• 한국분말재료학회지
• /
• 제17권4호
• /
• pp.312-318
• /
• 2010

High speed steels (HSS) were used as cutting tools and wear parts, because of high strength, wear resistance, and hardness together with an appreciable toughness and fatigue resistance. Conventional manufacturing process for production of components with HSS was used by casting. The powder metallurgy techniques were currently developed due to second phase segregation of conventional process. The powder injection molding method (PIM) was received attention owing to shape without additional processes. The experimental specimens were manufactured with T42 HSS powders (59 vol%) and polymer (41 vol%). The metal powders were prealloyed water-atomised T42 HSS. The green parts were solvent debinded in normal n-Hexane at $60^{\circ}C$ for 24 hours and thermal debinded at $N_2-H_2$ mixed gas atmosphere for 14 hours. Specimens were sintered in $N_2$, $H_2$ gas atmosphere and vacuum condition between 1200 and $1320^{\circ}C$. In result, polymer degradation temperatures about optimum conditions were found at $250^{\circ}C$ and $480^{\circ}C$. After sintering at $N_2$ gas atmosphere, maximum hardness of 310Hv was observed at $1280^{\circ}C$. Fine and well dispersed carbide were observed at this condition. But relative density was under 90%. When sintering at $H_2$ gas atmosphere, relative density was observed to 94.5% at $1200^{\circ}C$. However, the low hardness was obtained due to decarbonization by hydrogen. In case of sintering at the vacuum of $10^{-5}$ torr at temperature of $1240^{\circ}C$, full density and 550Hv hardness were obtained without precipitation of MC and $M_6C$ in grain boundary.

• 전기화학회지
• /
• 제6권4호
• /
• pp.266-270
• /
• 2003

우수한 전기화학적 특성을 갖는 $LiN_{0.8}Co_{0.2}O_2$ 정극 활물질을 평균 $1{\mu}m$ 이하의 균일한 입자 분포를 얻을 수 있는 액상 반응법의 하나인 졸겔법을 이용하여 제조하였다. 제조된 $LiN_{0.8}Co_{0.2}O_2$를 X선 회절과 TEM(transmission electron microscopy)분석을 통하여 미세구조를 분석하였다. 충방전 실험전과 실험후의 미세구조의 변화에 중점을 주어 실험하였으며, 그 결과 졸겔법으로 제조된$LiN_{0.8}Co_{0.2}O_2$ 정극 활물질은 높은 가역 용량을 가지며 뛰어난 싸이클 특성을 가지고 있다 이는 졸겔법으로 제소함으로 인하여 Ni과 Co양이온의 균일한 화학조성을 가지고 있기 때문이라 생각된다. 특히 $LiCoO_2$에서 관찰되었던 cubic spinel disordering과 심각한 구조적 결함이 관찰되지 않았다. 또한 Al 치환으로 인하여 싸이클 특성을 좋아졌지만 용량은 감소하였다.

• 비파괴검사학회지
• /
• 제23권2호
• /
• pp.98-106
• /
• 2003

비파괴시험(NDT)은 구조물의 기능에 손상을 주지 않으면서 콘크리트에 대한 많은 정보를 준다. 여러 가지 NDT 방법들 중에서, 초음파 속도법과 충격반향기법과 같이 탄성파의 속도를 이용하는 방법은 콘크리트의 압축강도, 탄성계수, 포아송비의 추정뿐만 아니라, 내부 미세구조 변화 모니터링과 결함 탐지 등을 위해 이용되고 있다. 본 연구에서는 물-결합재비가 $0.27{\sim}0.50$이고 시멘트 중량의 20%를 플라이 애쉬로 대체 사용한 콘크리트를 제조한 후, 동일한 콘크리트에 대해 초음파 속도법과 충격반향기법을 이용하여 종파 속도를 각각 측정하여 서로 비교하였다. 실험 결과, 콘크리트 공시체로부터 측정된 초음파 속도가 충격반향기법에 의해 측정된 종파 속도, 즉 막대파 속도보다 큰 경향을 나타내었으며, 이들의 차이는 재령이 증가함에 따라 그리고 콘크리트의 강도가 커질수록 각각 감소하는 경향을 나타내었다. 또한, 동포아송비, 정탄성계수, 동탄성계수, 속도-강도의 상관관계 등을 실험적으로 결정하였다. 그 결과, 동적인 방법으로 결정되는 포아송비와 탄성계수가 정적인 시험에 의한 것보다 크게 나타났다. 따라서, 탄성파 속도를 이용하여 콘크리트의 성질들을 보다 정확하게 추정하기 위해서는 속도 특성에 대한 이해가 필요할 것으로 사료된다.

• 한국재료학회지
• /
• 제10권6호
• /
• pp.403-408
• /
• 2000

본 연구에서는 고온용 고강도 Al 합금을 제조하기 위해 Al-Cr-Zr 복합금속분말을 attritor에서 300rpm의 회전속도로 20시간 동안 기계적 합금화방법으로 제조한 후 진공 고온 압축성형하였다. Al-Cr-Zr 합금의 미세구조 및 조직관찰은 XRD, TEM 등을 사용하여 분석하였고, 열적 안정성은 열적 노출시간에 따른 미소경도측정을 통하여 조사하였다. 진공 열간 압축성형 되었을 때 MA Al-Cr-Zr 합금의 이론 밀도의 97%에 이르는 조밀화르 f보였으며, $300^{\circ}C$에서 100시간 열처리 한 경우에는 경도변화가 거의 없었고, $500^{\circ}C$에서 100시간 열처리한 경우에도 감소가 6% 이내로 우수한 열적 안정성을 나타내었다. 이와 같은 MA Al-Cr-Zr 합금의 우수한 열적 안정성은 기계적 합금화에 의해 Al 기지 내에 미세하고 균일하게 분산된 Cr과 Zr이 고온 성형과 열처리 과정에 의해 $Al_3Zr,\;Al_{13}Cr_2$의 금속간 화합물들의 형성되었으며, 열처리 후의 이 합금의 최종 결정립 크기는 150mm 크기 이하이었다.

• Nuclear Engineering and Technology
• /
• 제47권5호
• /
• pp.608-616
• /
• 2015

The migration of silver (Ag) in silicon carbide (SiC) and $^{110m}Ag$ through SiC of irradiated tristructural isotropic (TRISO) fuel has been studied for the past three to four decades. However, there is no satisfactory explanation for the transport mechanism of Ag in SiC. In this work, the diffusion coefficients of Ag measured and/or estimated in previous studies were reviewed, and then pre-exponential factors and activation energies from the previous experiments were evaluated using Arrhenius equation. The activation energy is $247.4kJ{\cdot}mol^{-1}$ from Ag paste experiments between two SiC layers produced using fluidized-bed chemical vapor deposition (FBCVD), $125.3kJ{\cdot}mol^{-1}$ from integral release experiments (annealing of irradiated TRISO fuel), $121.8kJ{\cdot}mol^{-1}$ from fractional Ag release during irradiation of TRISO fuel in high flux reactor (HFR), and $274.8kJ{\cdot}mol^{-1}$ from Ag ion implantation experiments, respectively. The activation energy from ion implantation experiments is greater than that from Ag paste, fractional release and integral release, and the activation energy from Ag paste experiments is approximately two times greater than that from integral release experiments and fractional Ag release during the irradiation of TRISO fuel in HFR. The pre-exponential factors are also very different depending on the experimental methods and estimation. From a comparison of the pre-exponential factors and activation energies, it can be analogized that the diffusion mechanism of Ag using ion implantation experiment is different from other experiments, such as a Ag paste experiment, integral release experiments, and heating experiments after irradiating TRISO fuel in HFR. However, the results of this work do not support the long held assumption that Ag release from FBCVD-SiC, used for the coating layer in TRISO fuel, is dominated by grain boundary diffusion. In order to understand in detail the transport mechanism of Ag through the coating layer, FBCVD-SiC in TRISO fuel, a microstructural change caused by neutron irradiation during operation has to be fully considered.

• 보존과학회지
• /
• 제34권6호
• /
• pp.493-502
• /
• 2018

현재 유기공방에서는 전통기술로 하나의 방짜유기 숟가락을 만들기 위해 10단계의 작업 공정을 거쳤으며, 형태 제작에 큰 영향을 주는 열간 단조는 3~4단계의 과정을 거친다. 열간 단조를 통해 방짜유기 숟가락의 미세조직은 수지형상의 ${\alpha}$상이 미세화되고 잘게 분산되었으며, 두드림이 가해진 부분의 ${\alpha}$상에는 쌍정이 생성되었다. 또한 ${\alpha}$상은 가해지는 망치질에 따라 점점 다각형에서 원형으로 변형되었다. 이 과정에서 서로 근접한 ${\alpha}$상은 합쳐지는 현상이 발생하였고, 담금질 후에도 합쳐진 상태로 존재하였다. 이처럼 여러 개의 ${\alpha}$상이 합쳐진 미세조직은 방짜조성의 청동유물에서도 관찰되는 것으로 기술체계의 연관성을 보여준다. 방짜조성의 Cu-22%Sn 합금을 대상으로 실시한 열간 단조 실험결과, 주조 당시 형성된 수지상의 감소율은 가공횟수에 따라 비례했으며, 두드림 작업에 의한 결정립의 미세화는 재질의 강도를 높이는 효과를 준 것으로 판단된다. 고대 유적에서 출토된 청동유물과 전통 유기공방에서 만든 방짜유기에서 동일하게 관찰되는 메자국은 문헌으로 남아 있지 않은 고대의 방짜유기 기술체계가 오늘날의 방짜유기 전통기술로 전승되었음을 보여준다.

• 한국건설순환자원학회논문집
• /
• 제11권1호
• /
• pp.89-96
• /
• 2023

산업부산물인 페로실리콘을 사용한 시멘트 콘크리트의 내구성능을 평가하기 위하여 페로실리콘의 치환율을 3단계로 변화시켜 제조한 시멘트 경화체의 염화물침투저항성, 알칼리실리카 반응성에 대하여 평가하였다. 페로실리콘을 사용한 시멘트 콘크리트의 내구성능은 화학조성이 유사한 실리카흄과 비교하여 평가하였으며, 에너지 분산형 X선 분광법, 공극측정 및 X선 회절분석 등 기기분석을 통하여 페로실리콘 콘크리트의 미세 구조적 특성을 고찰하였다. 그 결과, 페로실리콘을 10 % 치환한 경우 OPC콘크리트보다 높은 강도발현 특성을 보인 반면 치환율이 20 %, 30 % 증가할수록 압축강도는 낮게 발현되었다. 그러나 염화물 침투저항성에 대한 결과는 치환율이 증가할수록 우수한 결과를 나타내었으며, 실리카흄을 사용한 경우에 비하여 페로실리콘을 사용한 콘크리트의 내구성은 약간 떨어지지만 OPC에 비해서는 우수한 결과를 나타내었다. 이는 페로실리콘의 실리카(SiO₂) 함량이 높아 더 많은 C-S-H 겔을 생성하여 더 밀실한 공극 구조를 만들었기 때문이라 생각된다. 길이변화시험을 통한 규산염 바인더에 대한 알칼리실리카반응의 위험성은 대부분 0.2 % 미만으로 나타났으며, 페로실리콘 및 실리카흄을 사용한 모르타르 모두 치환율이 증가할수록 알칼리실리카 반응에 대한 저항성은 우수한 것으로 나타났다. 따라서 고가의 실리카흄을 사용하는 대신 산업 폐기물을 재사용하면 제조 중 환경 부하를 줄이고 비용을 절약할 수 있을 것으로 판단된다.

• 한국주조공학회지
• /
• 제43권6호
• /
• pp.279-285
• /
• 2023

본 연구에서는 임계간 온도 범위에서 열처리한 구상흑연주철의 열처리 온도에 따른 물성 예측을 위해, 인장강도 450 MPa 급 구상흑연주철을 다양한 온도에서 열처리한 후 공냉하여 물성 예측에 필요한 미세조직을 분석하고 브리넬 경도를 측정하였다. 임계간 온도 구간에서 열처리 온도가 증가할수록 구상흑연주철 내 페라이트 분율은 감소함과 동시에 펄라이트 분율은 증가하였으나, 흑연 구상화율 및 구상흑연입수는 주방상태에서 측정된 값과 유사하였다. 열처리한 구상흑연주철의 브리넬 경도는 열처리 온도가 증가할수록 점점 증가하였다. 측정된 합금 조성 및 각 안정상의 분율, 그리고 문헌에 알려진 구상흑연주철의 브리넬 경도 예측 모델을 활용하여 열처리 온도 별 구상흑연주철의 경도 값을 계산해 본 결과, 측정값과 매우 유사한 값을 얻을 수 있었다. 또한 열역학 계산을 통해 예측된 상분율을 활용하여 정확한 경도 예측이 가능할지 확인해보기 위해, 열처리 온도 별로 구상흑연주철 내 흑연, 페라이트 및 오스테나이트의 부피를 계산한 후, 이를 면적으로 변환하여 동일한 구상흑연주철의 경도 예측 모델에 적용하였다. 이렇게 열역학 계산과 경도 예측 모델을 동시에 활용하여 계산된 구상흑연주철의 경도 값은 실제 측정한 브리넬 경도 대비 최대 27의 오차 범위 내에서 유사한 값을 나타내었다.