeated traffic loads. These distresses usually occur before pavements approach their design life, and therefore, a significant amount of national budget is spent for maintenance of roadway pavements. The purpose of this study is to establish a geosynthetics-asphalt pavement system. For the study, wheel tracking tests are conducted to analyze the controlling effect of geosynthetics on rutting of asphalt pavement. On the basis of these works, the reinforcement effect of geosynthetics on the rutting of the asphalt pavement is clarified and deformation characteristics of geosynthetics-asphalt mixture is examined.

• International Journal of Highway Engineering
• /
• v.20 no.1
• /
• pp.87-95
• /
• 2018

PURPOSES : A geo-grid pavement, e.g., a stress-absorbing membrane interlayer (SAMI), can be applied to an asphalt-overlay method on the existing surface-pavement layer for pavement maintenance related to reflection cracking. Reflection cracking can occur when a crack in the existing surface layer influences the overlay pavement. It can reduce the pavement life cycle and adversely affect traffic safety. Moreover, a failed overlay can reduce the economic value. In this regard, the objective of this study is to evaluate the bonding properties between the rigid pavement and a SAMI by using the direct shear test and the pull-off test. The predicted fractural energy functions with the shear stress were determined from a numerical analysis of the moving average method and the polynomial regression method. METHODS : In this research, the shear and pull-off tests were performed to evaluate the properties of mixtures constructed using no interlayer, a tack-coat, and SAMI with fabric and without fabric. The lower mixture parts (describing the existing pavement) were mixed using the 25-40-8 joint cement-concrete standard. The overlay layer was constructed especially using polymer-modified stone mastic asphalt (SMA) pavement. It was composed of an SMA aggregate gradation and applied as the modified agent. The sixth polynomial regression equation and the general moving average method were utilized to estimate the interlayer shear strength. These numerical analysis methods were also used to determine the predictive models for estimating the fracture energy. RESULTS : From the direct shear test and the pull-off test results, the mixture bonded using the tack-coat (applied as the interlayer between the overlay layer and the jointed cement concrete) had the strongest shear resistance and bonding strength. In contrast, the SAMI pavement without fiber has a strong need for fractural energy at failure. CONCLUSIONS : The effects of site-reflection cracking can be determined using the same tests on cored specimens. Further, an empirical-mechanical finite-element method (FEM) must be done to understand the appropriate SAMI application. In this regard, the FEM application analy pavement-design analysis using thesis and bonding property tests using cored specimens from public roads will be conducted in further research.