• International Journal of Highway Engineering
• /
• v.19 no.3
• /
• pp.1-10
• /
• 2017

PURPOSES : This paper focuses on strength development according to the mix design with cement type and mineral admixture from laboratory and field tests in cool weather. METHODS : Two methods evaluated the mix design of concrete pavement in cool weather. Firstly, laboratory tests including slump, air contents, setting time, strength, maturity, and freezing-thawing test were conducted. Three alternatives were selected based on the tests. Secondly, a field test was conducted and the optimum mix design in cool weather was suggested. RESULTS : It is an evident from the laboratory test that a mix with type III cement showed better performance than the one with type I cement. There was a delay in strength development of a mix with mineral admixture compared to mix design without any mineral admixture. In the field test, type III cement+flyash 20% mix design proved the best performance. CONCLUSIONS : For concrete pavement in cool weather, mix design using type III cement could overcome the strength delay due to mineral admixture. Moreover, it is possible to make sure of durability of pavement. Therefore, strength and durability problems due to cool weather would decrease.

• Advances in concrete construction
• /
• v.7 no.2
• /
• pp.75-85
• /
• 2019

The present study is focused on the mechanical and durability properties of ternary blended cement concrete mix of different grades 30 MPa, 50 MPa and 70 MPa. Three mineral admixtures (fly ash, silica fume and lime sludge) were used as a partial replacement of cement in the preparation of blended concrete mix. The durability of ternary blended cement concrete mix was studied by exposing it to acids HCl and $H_2SO_4$ at 5% concentration. Acid mass loss factors (AMLF), acid strength loss factor (ASLF) and acid durability factor (ADF) were determined, and the results were compared with the control mix. Chloride ions penetration was investigated by conducting rapid chlorination penetration test and accelerated corrosion penetration test on control mix and ternary blended cement concrete. From the results, it was evident that the usage of these mineral admixtures is having a beneficiary role on the strength as well as durability properties. The results inferred that the utilization of these materials as a partial replacement of cement have significantly enhanced the compressive strength of blended concrete mix in 30 MPa, 50 MPa and 70 MPa by 42.95%, 32.48% and 22.79%. The blended concrete mix shown greater resistance to acid attack compared to control mix concrete. Chloride ion ingress of the blended cement concrete mix was low compared to control mix implying the beneficiary role of mineral admixtures.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2003.11a
• /
• pp.49-52
• /
• 2003

The objective of this study the mechanical characteristics of prefoamed lightweight foamed concrete using the mineral foam agent which has high lightness, and strength. The compressive strength of lightweight foamed concrete using mineral foam agent are about 2 times degree high those the of lightweight foamed concrete using vegetable foam agent. Lightweight foamed concrete was able to obtain the result of 50kg/㎠ or more compressive strength, when was unit weight 0.8t/㎡. In the case of the same unit weight of concrete, it is influenced by w/c of foam agent ratio. The paper present extensive data on characteristics of compressive strength of the concrete manufatured with the different factors in mix design and also present optimum mix proportion.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2003.05a
• /
• pp.49.1-52
• /
• 2003

The objective of this study the mechanical characteristics of preformed lightweight foamed concrete using the mineral foam agent which has high lightness, and strength. The compressive strength of lightweight foamed concrete using mineral foam agent are about 2 times degree high those the of lightweight foamed concrete using vegetable foam agent. Lightweight foamed concrete was able to obtain the result of 50kg/$\textrm{m}^3$ or more compressive strength, when was unit weight 0.8t/$\textrm{m}^3$. In the can of the same unit weight of concrete, it is influenced by w/c of loan agent ratio. The paper present extensive data on characteristics of compressive strength of the concrete manufactured with the different factors in mix design and also present optimum mix proportion.

• Structural Engineering and Mechanics
• /
• v.58 no.1
• /
• pp.143-161
• /
• 2016

Utilization of mineral and chemical admixtures in concrete technology has led to changes in the formulation and mix design in recent decades, which has, in turn, made the concrete stronger and more durable. Lightweight concrete is an excellent solution in terms of decreasing the dead load of the structure, while self-compacting concrete eases the pouring and removes the construction problems. Combining the advantages of lightweight concrete and self-compacting concrete is a new and interesting research topic. Considering its light weight of structure and ease of placement, self-compacting lightweight concrete may be the answer to the increasing construction requirements of slender and more heavily reinforced structural elements. Twenty one laboratory experimental investigations published on the mix proportion, density and mechanical properties of lightweight self-compacting concrete from the last 12 years are analyzed in this study. The collected information is used to investigate the mix proportions including the chemical and mineral admixtures, light weight and normal weight aggregates, fillers, cement and water. Analyzed results are presented in terms of statistical expressions. It is very helpful for future research to choose the proper components with different ratios and curing conditions to attain the desired concrete grade according to the planned application.

• Resources Recycling
• /
• v.29 no.6
• /
• pp.48-56
• /
• 2020

In this study, raw mix was mixed with CaCl2 for analyzing characteristics of clinker added chlorine and chlorine was added by 2,000ppm at high concentration condition. The raw mix added chlorine was burned at 1250℃~1350℃ and maintained during 10minutes at each maximum temperature. Clinker target modulus was LSF 92, SM 2.5 and IM 1.6 in this study. The burnability of clinker added chlorine was identified by free-CaO content. Free-CaO content decreased as chlorine content increased and free-CaO content of 1350℃-2000ppm clinker decreased by 1.5%. Optical microscope and XRD Analyses were used for identify mineral properties of clinker added chlorine. The mineral of clinker could not be observed at 1250℃ and the size of alite grew larger as chlorine content increased at 1350℃. It showed a good crystallizability as chlorine content increased. As chlorine content of clinker increased, clinker showed a good burnability and mineral property.

• Journal of the Korea Concrete Institute
• /
• v.17 no.4 s.88
• /
• pp.559-567
• /
• 2005

The objective of this study is to optimize the use of mineral admixtures (silica fume, fly ash, and blast furnace slag) in high-performance concrete for bridge deck overlay. For this purpose, high-performance concrete, incorporating mineral admixtures, was tested for compressive strength and permeability. The Box Behnken design was used to determine the optimum mix proportions of the mineral admixtures. The optimized mix compositions were then technically evaluated. Test results are compare with the performance specification for high performance concrete overlay on bridge deck. The optimum mix proportions were shown to possess acceptable properties. Also, it is possible to save the construction and materials costs result from a reduction In actual material cost and from the use of widely avaliable truck mixers instead of mobile mixers.

• Journal of the Korean Ceramic Society
• /
• v.48 no.6
• /
• pp.589-594
• /
• 2011

Raw mix of molten clinker was fabricated using blast furnace slag as starting material. Raw mix was melted at 1620$^{\circ}C$ for molten clinker fabrication. It was found that molten clinker contained alite and belite equivalent to OPC clinker mineral by optical microscope and SEM. The size of alite was 10~50 ${\mu}m$ and that of belite was 20~80 ${\mu}m$. This result thought to be attributed low $Al_2O_3$ content and cooling condition. Interstitial phase increased with blast furnace slag content and gehlenite was formed by the condition of LSF and SM. So raw mix with 27~41% blast furnace slag could be converted into cement clinker by appropriate choice of melting andcooling methods in this study.

• Advances in concrete construction
• /
• v.7 no.4
• /
• pp.263-275
• /
• 2019

In the present work, Granulated Blast Furnace Slag (GBFS) and Fly ash (FA) were used as partial replacement of Natural Sand (NS) and Ordinary Portland Cement (OPC) by weight. One control mix, one with GBFS, three with FA and three with GBFS-FA combined mixes were prepared. Replacements were 50% GBFS with NS and 20%, 30% and 40% FA with OPC. Preliminary investigation on development of compressive strength was carried out at 7, 28 and 90 days to ensure sustainability of waste materials in concrete matrix at room temperature. After 90days, thermo-mechanical study was performed on the specimen for a temperature regime of $200^{\circ}-1000^{\circ}C$ followed by furnace cooling. Weight loss, visual inspection along with colour change, residual compressive strength and microstructure analysis were performed to investigate the effect of replacement of GBFS and FA. Although adding waste mineral by-products enhanced the weight loss, their pozzolanicity and formation history at high temperature played a significant role in retaining higher residual compressive strength even up to $800^{\circ}C$. On detail microstructural study, it has been found that addition of FA and GBFS in concrete mix improved the density of concrete by development of extra calcium silicate gel before fire and restricts the development of micro-cracks at high temperature as well. In general, the authors are in favour of combined replacement mix in view of high volume mineral by-products utilization as fire protection.

• Computers and Concrete
• /
• v.10 no.6
• /
• pp.587-607
• /
• 2012

The purpose of this research is to propose a design technique of concrete mix proportions satisfying service life through genetic algorithm (GA) and neural network (NN). For this, thirty mix proportions and the related diffusion coefficients in high performance concrete are analyzed and fitness function for diffusion coefficient is obtained considering mix components like w/b (water to binder ratio), cement content, mineral admixture (slag, flay ash and silica fume) content, sand and coarse aggregate content. Through averaging the results of 10 times GA simulations, relative errors to the previous data decrease lower than 5.0% and the simulated mix proportions are verified with the experimental results. Assuming the durability design parameters, intended diffusion coefficient for intended service life is derived and mix proportions satisfying the service life are obtained. Among the mix proportions, the most optimized case which satisfies required concrete strength and the lowest cost is selected through GA algorithm. The proposed technique would be improved with the enhancement of comprehensive data set including wider the range of diffusion coefficients.