• 한국전기전자재료학회논문지
• /
• 제21권6호
• /
• pp.575-579
• /
• 2008

Al-doped p-type ZnO films were fabricated on n-Si (100) and homo-buffer layers in pure oxygen at $450^{\circ}C$ of by RF magnetron sputtering. Target was ZnO ceramic mixed with 2 wt% $Al_2O_3$. XRD spectra show that the Al-doped ZnO thin films have ZnO crystal structure and homo-buffer layers are beneficial to Al-doped ZnO films to grow along c-axis. Hall Effect experiments with Van der Pauw configuration show that p-type carrier concentrations are ranged from $1.66{\times}10^{16}$ to $4.04{\times}10^{18}\;cm^{-3}$, mobilities from 0.194 to $2.3\;cm^2V^{-1}s^{-1}$ and resistivities from 7.97 to $18.4\;{\Omega}cm$. p-type sample has density of $5.40\;cm^{-3}$ which is smaller than theoretically calculated value of $5.67\;cm^{-3}$. XPS spectra show that Ols has O-O and Zn-O structures and Al2p has only Al-O structure. P-ZnO:Al/n-ZnO:Al junctions were fabricated by magnetron sputtering. V-I curves show that the p-n junctions have rectifying characteristics.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2007년도 추계학술대회 논문집
• /
• pp.408-409
• /
• 2007

Al-doped p-type ZnO films were fabricated on n-Si (100) and homo-buffer layers in pure oxygen at $450^{\circ}C$ by RF magnetron sputtering. Target was ZnO ceramic mixed with 2wt% $Al_2O_3$. XRD spectra show that the Al-doped ZnO thin films have ZnO crystal structure and homo-buffer layers are beneficial to Al-doped ZnO films to grow along c-axis. Hall Effect experiments with Van der Pauw configuration show that p-type carrier concentrations are ranged from $1.66{\times}10^{16}\;to\;4.04{\times}10^{18}cm^{-3}$, mobilities from 0.194 to $2.3cm^2V^{-1}s^{-1}$ and resistivities from 7.97 to $18.4{\Omega}cm$. P-type sample has density of $5.40cm^{-3}$ which is smaller than theoretically calculated value of $5.67cm^{-3}$. XPS spectra show that O1s has O-O and Zn-O structures and A12p has only Al-O structure. P-ZnO:Al/n-ZnO:Al junctions were fabricated by magnetron sputtering. V-I curves show that the p-n junctions have rectifying characteristics.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2007년도 하계학술대회 논문집 Vol.8
• /
• pp.55-56
• /
• 2007

The p-type ZnO thin film, fabricated by means of the ampoule-tube method, was used to make the ZnO p-n junction, and its characteristics was analyzed. The ampoule-tube method was used to make the p-type ZnO based on the As diffusion, and the hall measurement was used to confirm that the p-type is formed. the current-voltage characteristics of the ZnO p-n junction were measured to confirm the rectification characteristics of a typical p-n junction and the low leakage voltage characteristics. Using the ampoule-tube to fabricate the p-type ZnO will provide a very useful technology for producing the UV ZnO LED and ZnO-based devices.

• Transactions on Electrical and Electronic Materials
• /
• 제9권2호
• /
• pp.67-72
• /
• 2008

Al-doped p-type ZnO thin films were fabricated by RF magnetron sputtering on n-Si (100) and homo-buffer layers in pure oxygen ambient. ZnO ceramic mixed with 2 wt% $Al_2O_3$ was selected as a sputtering target. XRD spectra show that the Al-doped ZnO thin films have ZnO crystal structure. Hall Effect experiments with Van der Pauw configuration show that p-type carrier concentrations are arranged from $1.66{\times}10^{16}$ to $4.04{\times}10^{18}\;cm^{-2}$, mobilities from 0.194 to $198\;cm^2V{-1}s^{-1}$ and resistivities from 0.0963 to $18.4\;{\Omega}cm$. FESEM cross section images of different parts of a p-type ZnO:Al thin film annealed at $800^{\circ}C$ show a compact structure. Measurement for same sample shows that density is $5.40\;cm^{-3}$ which is smaller than theoretically calculated value of $5.67\;cm^{-3}$. Photoluminescence (PL) spectra at 10 K show a shoulder peak of p-type ZnO film at about 3.117 eV which is ascribed to electron transition from donor level to acceptor level (DAP).

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2007년도 추계학술대회 논문집
• /
• pp.410-411
• /
• 2007

To investigate the ZnO LED which are interested in the next generation of short wavelength LEDs and Lasers, the ZnO thin films were deposited by RF magnetron sputtering system. The p-type ZnO thin film, fabricated by means of the ampoule-tube method, was used to make the ZnO p-n junction, and its characteristics was analyzed. The ampoule-tube method was used to make the p-type ZnO based on the As diffusion, and the hall measurement was used to confirm that the p-type is formed. the current-voltage characteristics of the ZnO p-n junction were measured to confirm the rectification characteristics of a typical p-n junction and the low leakage voltage characteristics. Analysis of ZnO LED V-I curve will provide a very useful technology for producing the UV ZnO LED and ZnO-based devices.

• Transactions on Electrical and Electronic Materials
• /
• 제10권3호
• /
• pp.89-92
• /
• 2009

High-quality Al-N doped p-type ZnO thin films were deposited on Si and buffer layer/Si by DC magnetron sputtering in a mixture of $N_2$ and $O_2$ gas. The target was ceramic ZnO mixed with $Al_2O_3$ (2 wt%). The p-type ZnO thin films showed a carrier concentration in the range of $1.5{\times}10^{15}{\sim}2.93{\times}10^{17}\;cm^{-3}$, resistivity in the range of 131.2${\sim}$2.864 ${\Omega}cm$, mobility in the range of 3.99${\sim}$31.6 $cm^2V^{-1}s^{-l}$, respectively. It was easier to dope p-type ZnO films on Si substrates than on buffer layer/Si. The film grown on Si showed the highest quality of photoluminescence (PL) characteristics. The Al donor energy level depth $(E_d)$ of Al-N codoped ZnO films was reduced to about 50 meV, and the N acceptor energy level depth $(E_a)$ was reduced to 63 meV.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2009년도 하계학술대회 논문집
• /
• pp.319-320
• /
• 2009

In this study, high-quality Al-N doped p-type ZnO thin films were deposited on n-type Si (100) wafer or Si coated with buffer layer by DC magnetron sputtering in the mixture of $N_2$ and $O_2$ gas. The target was ceramic ZnO mixed with $Al_2O_3$ (2 wt%). The p-type ZnO thin film showed higher carrier concentration $2.93\times10^{17}cm^{-3}$, lower resistivity of $5.349\;{\Omega}cm$ and mobility of $3.99\;cm^2V^{-1}S^{-1}$, respectively. According to PL spectrum, the Al donor energy level depth ($E_d$) of Al-N codoped p-type ZnO film was reduced to about 51 meV, and the N acceptor energy level depth ($E_a$) was reduced to 63 meV, respectively.

• 한국산학기술학회논문지
• /
• 제8권3호
• /
• pp.472-476
• /
• 2007

본 연구에서는 p-형 ZnO 박막 증착법 및 특성의 안정화 방안에 대하여 조사하였다. p-형 ZnO는 AlAs와 ZnO target을 사용하여 RF magnetron sputtering 기법으로 co-deposition하여 제작하였으며 특성 변화를 조사하기 위해 $250^{\circ}C$에서 144시간까지 스트레스 인가 시간을 변화하며 Photoluminescence 및 Hall 측정을 수행하였다. 연구 결과 co-deposition 은 p-형 박막을 제작하기 위해 유효한 방법인 것으로 밝혀졌으며, 특히 고온에서 이루어지는 과정을 수행하기 전 30% H2O2용액에 1분간 처리하는 것이 이후의 열처리 과정 중 발생하는 특성 변화를 크게 억제하는 것으로 관찰되었다.

• Transactions on Electrical and Electronic Materials
• /
• 제12권4호
• /
• pp.169-173
• /
• 2011

In this study, Al-N codoped p-type zinc oxide (ZnO) thin films were deposited on Si and homo-buffer layer templates in a mixture of $N_2$ and $O_2$ gas with ceramic ZnO:(2 wt% $Al_2O_3$) as a sputtering target using DC- magnetron sputtering. X-ray diffraction spectra of two-theta diffraction showed that all films have a predominant (002) peak of ZnO Wurtzite structure. As the $N_2$ fraction in the mixed $N_2$ and $O_2$ gases increased, field emission secondary electron microscopy revealed that the surface appearance of codoped films on Si varied from smooth to textured structure. The p-type ZnO thin films showed carrier concentration in the range of $1.5{\times}10^{15}-2.93{\times}10^{17}\;cm^{-3}$, resistivity in the range of 131.2-2.864 ${\Omega}cm$, and mobility in the range of $3.99-31.6\;cm^2V^{-1}s^{-1}$ respectively.

• 한국산학기술학회논문지
• /
• 제8권5호
• /
• pp.1057-1061
• /
• 2007

본 연구에서는 AlAs와 ZnO target을 사용하여 RF magnetron sputtering 시스템에서 layer-by-layer 방법으로 증착한 ZnO 박막의 특성에 대하여 조사하였다. 또한 열처리 전에 $H_2O_2$용액을 사용한 처리가 박막 특성에 미치는 영향도 조사하였다. 연구 결과 열처리 조건에 따라 n-형 또는 p-형 박막이 형성되는 것으로 관찰되었다. 이러한 결과는 박막의 전도 형태를 임의로 수정할 수 있음을 의미하는 동시에 박막 특성의 열적 불안정성을 암시하는 것이기도 하다. 144시간까지 스트레스를 인가한 후 측정한 박막 특성 결과 열처리 과정 중 발생하는 이러한 박막 특성 변화는 열처리 전 박막을 30% $H_2O_2$용액에 1분간 처리함으로써 억제할 수 있는 것으로 관찰되었다.