This study evaluated the quality characteristic of red pepper powders of Hanbando and Cheongyang cultivars by particle size. Two types of powder samples for pepper paste and Kimchi were prepared, and capsaicinoid contents, Hunter Lab color values, and ASTA values by particle size distribution were investigated. Particle size distribution was normal in the pepper paste powder; however, an abnormal distribution was shown for the Kimchi powder. In addition, the greatest particle sizes were $300{\sim}425\;{\mu}m$ in the pepper paste powder. In accordance with smaller particle size, redness (a-value), ASTA values, and capsaicinoid contents increased. Redness (a-value) by particle size was in the range of 15.13~31.34, and ASTA values were in the range of 53.35~96.87. Capsaicinoid contents by particle size were in the range of 1.90~6.05 mg/100 g for Hanbando and 156.65~235.10 mg/100 g for Cheongyang.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09a
• /
• pp.654-655
• /
• 2006

This is about the effects deoxidization, carbonization and alloying preparation on fine grain W, WC, and grade YG8 powder reduced by "yellow tungsten oxide" and "blue tungsten oxide". The result indicates that yellow tungsten has single composition and blue tungsten oxide has complex composition. With this feature, yellow tungsten oxide got better uniformity and concentration distribution on fine particle size W and WC powder than blue tungsten oxide's. The grade alloy YG8 that made of this W or WC powder has uniform alloy construction, concentrated WC grain distribution and better alloy properties.

• Journal of Powder Materials
• /
• v.18 no.3
• /
• pp.221-225
• /
• 2011

In the current study, the effects of particle size on compaction behavior of water-atomized pure iron powders are investigated. The iron powders are assorted into three groups depending on the particle size; 20-45 ${\mu}M$, 75-106 ${\mu}M$, and 150-180 ${\mu}M$ for the compaction experiments. The powder compaction procedures are processed with pressure of 200, 400, 600, and 800 MPa in a cylindrical die. After the compaction stage, the group having 150-180 ${\mu}M$ of particle size distribution shows the best densification behavior and reaches the highest green density. The reason for these results can be explained by the largest average grain size in the largest particle group, due to the low plastic deformation resistance in large grain sized materials.

• Journal of Powder Materials
• /
• v.2 no.1
• /
• pp.29-35
• /
• 1995

In this study the calcined condition and characteristic of Cu-Ni-Zn ferrite powder were investigated. The Cu-Ni-Zn ferrite powder has been synthesized by the thermal decomposition of the organic acid salt. This process did not require a strict pH control and provided the uniform composition and fine powder with about 0.3 $\mu\textrm{m}$. The XRD diffraction pattern of this powder showed about 50% spinel phase. The optimum calcination was found to be done at $700^{\circ}C$ for one hour. After the calcination, the amount of spinel increased to 90%. The distribution of the particle size showed bimodal peaks, one was about 0.5 $\mu\textrm{m}$ and the other was about 20 $\mu\textrm{m}$. The large particles of 20 $\mu\textrm{m}$ were the agglomeration of fine Particles. The mean Particle size of the powder was about 0.4 $\mu\textrm{m}$. The powder was compacted under 100 MPa pressure and sintered at 1100~ $1250^{\circ}C$ for one hour in air. The density of ferrites specimen was a function of the sintering temperature. The higher the temperature, the denser the ferrite. The maximum relative density of the sintered ferrite was about 93% at $1250^{\circ}C$. The grain size of sintered specimen at $1200^{\circ}C$ was 5 $\mu\textrm{m}$ and homogeneous.

• Elastomers and Composites
• /
• v.38 no.2
• /
• pp.128-138
• /
• 2003

It goes to be serious with environmental pollution because of great number of waste tires scrapped each you. That is why there are lots of studies for efficient recycle. We tried to reduce particle size of the waste tire powder using a new technology of self-designed grinding machine (SDGM) and ultrasonic treatment. The purpose of this study is to improve the physical properties of reduced waste tire powder. We investigated the fine powder by particle size distribution(PSD) analysis. And also we examined the physical and mechanical properties and cross-link density at various particle sire. Also we carried out morphological studies after making the products by SEM.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09b
• /
• pp.1266-1267
• /
• 2006

[ $MgZn_{4.3}Y_{0.7}$ ] alloy powders were prepared using an industrial scale gas atomizer, followed by warm extrusion. The powders were almost spherical in shape. The microstructure of powders as atomized and bars as extruded was examined as a function of initial powder size distribution using Scanning Electron Microscope (SEM), Energy Dispersive X-ray Spectroscope (EDS) and X-ray Diffractometer (XRD). The grain sizes were decreased with extruding as well as decreasing the initial powder sizes. Both the ultimate strength and elongation were enhanced as the initial powder sizes were decreased.

• Journal of Korea Foundry Society
• /
• v.10 no.2
• /
• pp.154-161
• /
• 1990

The microstructures of sintered products of $Fe_2O_3$or $Fe_3O_4$-Oxide added cast iron powder was investigated. And the effects of particle size distribution was investigated too. As the result, the structures of sintered products did not related to the species of Fe-Oxide. Th porosity of sintered products was decreased in size and spherodized with increasing sintering temperature, decreasing Fe-Oxide quantity. Fe-Oxide itself did not hinder sintering of cast iron powder particularly, therefore sintering could be occurred without termination of reduction of it. And the sintered products of finer particle size distribution had finer and more spherodized porosity, and had minimized the deviation of size and shape of porosity.

• Resources Recycling
• /
• v.14 no.6 s.68
• /
• pp.21-27
• /
• 2005

As one of the hydrometallurgical processes available in the recycling of silver-bearing wastes, the preparation of Ag nano-powder was investigated by a reductive precipitation reaction in silver solution using sodium formaldehydesulfoxylate and ascorbic acid as a reducing agent. Silver solution was prepared by dissolving silver nitrate with distilled water, and Tamol NN8906, PVP, SDS and caprylic acid were also used respectively as the dispersant to avoid the agglomeration of particles during the reductive reaction. Ag particles obtained from the reduction reaction from silver solution were characterized using the particle size analyzer and TEM to determine the particle size distribution and morphology. It was found that about $40\%$ excess of sodium formaldehydesulfoxylate was required to reduce completely silver ions in the solution. It alto appeared that the particle size generated with sodium formaldehydesulfoxylate was much greater than that with ascorbic acid. As far as the effect of dispersant on the Ag particles was concerned, the particle size distribution showed typically bimodal distribution in case of Tamol/FVP while very broad distribution ranged from 0.01 to $100{\mu}m$ appeared in case of SDS/caprylic acid.

• Resources Recycling
• /
• v.12 no.6
• /
• pp.38-46
• /
• 2003

In this study, nano-sized Ni-ferrite and $Fe_2$$O_3$＋NiO powder was fabricated by spray pyrolysis process in the condition of 1kg/$\textrm{cm}^2$ air pressure using the Fe-Ni complex waste acid solution generated during the manufacturing process of shadow mask. The average particle size of the produced powder was below 100 nm. The effects of the reaction temperature, the concentration of raw material solution and the nozzle tip size on the properties of powder were studied. As the reaction temperature increased from $800 ^{\circ}C$ to $1100^{\circ}C$, the average particle size of the powder increased from 40 nm to 100 nm, the structure of the powder gradually became solid, yet the distribution of the particle size appeared more irregular. Along with the increase of the reaction temperature, the fraction of the Ni-ferrite phase were also on the rise, and the surface area of the powder was greatly reduced. As the concentration of Fe in solution increased from 20g/l to 200g/l, the average particle size of the powder gradually increased from 30 nm to 60 nm, while the distribution of the particle size appeared more irregular. Along with the increase of the concentration of solution, tie fraction of the Ni-ferrite phase was on the rise, and the surface area of the powder was greatly reduced. Along with the increase of the nozzle tip size, the distribution of the particle size appeared more irregular, yet the average particle size of the powder showed no significant change. As the nozzle tip size increased from 1 mm to 2 mm, the fraction of the Ni-ferrite phase showed no significant change, while the surface area of the powder slightly reduced. As the nozzle tip size increased to 3 mm and 5 mm, the fraction of the Ni-ferrite phase gradually reduced, and the surface area of the powder slightly increased.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09b
• /
• pp.994-995
• /
• 2006

The microstructure of the extruded Al-20Si bars showed a homogeneous distribution of eutectic Si and primary Si particles embedded in the Al matrix. The grain size of ${\alpha}-Al$ varied from 150 to 600 nm and the size of the eutectic Si and primary Si in the extruded bars was about 100 - 200 nm. The room temperature tensile strength of the alloy with a powder size $<26{\mu}m$ was 322 MPa, while for the coarser powder ($45-106{\mu}m$) it was 230 MPa. With decreasing powder size from $45-106{\mu}m$ to $<26{\mu}m$, the specific wear of all the alloys decreased significantly at all sliding speeds due to the higher strength achieved by ultrafine-grained constituent phases. The fracture mechanism of failure in tension testing and wear testing was also studied.