• Journal of Korea Technical Association of The Pulp and Paper Industry
• /
• v.39 no.1 s.119
• /
• pp.25-29
• /
• 2007

Print mottle is the spotty and cloudy appearance of the ink on the substrate. Print mottle is influenced significantly by the characteristics of the paper with regard to homogeneity of its structure and its coating. The print mottle can be counteracted, in particular by altering the absorption characteristics of the inks, by changing sequence in which the inks are printed, or by using a advanced coated paper. In this study, we investigated the effect of ink dispersion to the print mottle through trial printing test and also analyzed the correlation between properties of coated paper and subjective results by statistic method. The result of this study is expected to be applied the basic data to solve the problem of printing mottle.

• Journal of Korea Technical Association of The Pulp and Paper Industry
• /
• v.45 no.5
• /
• pp.37-43
• /
• 2013

This study was focused on applying a new paper coating binder, vinyl acetate-ethylene(VAE) emulsion, with SB-latex and acrylic emulsion for paper coating application. VAE emulsion has a low monomer cost and is non-toxic chemical than conventional adhesive for paper coating such as styrene-butadiene latex( SB-latex) and acrylic emulsion. We conducted double coating in order to test VAE emulsion, which was applied on top surface only. The results showed that optical properties of the coated paper with VAE were similar with the SB-latex binders. In case of bonding strength, dry-pick of the coated paper with VAE showed almost same with other binders while wet-pick of the coated paper with VAE had a little bit lower strength than that with SB-latex.

• Journal of Korea Technical Association of The Pulp and Paper Industry
• /
• v.38 no.4 s.117
• /
• pp.47-52
• /
• 2006

This study is about the effect from properties of coated paper and ink dispersion to the printed mottle. Ink receptivity would be expected that it is mainly effected by roughness of coated paper Because the transfer of ink can not be uniform with rough surface, it will cause the optical appearance such like printed mottle. And also it may be able to cause the printed mottle from uneven transfer of ink due to absorption property of based paper, depend on size degree, by using dampening in Off-set printing. Each different specific of surface and ink dispersion could cause printed mottle. Therefore this study was carried out by using densitometer and image analysis to show the interaction between properties of domestic coated paper and ink dispersion.

• Journal of Korea Technical Association of The Pulp and Paper Industry
• /
• v.43 no.4
• /
• pp.76-81
• /
• 2011

This study was carried out in order to develop a speciality functional coated paper, which can be recognized under a ultraviolet lamp. The special fluorescent whitening agent (FWA) which absorbs ultraviolet light (397~410 nm) and emits it as yellowish light (570~500nm) was used. The special FWA was applied in a coating color in two ways: (1) direct application to a coating color as a FWA; (2) application on pigment surface, drying it and application it as a fluorescence whitening pigments (colored pigments). The effects of the special FWA on coating color properties were tested and the distribution of colored pigments in coated paper was evaluated under a ultraviolet lamp. The results showed that the colored pigments didn't affect on coating color properties. Experimental results showed the possibility of producing a security coated paper using the special FWA. To produce a speciality functional paper, it was found to be proper to apply the special FWA in the form of colored pigment.

• Proceedings of the Korea Technical Association of the Pulp and Paper Industry Conference
• /
• 1999.04a
• /
• pp.1-6
• /
• 1999

A study was made to determine the effect of plastic pigment on the coating structure and printability of coated paper. Three basic plastic pigments were investigated such as solid-bead type of plastic pigment, binder type of plastic pigment and hollow type of plastic pigment. In the systems investigated, it was observed that particle shape and structure of plastic pigment had influenced on the rheology of coating color, the state of packing, and the properties of coated paper. The materials investigated were restricted to plastic pigments commonly uesd in paper coating formualtion. Inorganic pigments used in this research were kaolin clay which is platelets and calcium carbonate which is rhombic. Three kinds of plastic pigments were blended in the color made up with two inorganic pigments, respectively. The combination of pigments were carried out (1) to determined the effect of paticle structure of plastic pigment on the state of dispersion of coating color, (2) to observe the effect of temperature of calender on the property of coated paper prepared with plastic pigment. The data indicated that binder and hollow type of plastic pigment had the best results on improving the properties of coated paper such as paper gloss, opacity and air permeability ect. and solid-bead type of plastic pigment in the next place.

• Journal of Korea Technical Association of The Pulp and Paper Industry
• /
• v.48 no.1
• /
• pp.27-33
• /
• 2016

This study was carried out in order to investigate the effect of binder properties in pre-coating layer on the characteristics of top-coating layer and print mottle of coated paper. Four different latices were used as a binder in pre-coating layer, and coating color prepared with a same formulation was applied for top-coating. The properties and print mottle of coated paper were evaluated. It was found that glass transition temperature (Tg) was the important factor to control the properties of pre- and top-coating layer. PPS roughness of coated paper was decreased and paper gloss was increased with applying binder which has lower Tg. Properties of top-coating layer were affected by the binder used in pre-coating layer. Print mottle of coated paper was improved with using binder which has lower Tg in pre-coating layer. These results indicate that final printability and properties of top-coating layer can be improved with using suitable binder in pre-coating layer.

• Journal of Korea Technical Association of The Pulp and Paper Industry
• /
• v.48 no.2
• /
• pp.61-67
• /
• 2016

This study was carried out in order to investigate the effect of pigment properties in a pre-coating layer on the characteristics of a top-coating layer and the print mottle of the coated paper. Five different pigments were applied for this study as raw materials for the pre-coating layer. The properties and print mottle of the coated paper samples were evaluated according to the coating color formulation. Type of pigments appliied in a pre-coating layer was one of the most important factor to control the properties of pre and top coating layer. Surface properties of pre and top coated paper were improved by blending GCC which had smaller particle size, with clay. Properties of a top-coating layer was affected by the pigment properties used in the pre-coating layer. It was found that print mottle of coated paper can be improved by replacing part of GCC with smaller particle size GCC or clay in pre-coating layer.

• Journal of Korea Technical Association of The Pulp and Paper Industry
• /
• v.43 no.3
• /
• pp.30-34
• /
• 2011

This study was carried out in order to evaluate the effect of coated weight and calender pressure on conductivity of printed RFID tags. The printed RFID tags have been manufactured with gravure printing and it has been well known that the efficiency of printed RFID tags is influenced by surface properties of substrate. In this study, coated paper was prepared with four different coated weight and three different calender pressure. After printing conductivity ink on coated paper, surface resistance was measured to evaluate the efficiency of the printed RFID tag. It was found that, with increasing of coated weight and calender pressure, the paper gloss, smoothness, brightness and gravure printability were improved while the surface resistance of the printed RFID tag was decreased.

• Journal of Korea Technical Association of The Pulp and Paper Industry
• /
• v.44 no.2
• /
• pp.1-7
• /
• 2012

Hanji made of mulberry fibers has the lower printability due to their long fiber length, the diffusible property of ink, and low smoothness. This study was carried out to analyze the physical and optical properties of machine-made Hanji controlled by the different contents of paper mulberry 20, 40, 60, 80 and 100%. In this study, the results of comparing machine-made Hanji controlled by the different contents of $Paper$ $mulberry$ with commercial paper and inkjet coated paper are as following: Tearing strength of machine-made Hanji is higher than domestic paper and inkjet coated paper. By increasing paper mulberry contents of machine-made Hanji appeared that tensile strength increased and smoothness gradually decreased. Printability of machine-made Hanji is less than domestic paper and inkjet coated paper. However, there were significant possibility to use for printing paper.

• Journal of Korea Technical Association of The Pulp and Paper Industry
• /
• v.30 no.2
• /
• pp.62-73
• /
• 1998

The aim of this work was to investigate the effects of pigment composition on the calendering response and structure of the coated paper. Calendering response of the coated paper was determined from the gloss values of the uncalendered and calendered coated papers, and the relationship between gloss and coating structure was discussed. The surface and cross section of the coating layer was observed using a scanning electron microscope to examine the coating structure. Coating layers were hardened in epoxy resin and polished with carbimet paper disc for preparing SEM samples. Maximum calendering response was obtained for the coated paper prepared from 80pph of clay and 20pph of ground calcium carbonate (GCC) as pigments. Photomicrographs of the surface and cross section of the coating layer show that clay tends to form dense coating structure, while GCC tends to form bulky coating layer.