• 폴리머
• /
• 제37권1호
• /
• pp.15-21
• /
• 2013

폴리스티렌을 쉘 물질로 하여 상변환물질인 파라핀 왁스 코어 물질을 나노캡슐화하는 방법과 형성된 입자들의 열적 특성을 연구하였다. 나노캡슐화의 방법으로는 미니에멀젼 중합법을 채택하였다. 중합시 사용된 가교제의 성질, 유화제의 양, 상변환 물질과 단량체의 비율, 개시제의 친수성 등이 나노캡슐화된 상변환물질의 열적 특성에 미치는 영향을 분석하였다. 오스왈드 숙성에 의한 입자의 크기 변화, 형태 변화는 캡슐 입자의 열적 특성에 가장 큰 영향을 미치는 것으로 나타났으며, 또한 폴리스티렌 쉘의 친수성과 가교밀도도 캡슐 입자의 형태 변화와 이로 인한 열적 특성에 영향을 주는 것으로 나타났다.

• Korea-Australia Rheology Journal
• /
• 제16권3호
• /
• pp.135-140
• /
• 2004

Morphological and rheological properties of the poly(methyl methacrylate) (PMMA) and polystyrene (PS) blends were studied by scanning electron microscopy (SEM) and advanced rheometric expansion system (ARES). From the SEM results, the PMMA-PS blends showed dispersed morphology and the particle size of the dispersed phase was quite small (0.1~0.6 $\mu\textrm{m}$ compared with other immiscible polymer blends. Values of the interfacial tension of the PMMA-PS blend were obtained from the Choi-Schowalter and the Palierne emulsion models using the storage modulus of the PMMA and PS, and found to be 1.0 and 2.0 mN/m, respectively. The interfacial tension between the PMMA and PS was also calculated from the Flory-Huggins polymer-polymer interaction parameter ($\chi$) and found to be from 0.98 to 1.86 mN/m depending on the molecular weight and composition. Comparing the values of the interfacial tension from the Flory-Huggins polymer-polymer interaction parameter and the values measured by oscillatory rheometer, it is suggested that the interfacial tension of the PMMA-PS blend obtained from the polymer-polymer interaction parameter are in good agreement with the values obtained by rheological measurements.

• 한국분말재료학회지
• /
• 제18권4호
• /
• pp.347-358
• /
• 2011

Two different schemes were adopted to fabricate ordered macroporous structures with face centered cubic lattice of air spheres. Monodisperse polymeric latex suspension, which was synthesized by emulsifier-free emulsion polymerization, was mixed with metal oxide ceramic nanoparticles, followed by evaporation-induced self-assembly of the mixed hetero-colloidal particles. After calcination, inverse opal was generated during burning out the organic nanospheres. Inverse opals made of silica or iron oxide were fabricated according to this procedure. Other approach, which utilizes ceramic precursors instead of nanoparticles was adopted successfully to prepare ordered macroporous structure of titania with skeleton structures as well as lithium niobate inverted structures. Similarly, two different schemes were utilized to obtain disordered macroporous structures with random arrays of macropores. Disordered macroporous structure made of indium tin oxide (ITO) was obtained by fabricating colloidal glass of polystyrene microspheres with low monodispersity and subsequent infiltration of the ITO nanoparticles followed by heat treatment at high temperature for burning out the organic microspheres. Similar random structure of titania was also fabricated by mixing polystyrene building block particles with titania nanoparticles having large particle size followed by the calcinations of the samples.

• Advances in nano research
• /
• 제2권2호
• /
• pp.121-133
• /
• 2014

Polymer nanocomposites are advanced nanomaterials which exhibit dramatic improvements in various mechanical, thermal and barrier properties as compared with the neat polymer. Polystyrene/ alumina nanocomposites were prepared by an ultrasound-assisted solution casting method at filler loadings ranging from 0.2 to 2% and also at different ultrasonic frequencies, viz. 58 kHz, 192/58 kHz, 430 kHz, 470 kHz and 1 MHz. The composites were subjected to mechanical property tests (tensile and impact tests) and cavitation erosion tests to study the enhancement in functional properties. Filler dispersion in the polymer matrix was observed by SEM analysis. The effect of frequency on filler dispersion in the matrix was studied by SEM analysis and functional property enhancement of the composite material. The composites prepared at dual (high/ low) frequency (192/58 kHz) were found to show better property enhancement at low filler loadings as compared with neat polymer and also with composites prepared without ultrasound, thus reinforcing the finding that ultrasound-assisted synthesis is a promising method for the synthesis of nanocomposites.

• 한국주조공학회지
• /
• 제17권1호
• /
• pp.93-99
• /
• 1997

A possibility of production of aluminium matrix composites by using the lost foam process was investigated. Silicon carbide particles, graphite particles, and stainless steel wires were used as reinforcement materials. The reinforcement materials were introduced to the polystyrene to form patterns via injection molding process. The results obtained from this experiment can be summarized as follows. In Al/SiCp system, the particles with the radius of $100{\mu}m$ and over were entrapped in the matrix in the case of upward freezing of which solidification direction was opposite to floating direction of the particles. And few particles were entrapped in the matrix in downward freezing. In Al/graphite system, almost no particles were entrapped in the matrix except the area chill attatched. When the thickness of polystyrene slice was 4mm in Al/stainless steel wire system, the floating tendency of fibers was observed to increase as the distance from the ingate was increased.

• 폴리머
• /
• 제30권1호
• /
• pp.50-55
• /
• 2006

분산중합으로 제조된 폴리스티렌(PS) 시드 고분자 미립자에 가교단량체인 HDDA(1,6-hexanedioldiacrylate)를 one-step으로 흡수시키고 이를 중합하여 단분산 가교고분자 미립자를 제조할 시 1) 시드 고분자의 분자량, 2) 흡수된 가교단량체와 시드의 중량비, 3) 중합반응속도 등의 변화에 따른 가교고분자 입자의 표면 모폴로지 변화 등을 관찰하였다. 이번 연구를 통해 PS/HDDA계에서는 시드 고분자의 분자량 및 가교단량체 흡수비에 관계없이 가교고분자 입자표면에 분화구 형태의 모폴로지가 관찰되었으며, 이와 같은 표면 모폴로지는 중합반응속도를 조절함으로써 조절이 가능함을 알 수 있었다.

• Korean Chemical Engineering Research
• /
• 제50권3호
• /
• pp.588-593
• /
• 2012

불포화 폴리에스터(unsaturated polyester, UP)와 저수축제(low profile agent, LPA), 폴리스틸렌(polystyrene, PS)과의 compatibility가 불포화 폴리에스터와 저수축제의 비율, 혼합시간, 혼합온도 그리고 추가로 투입되는 불포화 폴리에스터 수지량과 같은 다양한 조건하에서 확인되었다. 1단계로 1700 rpm의 교반속도에서 제조된 수지 혼합액의 경우, 불포화 폴리에스터 수지(unsaturated polyester resin, UPR) 투입량 25 g, 약 $30^{\circ}C$의 반응온도에서 상대적으로 작은 입자 크기 및 상분리율을 나타내었다. 2단계 수지 혼합액의 경우, 2차로 투입된 45 g의 불포화 폴리에스터 수지 혼합액에서 향상된 compatibility를 보였다. 이러한 결과는 혼합조건이 불포화 폴리에스터 수지와 저수축제 혼합액의 compatibility에 중요한 역할을 한다는 것을 의미한다. 또한, 상기조건을 통해 제조된 sheet molding compound (SMC)를 사용해서 만든 샘플은 흡수율, 수축율 및 광택도에서 향상된 결과를 나타내었다.

• Composites Research
• /
• 제21권2호
• /
• pp.31-35
• /
• 2008

자성 금속 코팅을 위해 폴리스티렌 submicron 입자를 제조하였다. 니켈과 철 코팅을 위해 무전해 도금을 적용하였고 열처리를 통해 폴리스티렌을 탄화 시켜 중공형 구조를 형성하였다. 이러한 중공형 자성 입자는 가볍고 효율이 우수한 전자파 흡수체 제조에 적용될 수 있다. 코팅 층의 두께, 성분 및 표면 형상은 SEM/EDS/TEM 으로 관찰하였고, 중공 자성 입자의 전자파 특성 비교를 위해 고분자 복합재료를 제조하였다. 복합재료의 투자율 측정 결과, 중공형 철이 니켈에 비해 우수하였으며 바륨 페라이트 (Barium ferrite)와 같은 기존의 자성 재료보다 우수하였다.

• Macromolecular Research
• /
• 제16권4호
• /
• pp.329-336
• /
• 2008

Core/shell ($\pm$)PS/(-)silica nanocomposite particles were synthesized by dispersion polymerization using an amphoteric initiator, 2,2'-azobis [N-(2-carboxyethyl)-2,2-methylpropionamidine] ($HOOC(CH_2)_2HN$(HN=) $C(CH_3)_2CN$=NC $(CH_3)_2C$(=NH)NH $(CH_2)_2COOH$), VA-057. Negatively charged (-6.9 mV) silica was used as the stabilizer. The effects of silica addition time and silica and initiator concentrations were investigated in terms of polymerization kinetics, ultimate particle morphology, and size/size distribution. Uniform hybrid microspheres with a well-defined, core-shell structure were obtained at the following conditions: silica content = 10-15 wt% to styrene, VA-057 content=above 2 wt% to styrene and silica addition time=0 min after initiation. The delay in silica addition time retarded the polymerization kinetics and broadened the particle size distribution. The rate of polymerization was strongly affected by the silica content: it increased up to 15 wt% silica but then decreased with further increase in silica content. However, the particle size was only marginally influenced by the silica content. The zeta potential of the composite particles slightly decreased with increasing silica content. With increasing VA-057 concentration, the PS microspheres were entirely coated with silica sol above 1.0 wt% initiator.

• 대한기계학회논문집B
• /
• 제36권3호
• /
• pp.241-249
• /
• 2012

본 논문에서는 유체흐름방향과 예각으로 놓여있는 평면 교차전극 위를 지나가는 입자의 크기에 따른 측면방향 변위에 대하여 소개한다. 아울러, 유체흐름방향과 평면 교차전극 사이의 각도에 따른 측면방향 변위의 변화를 보인다. 본 논문에서는 선전하(line charge) 모델을 이용하여 크기가 다른 세 종류의 형광 polystyrene(PS) 입자의 측면방향 변위를 이론적으로 예측하였다. 크기에 따른 입자의 측면방향 변위의 변화를 이용하여, 크기별로 입자를 연속적으로 분리할 수 있는 측면방향 유전영동 미세분리기를 개발하였다. 3, 5, 10 ${\mu}m$ PS 입자의 혼합물을 이용하여 분리한 실험결과로 부터 개발된 측면방향 유전영동 미세분리기는 3 ${\mu}m$ PS 입자를 99.86%, 5 ${\mu}m$를 98.82%, 10 ${\mu}m$를 99.69%의 높은 효율로 각각 분리할 수 있음을 확인하였다. 이로부터 제안된 측면방향 유전영동 미세분리기는 다종 혼합물로부터 다양한 크기의 입자들을 한 번에 분리하는 기술로 널리 활용될 수 있을 것으로 기대된다.