• Proceedings of the Korean Vacuum Society Conference
• /
• 2011.02a
• /
• pp.334-334
• /
• 2011

We applied N-ion bombardment and heat treatment to the Cu thin films deposited on aluminum oxide layer for the enhancement of adhesion. With e-beam evaporation method. $1,000{\AA}$ thick Cu pre-bombardment layer was deposited on the aluminum oxide surface and then N-ion beam was bombared in order to mix the atoms at the film/substrate interface. Additional $4,000{\AA}$-thick Cu film was the coated. Subsequently, the ion mixide Cu on aluminum oxide was annealed at $200^{\circ}C$ and $300^{\circ}C$ in vacuum.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09b
• /
• pp.1000-1001
• /
• 2006

Two atomized alloy powders were pre-compacted by cold and subsequently hot forged at temperatures ranging from 653K to 845K. The addition of Cu and Mg causes a decrease in the eutectic reaction temperature of Al-10Si-5Fe-1Zr alloy from 841K to 786K and results in a decrease of flow stress at the given forging temperature. TEM observation revealed that in addition to Al-Fe based intermetallics, $Al_2Cu$ and $Al_2CuMg$ intermetallics appeared. The volume fraction of intermetallic dispersoids increased by the addition of Cu and Mg. Compressive strength of the present alloys was closely related to the volume fraction of intermetallic dispersoids.

• Corrosion Science and Technology
• /
• v.6 no.4
• /
• pp.198-205
• /
• 2007

The initial stages of electrochemical oxidative CuI film formation on Cu(111), as studied by means of Cyclic Voltammetry (CV), in-situ Scanning Tunneling Microscopy (STM) and ex-situ Synchrotron X-ray Photoemission Spectroscopy (SXPS), indicate a significant acceleration of copper oxidation in the presence of iodide anions in the electrolyte. A surface confined supersaturation with mobile CuI monomers first leads to the formation of a 2D-CuI film via nucleation and growth of a Cu/I-bilayer on-top of a pre-adsorbed iodide monolayer. Structurally, this 2D-CuI film is closely related to the (111) plane of crystalline CuI (zinc blende type). Interestingly, this film causes no significant passivation of the copper surface. In an advanced stage of copper dissolution a transition from the 2D- to a 3D-CuI growth mode can be observed.

• 한국초전도학회:학술대회논문집
• /
• v.9
• /
• pp.315-318
• /
• 1999

Bi$_{2}Sr_{2}CaCu_{2}O_{\delta}$ superconducting films were rapidly fabricated on copper tape by liquid reaction between a Cu-free precursor and Cu tape (LiReac-PreCu) method. Those thick films were well oriented along the c-axis. The precursor was made by melt-quenched technology using twin roller. The melt-quenched films were transparent and glossy yellow in appearance. These films which were the compostion of Bi$_2SrCaO_y$, Bi$_3Sr_2CaO_z$ were placed on copper tape and then heated at various temperatures for several minutes in air. They were analyzed using X-ray powder diffraction, SEM, a DC four-probe method. The mechanism of superconducting phase formation . from the melt-quenched precursor on Cu tape was studied

• ETRI Journal
• /
• v.33 no.6
• /
• pp.864-870
• /
• 2011

As an isotropic conductive adhesive, that is, a hybrid Cu paste composed of Cu powder, solder powder, and a fluxing resin system, has been quantitatively characterized. The mechanism of an electrical connection based on a novel concept of electrical conduction is experimentally characterized using an analysis of a differential scanning calorimeter and scanning electron microscope energy-dispersive X-ray spectroscopy. The oxide on the metal surface is sufficiently removed with an increase in temperature, and intermetallic compounds between the Cu and melted solder are simultaneously generated, leading to an electrical connection. The reliability of the hybrid Cu paste is experimentally identified and compared with existing Ag paste. As an example of a practical application, the hybrid Cu paste is used for LED packaging, and its electrical and thermal performances are compared with the commercialized Ag paste. In the present research, it is proved that, except the optical function, the electrical and thermal performances are similar to pre-existing Ag paste. The hybrid Cu paste could be used as an isotropic conductive adhesive due to its low production cost.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.17 no.1
• /
• pp.21-27
• /
• 2016

Global warming due to greenhouse gas emissions is considered as a major problem worldwide, and many countries are making great efforts to reduce carbon dioxide emissions. Many technologies in post-combustion, pre-combustion and oxy-fuel combustion $CO_2$ capture have been developed. Among them, a hybrid pre-combustion $CO_2$ capture system of a water gas shift (WGS) reactor and a membrane gas separation unit was investigated. The 2 stage WGS reactor integrated high temperature shift (HTS) with a low temperature shift (LTS) was used to obtain a higher CO conversion rate. A Pd/Cu dense metal membrane was used to separate $H_2$ from $CO_2$ selectively. The performance of the hybrid system in terms of CO conversion and $H_2$ separation was evaluated using a 65% CO, 30 % $H_2$ and 5% $CO_2$ gas mixture for applications to pre-combustion $CO_2$ capture. The experiments were carried out over the range of WGS temperatures ($200-400^{\circ}C$), WGS pressures (0-20bar), Steam/Carbon (S/C) ratios (2.5-5) in a feed gas flow rate of 1 L/min. A very high CO conversion rate of 99.5% was achieved with the HTS-LTS 2 stage water gas shift reactor, and 83% $CO_2$ was concentrated in the retentate using the Pd/Cu membrane.

• Journal of Powder Materials
• /
• v.25 no.4
• /
• pp.322-326
• /
• 2018

The hydrogen reduction behavior of $MoO_3-CuO$ powder mixture for the synthesis of homogeneous Mo-20 wt% Cu composite powder is investigated. The reduction behavior of ball-milled powder mixture is analyzed by XRD and temperature programmed reduction method at various heating rates in Ar-10% $H_2$ atmosphere. The XRD analysis of the heat-treated powder at $300^{\circ}C$ shows Cu, $MoO_3$, and $Cu_2MoO_5$ phases. In contrast, the powder mixture heated at $400^{\circ}C$ is composed of Cu and $MoO_2$ phases. The hydrogen reduction kinetic is evaluated by the amount of peak shift with heating rates. The activation energies for the reduction, estimated by the slope of the Kissinger plot, are measured as 112.2 kJ/mol and 65.2 kJ/mol, depending on the reduction steps from CuO to Cu and from $MoO_3$ to $MoO_2$, respectively. The measured activation energy for the reduction of $MoO_3$ is explained by the effect of pre-reduced Cu particles. The powder mixture, hydrogen-reduced at $700^{\circ}C$, shows the dispersion of nano-sized Cu agglomerates on the surface of Mo powders.

• Transactions of Materials Processing
• /
• v.4 no.2
• /
• pp.169-179
• /
• 1995

Static restoration mechanism during hot interrupted deformation of Cu-Zn alloy was studied in the temperature range from $550^{\circ}C$ to $750^{\circ}C$ and at a constant strain rate of 0.1/sec. At a given temperature, the hot interrupted deformations were performed with variation of interrupted time $t_i$ form 1 to 50 sec and of interrupted strain ${\varepsilon}_i$ from 0.15 to 0.90. From the analysis of the values of the critical strain of ${\varepsilon}_c$ for tje initiation of dynamic recrystallization and the peak strain of${\varepsilon}_p$, the relationship ${\varepsilon}_c{\fallingdotseq}0.7{\varepsilon}_p$ was obtained. It was clarified that the softening of the interrupted deformation was mainly the static recrystallization and the fractional softening(FS) which was over 30% mostly confirmed this result. The fractional softening of the interrupted time $t_i$ especially and pre-strain. The FS increased with increasing strain rate, interrupted time and pre-strain. The change of microstructures after hot deformation could be predicted by the FS. when the FS was 30~100%, static recrystallization was happened and grain growth was observed at the condition which was $750^{\circ}C$ deformation temperature, 0.45 prestrain and this condition's FS value was over 100%.

• Textile Coloration and Finishing
• /
• v.12 no.6
• /
• pp.389-395
• /
• 2000

A natural colorants was extracted from cherry by 10wt% aqueous acetic acid solution as an extractant. Silk and cotton fabrics were dyed with the cherry extract in the temperature range of $40-80^\circ{C}$ and for the time range of 30-60min. by pre- and post-mordanting with various mordants, their dyeability and fastness were investigated. The natural cherry extract prepared in this study has a maximum absorbance at 520nm. It was found that the optimum dyeing temperature and time were $40^\circ{C}$ and 50min, respectively. The pre-mordanting method was more effective than post-mordanting. All mordants except $SnCl_2\cdot{2H}_2O\;and\;FeSO_4\cdot{7H}_2O$ were effective for silk fabrics. However, the dyeability on cotton fabrics increased in the order of $CrK(SO_4)_2\cdot{12H_2O>(CH_3COO)_2Cu\cdot{H}_2O>CuSO_4\cdot{5H}_2O>AlK(SO_4)_2\cdot{12H}_2O>FeSO_4\cdot{7H}_2O>SnCl_2\cdot{2H}_2O$ among the mordants used in this study Fastness(light, water, washing, perpspiration fastness) on the silk and cotton fabrics increased with using mordants. The post-mordanting using mordant$(CH_3COO)_2Cu\cdot{H}_2O$ among the various mordants in this study gave the best fastness.

• Journal of the Korean institute of surface engineering
• /
• v.35 no.5
• /
• pp.279-288
• /
• 2002

Zinc phosphating for cold forming of steel was studied with emphasis on decreasing phosphating temperature. To lower phosphating temperature, some techniques, such as adding Cu ion into bath, using activator in the form of pre-dip, and aeration in bath, instead of using conventional accelerator, namely oxidizing agent, have been tried. It was revealed that phosphating, leading to coatings of Improved uniformity and fine crystal size, can be carried out using above techniques at lower temperature ($55^{\circ}C$) compared to conventional phosphating temperature ($80 ~ 90^{\circ}C$ ). Under present condition, it was seen that optimum concentrations of Cu ion in phosphating bath and activator in pre-dip are 0.015% (w/w) and 2.0 g/1, respectively. The coating weight was within the range of 15 ~ 20 g/$\m^2$. When lubricant was applied into phosphating coatings, the amount of lubricating component (total soap) was found to be 6 ~ 10 g/$\m^2$ and the lubricated panel revealed excellent lubricating properties.