• Journal of the Korean Applied Science and Technology
• /
• v.30 no.4
• /
• pp.754-760
• /
• 2013

We investigated an electrochemical properties for Langmuir-Blodgett (LB) monolayer films of sphingomyelin(SP) and polyamic acid(PAA) mixture(1:1, 2:1 and 3:1 molar ratio). LB monolayer films of mixture was deposited by the LB method on the indium tin oxide(ITO) glass. The electrochemical properties measured by cyclic voltammetry with three-electrode system in 0.1N $KClO_4$ solution. As a result, LB monolayer films of SP and PAA mixture was appeared on irreversible process caused by the reduction current from the cyclic voltammogram. Diffusion coefficient(D) in the SP and PAA mixture was calculated $2.670{\times}10^{-5}$, $3.562{\times}10^{-5}$ and $1.005{\times}10^{-5}cm^2s^{-1}$ at 1:1, 2:1 and 3:1 molar ratio, respectively.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.15 no.8
• /
• pp.695-701
• /
• 2002

Maxwell displacement current (MDC) measuring technique has been applied on the study of monolayers of fatty acid and polyamic acid mixture. The displacement current was generated from monolayers on the water surface by monolayer compression and expansion. Displacement current was generated when the area per molecule was about 132 $^2$and 115 $^2$just before the initial rise of the surface pressure during the 1st and 2nd mixed monolayer compressions cycle, respectively. Maxwell displacement currents were investigated in connection with mixed monolayer compression cycles. It was found that the maximum of MDC appeared at the molecular area just before the initial rise of surface pressure in compression cycles. Ultra thin film of fatty acid and polyamic acid mixture was prepared on the hydrophilic quartz plate by Langmuir-Blodgett (LB) method. The precursor LB film was heated in a vacuum dry oven at 12$0^{\circ}C$ in order to convert it into the LB film of polyimide. The absorption spectra of LB films were also induced photoisomerization by UV and visible light irradiation.

• Journal of the Korean Graphic Arts Communication Society
• /
• v.15 no.2
• /
• pp.117-130
• /
• 1997

Studies have been conducted to explore thermal imidization of polyamic acid. Aromatic polyimides are well recognized as high temperature linear polymers, and polyimide are used as structural materials, fibers, and adhesive. Two different kinds of polyimide were prepared by theimidization of polyamic acid which were synthesized from 2,2-bis[4-(4-aminophenoxy)phenyl]- hexafluoropropane, 2,2-bis [4-(4-aminophenxy)phenyl] - hexamethylpropane and caprolactam and pyromelliti dianhydride under N-Methly-pyrrolidinone solvent. Polyamic acids were converted to polyimides containing imide bond by thermal imidization. The weight 50% loss temperatures of polyimide by TGA thermogram were recorded in the range of 700 ~ 720$^{\circ}$C in nitrogen gas. According, as a results, we conclued polyamic acid were cycliation after H2O molecule separationed, and this polyimide film could be used for Printed Circuit Boand.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1997.11a
• /
• pp.298-301
• /
• 1997

This paper describes the thermally stimulated current(TSC) measurements arachidic acid(AA) and polyamic acid alkylamine salts(PAAS) LB film, which is a precursor of polyimide(PI). The measurements were performed from room temperature to about 250$^{\circ}C$ and the temperature was increased at a rate of 0.02 $^{\circ}C$/s linearly[4]. It shows that peaks of TSC are observed at about 80$^{\circ}C$ in the arachidic acid and about 80$^{\circ}C$, 160$^{\circ}C$ in the PAAS LB films. The DSC and TGA of PAAS, arachidic acid are measure. Monolayer phases on the water subphase such as Langmuir(L) films and the phase transitions from gas phase to solid phase via liquid phase are observed using Brewster angle microscopy(BAM). BAM is also used to observe the Langemuir-Blodgett(LB) films.

• Korean Journal of Materials Research
• /
• v.9 no.1
• /
• pp.65-72
• /
• 1999

In order to minimize flexible printed circuit(FPC), which is used in computer, communication, medical facility, aviation space industry, it is required to improve the interfacial adhesion of polymide/epoxy or polyimide/polyimide consists of FPC. In this study, it was considered to improve the adhesion strength of polyimide/epoxy joint by introducing functional group on polyimide film and improving mechanical property of epoxy. Functional group on polyimide film was introduced by changing polyimide film surface to polyamic acid in KOH aqueous solution. The optimum conditions for surface modification were the concentration of 1M KOH and treatment time of 5min. Also, the optimum adhesion strength of polyimide/epoxy joint was obtained using rubber modified epoxy and polyamic acid as a base resin and curing agent of epoxy adhesive, respectively. The degree of surface modification of polyimide film examined with contact angle measurement of FTIR, thus modification of polyimide to polyamic acid was identified. Fracture surface of plymide/epoxy joint was analyzed by scanning electron microscopy, and modified polyamic acid reimidezed to polymide as increasing curing temperature.

• Polymer(Korea)
• /
• v.26 no.5
• /
• pp.634-643
• /
• 2002

Ultrathin film of polyamic acid having benzene and sulfonyloxyimide moieties was prepared using the Langmuir-Blodgett (LB) technique, and then photosensitive polyimide LB film was obtained by the thermal treatment of precursor polyamic acid multilayers at 200$\^{C}$ for 1 hr. The polyamic acid was synthesized by condensation polymerization under THF and pyridine cosolvent. All monomers and polymers were identified through elemental analysis, FT-IR and $^1$H-NMR spectroscopic measurements. The microarray patterning of photosensitive polyimide LB film on a gold substrate was generated with a deep UV lithography technique. The well-characterized monolayer of cytochrome c was immobilized on the microarray patterns using two different self-assembly processes. Physical and electrochemical properties of the self-assembled cytochrome c monolayer were investigated based on cyclic voltammetry and atomic force microscopy (AFM). Also, its application in bioelectronic device was examined.

• Polymer(Korea)
• /
• v.24 no.2
• /
• pp.228-236
• /
• 2000

The preparation of organophilic clay from Na$^{+}$-MMT was achieved by intercalation of alkylammonium bromide. The dispersed organophilic clay in NMP was then added to the solution of polyamic acids (BPDA-PPD, BTDA-ODA/ MPD) in NMP. After curing at 30$0^{\circ}C$, thin films of the polyimide/clay nanocomposite were prepared. The results of X-ray diffraction (XRD) shelved that the d-spacings of dried polyamic acid (PAA)-clay complexes increased in proportion to the chain length of the onium ion and patterns of two kinds of PAA-clay complexes were similar. The d-spacings of approximately 13.2 $\AA$ for the polyimide/clay nanocomposites were independent of the initial onium ion chain length and the species of PAA. From the study of XRD and transmission electron microscopy (TEM), we found layered silicates were dispersed in polyimide matrix and the resultants were intercalated nanocomposites. TGA result showed thermal stability of polyimide nanocomposite improved a little more than the pure polyimide. From the result of dynamic mechanical property, we found that the storage modulus of the nanocomposites had increased by 1.2-1.8 times of the pure polyimides.s.

• Korean Journal of Materials Research
• /
• v.26 no.9
• /
• pp.478-485
• /
• 2016

An amide group was introduced to restrain the cohesion of silica nano-particles and copolymerized with polyamic acid. Amide block copolymers were prepared using silica and (3-mercaptopropyl) trimethoxysilane (MPTMS) with a siloxane group, using 2, 6-Lutidine as a catalyst. Amide block polymers and copolymers were synthesized via ATRP after brominating pyromellitic dianhydride (PMDA) and polyamic acid of methylene diphenyl diamine (MDA) using ${\alpha}$-bromo isobutyryl bromide. Characteristic peaks of copolymer with amide and imide groups and patterns of amorphous polymers were studied using FT-IR and XRD analyses; an analysis of the surface characteristic groups was conducted via XPS. Changes in the thermal properties were examined through DSC and TGA; solubility for solvents was also studied.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1996.11a
• /
• pp.147-151
• /
• 1996

Brewster angle microscopy(BAM) makes it possible to observe the monolayer states on the water subphase and the phase transitions from a gaseous phase via a expanded phase to a condensed phase. Also BAM can be used to observe the films on the solid substrate such as Langmuir-Blodgett(LB) films. In this Paper Polyamic Acid Alkylamine Salts(PAAS) was used for forming L films and LB films and $\pi$-A isotherm showed pressure of each phase. We obtained BAM images as surface pressure increased. Images of LB films were compared with data from ellipsometry which was used to measure the film thickness. Images of both L films and LB films were analyzed with computer in the point of brightness.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2000.11a
• /
• pp.53-56
• /
• 2000

Langmuir-Blodgett(LB) technique is the best candidate for the future molecular electronic devices. But, these molecular thin film devices require the bulk properties that are influenced by the molecular orientations. So, this is of current interest in molecular electronic device fabrications of new materials. In this study, quantitative evaluation of molecular orientation in LB films of PAAS was performed by comparing the absorption intensities of the FT-IR transmission and reflection-absorption spectra and the polarized UV/visible absorption spectra. It was found that the polar angle( $\theta$ ) of the dipole moment is about 68$^{\circ}$ and the tilting angle of the alkyl chain is about 11.5$^{\circ}$