• Polymer(Korea)
• /
• v.39 no.3
• /
• pp.365-369
• /
• 2015

In this study, the bulk and solution polymerizations of L-lactide using an aluminium compound, methylaluminoxane (MAO), were performed. In the bulk polymerization, the conversion of polymerization was increased with increasing the amount of catalyst in feed. The largest molecular weight (Mw), 60800 g/mol, was shown at the MAO amount in feed of 0.15 mmol, and Mw was decreased above 0.15 mmol of MAO in feed. At the 0.15 mmol of MAO in feed, turn of frequency (TOF) was the highest, and it was decreased with increasing MAO amount in feed. In the solution polymerization, the induction time of 30 min was shown. The conversion of polymerization was linearly increased with the polymerization time, and the highest Mw, 54700 g/mol, was achieved at the polymerization time of 6 h.

• Journal of the Korean Chemical Society
• /
• v.54 no.1
• /
• pp.23-26
• /
• 2010

A Schiff base ligand (Z)-N-((Z)-2-(sec-butylimino)-1,2-diphenylethylidene)butan-2-amine was synthesized by condensation of benzil with sec-butyl amine. Complexation of the ligand was carried out with first row transition elements, manganese(II) and nickel(II). Ligand and complexes were characterized by FTIR, elemental analysis and thermogravimetric analysis in solid state and by NMR ($^1H,\;^{13}C$) in solution form. Both the complexes demonstrate good catalytic activity for butadiene oligomerization under mild conditions with methylaluminoxane (MAO) as co-catalyst.

• Analytical Science and Technology
• /
• v.9 no.2
• /
• pp.203-209
• /
• 1996

Kaminsky catalyst system($Et(Ind)_2ZrCl_2$ and MAO(methylaluminoxane)) was prepared. Propylene was polymerized at $60^{\circ}C$ in this system. The microstructure was studied by using the $^{13}C$ NMR spectrometer. From the $^{13}C$ NMR data, the 2, 1-insertion of propylene was controlled stereospecific by Kaminsky catalyst due to the structures of meso and racemo I. After the 2, 1-insertion of propylene, 1, 2-insertion of the chain end was less stereospecifically controlled by the catalyst.

• Macromolecular Research
• /
• v.12 no.4
• /
• pp.336-341
• /
• 2004

A new type of cross-linked methylaluminoxane (MAO)-supported cocatalyst has been prepared by the reaction of a soluble MAO and a cross-liking agent such as an aromatic diamine compound. The cross-linked MAO-supported cocatalyst was used for the polymerization of ethylene in the presence of bis(n-butylcyclopentadienyl) zirconium dichloride, (n-BuCp)$_2$ZrCl$_2$. The catalyst activity of (n-BuCp)$_2$ZrCl$_2$ cocatalyzed with the new supported cocatalyst was higher than that of the commercial silica-supported MAO (SMAO) cocatalyst. The molecular weight and the bulk density of the polyethylene produced by using the new supported cocatalyst were slightly higher than those of polyethylene synthesized using commercial SMAO. The resulting polyethylene particles possess spherical morphologies with very few fine particles.

• Macromolecular Research
• /
• v.14 no.3
• /
• pp.338-342
• /
• 2006

The kinetic features of polymerization with an active site comprising cobalt dihalides ($CoX_2$, where X=Cl, Br, I) activated by methylaluminoxane (MAO) were investigated in 1,3-butadiene polymerization. The catalytic system exhibited the characteristic features of living polymerization. The initiation ($k_i$) and propagation ($k_p$) rate coefficients were estimated using the kinetic model for slow initiation previously reported by Shiono et al. The energy of activation fur the propagation reaction was calculated to be 27-30 $kJmol^{-1}$. The marked changes in reaction rate observed with different halides could be adequately described in terms of variations in the initiation process, with the same Arrhenius curve fitting propagation rate coeffcients estimated from all three halides, suggesting that the halide does not participate in the growing chain end.

• Applied Chemistry for Engineering
• /
• v.25 no.4
• /
• pp.396-400
• /
• 2014

The pore surface of mesoporous materials, SBA-15 and MCM-41 were functionalized with organosilanes, 3-aminopropyltrimethoxysilane (1NS) and N-[(3-trimethoxysilyl)propyl]ethylenediamine (2NS) via grafting method. $(n-BuCp)_2ZrCl_2$ and methylaluminoxane (MAO) were impregnated on the surface-functionalized mesoporous materials for the application to ethylene polymerization. In the case of SBA-15/2NS/$(n-BuCp)_2ZrCl_2$ supported Zr and Al contents decreased as grafted 2NS content increased. However, in the case of MCM-41/2NS/$(n-BuCp)_2ZrCl_2$ supported Al content decreased, but Zr content increased as grafted 2NS content increased. The polymerization activity of SBA-15/2NS/$(n-BuCp)_2ZrCl_2$ increased as the amount of grafted 2NS increased. Increase in the amount of grafted 2NS should caused decrease in pore volume and diameter. Consequently, it decreased the amount of supported metallocene and MAO in general. However, the smaller pore-sized MCM-41 could have lower supported MAO content due to its large molecular size in case that MCM-41 was surface-functionalized with 2NS. Therefore, the supported metallocene content could increase and its polymerization activity was higher than that of SBA-15.

• Polymer(Korea)
• /
• v.36 no.1
• /
• pp.111-116
• /
• 2012

A functionalization of mesoporous materials with organosilane was carried out via a post-synthesis grafting method and $(n-BuCp)_2ZrCl_2$/methylaluminoxane (MAO) as subsequently immobilized on the functionalized mesoporous materials for ethylene polymerization. Organosilanes having amine, cyano or imidazoline group such as $N$-[(3-trimethoxysilyl)propyl]ethylenediamine (2NS), 4-(triethoxysilyl)butyronitrile (1NCy), 1-(3-triethoxysilylpropyl)-2-imidazoline (2NIm) were used for the surface functionalization of mesoporous materials. In the SBA-15/2NS/$(n-BuCp)_2ZrCl_2$ catalyst preparation, the amount of MAO in feed increased with an decrease in the Zr content of the supported catalyst, and Al content in the supported catalyst increased. The ethylene homopolymerization activity of SBA-15/2NS/$(n-BuCp)_2ZrCl_2$ dramatically increased as the amount of MAO in feed increased. Furthermore, when the immobilization time was 6 hrs, SBA-15/2NS/$(n-BuCp)_2ZrCl_2$ showed the highest activity. The activities of supported 2NS-, 1NCy-, 2NIm-functionalized catalysts decreased in the following order, SBA-15/2NS/ > SBA-15/2NIm/ > SBA-15/1NCy/$(n-BuCp)_2ZrCl_2$. 2NS and 2NIm which have two amine groups per silane molecule were shown to interact with $(n-BuCp)_2ZrCl_2$ strongly compared to 1NCy which has one amine group. Thus, the activities increased with an increase in the nitrogen and the Zr content of the supported catalysts.

• Macromolecular Research
• /
• v.9 no.2
• /
• pp.71-83
• /
• 2001

The metallocene compounds had been applied to the polymerizations of olefins and vinyl monomers with methylaluminoxane (MAO) cocatalyst, and they have usually one transition metal atom per molecule, i.e., mononuclear metallocene. Recently it has been found that the dinuclear metallocene compounds containing two transition metal atoms exhibit the peculiar polymerization behaviors for olefins and vinyl monomers. In this article, the dinuclear metallocenes are classified into four groups of dinuclear bent-metallocene, dinuclear ansa-metallocene, dinuclear constrained geometry catalyst and dinuclear half-metallocene, and then the synthesis of dinuclear metallocene of each group as well as the polymerization behaviors for ethylene, propylene, and styrene are described.

• Applied Chemistry for Engineering
• /
• v.27 no.1
• /
• pp.86-91
• /
• 2016

Three amorphous silicas and SBA-15 were employed as supports, which were capable of confining ionic liquid (IL) and metallocene in the nanopore. Ionic liquid functionalized silica was prepared by the interaction between the chloride anions of 1,3-bis(cyanomethyl)imidazolium chloride and the surface OH groups. Metallocene and methylaluminoxane (MAO) were subsequently immobilized on the ionic liquid functionalized silica for ethylene polymerization. The metallocene supported on ionic liquid functionalized XPO-2412 and XPO-2410 having a larger pore diameter compared to SBA-15 showed higher activity than that of using supported catalyst without ionic liquid functionalization. However, the activity of metallocene supported on SBA-15 decreased after ionic liquid functionalization, suggesting that the diffusion of ethylene monomer and cocatalyst to the active site of nanopore was restricted during ethylene polymerization. This could be resulted from significant reduction of the pore diameter due to the immobilization of ionic liquid and $(n-BuCp)_2ZrCl_2$ and MAO. The effect on polymerization activity in accordance with the concentration of hydroxyl groups on the surface was also investigated. The polymerization activity increased as the concentration of hydroxyl groups on amorphous silica increased. The polymerization activities of metallocene supported on silica showed the similar trend after ionic liquid functionalization.

• Macromolecular Research
• /
• v.15 no.3
• /
• pp.221-224
• /
• 2007

A silica-magnesium bisupport (SMB) was prepared by a sol-gel method for use as a support for a metal-locene/Ziegler-Natta hybrid catalyst. The prepared $rac-Et(Ind)_2ZrCl_2/TiCl_4$/MAO(methylaluminoxane)/SMB catalyst was applied to the copolymerization of ethylene with l-hexene using a variable triethylaluminum (TEA)/transition-metal (Ti) ratio and fixed MAO/transition-metal (Zr) ratio. The effect of the Al(TEA)/Ti ratio on the physical properties and chemical composition distributions (CCDs) of the ethylene-hexene copolymers produced by the hybrid catalyst was investigated. In the ethylene-hexene copolymers, two melting temperatures attributed to the metal-locene and Ziegler-Natta catalysts were clearly observed. The number of CCD peaks was increased from six to seven and the temperature region in which the peaks for the short chain branches of the ethylene-hexene copolymer were distributed became lower as the Al(TEA)/Ti ratio was increased from 300 to 400. Furthermore, the temperature regions corresponding to the lamellas in the copolymer became lower and those corresponding to the small lamellas in the copolymer became higher as the Al(TEA)/Ti ratio was increased from 300 to 400. In the copolymer produced with Al(TEA)/Ti = 500, however, only four CCD peaks were observed and the short chain branches were poorly distributed.