• Journal of Korea Technical Association of The Pulp and Paper Industry
• /
• v.43 no.1
• /
• pp.29-35
• /
• 2011

Since the role of lignin in the wood cell wall is to keep integrity and structure rigidity of lignocellulosic substrate, lignin of the cell wall has to be destroyed before enzymatic hydrolysis of wood polysaccharides. The aspen wood meals were delignified with ozone in acidic condition. The chemical characteristics of wood meal were investigated. The 60% of lignin and almost zero % of polysaccharides in aspen wood meal was degraded with 10min. ozone treatment. The phenolic hydroxyl groups of lignin in ozonated wood meal were increased with ozonation time. The sugar composition of ozonated wood meal showed that the hemicellulose was more susceptible to ozonation than cellulose. The yield of aldehyde was increased in some degree with 10min. ozone treatment and decreased with longer ozone treatment.

• Journal of Korea Technical Association of The Pulp and Paper Industry
• /
• v.42 no.3
• /
• pp.67-73
• /
• 2010

Pine (Pinus densiflora) and aspen (Populus euramericana) wood meals were treated with ozone at various time schedule in acidic condition. The lignin contents and surface area of the ozone treated wood meals were determined and the enzymatic hydrolysis rate of ozonated wood meals was evaluated. The feasibility of enzymatic hydrolysis of the ozone treated wood meal was obviously influenced with the degree of delignification. After ozone treatment of wood meal for 10min, total pore volume were slightly increased in the surface of wood meal. When wood meals were treated with ozone longer than 10min, few change in the pore volume was observed. However, the area of over $50{\AA}$ of pore size is increased with ozonation time. As a conclusion, the rate of enzymatic hydrolysis of wood is more effective with the pore size distribution than the total pore volume.

• Journal of the Korean Wood Science and Technology
• /
• v.25 no.2
• /
• pp.75-80
• /
• 1997

This research has been examined to measure the degree of the fiber damage of ozonenation high yield pulp in the beating process. Ozone treated the TMP(Thermomechanical Pulp) and CTMP(Chemithermomechanical Pulp) of spruce and the CTMP of birch has been beaten to be reached 200ml(freeness) of its content. It had been studied the forming of fiber distribution by treatment for long fiber, short fiber, fine with the above method. As ozone treatment time gets longer, the pulp has showed the tendency of increasing the fiber content of 28, 48mesh. Ozone treated fiber has been increased long fiber content by being added softness. By given longer ozone treatment time, the TMP and CTMP of spruce has showed the decreasing of fiber content. On the contrary, CTMP of birch has showed the increasing its fiber content. It had proved that the results of difference are rather closer to the species of tree than closer to the kinds of pulp. The fiber content of over 200mesh which has created in beating process demonstrates the decreasing of its fiber content by getting longer ozone treatment time. The softness of fiber can be extracted by the lignin of fiber surface that had been formed by ozone treatment. Thus we assume that the fiber in the process of beating obtains less physical damage.

• Journal of Korea Technical Association of The Pulp and Paper Industry
• /
• v.47 no.1
• /
• pp.1-9
• /
• 2015

Wood fibers for medium density fiberboard (MDF) was used in the filler layer of the white duplex board for increasing thickness and bulk of the board. The MDF fibers were treated with ozone (3% based on dry weight of the fibers), and mixed together with OCC (old corrugated container) to form paper. Ozone-treated MDF fibers gave high bulk, high tensile strength, high internal bond and fast drainage to the furnish mixed with OCC. It was shown that there were possibilities to reduced basis weight of the filler layer without loss of thickness, stiffness, and tensile strength. Furthermore, it showed the possibility to develop a new kind of board product that has high stiffness as well as high strength properties with light basis weight by application of the ozone-treated MDF fibers.

• Journal of the Korean Wood Science and Technology
• /
• v.43 no.1
• /
• pp.9-16
• /
• 2015

This study was carried out to investigate the effect of delignification on properties of lignocellulose nanofibers (LCNFs) prepared by wet disk-milling (WDM) after steam and ozone oxidation pre-treatments and their nanopaper sheets. Delignification treatment was effective to obtain fine morphology with uniform fiber diameter less than 35 nm without aggregation, and increased the specific surface area (SSA) and filtration time of LCNFs. In particular, SSA and filtration time of the LCNFs prepared by WDM after ozone pretreatment increased 1.5 and 5.4 times after further delignification. Delignification also increased whiteness and decreased the redness of nanopaper sheets. The highest color difference (41.9) before and after the delignification was obtained in LCNFs prepared by WDM after the steam pretreatment. Tensile properties of nanopaper sheets were also increased by further delignification. The highest tensile strength was found to be 142 MPa.

• Journal of the Korean Wood Science and Technology
• /
• v.36 no.4
• /
• pp.37-43
• /
• 2008

The research attempted to develop an eco-friendly wood adhesive based on vegetable oil (soybean oil), the renewable and sustainable natural resources, using ozonification technology for the chemical structure modification. The soybean oils (SBO) were reacted with $O_3$ at the rate of 7.13 g/h for different times, 15 minutes, 30 minutes, 60 minutes, and 120 minutes. Modified chemical structure of the ozonized SBOs were examined by Fourier transform Infrared (FT-IR) spectrum. The FT-IR spectrum of SBO had an absorbance peak at $3010cm^{-1}$ that is the characteristic peak of the unsaturated double bonds. As ozone treatment time increased, the peak of the double bond was disappeared and aldehyde or carboxyl peak appeared at $1700cm^{-1}$. The dry, wet, and cyclic boiling bond strengths of the ozonized SBO mixed with polymeric diphenylmethane-4, 4-diisocyanate (pMDI) were also investigated. In the dry shear test, all strengths met constantly the standard requirement of $7.0kgf/cm^2$ (KS F3101 2006). The bond strengths gradually increased with increasing ozone treatment time. The highest strength showed at 60 minutes ozone treatment and decreased values at 120 minutes. In the cyclic boiling shear test, 30, 60 and 120 minutes exceeded the standard requirement.

• Proceedings of the Korea Technical Association of the Pulp and Paper Industry Conference
• /
• 1999.11b
• /
• pp.61-69
• /
• 1999

Contaminants such as fatty acids, triglycerides, resin acids and foam collected from a high yield sulfite weak liquor storage tank lowered the water surface tension and reduced inter-fibre bonding but also tended to benefit sheet opacity. Some common wet end additives such as defoamers and dispersants gave similar results. Lignosulfonate and naphthalene sulfonate showed little if any negative effect on both surface tension and sheet strength properties. Among the natural wood extractives. fatty acids were identified to be most detrimental followed by triglycerides and then resin acids. In order to alleviate the detrimental impact of these contaminants, membrane separation, air floatation and ozone treatment were carried out on paper machine white water samples. The effect of these treatments on removal of fatty and resin acids was quantified by a GC-Mass analysis. Reverse osmosis with a 1000 molecular weight cut off membrane failed to totally reject fatty and resin acids, but markedly reduced losses of sheet properties due to contaminants. Ozone treatment resulted in a significant increase of the surface tension and air floatation was considered to be a practical and useful method for removing fatty and resin acids from the machine white water.

• Journal of Korean Society of Environmental Engineers
• /
• v.28 no.12
• /
• pp.1280-1286
• /
• 2006

Three different virgin activated carbons made of each coal(Calgon), coconut(Samchully) and wood(Picabiol) based activated carbon(AC) were tested for an adsorption performance of 1,4-dioxane in a continuous adsorption column. Breakthrough behavior was Investigated that the breakthrough points of coal, coconut and wood based AC were observed as 3600 bed volumn(BV), 1440 BV and 144 BV respectively. Adsorption capacity(X/M) of coal, coconut and wood based AC was observed. The reported results of adsorption capacity showed that coal based AC was highest(578.9 ${\mu}g/g$), coconut based AC was intermediate(142.3 ${\mu}g/g$) and wood based AC was lowest(7.4 ${\mu}g/g$) due to increasing specific surface area. Moreover, carbon usage rates(CURs) for coal, coconut and wood based AC had been shown as 0.48 g/day, 1.41 g/day and 6.9 g/day respectively. The constant characteristic of the system, k of coal based AC was found to be 91.5 and k of coconut based AC was found to be 17.9. Removal efficiencies of 1,4-dioxane with different ozonation dosages(2 and 5 mg/L) for 20 min ozonation had been shown 38% and 87% respectively. There was no observation for biological removal of 1.4-dioxane by attached micro-organisms when used(3.1 years and over 5 years) biological activated carbon(BAC) without pretreatment of oxidation were employed. When a combination of ozonation(2 mg/L and 5 mg/L) and BAC process for $10{\sim}30$ min was applied, removal efficiency for 1,4-dioxine increased only $2{\sim}6%$ compared to only applying ozonation. Therefore removal efficiency of BAC process prior to using oxidation was proven to negligible. Consequently, the results presented in this paper provide a better insight into the adsorption performance of 1,4-dioxane. This observation suggests that using virgin activated carbon made of coal is the best selection for removal of 1,4-dioxane in the water treatment for an advanced treatment. It is clear from this research that longer EBCT for ozonation or higher ozone concentration are more effective operation methods for removal of 1,4-dioxane than longer EBCT in the BAC process.

• Journal of the Korean Wood Science and Technology
• /
• v.38 no.4
• /
• pp.316-322
• /
• 2010

The research attempted to develop a wood adhesive based on waste cooking oil, using ozonification technology for the chemical structure modification. The waste cooking oil (WCO) was reacted with $O_3$ for different times; 1 h, 2 h, and 3 h. The chemical structure modifications of the ozonized WCOs were examined by Fourier transform Infrared (FT-IR) spectrum. The FT-IR spectrum of WCO had an absorbance peak at 3,010 $cm^{-1}$ that was the characteristic peak of the unsaturated double bonds. As ozone treatment time increased, the peak of the double bond was disappeared and carboxyl peak appeared at 1,700 $cm^{-1}$. Especially, the double bond of 3 hrs-ozonized WCO was vanished almost. In results of the dry bonding strengths of the 3 hrs-ozonized WCO mixed with polymeric methylene diphenyl diisocyanate (pMDI) were the strengths of weight ratio of 3hrs-ozonized WCO : pMDI, 1 : 0.5, 8.08 kgf/$cm^2$, 1 : 0.75, 9.53 kgf/$cm^2$ 1 : 1, 44.16 kgf/$cm^2$, 1 : 2, 58.08 kgf/$cm^2$, 1 : 3, 61.41 kgf/$cm^2$, and 1 : 4, 46.95 kgf/$cm^2$. Therefore, it was found that the optimum equivalent ratio was formed at the ratio of 1 : 2 or 1 : 3. Under wetting the bonding strength of 1 : 3 ratio was appeared higher than that of 1 : 2 ratio, while the results obtained from hot-water and cyclic boiling shear test were similar.