• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.6 no.6
• /
• pp.468-472
• /
• 2005

In order to prevent adhering of molten glass on a mold wall, the wall is swabbed with lubricant oil before forming. However, the swabbing process can be removed from the entire processes of the glass forming if the mold wall is made of a porous sintered material. The purpose of the present study is to manufacture a sintered material(having a sintered density of $85{\~}90\%$)which is the most appropriate into. plane material for a glass mold. For the research, SUS310L-based coarse powder (${\~}150{\mu}m$) and SUS420J2-based fine powder ($40{\~}50{\mu}m$) were used for the compact materials, and effects of compaction pressure and sintering condition(atmosphere, temperature) were investigated. The results obtained were as fellows. (1) By means of solid phase sintering, a desired sintering density could not be achieved in any case when using a 310L-based powder having a large particle size. (2) When sintering green compacts(compaction pressure of $2ton/cm^2$) in a commercial vacuum furnace(at $1300^{\circ}C$ for 2 hours), the sintered compacts had densities of $6.2g/cm^3(79\%)$ for 310L + 0.03$\%$B, $6.6g/cm^3 (86\%)$ for 420J2, $7.3g/cm^3(95\%)$ for 420J2+(0.03)$\%$B, and $7.6g/cm^3(99\%)$ for 420j2+(0.06)$\%$B, respectively. As a result, it is regarded that sintered compacts having a desired porosity may be achieved by vacuum sintering the 420J2-based powder (low pressure compaction) and the 310L+0.03$\%$B-based powder (high pressure compaction).

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2004.11a
• /
• pp.84-85
• /
• 2004

• Journal of the Korean Ceramic Society
• /
• v.53 no.1
• /
• pp.43-49
• /
• 2016

This analyzed a Young's modulus (E), a thermal expansion coefficient (TEC, ${\beta}$) and a thermal conductivity (${\kappa}$) of the material with simple cubic particulate inclusion using two model structures: a parallel structure and a series structure of laminated layers. The derived ${\beta}$ equations were applied to calculate the ${\beta}$ value of the W-MgO system. The accuracy was higher for the series model structure than for the parallel model structure. Young's moduli ($E_c$) of sintered porous alumina compacts were theoretically related to the development of neck growth of grain boundary between sintered two particles and expressed as a function of porosity. The series structure model with cubic pores explained well the increased tendency of $E_c$ with neck growth rather than the parallel structure model. The thermal conductivity of the three phase system of alumina-mullite-pore was calculated by a theoretical equation developed in this research group, and compared with the experimental results. The pores in the sintered composite were treated as one phase. The measured thermal conductivity of the composite with 0.5-25% porosity (open and closed pores) was in accordance with the theoretical prediction based on the parallel structure model.

• Journal of the Korean Ceramic Society
• /
• v.51 no.1
• /
• pp.19-24
• /
• 2014

Three-layer porous alumina-mullite composites with a symmetric gradient porosity are prepared using a controlled freeze/gel-casting method. In this work, tertiary-butyl alcohol (TBA) and coal fly ash with an appropriate addition of $Al_2O_3$ were used as the freezing vehicle and the starting material, respectively. When sintered at $1300-1500^{\circ}C$, unidirectional macro-pore channels aligned regularly along the growth direction of solid TBA were developed. Simultaneously, the pore channels were surrounded by less porous structured walls. A high degree of solid loading resulted in low porosity and a small pore size, leading to higher compressive strength. The sintered porous layered composite exhibited improved compressive strength with a slight decrease in its porosity. After sintering at $1500^{\circ}C$, the layered composite consisting of outer layers with a 50 wt% solid loading showed the highest compressive strength ($90.8{\pm}3.7MPa$) with porosity of approximately 26.4%.

• Resources Recycling
• /
• v.14 no.2
• /
• pp.19-27
• /
• 2005

The recycling possibility of aluminum waste dross(AWD) as a ceramic raw material of porous light-weight material was examined. A aluminum waste dross was washed 4-7 consecutive times and roasted at 900$^{\circ}% for 1hour as pre-treatments. The properties of the pre-treatment of aluminum waste dross was investigated. It was conformed by XRD result that the spinel crystalline was grown in AWD, after roasting. After the roasted AWD was ground in aqueous state, the sodium hexaphosphate(SHP) as a dispersant which is used for stabilizing the concentrated slurry was added to the AWD slurry. The porous material was prepared by slurry foaming method with surfactant at room temperature. The foamed slurry volumes were 2 and 3 times of the original slurry volume. The properties of porous material with extended volume of 3 times was following: the porosity was about 84%, bulk density was 0.59 g/cm$^3$, the range of pore was from 50 ${\mu}m$ to 500 ${\mu}m$ and mean pore size was about 200 ${\mu}m$. AWD porous material was sintered at 1150$^{\circ}C-1250$^{\circ}C. It was colcluded that AWD was sintered well at 1200$^{\circ}C from material surface observation by SEM.

• Journal of Powder Materials
• /
• v.11 no.6 s.47
• /
• pp.528-534
• /
• 2004

Using the nano Fe powders having 50 nm in diameter, Fe compact bodies were fabricated by injec-tion molding process. The relationship between microstructure and material properties depending on the volume ratio of powder/binder and sintering temperature were characterized by SEM, TEM techniques. In the compact body with the volume percentage ratio of 45(Fe powder) : 55(binder), which was sintered at $700^{\circ}C,$ the relative density was about $97{\%},$ and the values of volume shrinkage and hardness were about $66.3{\%}$ and 242.0 Hv, respec-tively. Using the composition of 50(Fe powder) : 50(binder) and sintered at $700^{\circ}C,$ the values of relative density, volume shrinkage and hardness of Fe sintered bodies were $73.3{\%},\;47.6{\%}$ and 152.8 Hv, respectively. They showed brittle fracture mode due to the porous and fine microstructure.

• The Journal of the Korean dental association
• /
• v.47 no.12
• /
• pp.823-829
• /
• 2009

Purpose : The aim of this study was to evaluate the survival rate of sintered porous-surfaced implants placed in the edentulous posterior mandibles, in relation to implant length and diameter, crown-to-implant ratio, and types of prostheses, for a maximum of eight years of functioning. Material and Methods : The study group consisted of 43 partially edentulous patients who visited Catholic University Hospital of Daegu and one private dental clinic. A total of 122 sintered porous-surfaced implants n $Endopore^{(R)}$ (Inn ova Life Sciences, Toronto, Ontario, Canada) -- were placed in the edentulous posterior mandibles, Two diameter sizes (4.1 mm and 5.0 mm) and four lengths (5.0 mm, 7.0 mm, 9.0 mm, and 12.0 mm) were used. One hundred and three implants were splinted and 21 implants were nonsplinted. The survival rates of the implants in relation to length, diameter, crown-to-implant ratio, and types of prostheses were investigated. Statistical data were analyzed using SPSS Win.Ver 14.0 software with the Chi-square test. Results : The survival rate of the 4.1mm diameter implants was 100% and 91.2% for the 5.0mm diameter implants. The survival rates of the implants of differing diameters were found to be statistically different (p=0.005). The survival rates of both the 5.0mm and 7.0 mm length implants were 100%. The survival rate of the 9.0mm length implants was 97.9% and for the 12.0mm length implants was 95.1%. There was no statistical difference in survival rates for the differing lengths of implants. Of the 103 prostheses that were splinted, the survival rate was 98.0%. The survival rate of splinted prostheses was higher than that of the non-splinted prostheses, but was found to be not statistically different. There were no failed cases when the crown-to-implant ratio was under 1.0. When the crown-to-implant ratio was between 1.0 and 1.5, the failure rate of the implants was 6.7%. No failure was recorded with the ratio range of 1.5 to 2.0. Relative to the crown-to-implant ratio of 1.0, the failure rates were statistically different (p=0.048). Discussion and Conclusion : The cumulative survival rate of the porous-surfaced implants placed in the edentulous posterior mandibles was 97.5%. Short porous-surfaced implants showed satisfactory results after a maximum of nine years of functioning in the edentulous posterior mandibles.

• Composites Research
• /
• v.13 no.5
• /
• pp.31-36
• /
• 2000

The effect of several important processing variables was investigated on formation of porous mullite with acicular microstructure. Experimental results demonstrated that microstructure and porosity of porous mullite are depending on concentration of $AlF_3$, holding time at $900^{\circ}C$ and starting material. Acicular mullite was developed by increasing amount of $AlF_3$ and holding time at $900^{\circ}C$. Mullite began to be formed at $1200^{\circ}C$ and the resultant microstructure sintered at this temperature is similar to those at higher temperatures. Porosity increases with increase in amounts of $AlF_3$ and holding time at $900^{\circ}C$ . Therefore, it is found that microstructure of reaction-sintered porous mullite can be controlled by governing the amount of $AlF_3$ and holding time at $900^{\circ}C$.

• Korean Journal of Materials Research
• /
• v.34 no.1
• /
• pp.12-20
• /
• 2024

This study successfully prepared high-porosity aluminosilicate fibrous porous ceramics through vacuum suction filtration using aluminosilicate fiber as the primary raw material and glass powder as binder, with the appropriate incorporation of glass fiber. The effects of the composition of raw materials and sintering process on the structure and properties of the material were studied. The results show that when the content of glass powder reached 20 wt% and the samples were sintered at the temperature of 1,000 ℃, strong bonds were formed between the binder phase and fibers, resulting in a compressive strength of 0.63 MPa. When the sintering temperatures were increased from 1,000 ℃ to 1,200, the open porosity of the samples decreased from 89.08 % to 82.38 %, while the linear shrinkage increased from 1.13 % to 10.17 %. Meanwhile, during the sintering process, a large amount of cristobalite and mullite were precipitated from the aluminosilicate fibers, which reduced the performance of the aluminosilicate fibers and hindered the comprehensive improvement in sample performance. Based on these conditions, after adding 30 wt% glass fiber and being sintered at 1,000 ℃, the sample exhibited higher compressive strength (1.34 MPa), higher open porosity (89.13 %), and lower linear shrinkage (5.26 %). The aluminosilicate fibrous porous ceramic samples exhibited excellent permeability performance due to their high porosity and interconnected three-dimensional pore structures. When the samples were filtered at a flow rate of 150 mL/min, the measured pressure drop and permeability were 0.56 KPa and 0.77 × 10^-6 m² respectively.

• Journal of Powder Materials
• /
• v.18 no.4
• /
• pp.327-331
• /
• 2011

In order to fabricate the porous metal with controlled pore characteristics, unique processing by using metal oxide powder as the source and camphene as the sublimable material is introduced. CuO powder was selected as the source for the formation of Cu metal via hydrogen reduction. Camphene-based CuO slurry, prepared by milling at $47^{\circ}C$ with a small amount of dispersant, was frozen at $-25^{\circ}C$. Pores were generated subsequently by sublimation of the camphene. The green body was hydrogen-reduced at $200^{\circ}C$ for 30 min, and sintered at $500-700^{\circ}C$ for 1 h. Microstructural analysis revealed that the sintered Cu showed aligned large pore channels parallel to the camphene growth direction, and fine pores are formed around the large pore. Also, it showed that the pore size was controllable by the slurry concentration.