• Transactions on Electrical and Electronic Materials
• /
• v.1 no.3
• /
• pp.29-33
• /
• 2000

The crystallographic and high frequency characteristics of $Fe_{73.9}Cu_{1.0}Nb_{3.5}Si_{14.0}B_{7.6}$ soft magnetic alloys were investigated under magnetic field annealing, The crystallization fraction of annealed samples with longitudinal magnetic fields is higher than that of samples without magnetic field. When the transverse magnetic field is applied, the crystallization fraction does not increases but decreases until $500^{circ}C$. It is found that for samples, the saturation induction are all same with 1.3 T. The coercive field of as-cast samples is 1.03 A/cm, but in annealed samples it decrease from 0.56 to 0.1A/cm with increasing annealing temperature from 400 to $550^{circ}C$. The squareness of annealed samples under transverse magnetic field has a small value than that of both without field and with longitudinal field annealing. It is noted that the magnetic field annealing with transverse direction to amorphous $Fe_{73.9}Cu_{1.0}Nb_{3.5}Si_{14.0}B_{7.6}$ profoundly influenced on the Mossbauer spectra in contrast to that with longitudinal direction and without magnetic field.

• Journal of Powder Materials
• /
• v.14 no.5
• /
• pp.303-308
• /
• 2007

The oxidation of $Fe_{73}Si_{16}B_7Nb_3Cu_1$ nanocrystalline powder has been conducted to investigate its influence on the electromagnetic wave absorption characteristics of the soft magnetic material. Oxidation occurred primarily on the surface of nanocrystals. Oxidation reduced the real part of complex permeability due to the reduction of the relative volume of the powder, which otherwise contributes to the permeability. Oxidation reduced the absorption efficiency of the sheet at frequencies over 1GHz, indicating that the relative contribution of skin depth increments to the absorption was not significant. The pulverization and milling process lowered the optimum crystallization temperature of the material by $40{\sim}50^{\circ}C$ because of the internal energy accumulated during the fragmentation and powder thinning processes.

• Journal of IKEEE
• /
• v.23 no.2
• /
• pp.599-605
• /
• 2019

Ferrite cores are used as a soft magnetic material in the fabrication of couplers for inductive powerline communication (PLC). However, it is difficult to adjust the size freely according to the power-line and power-grid environment. In this paper, we report that a nano-crystalline alloy with higher permeability than ferrite can be used as an inductive coupler for non-contact PLC. Since nano-crystalline are produced in the form of a thin ribbon, the size of the coupler can be freely controlled by the number of ribbons wound on the toroidal core. It was fabricated with induction type coupler and showed to be suitable for non-contact power line communication. Experimental results show that the communication bandwidth is 45 Mbps for 100 m and 8 Mbps for 200 m under the current fluctuation of less than 100 A, and the reception ratio is 100%.

• Journal of Magnetics
• /
• v.21 no.2
• /
• pp.192-196
• /
• 2016

The Fe-Si-B-Nb-Cu alloys containing Ca and Al were rapidly solidified to thin ribbons by melt-spinning. The ribbons were ball-milled to make powders, and then mixed with 1 wt.% water glass and 1.5 wt.% lubricant. The mixed powders were burn-off, and then compacted to form toroidal-shaped cores, which were heat treated to crystallize the nano-grain structure and to remove residual stress of material. The characteristics of the powder cores were analyzed using a differential scanning calorimetry (DSC) and a B-H meter. The microstructures were observed using transmission electron microscope (TEM). The optimized soft magnetic properties (${\mu}_i$ and $P_{cv}$) of the powder cores were obtained from the Ca and Al containing alloys after annealing at $530^{\circ}C$ for 1 h. The core loss of Fe-Si-B-Nb-Cu-based powder cores was reduced by the addition of Ca element, and the initial permeability increased due to the addition of Al element.