• Journal of Adhesion and Interface
• /
• v.22 no.4
• /
• pp.136-143
• /
• 2021

Polyurea has been investigated as a polymer matrix for composite materials because of its high mechanical strength. Although polyurea has a similar chemical structure to polyurethane, it has much higher strength and durability. In this study, the fabrication of polyurea composites reinforced with carbon nanotube (CNT) and graphene oxide (GO) is demonstrated to enhance the tensile strength of the glass fibers composite. Using FTIR and Raman spectroscopies, the chemical structures of polyurea, CNT, and GO are investigated. As a result, spectroscopy analysis reveals that the chemical structure of CNT, GO, and polyurea is maintained during the fabrication of the composite structure. Scanning electron microscopy reveals the uniform distribution of CNT and GO across the polyurea matrix. The reinforcement of 1 wt% CNT in polyurea enhances the tensile strength of CNT/polyurea composites. In contrast, the reinforcement of GO in polyurea induces the degradation of the tensile strength of GO/polyurea composites.

• Elastomers and Composites
• /
• v.47 no.4
• /
• pp.297-309
• /
• 2012

Different amounts of foaming agents were employed in natural rubber(NR)/butadiene rubber(BR) blends to understand the foaming behavior in presence of nano-reinforcing agent, zinc methacrylate (ZMA). The ZMA greatly improved most of the mechanical properties of the rubber foams, however it did not show considerable effect on the cell morphology, such as cell size, density and porosity. It was also observed that the foaming agent concentration affected all the mechanical parameters. When the content of foaming agent was increased, the number of foams was increased leading to a decrease in density of the compounds. But the size and distribution of foams remained unchanged with increased foaming agent. The effect of high styrene-butadiene rubber (HSBR) was also studied. The size of cells became smaller and the cell uniformity was improved with increasing HSBR. The foam rubber compounds showed much efficient energy absorbing capability at higher strains.

• Textile Coloration and Finishing
• /
• v.28 no.2
• /
• pp.101-108
• /
• 2016

Polypropylene(PP)/multiwalled carbon nanotubes(MWCNT) nanocomposites films and PP/poly(vinyl alcohol)/CNT nanocomposites films were prepared through melt mixing method by the extruder. The PP/CNT nanocomposites films, which contain CNT of a variable content, were prepared for the first time and research on a appropriate content of the CNT on the PP/CNT nanocomposites films was conducted. The effects of take-up speed of the extruder on the mechanical and chemical properties of the PP/CNT and PP/PVA/CNT nanocomposites film were studied. Field emission scanning electron microscope(FE-SEM) was used to examine the surface morphology and the DSC measurement and tensile test were conducted. It was found that the properties decreased when take-up speed was increased.

• Elastomers and Composites
• /
• v.43 no.4
• /
• pp.213-220
• /
• 2008

In this study, the effects of curing system on the hardness of rubber materials at various temperature were investigated. NR and SBR were compounded with various sulfur or peroxide content, in order to obtain various crosslink densities. The changes of hardness and crosslink density were measured as a function of temperature and the relationship was examined. The thermal stresses were also measured in order to investigate the effect of entropy as a function of temperature. The hardness of NR and SBR compounds increased with increasing temperature above room temperature, and the measured thermal stress increased as temperature increased. However, the crosslink densities were not changed by temperature change.

• Korean Journal of Materials Research
• /
• v.19 no.2
• /
• pp.85-89
• /
• 2009

Nano-crystalline hydroxyapatite (HAp) films were formed at the Ti surface by a single-step microarc oxidation (MAO), and HAp-zirconia composite (HZC) films were obtained by subsequent chemical vapor deposition (CVD) of zirconia onto the HAp. Through the CVD process, zero- and one-dimensional zirconia nanostructures having tetragonal crystallinity (t-ZrO2) were uniformly distributed and well incorporated into the HAp crystal matrix to form nanoscale composites. In particular, (t-$ZrO_2$) was synthesized at a very low temperature. The HZC films did not show secondary phases such as tricalcium phosphate (TCP) and tetracalcium phosphate (TTCP) at relatively high temperatures. The most likely mechanism for the formation of the t-$ZrO_2$ and the pure HAp at the low processing temperature was proposed to be the diffusion of $Ca^{2+}$ ions. The HZC films showed increasing micro-Vickers hardness values with increases in the t-$ZrO_2$ content. The morphological features and phase compositions of the HZC films showed strong dependence on the time and temperature of the CVD process. Furthermore, they showed enhanced cell proliferation compared to the $TiO_2$ and HAp films most likely due to the surface structure change.

• Carbon letters
• /
• v.26
• /
• pp.51-60
• /
• 2018

An electroless deposition method was used to modify the surface properties of rice husk ceramic particles (RHC) by depositing nano-nickel on the surface of the RHC (Ni-RHC). The dry tribological performances of aluminum matrix composite adobes containing different contents of RHC and Ni-RHC particles have been investigated using a micro-tribometer. Results showed that the Ni-RHC particles substantially improved both the friction and wear properties of the Ni-RHC/aluminum matrix adobes. The optimal concentration was determined to be 15 wt% for both the RHC and Ni-RHC particles. The improvements in the tribological properties of aluminum adobes including the Ni-RHC were ascribed to friction-induced peeling off of Ni coating and formation of protection layer on the wear zone, both of which led to low friction and wear volume.

• 한국신재생에너지학회:학술대회논문집
• /
• 2009.06a
• /
• pp.765-768
• /
• 2009

In this work, we prepared the activated multi-walled carbon nanotubes (Acti-MWNTs) with well developed physical surface structures, high specific surface area, and higher adsorption capacity by a physical activation process, in order to enhance the hydrogen storage capacity. The Acti-MWNTs' changes in the crystalline phase and in their lattice distortions were characterized by X-ray diffraction (XRD). The textural properties of the Acti-MWNTs were investigated by a nitrogen adsorption isotherms by Brunauer-Emmett-Teller (BET) equation and Harvath-Kawazoe (H-K) calculation, respectively. The hydrogen storage capacity of the Acti-MWNTs was investigated by BEL-HP at 298 K/100 bar. The hydrogen storage capacity of the Acti-MWNTs was improved with the physical activation, resulted from the formation of new hydrogen-favorable sites on the Acti-MWNT surfaces. In conclusion, the physical activation was one of the effective method to enhance the hydrogen storage capacity of the MWNTs.

• Journal of Powder Materials
• /
• v.16 no.4
• /
• pp.280-284
• /
• 2009

The pressureless sintering behavior of $Al_2O_3$/Cu powder mixtures, prepared from $Al_2O_3$/CuO and $Al_2O_3$/Cu-nitrate, has been investigated. Microstructural observation revealed that $Al_2O_3$ powders with nano-sized Cu particles could be synthesized by hydrogen reduction method. The specimens, pressureless-sintered at $1400^{\circ}C$ for 4 min using infrared heating furnace with the heating rate of $200^{\circ}C$/min, showed the relative density of above 90%. Maximum hardness of 16.1 GPa was obtained in $Al_2O_3$/MgO/Cu nanocomposites. The nanocomposites exhibited the enhanced fracture toughness of 4.3-5.7 $MPa{\cdot}m^{1/2}$, compared with monolithic $Al_2O_3$. The mechanical properties were discussed in terms of microstructural characteristics.

• Journal of Powder Materials
• /
• v.16 no.3
• /
• pp.209-216
• /
• 2009

A composite of rapidly solidified Al-6061 alloy powder with graphite particle reinforcements was prepared by ball milling and subsequent hot extrusion. The microstructure and mechanical properties of these composites were investigated as a function of milling time. With increasing milling time, the gas atomized initially and spherical powders became elongated with a maximum aspect ratio after milling for 30 h. Then, refinement and spheroidization were achieved by further milling to 70 h with a homogeneous and fine dispersion of graphite particles forming between the matrix alloy layers. The best compression and wear properties were obtained in the powder milled for 70 h, associated with the increased fine and homogeneous distribution of graphite particles in the aluminum alloy matrix.

• Journal of Powder Materials
• /
• v.12 no.6 s.53
• /
• pp.393-398
• /
• 2005

In-situ processing route was adopted to disperse carbon nanotubes (CNTs) into $Al_2O_3$ powders homogeneously. The $Al_2O_3$ composite powders with homogeneous dispersion of CNTs could be synthesized by a catalytic route for in-situ formation of CNTs on nano-sized Fe dispersed $Al_2O_3$ powders. CNTs/Fe/$Al_2O_3$ nanopowders were densified by spark plasma sintering (SPS). The hardness and bending strength as well as electrical conductivity increased with increasing sintering temperature. However, the electrical conductivity of the composites sintered at above $1500^{\circ}C$ showed decreased value with increasing sintering temperature due to the oxidation of CNTs.