• Structural Engineering and Mechanics
• /
• v.86 no.4
• /
• pp.487-501
• /
• 2023

Nanoparticles have lower size and larger specific surface area, good stability and less toxic and side effects. In recent years, with the development of nanotechnology, its application range has become wider and wider, especially in the field of biomedicine, which has received more and more attention. Bone defect repair materials with high strength, high elasticity and high tissue affinity can be prepared by nanotechnology. The purpose of this paper was to study how to analyze and study the composite materials for sports bone injury based on multifunctional nanomaterials, and described the electrospinning method. In this paper, nano-sized zirconia (ZrO₂) filled micro-sized hydroxyapatite (HAP) composites were prepared according to the mechanical properties of bone substitute materials in the process of human rehabilitation. Through material tensile and compression experiments, the performance parameters of ZrO₂/HAP composites with different mass fraction ratios were analyzed, the influence of filling ZrO₂ particles on the mechanical properties of HAP matrix materials was clarified, and the effect of ZrO₂ mass fraction on the mechanical properties of matrix materials was analyzed. From the analysis of the compressive elastic modulus, when the mass fraction of ZrO₂ was 15%, the compressive elastic modulus of the material was 1222 MPa, and when 45% was 1672 MPa. From the analysis of compression ratio stiffness, when the mass fraction of ZrO₂ was 15%, the compression ratio stiffness was 658.07 MPa·cm³/g, and when it was 45%, the compression ratio stiffness is 943.51MPa·cm³/g. It can be seen that by increasing the mass fraction of ZrO₂, the stiffness of the composite material can be effectively increased, and the ability of the material to resist deformation would be increased. Typically, the more stressed the bone substitute material, the greater the stiffness of the compression ratio. Different mass fractions of ZrO₂/HAP filling materials can be selected to meet the mechanical performance requirements of sports bone injury, and it can also provide a reference for the selection of bone substitute materials for different patients.

• Advances in nano research
• /
• v.14 no.5
• /
• pp.435-442
• /
• 2023

Sports activities, including playing tennis, are popular with many people. As this industry has become more professionalized, investors and those involved in sports are sure to pay attention to any tool that improves athletes' performance Tennis requires perfect coordination between hands, eyes, and the whole body. Consequently, to perform long-term sports, athletes must have enough muscle strength, flexibility, and endurance. Tennis rackets with new frames were manufactured because tennis players' performance depends on their rackets. These rackets are distinguished by their lighter weight. Composite rackets are available in many types, most of which are made from the latest composite materials. During physical exercise with a tennis racket, nanocomposite materials have a significant effect on reducing injuries. Materials as strong as graphite and thermoplastic can be used to produce these composites that include both fiber and filament. Polyamide is a thermoplastic typically used in composites as a matrix. In today's manufacturing process, materials are made more flexible, structurally more vital, and lighter. This paper discusses the production, testing, and structural analysis of a new polyamide/Multi-walled carbon nanotube nanocomposite. This polyamide can be a suitable substitute for other composite materials in the tennis racket frame. By compression polymerization, polyamide was synthesized. The functionalization of Multi-walled carbon nanotube (MWCNT) was achieved using sulfuric acid and nitric acid, followed by ultrasonic preparation of nanocomposite materials with weight percentages of 5, 10, and 15. Fourier transform infrared (FTIR) and Nuclear magnetic resonance (NMR) confirmed a synthesized nanocomposite structure. Nanocomposites were tested for thermal resistance using the simultaneous thermal analysis (DTA-TG) method. scanning electron microscopy (SEM) analysis was used to determine pores' size, structure, and surface area. An X-ray diffraction analysis (XRD) analysis was used to determine their amorphous nature.

• Restorative Dentistry and Endodontics
• /
• v.47 no.4
• /
• pp.43.1-43.13
• /
• 2022

Objectives: This study compared the surface gloss (SG), gloss retention (GR), and color stability (CS) of 2 universal resin composites after chemical (CA) and mechanical (MA) aging. Materials and Methods: Twenty disc-shaped samples of G-ænial A'Chord (GC-Europe) and Filtek Universal (3M-ESPE) were polished with sequential abrasive papers. For CA, specimens were stored in 1 mL of 75% ethanol for 15 days at 37℃, and readings (SG, GR, and CS) were obtained at baseline and 5, 10, and 15 days. For MA, specimens were subjected to 10,750 simulated brushing cycles. SG and CS were evaluated after every 3,583 cycles. SG was measured with a glossmeter (geometrical configuration: 60°), and values were expressed in gloss units. Color was measured with a spectrophotometer using the CIE-L^*a^*b^* color system. The Student's t-test, 1-way analysis of variance, and Scheffé test were used for statistical analysis (α = 0.05). Results: G-ænial presented significantly higher SG values than Filtek (p = 0.02), with GR reductions of 5.2% (CA) and 5.3% (MA) for G-ænial and 7.6% (CA) and 7.2% (MA) for Filtek. The aging protocol had no statistically significant effect on SG or GR (p = 0.25) from baseline to the final readings. G-ænial-MA presented the lowest color difference (ΔE = 1.8), and G-ænial-CA and Filtek-CA had the largest changes (ΔE = 8.6 and ΔE = 11.8, respectively). Conclusion: G-ænial presented higher SG values and better CS. Both restorative materials demonstrated acceptable GR and CS. Aging protocols impacted these properties negatively.

• Advances in materials Research
• /
• v.13 no.3
• /
• pp.221-232
• /
• 2024

Waste tire management and recycling have grown to be significant issues because they bring up a global environmental concern. Thus, turning recycled waste tires into useful products may help tackle the environmental issue. This research aims to study and compare the effect of recycled carbon black (rCB) and commercial carbon black (CB) at certain 15 vol. % of filler loading on the mechanical, thermal, morphology and electrical properties of epoxy/CB composites. For this project, epoxy resin, diethyltoluenediamine (DETDA), recovered carbon black (rCB) and commercial carbon black (CB) graded N330, N550, N660 and N774 were mixed and compared accordingly to the formulation determined. The CB content was dispersed in the epoxy matrix using the mechanical mixing technique. The distribution and dispersion of CB in the epoxy matrix affect the characteristics of the conductive composites. rCB content at 15 vol% was selected at fixed content for comparison purposes due to the optimum value in electrical conductivity results. The flexural strength results followed the sequence of rCB>N774>N660>N550>N330. As for electrical conductivity results, epoxy/N330 exhibited the highest conductivity value, while the others achieved a magnitude of X10^-3 due to the highest external surface area of N330. In terms of thermal stability, epoxy/N330 and epoxy/N774 were slightly more stable than epoxy/rCB.

• Composites Research
• /
• v.33 no.5
• /
• pp.282-287
• /
• 2020

In the present study, a high-strength polyethylene terephthalate (PET) sheet was fabricated through a densification process of low melting PET fiber (LMF) combined PET sheet. During the thermal heat treatment process of the combined LMF, individual PET fiber was connected, which in turn leads to the improvement of the interfacial bonding force between the fibers. Also, the densification of the PET sheet leads to reduce macrospore density and in return could enhance the binding force between the overlapped PET networks. Consequently, the asprepared LMF-PET sheet showed about 410% improved tensile strength and the same elongation compared to before compression. Besides, the enhanced bonding force can prevent the shrinkage of the PET fiber network and exhibited excellent dimensional stability.

• Korean Journal of Materials Research
• /
• v.17 no.1
• /
• pp.11-17
• /
• 2007

Turbulent in-situ mixing process is a new material process technology to get dispersed phase in nanometer size by controlling reaction of liquid/solid, liquid/gas, flow ana solidification speed simultaneously. In this study, mixing which is the key technology to this synthesis method was studied by computational fluid dynamics. For the simulation of mixing of liquid metal, static mixers investigated. Two inlets for different liquid metal meet ana merge like 'Y' shape tube having various shapes and radios of curve. The performance of mixer was evaluated with quantitative analysis with coefficient of variance of mass fraction. Also, detailed plots of intersection were presented to understand effect of mixer shape on mixing. The simulations show that the Reynolds number (Re) is the important factor to mixing and dispersion of $TiB_2$ particles. Mixer was designed according to the simulation, and $Cu-TiB_2$ nano composites were evaluated. $TiB_2$ nano particles were uniformly dispersed when Re was 1000, and cluster formation and reduction in volume fraction of $TiB_2$ were found at higher Re.

• Journal of Powder Materials
• /
• v.21 no.1
• /
• pp.16-20
• /
• 2014

In order to fabricate the porous $Al_2O_3$ with dispersion of nano-sized Cu particles, freeze-drying of camphene/$Al_2O_3$ slurry and solution chemistry process using Cu-nitrate are introduced. Camphene slurries with 10 vol% $Al_2O_3$ was frozen at $-25^{\circ}C$. Pores were generated by sublimation of the camphene during drying in air. The sintered samples at 1400 and $1500^{\circ}C$ showed the same size of large pores which were aligned parallel to the sublimable vehicles growth direction. However, the size of fine pores in the internal walls of large pores decreased with increase in sintering temperature. It was shown that Cu particles with the size of 100 nm were homogeneously dispersed on the surfaces of the large pores. Antibacterial test using fungus revealed that the porous $Al_2O_3$/1 vol% Cu composite showed antifungal property due to the dispersion of Cu particles. The results are suggested that the porous composites with required pore characteristics and functional property can be fabricated by freeze-drying process and addition of functional nano particles by chemical method.

• Elastomers and Composites
• /
• v.46 no.2
• /
• pp.102-111
• /
• 2011

The innerliner for a tire has excellent impermeability, air retention and good flex properties. The innerliner offers a role to improve performance parameter, such as air retention and tire durability that is of praricular importance for commercial tires. In order to improve the gas barrier properties of a innerliner, most of the innerliner rubbers, such as a halogenated butyl rubber(HIIR), brominated poly(isobutylene-co-isoprene)(BIIR), brominated polyisobutylene-co-paramethylstyrene(BIMS) are used as nanocomposites with nano fillers such as silicates, graphite etc. Innerliners based on nanocomposites may allow gauge adjustments and permeability reductions with potential improvement in tire durability. This article discusses potential innerliner permeablity reduction and compounding parameters on the properties of nanocomposite based innerliners.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.13 no.6
• /
• pp.309-314
• /
• 2003

A spark plasma sintering technique has been used for the fabrication of $Al_2O_3$-SiC nanocomposites at the low temperature of $1100^{\circ}C$∼$1500^{\circ}C$. The sintered $Al_2O_3$-SiC composites shows very homogeneous microstructure without any particular abnormal grain growth, indicating that the addition of nano-sized SiC particles is very effective to control grain growth and to induce the residual stress in the $Al_2O_3$ matrix, resulting in the intragranular fracture. These SiC particles are present in the grain boundaries and also intragrain, depending on the sintering condition, and improve remarkably the mechanical properties of $Al_2O_3$-SiC composite through the mechanisms of strengthening and toughening induced by crack diffraction and crack bridging.

• Elastomers and Composites
• /
• v.43 no.3
• /
• pp.173-182
• /
• 2008

Rubber-pad forming process for materials such as metal in which portions of the die which act upon the material is composed of a natural or synthetic rubber or elastomer material. This makes the rubber pad forming process relatively cheap and flexible, high accuracy for small product series in particular. In this study, we carried out the physical test and finite element analysis of elastomer such as natural rubber and urethane for steel rack rube forming. The non-linear property of elastomer which are described as strain energy function are important parameter to design and evaluate of elastomer component. These are determined by material tests which are uni-axial tension and bi-axial tension. This study is concerned with simulation and investigation of the significant parameters associated with this process.