• Journal of the Korean Society for Railway
• /
• v.12 no.4
• /
• pp.590-596
• /
• 2009

In this study, the failure modes and energy absorption characteristics of four different kinds of circular tubes made of carbon, glass, Kevlar and carbon-Kevlar hybrid fibres composites with epoxy resin have been evaluated. To achieve these goals, compressive tests were conducted for the tubes under 10mm/min loading speed. Based on the test results, the carbon/epoxy tube showed the best energy absorption capability, while carbon-Kevlar/epoxy tubes were worst. In the failure mode during crushing, both of the carbon/epoxy tubes and the glass/epoxy tubes were crushed by brittle fracturing mode. The Kevlar/epoxy tubes were collapsed by local buckling mode like steel, while the carbon-Kevlar hybrid tubes were collapsed by mixed mode of local buckling and lamina bending.

• Polymer(Korea)
• /
• v.27 no.6
• /
• pp.576-582
• /
• 2003

When the halogenated flame retardant, decabromodiphenyl oxide, was added to the polypropylene/nylon blend, and was compounded with montmorillonite and compatibilizer, maleic anhydride polypropylene, the improvement of flame retardancy and mechanical properties was investigated. The degree of dispersion between polymer resin and inorganic nanoparticles was investigated, and the flame retardancy and mechanical properties was measured quantitatively. XRD results showed that the montrnorillonite was com-pletely exfoliated after polypropylen/nylon nanocomposites was mixed above twice. By compounding with montmorillonite, polypropylene/nylon blend system was overcome the deterioration of flame retardancy. The tensile strength and impact strength were slightly increased, and by compounding with montmorillonite, the additional increase in mechanical properties was obtained. Therefore, the flame retardancy of polypropylene / nylon blend was decreased by adding nylon, but by compounding with inorganic nanoparticle, improvement of the flame retardancy and mechanical properties was obtained.

• Journal of Nuclear Fuel Cycle and Waste Technology(JNFCWT)
• /
• v.2 no.4
• /
• pp.231-238
• /
• 2004

The conditions are obtained for the decomposition of solid radioactive wastes, including ion exchange resin, zeolite, charcoal, and sludge from nuclear power plant. In the process of decomposing the radioactive wastes was used the microwave acid digestion method with mixed acid. The solution after acid digestion by the following method was colorless and transparent. Each solution was analyzed with ICP-AES and AAS and the recovery yield for 5 different elements added into the simulated radioactive wastes were over $94{\%}$. The elemental analysis of destructive low and medium level radioactive wastes by the proposed microwave acid digestion conditions concerning the chemical characteristics of each radioactive waste are expected to be useful basic data for development of optimal glass formulation.

• Journal of the Korean institute of surface engineering
• /
• v.49 no.2
• /
• pp.218-224
• /
• 2016

Thermal radiation pastes were prepared by dispersing carbon materials as fillers with a content of 1 weight percent in an acrylic resin. The kind of fillers was as follows; $25{\mu}m$ graphite, $45{\mu}m$ graphite, $15{\mu}m$ carbon nanotube(CNT), a 1:1 mixture of $25{\mu}m$ graphite and $15{\mu}m$ CNT, and a 1:1 mixture of $45{\mu}m$ graphite and $15{\mu}m$ CNT. Thermal emissivity was measured as 0.890 for the samples with graphite only, 0.893 for that with CNT only, and 0.892 for those containing both. After coating prepared pastes on a side of 0.4 mm thick aluminium plate and placing the plate over an opening of a box maintained at $92^{\circ}C$ with the coated side out, the temperatures on the uncoated side of the plates were measured. The samples containing graphite and CNT showed the lowest temperatures. The paste with mixed fillers was coated on the back side of the PCB of an LED module and thermal analysis was carried out using Thermal Transient Tester (T3ster) in a still air box. The thermal resistance of the module with coated PCB was measured as 14.34 K/W whereas that with uncoated PCB was 15.02 K/W. The structure function analysis of T3ster data revealed that the difference between junction and ambient temperatures was $13.8^{\circ}C$ for the coated case and $18.0^{\circ}C$ for the uncoated. From the infrared images of heated LED modules, the hottest-spot temperature of the module with coated PCB was lower than that of the uncoated one for a given period of LED operation.

• Korean Journal of Materials Research
• /
• v.19 no.7
• /
• pp.403-406
• /
• 2009

The friction characteristics of automotive brake friction materials that contained different ceramic content were investigated. Several kinds of raw materials, such as resin-based binder, reinforcing fiber, friction restraint, abrasive, and filling materials were mixed, pressed, and heated in order to make the brake friction materials. The contents of SiC and $BaSO_4$ changed from 5 vol% to 20 vol%, respectively. In addition to this, the content of $Al_2O_3$ adjusted from 1 vol% to 16 vol%. The surface morphology of the SiC containing sample appeared rough while more debris was observed when the contents of SiC increased. This implies that the SiC containing brake composite was not adequate for the automobile. However, the relatively smooth surface was observed in samples that contained the $Al_2O_3$. But the roughness was low with a content of 11 vol% $Al_2O_3$ compared to the other samples. This is consistent with the abrasive properties of the samples. In the case of $BaSO_4$ containing samples, the smoothes surface was observed in the contents of 15 vol% $BaSO_4$. Thus, it was concluded that the 11 vol% $Al_2O_3$ and 15 vol% $BaSO_4$ containing composite would be the optimum content for the brake composite. Similar to the results of the surface morphology, the abrasion resistance consistently decreased when the content of SiC increased. On the contrary, the sample that contained 11 vol% $Al_2O_3$ and 15 vol% $BaSO_4$ showed the highest abrasion resistance compared to the other samples.

• Polymer(Korea)
• /
• v.33 no.2
• /
• pp.175-182
• /
• 2009

Waterborne polyurethanes (WPUs) based on isophorone diisocyanate and mixed polyols of poly(tetramethylene glycol) (PTMG)/polycarbonate diol (PCD) were synthesized. The variation of mechanical and dyeing properties and alkali resistance of the WPU films were analyzed according to the polycarbonate (PC) content. The tensile strength of the films increased and the elongation at break decreased with the PC content in the WPU film. The incorporation of PC component in the WPU film did not affect the alkaline hydrolysis behavior. The synthesized WPU solutions were used as impregnating resins for the production of PET artificial leathers. The prepared WPU resins showed the good color fastness to washing, rubbing, and light of the artificial leather fabrics. The improvement of the properties became greater with the PC content in the WPU resin.

• Korean Journal of Dental Materials
• /
• v.43 no.1
• /
• pp.81-89
• /
• 2016

The purpose of this study was to evaluate the effect of the experimental and commercial fluoride varnishes on the Vickers hardness of bovine teeth. The experimental fluoride varnishes with 5 wt.% NaF were fabricated using Bis-GMA or rosin as the resin base. The components were mixed with over-head stirrer under warming up in a double boiler for 30 minutes. Four commercial fluoride varnishes (V-varnish, Flor-opal, Cavity shield, Fluor protector) were compared with the experimental fluoride varnishes. Vickers hardness was measured on the labial surface of bovine anterior teeth after applying fluoride varnish on 5th and 30th day. The surface of bovine teeth was observed with a scanning electron microscope before and after applying fluoride varnish and the change of the components on the bovine teeth surface was measured with EDX. In terms of hardness, the experimental rosin-based fluoride varnish showed significantly higher hardness on the 5th and 30th day than the control (bovine teeth without fluoride treatment)(p<0.05). EDX results showed that the fluoride content on the surface of bovine teeth treated with the experimental rosin-based fluoride varnish was highest on the 1st and 10th day. The higher hardness and fluoride content of experimental rosin-based fluoride varnish can be considered to be used as an effective fluoride varnish to prevent dental caries.

• Composites Research
• /
• v.34 no.5
• /
• pp.277-282
• /
• 2021

Graphene oxide can be reduced to graphene under supercritical fluid condition even without using a specific reducing agent or applying a high thermal process. In this study, a process for converting graphene oxide into graphene was studied under supercritical fluid conditions in methanol and ethanol solvents. When the structure of asprepared graphene was analyzed by using FE-SEM and XRD, the reduction of graphene oxide in supercritical fluid condition was more affected by the change of solvent than other variables such as concentration of graphene oxide and reaction time. The use of ethanol showed better results for the reduction than the use of methanol. The graphene prepared in this study was mixed with epoxy resin up to 20 wt.% to make composites, and the thermal conductivity of the composites were analyzed. Thermal conductivity of the composite increased proportionally with graphene loadings. The graphene prepared in supercritical ethanol condition was more effective on the thermal conductivity of the composite.

• Nuclear Engineering and Technology
• /
• v.53 no.12
• /
• pp.4158-4165
• /
• 2021

In this study, tissue equivalency (TE) of a newly developed epoxy-based phantom to 3-5 years child's tissue was investigated in paediatric energy range. Epoxy-based TE-phantoms were produced at different glandular/adipose (G/A) ratios of 17/83%, 31/69%, 36/64% and 10/90%. A procedure was developed in which specific amounts of boron, calcium, magnesium, sulphur compounds are mixed with epoxy resin, together with other minor substitutes. In paediatric energy range of 40-60 kV_p half-value layer (HVL) values were measured and then Hounsfield Units (HU) were determined from Computed Tomography(CT) scans taken in the X-ray energy range of 80-120kV_p. It is found that radiation absorption properties of these phantoms in terms of the measured HVL values related to linear attenuation coefficients (µ) are very well mimicking a 3 years child's soft tissue in case a ratio of 10/90%G/A. Additionally, the HU values of phantoms were determined from the CT scans. The HU = 47.8 ± 4.8 value was found for the epoxy-based phantom produced at a ratio of 10/90%G/A. The obtained HVL and HU values also support the suitability of the new epoxy based-phantom produced at a ratio of 10/90%G/A for a satisfactory mimicking a 3 years child's soft tissue by 5%. Thus they can have a potential use to perform the quality controls of medical X-ray systems and dose optimization studies.

• Journal of Korean Academy of Oral Health
• /
• v.41 no.4
• /
• pp.231-236
• /
• 2017

Objectives: The objectives of this study were to investigate the changes in bisphenol A (BPA) concentrations in urine from before to after sealant filling and the relationship between BPA and the number of teeth with sealed surfaces. Methods: Thirty-one children aged 6 and 7 years from three elementary schools in Daegu city who did not have any sealant and resin filling were selected as subjects. Urine samples were collected before and after sealant filling until 24 hours, with informed consent from their caregivers. The BPA concentration in all the collected urine samples was analyzed at Seegene Medical. Statistical analysis was performed using the Friedman test, Scheirer-Ray-Hope test, and the repeated-measures generalized linear mixed model of SPSS version 22.0. Results: The BPA concentrations increased from $3.49-{\mu}g/g$ creatinine before to $4.91-{\mu}g/g$ creatinine 2-3 hours later and to $4.15-{\mu}g/g$ creatinine after 24 hours. The more teeth with sealed surfaces, the higher the BPA concentration in children, but the difference was not statistically significant (P>0.05). Conclusions: The BPA concentrations were highest at 2-3 hours after sealant filling and decreased at 24 hours. Exposure to the sealant appears to have a meaningful correlation with the concentration of BPA in the urine of children.