• Journal of Industrial Technology
• /
• v.24 no.A
• /
• pp.165-171
• /
• 2004

Latex modification of concrete provides the material with higher flexural strength, as well as high bond strength and reduced water permeability. However, If the thermal expansion properties of overlay concrete (latex-modified concretes) are big different from that of substrate (ordinary portland cement concrete), these would cause a big interfacial stresses and result in premature failure. Therefore, the purposes of this study were to investigate thermal expansion characteristics of latex-modified concrete with cement types. The result of thermal expansion showed the coefficient of thermal expansion of concretes increased with latex inclusion. The coefficient of thermal expansion of RSLMC was a little smaller than that of LMC, which might be due to the finer cement grain, compacter internal, and stiffer properties of concrete. However, the coefficients of LMC and RSLMC were quite similar to that of ordinary cement concrete. Thus, this would not cause an interfacial stresses and will enable to ensure long-term performance of concrete bridge deck overlays.

• International Journal of Highway Engineering
• /
• v.4 no.2 s.12
• /
• pp.1-8
• /
• 2002

Latex modified concrete(LMC) became to be applied as a new material for newly constructed bridge deck overlays in Korea due to its excellent bond strength, flexural strength and impermeability against water and chloride. However, it could not be adopted at repair job site because of its long curing time required. Thus, a research on latex modified concrete with rapid-setting cement(RSLMC) is necessary if it could develope the sufficient strength for early opening to traffic. This study focused on the durability of latex modified concrete with rapid-setting cement mainly on water permeable resistance and freeze-thaw resistance. The main experimental variables were latex contents(0, 5, 10, 15 and 20%) and antifoamer contents (0, 1.6, 3.2, 4.8 and 6.4%). Test results show that the permeability of RSLMC is very low indicating below 100 coulombs at 15% of latex contents at all antifoamer contents. The freeze-thaw resistance of RSLMC maintains above 90% of relative dynamic modulus at 3.2% of antifoamer content until 300 freezing-thawing cycles.

• Journal of the Korea Concrete Institute
• /
• v.15 no.1
• /
• pp.95-101
• /
• 2003

Drying shrinkage cracking which may be caused by the relatively large specific surface is a matter of grave concern for latex modified concrete(LMC) overlay and rapid-setting cement latex modified concrete(RSLMC) overlay. LMC and RSLMC were studied for field applications very actively in terms of strength and durability in Korea. However, there were no considerations in drying shrinkage. Therefore, the purpose of this dissertation was to study the drying shrinkage properties of LMC and RSLMC with the main experimental variables such as cement types(ordinary portland cement, rapid setting cement), latex contents(0, 5, 10, 15, 20%) and curing days at a same controlled environment of 60% of relative humidity and $20^{\circ}C$ of temperature. The drying shrinkage for specimens was measured with a digital dial gauge of Demec. The test results showed that the drying shrinkage of LMC and RSLMC were considerably lower than that of OPC and RSC, respectively. This might be attributed to the interlocking of hydrated cement and aggregates by a film of latex particles, water retention due to hydrophobic, and colloidal properties of the latexes resulting in reduced water evaporation.

• Journal of Industrial Technology
• /
• v.21 no.B
• /
• pp.249-256
• /
• 2001

The purpose of this study was to remove the excessive air foaming which was produced in mixing the RSLMC(latex-modified concrete with rapid-setting cement) by choosing the best antifoam agent type. A series of RSLMM(latex-modified mortar with rapid-setting cement) experiments were carried out as a basic experiments for RSLMC with the main experimental variables such as antifiamer types(A, B, C, D), antifoamer contents(0, 1, 2, 3%), and latex contents(10, 15%). Air content test and compressive strength tests were carried out to measure the improved properties of RSLMM. SEM analysis, also, was carried to observe the formation of latex film. The results of RSLMM showed that the decrease of 50% air content was obtained by admixturing an antifoam agent by 1%. This made the strength enhanced and the workability be within the purposed. The best properties of compressive strengths was obtained at latex content of 15% and D antifoam agent of 1%. compressive strength increased about 32.6%. The analysis of SEM results no difference in a formation of later film.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2002.10a
• /
• pp.757-762
• /
• 2002

This study focused on the investigation of durability of latex modified concrete in the points of surface scaling resistance as cement types variated and latex content variated such as 5%, 10%, 15%, and 20%. An increasing the amount of latex produced concrete with increased flexural strength, but with slightly lower compressive strength. The increase in flexural strength might be attributed to the latex films between the hydrated cement and aggregates, and the decrease in compressive strength to the flexibility of the latex component named by Butadiene. The surface scaling resistance test was used to evaluate the durability of latex-modified concretes and rapid setting latex-modified concretes. The surface scaling resistance of LMC was quite good comparing to conventional concrete. Further, surface scaling resistance of RSLMC was improved with increasing the latex content.