Reduction of the propagation noise generated during pass-by of KTX by noise barrier was measured and analysed for the two kinds of top-shaped noise reduction devices; one as a plywood board and the other as a PVC pipe were placed periodically. The height and length of reference noise barrier are 2.4 m and 50 m, respectively. The noise reduction with and without noise reduction devices was investigated.

• Journal of the Korean Wood Science and Technology
• /
• 제20권1호
• /
• pp.72-78
• /
• 1992

지진과 관련있는 하중 속도에서 damping을 측정하기 위하여 합판과 목재 사이에 한개의 못을 사용한 접합에 대하여 조사 했다. 조사된 하중은 sine function 의 15Hz와 ASTM하중 속도 사이에서 행했다. Damping 율은 4Hz까지의 하중 속도에서는 증가를 보였으며 그후 15Hz 까지는 점진적으로 감소하였다. 강성은 높은 하중 범위에서 slip moduli가 지속적으로 증가 하였다. 낮은 하중 범위에서 2.5Hz까지 증가 하였으며 그후는 감소 하였다. Damping 율과 slip modulus는 하중 속도와 상관 관계가 낮은 반면 work capacity와 dissipated energy는 높은 상관 관계를 보았다.

• 대한예방의학회:학술대회논문집
• /
• 대한예방의학회 1996년도 제48차 추계 학술대회 연제집
• /
• pp.413-414
• /
• 1996

• Journal of the Korean Wood Science and Technology
• /
• 제36권6호
• /
• pp.49-58
• /
• 2008

본 연구는 내구성이 우수하며 포름알데히드방출이 적은 페놀수지 사용 메란티합판을 마루판용 대판으로 사용하고 북미산 벚나무 단판을 표면재료로 사용한 마루판의 제조과정에서 접착제 및 도료에 녹차잎 분말을 첨가하였을 때 마루판으로부터 방출하는 총휘발성유기화합물(TVOC)과 포름알데히드의 감소효과와 녹차잎 분말의 적정 첨가량을 구명하였다. 1) 녹차잎 분말의 폴리페놀화합물량은 9.85%였다. 2) 녹차잎 분말은 FT-IR 결과 벤즈알데히드와 에틸헥사알콜과 반응하여 화학결합을 하는 것으로 나타났다. 3) 페놀수지메란티대판에 벚나무단판오버레이 마루판 제조를 위한 접착제와 UV도료에 전건중량기준으로 2.5%의 녹차잎 분말을 각각 첨가하는 것이 총휘발성유기화합물과 포름알데히드의 방산제거 효과가 매우 적절한 것으로 나타났다. 4) 20L 소형챔버법에 의한 녹차잎 분말 2.5%를 접착제와 도료에 각각 첨가한 온돌용 마루판의 7일째 TVOC는 $0.089mg/m^2hr$이고 포름알데히드는 $0.001mg/m^2hr$를 나타내 최우수등급으로 나타났다.

• 한국화재소방학회논문지
• /
• 제30권2호
• /
• pp.7-18
• /
• 2016

본 연구는 주택이나 창고 등의 내부 마감재로 사용하는 합성 목재의 연소 독성평가에 관한 것으로 SEM, 콘 칼로리미터, FTIR를 활용해 집성판, MDF, 미송합판, 코어합판, 나왕 방부목 5종의 재료별 연소가스 독성을 실험 및 분석하였다. 각 재료별 독성특성 중 나왕 방부목에서 이산화탄소($CO_2$)의 치사농도인 100,000 ppm을 2.5배 초과하는 256,965 ppm, 이산화황($SO_2$)의 치사농도인 400 ppm의 3.6배를 초과하는 1,475 ppm이 검출되었다. 집성판은 이산화질소($NO_2$)가 1,569 ppm으로 치사농도인 250 ppm의 6배가 측정되었고, 암모니아($NH_3$)는 MDF에서 치사농도 값인 750 ppm 대비 795 ppm이 측정되었다. 따라서 대부분의 건축 재료에서 인체에 치명적인 가스가 발생되는 것을 확인하였고, 향후 건축 재료의 위해성을 평가하기 위한 기초데이터로 활용하고자 한다.

• Journal of the Korean Wood Science and Technology
• /
• 제19권1호
• /
• pp.22-30
• /
• 1991

This study was carried out to determine the Joint characteristic of L-type specimens. L-type specimens were made of two kinds uf solid woods(Antiaris, Sepetir) and three kinds of wood based materials(plywood, particleboard, medium density fiberboard). They were constructed with PVC anchor and screw, and were discussed with joint strength and stiffness coefficients. The obtained results were as follows: 1. Bending strength showed very high increasing rate from one to three used PVC anchor and screw but was a little rise from three to four used PVC anchor and screw in solid wood. However. in wood based materials, it was unchanged without increasing rate or slight decreased from three to four used PVC anchor and screw. 2. The stiffness coefficients, or Z-values, were in the range from $4.704\times10^{-4}$ to $1.864\times10^{-3}$(rad/kgf-cm). They showed $10^{-3}$ level in one PVC anchor and screw but $10^{-4}$ level in two, three. four PVC anchor and screw. Accordingly, they indicated flexible joints in one PVC anchor and screw and relatively stable joints in two, three. four PVC anchor and screw. 3. Measured ultimate bending moments were 258.70kgf-cm in plywood and 142.68kgf-cm in medium density fiberboard. 4. Comparing with dowel joint. the joint strength used PVC anchor screw was inferior to 8mm and 10mm dowel diameter but differ little from 6mm dowel diameter.

• Journal of the Korean Wood Science and Technology
• /
• 제19권3호
• /
• pp.62-71
• /
• 1991

An evaluation of bending test of composite I and Box beams for determining the ultimate strength limit design criteria was presented. Maxium loads of composite I beams were found in beams composed of thicker upper flanges and/or vertical LVL flanges. These loads of plywood web beams were greater than those of PB web beams. Maximum loads of unsymmetrical box beams were less than those of symmetrical box beams. Thus, it took on different phase in box type beams. Ultimate loads of composite beams were greater than those of solid. The failure of composite beams were abrupt and failure mode was classified into following categories; Edgewise shear failure in web, delamination in flange-web joint, tension failure and tearing in LVL flanges, and web delamination. These failures of composite beams were appeared at the mixed mode. The influence factor affecting the performance of tested composite beams was shear strength of PB-web composite beams and compressive strength in plywood-web composite beams. It was also assumed that the influence factors on structural performance on composite beams were flange quality, web material and geometry of cross section. As one of the design methods resisting to compressive stress that was required in the case of small span to depth ratio and deep beams. composite I-beams composed of thicker upper flanges comparing to lower flanges were very effective in structural performance.

• Journal of the Korean Wood Science and Technology
• /
• 제46권6호
• /
• pp.726-734
• /
• 2018

In this study, for using effectively domestic (temperate) small and medium diameter logs as a wooden floorboard, cross-laminated wood panels were manufactured using domestic larch and tulip woods as a base material for teak and merbau wood flooring, and static bending strength performances were measured to investigate the applicability as the base materials of wooden flooring in place of plywood. Static bending MOE was much influenced by the strength performances of the top layer lamina than that of the laminae for base materials. Bending MOR showed the higher values in tulip wood that was hardwoods than in larch wood that was softwoods regardless of the strength performances of the top layer laminae, and it was found that the values were much influenced by the strength performances of the base materials used in the core and bottom layers. However these values were 1.4-2.5 times higher values than the bending strength of the wooden floorboards specified in KS, it was found that it can be sufficiently applied to the base materials of wooden floorboards in place of plywood.

• Journal of the Korean Wood Science and Technology
• /
• 제34권4호
• /
• pp.31-36
• /
• 2006

본 연구는 UF resin의 접착성능을 개선하여 그 사용처의 확대하기 위하여 각 F/U 몰비별로 제조된 UF resin에 접착성능이 우수한 지방산-글리세롤-pMDI 당량비 1:1:4인 비교적 저가의 isocyanate prepolymer접착제를 선정하여 UF resin의 수지고형분 기준으로 0 wt%(대조구), 2 wt%, 5 wt%, 10 wt%, 25 wt%, 50 wt%로 첨가 혼합하여 접착 성능을 조사하였다. 그 결과, 상태 접착력(Type 2)은 F/U 몰비 1.4에서 가장 우수한 접착력을 준내수 접착력(Type 1.5)은 FGMDI첨가량이 25% 이상에서 KS 합판 접착성 기준인 $7.5kgf/cm^2$를 모두 상회하는 $11kgf/cm^2$ 이상을 나타내었다. 상태접착력대비 준내수 접착력의 평균 감소율은 F/U 몰비가 높아질수록, 지방산-글리세롤-pMDI접착제의 첨가량이 많아질수록 그 감소의 폭이 둔화되었다.

• Journal of the Korean Wood Science and Technology
• /
• 제41권1호
• /
• pp.33-41
• /
• 2013

본 연구에서는 최근 파티클보드(Particle Board ; 이하 PB)의 원재료로 재활용되고 있는 목재 폐기물 중 합판공장의 부산물을 원재료로 사용하고 비포름알데히드계 EMDI접착제의 적용을 통한 제조조건을 최적화하여 재활용 원재료의 효과적인 활용을 통한 고(高)내수성 PB의 개발과 그에 대한 물리 기계적 특성을 규명하고자 하였다. 그 결과, (1) 베니어 적층 복합보드에 EMDI수지를 사용하였을 경우 휨 강도가 섬유방향 57.7 $N/mm^2$, 섬유 직각방향 25.1 $N/mm^2$의 강도를 나타내었다. (2) 두께팽윤율과 수분흡수율은 U형, M형, P형 실험에서 EMDI수지가 UF수지보다 높은 수준의 내수성을 나타내었다. (3) 잔존 포름알데히드의 양을 줄이고자 실행하였던 72시간 수침전처리는 파티클보드의 포름알데히드 방산량을 증가시키는 결과를 초래하였다.