• Journal of Welding and Joining
• /
• v.19 no.5
• /
• pp.512-519
• /
• 2001

Sink roll has been used in molten Zn-0.2%Al alloy bath of continuous galvanizing line in sinking and stabilizing process of the steel strip in molten metal bath. In this process, although the scraper scraps off the sink roll surface, the dross compounds is builded up on the sink roll surface and the life time of the sink roll is shorten by the dross compounds. The present study was investigated the application of the spray coating layer on sink roll body for improving durability In molten Zn-0.2%Al alloy. Through the durability tests in molten Zn-0.2%Al alloy with various ceramic and cermet coating layer, the optimum bond and top coating material was obtained. As the results, the system of STS430F base metal, WC-l7Co bond and $ZrO_2-SiO_2$ top coating was clarified to be the best quality of durability in molten Zn-0.2%Al alloy.

• Journal of Korea Foundry Society
• /
• v.30 no.6
• /
• pp.231-234
• /
• 2010

The effect of $C_2Cl_6$ for preventing to the surface oxidation and ignition of molten Mg alloy was studied with metallographic analysis, X-ray diffraction, scanning electron microscopy and energy dispersive spectroscopy. The alloy used for this study was AM100A Mg casting alloy with high strength. In order to investigate the surface protective characteristic of this molten alloy by $C_2Cl_6$ addition, we added them into molten AM100A alloy at $700^{\circ}C$ and then the melts were slowly cooled under a protective atmosphere of air containing Ar gas and $C_2Cl_6$ flux addition. The result found that the surface oxidation and ignition reaction of molten AM100A Mg alloy by adding $C_2Cl_6$ flux was more slowly occurred than that of the only a protective atmosphere of containing Ar gas with increasing time. This result was due to a dense protective film formed containing $MgCl_2$ on surface of molten Mg alloy during casting and solidification. The $MgCl_2$ was formed by a reaction of $C_2Cl_6$ with molten Mg.

• Journal of the Korean Society of Industry Convergence
• /
• v.23 no.4_1
• /
• pp.541-547
• /
• 2020

This paper relates a rheo die casting using electromagnetic force, which is one of the representative semi-solid methods for aluminum. The most important factors in electromagnetic stirring would be the melt temperature, sleeve temperature, electromagnetic force, and input time. The effect of the temperature of molten alloy on the direct rheo-casting is assessed in this study. The temperature of the molten alloy is set to 590 ℃ with a solidification of 40%, 600 ℃ with 30%, and 610℃ with less than 20%. Under the condition of 590 ℃ with a solidification of 40%, the whole molten alloy is solidified, causing non-forming during forming process. Meanwhile, under the condition of 600 ℃, where the solidification was 30%, appropriate amount of molten alloy is solidified, filled well into the mold, resulting in good forming, while at 610 ℃ with the solidification of 20%, the molten alloy is not sufficiently solidified and scattered away. The investigation of the defects inside the product with the help of the X-ray equipment shows that the electromagnetic stirring at 590 ℃ with a solidification of 30% produces many air-pores inside the product.

• Journal of Korea Foundry Society
• /
• v.35 no.3
• /
• pp.62-66
• /
• 2015

Tape casting is an important forming operation used to prepare flat sheets in the various industries. In this study, Doctor Blade tape casting of In-based low melting point alloy was carried out. The purpose of this investigation was to determine the possibility of applying the Doctor Blade tape casting process to the manufacture of low melting point alloy sheets that can be used as thermal fusible parts of battery safety systems. In-based molten alloy that has a melting point of $95^{\circ}C$ was produced; it's viscosity was measured at various temperatures. The molten alloy was used as a slip in the caster of the Doctor Blade tape casting system. The effects of the molten alloy temperatures and carrier speeds on the produced sheet shape were observed. For the casting conditions of 1.5 cm slip height, $120^{\circ}C$ slip temperature, 0.05 mm blade gap and 60 m/min. carrier speed, an In-based alloy thin tape well shaped with 0.16 mm uniform thickness was continuously produced.

• Korean Journal of Materials Research
• /
• v.32 no.7
• /
• pp.326-331
• /
• 2022

AZ31 magnesium alloy was used to manufacture a thin plate using a melt drag method. The effects of roll speed, molten metal temperature, and molten metal height, which are the basic factors of the melt drag method, on the surface shape, the thickness of the thin plate, Vickers hardness, and microstructure of the thin plate were investigated. It was possible to manufacture AZ31 magnesium alloy thin plate at the roll speed range of 1 to 90 m/min. The thickness of the thin plate, manufactured while changing only the roll speed, was about 1.8 to 8.8 mm. The shape of the solidified roll surface was affected by two conditions, the roll speed and the molten metal height, and the Vickers hardness of the manufactured magnesium alloy thin plate value ranged from Hv38~Hv60. The microstructure of the thin plate produced by this process was an equiaxed crystal and showed a uniform grain size distribution. The grain size was greatly affected by the contact state between the molten metal and the solidification roll, and the amount of reactive solids and liquids scraped at the same time as the thin plate. The average grain size of the thin plate fabricated in the range of these experimental conditions changed to about 50-300 ㎛.

• Journal of Welding and Joining
• /
• v.18 no.3
• /
• pp.51-59
• /
• 2000

Sink roll has been used in molten 55%Al-Zn alloy bath of continuous galvanizing line for sinking and stabilizing working steel strip in molten metal bath. In the process, the sink roll body inevitably build up dross compounds and pitting on the sink roll surface during 55%Al-Zn alloy coated strip production, and the life time of the sink roll is shorten by build up dross compounds and pitting. The present study examined the application of thermally sprayed ceramic coatings method on sink roll body for improving erosion resistance at molten 55% Al-Zn pool. In this experiment, the stainless steels such as STS 316L and STS 430F were used as the substrate materials. The CoNiCr and WE-Co powder were selected as bond coating materials. Moreover $Al_2O_3-ZrO_2-SiO_2 and ZrO_2-SiO_2$ powders selected as the top coating materials. Appearances of the specimens before and after dipping to molten 55%Al-Zn pool were compared and analyzed. As a result of this study, STS430F of substrate, WC-Co of bond spray coatings, $ZrO_2-SiO_2$ power of top spray coatings is the best quality in erosion resistance test at molten 55%Al-Zn pool

• Journal of Power System Engineering
• /
• v.5 no.4
• /
• pp.74-81
• /
• 2001

The infiltration behavior of molten Al-alloy, microstructures, hardness, and the interfacial reactions of $SiC_p/Al$ composites fabricated by the pressureless infiltration technique were investigated. It was made clear that both the weight fraction of SiC reinforcement and additive Mg content considerably influenced on the infiltration behavior of the molten Al-alloy matrix. Complete infiltration of molten Al-alloy achieved under the conditions that weight fraction of SiC content is more than 30wt%, and additive Mg content is more than 9wt%. Interfacial region of Al-alloy matrix and SiC reinforcement phase, $Mg_2Si$ was formed by the reaction between Mg and SiC. Another reaction product AlN was also formed by the reaction between Al-alloy matrix and gas atmosphere nitrogen.

• Corrosion Science and Technology
• /
• v.6 no.4
• /
• pp.147-153
• /
• 2007

This study sought to investigate the reaction of Co-binder containing tungsten with molten zinc. Four kinds of Co-W alloys (pure, 10%W, 20%W, 30%W) were prepared using the powder metallurgy method. The specimens were immersion-tested in molten pure zinc baths at $460^{\circ}C$. To evaluate the corrosion property in molten zinc, the weight loss of the specimen was measured after the immersion tests at different immersion times (10~300 min.). Co-10%W alloys, compared with pure cobalt, showed no effect of tungsten addition on the reaction rate in molten zinc. The relationship between the weight loss and the square root of immersion period represents a straight line in both pure cobalt and Co-10%W alloy. The Co-Zn reaction layer in Co- 1O%W alloy consists of $\gamma2$, $\gamma1$, $\gamma$ and ($\beta1$ phases. The rate of weight loss significantly increases and the weight loss behavior is not well accord with the linear relationship as the tungsten content in the Co-W alloy increases. The $\beta1$ layer was not formed on the Co-20%W alloy and neither was a stable Co-Zn intermetallic compound layer found on the Co-30%W alloy. The main cause of increase in reaction rate with increasing tungsten content is related with the instability of the Co-Zn reaction phases as seen on micro-structural analysis.

• Korean Journal of Materials Research
• /
• v.12 no.1
• /
• pp.3-9
• /
• 2002

The corrosion behavior of alloys in a molten salt was investigated along with the oxidation characteristics in the air. The basic composition of alloys in the study was Fe-25Ni-7Cr with Si and RE(rare-earth metal) as additives. The corrosion rate of the alloys was low in a molten salt of LiCl while the rate was high in the mixed molten salt of LiCl and $Li_2O$. When Si is added to the base alloy of Fe-25Ni-7Cr, corrosion resistance was improved as the Si content is increased up to 3%, however, it was observed that the corrosion resistance was getting worse as the Si content is increased. The base alloy with 2.43% of Si and 0.9% of RE(KSA-65), showed higher corrosion rate compared to that of KSA-63 alloy with an equivalent amount of only Si. The corrosion resistance of KSA-65 was similar to that of the base alloy(KSA-60). The oxidation resistance of KSA-65 alloy was greatly increased even at $850^{\circ}C$ for a long term exposure.

• Nuclear Engineering and Technology
• /
• v.53 no.3
• /
• pp.920-926
• /
• 2021

Capsules containing NaCl-MgCl₂ salt with 316L stainless steel or alloy N samples were irradiated in the Ohio State University Research Reactor for 21 nonconsecutive hours. A custom irradiation vessel was designed for this purpose, and details on its design and construction are given. Stainless steel samples that were irradiated during exposure had less corrosive attack than samples exposed to the same conditions without irradiation. Alloy N samples showed no significant effect of irradiation. This work shows a method for conducting in-reactor irradiation-corrosion experiments in static molten salts and presents preliminary data showing that neutron irradiation may decelerate corrosion of alloys in molten chloride salts.