Aluminum nitride (AlN) thin films with a TiN buffer layer have been fabricated on SUS430 substrate by RF reactive magnetron sputtering at room temperature under 25~75% $N_2$ /Ar. The characterization of film properties were performed using surface profiler, X-ray diffraction, X-ray photoelectron spectroscopy(XPS), and pressure-voltage measurement system. The deposition rates of AlN films were decreased with increasing the $N_2$ concentration owing to lower mass of nitrogen ions than Ar. The as-deposited AlN films showed crystalline phase, and with increasing the $N_2$ concentration, the peak of AlN(100) plane and the crystallinity became weak. Any change in the preferential orientation of the as-deposited AlN films was not observed within our $N_2$ concentration range. But in the case of 50% $N_2$ /Ar condition, the peak of (002) plane, which is determinant in pressure sensing properties, appeared. XPS depth profiling of AlN/TiN/SUS430 revealed Al/N ratio was close to stoichiometric value (45:47) when deposited under 50% $N_2/Ar$ atmosphere at room temperature. The output signal voltage of AlN sensor showed a linear behavior between 26~85 mV, and the pressure-sensing sensitivity was calculated as 7 mV/MPa.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.27 no.12
• /
• pp.815-819
• /
• 2014

Aluminum nitride (AlN) thin film and TiN film as a buffer layer were deposited on INCONEL 600 substrate by reactive RF magnetron sputtering at room temperature(R.T.) under 25~75% $N_2/Ar$ atmosphere. The as-deposited AlN films at 25~50% $N_2/Ar$ showed a polycrystalline phase of hexagonal AlN, and an amorphous phase. The peak of AlN (002) plane, which was determinant on a performance of piezoelectric transducer, became strong with increasing the $N_2/Ar$ ratio. Any change in the preferential orientation of the as-deposited AlN films was not observed within our $N_2$ concentration range. The piezoelectric sensing properties of AlN module were performed using pressure-voltage measurement system. The output signal voltage of AlN module showed a linear behavior between 20~80 mV in 1~10 MPa range, and the pressure-sensing sensitivity was calculated as 3.6 mV/MPa.

• Korean Journal of Materials Research
• /
• v.18 no.10
• /
• pp.535-541
• /
• 2008

Growth behavior of InGaN/GaN self-assembled quantum dots (QDs) was investigated with respect to different growth parameters in low pressure metalorganic chemical vapor deposition. Locally formed examples of three dimensional InGaN islands were confirmed from the surface observation image with increasing indium source ratio and growth time. The InGaN/GaN QDs were formed in Stranski-Krastanow (SK) growth mode by the continuous supply of metalorganic (MO) sources, whereas they were formed in the Volmer-Weber (V-W) growth mode by the periodic interruption of the MO sources. High density InGaN QDs with $1{\sim}2nm$ height and $40{\sim}50nm$ diameter were formed by the S-K growth mode. Dome shape InGaN dots with $200{\sim}400nm$ diameter were formed by the V-W growth mode. InN content in InGaN QDs was estimated to be reduced with the increase of growth temperature. A strong peak between 420-460 nm (2.96-2.70 eV) was observed for the InGaN QDs grown by S-K growth mode in photoluminescence spectrum together with the GaN buffer layer peak at 362.2 nm (3.41 eV).

• Korean Journal of Optics and Photonics
• /
• v.16 no.4
• /
• pp.384-391
• /
• 2005

A polymer optical microring resonator, which is laterally coupled to a straight bus waveguide, has been proposed and demonstrated using a nanoimprint technique. The propagation loss of the ring waveguide and the optical power coupling between the ring and bus waveguides was calculated by using a beam propagation method, then the dependence of the device performance on them was investigated using a transfer matrix method. We have especially introduced an imprint stamp incorporating a smoothing buffer layer made of a silicon nitride thin film. This layer played an efficient role in improving the sidewall roughness of the waveguide pattern engraved on the stamp and thus reducing the scattering loss. As a result the overall Q factor of the resonator was greatly increased. Also it reduced the gap between the ring and bus waveguides effectively to enhance the coupling between them, without relying on the direct writing method based on an e-beam writer. As for the achieved device performance at the wavelength of 1550 nm, the quality factor, the extinction ratio, and the free spectral range were ~103800, ~11 dB, and 1.16 m, respectively.