• Polymer(Korea)
• /
• v.30 no.2
• /
• pp.162-167
• /
• 2006

Polyamic acid (PAA) was prepared from cyclobutane-1,2,3,4-tetracarboxylic dianhydride (CBDA) and 4,4'-fiaminodiphenyl ether (DDE). In order to impart a photosensitivity to the PAA, diazonaphthoquinone (DNQ) derivative (DI) was added. However, the addition of the DI was not enough to inhibit the dissolution of the PAA for a aqueous alkal solution. Therefore, we had synthesized poly(amic acid ester)s by an adding 1,2-epoxy-3-phenoxypropane to the PAA. That is, an acidity of the PAA could be controlled by an esterification reaction of 1,2-epoxy-3-phenoxypropane with the PAA. Significant difference of a dissolution rate of the poly(amic acid ester) between an o(posed and unexposed area was observed at an acid content of 60% and less. Resolution of the positively patterned film showed about $25{\mu}m$ at the exposure dose of $200mJ/cm^2$.

• Polymer(Korea)
• /
• v.38 no.5
• /
• pp.632-639
• /
• 2014

2,7-Dihydroxynaphthalene bis(trimellitate anhydride) (2,7-TA) was synthesized from trimellitic anhydride chloride and 2,7-dihydroxynaphthalene. Copolyimides (Co-PI) containing ester group were synthesized from 2,7-TA, pxylylenediamine, and 2,2'-bis(trifluoromethyl)benzidine (TFB). The Co-PI films were obtained from poly(amic acid) by solution casting through thermal imidization on a glass plate. The thermal property, gas permeation, and optical transparency of the Co-PI films with various TFB monomer contents were investigated. These Co-PIs could be solution-cast into a flexible and tough film. The cast Co-PI films exhibited high optical transparency with a cut-off wavelength of 370~395 nm in UV-vis. absorption and a low yellow index value of 3.55~7.63. The thermal property of Co-PI films increased linearly with increasing TFB content. However, the oxygen permeation and optical transparency of the Co-PI films was found to worsen with increasing TFB content.

• Polymer(Korea)
• /
• v.37 no.5
• /
• pp.618-624
• /
• 2013

Hydroquinone bis(trimellitic anhydride) (HQ-TA) was synthesized from trimellitic anhydride chloride and hydroquinone. Poly(amic acid)s (PAAs) were synthesized by reacting a HQ-TA with six different diamines, which were cyclized to yield polyimides (PIs) containing ester linkages by chemical- and thermal-imidization methods. The various PIs were synthesized from structurally different aromatic diamines. The glass transition temperatures ($T_g$) were in the range of 167-$215^{\circ}C$, and the decomposition temperatures (${T_D}^i$) were in the range of $364-451^{\circ}C$. The maximum improvements in coefficient of thermal expansion (CTE) and barrier to oxygen permeation were observed in PIs using TFB (3.23 $ppm/^{\circ}C$) and 4,4-ODA (< $10^{-2}cc/m^2/day$), respectively. The PI films possessed a transmittance of 65-89% at 500 nm and had a yellowish color with a yellow index (YI) of 3.01-69.52.