• 한국결정성장학회지
• /
• 제22권6호
• /
• pp.279-285
• /
• 2012

BCP, Mg-BCP, Si-BCP 분말을 공침법(co-precipitation process)을 이용하여 합성하였다. 제조된 분말을 X-선 회절 분석(XRD), 적외선분광분석(FTIR)을 이용하여 특성을 분석하였다. Ca/P 몰 비율이 1.602인 칼슘 결손 아파타이트 공침물을 제조하여 $1000^{\circ}C$ 열처리 과정을 통하여 HAp와 ${\beta}$-TCP 상이 혼재된 BCP, Mg-BCP, Si-BCP을 합성할 수 있었다. 제조된 분말의 생체활성 거동을 평가하기 위하여 Hanks' Balanced Salt Solution(HBSS)에 침적시켜 시간에 따라 형상의 변화 및 결정상을 분석한 결과, BCP 분말에 비하여 금속 이온이 치환된 BCP 분말에서 빠른 생체활성을 관찰할 수 있었다. MTT assay를 통한 세포 성장률 평가에서모든 분말에서 시간 경과에 따라 독성을 나타내지 않았으며, 세포의 활성이 증가하였다.

• 한국재료학회지
• /
• 제13권8호
• /
• pp.537-542
• /
• 2003

($Y_{l-x}$ $Gd_{x}$ )$O_2$$_3$: $Eu^{ 3＋}$ red phosphors were prepared with the solvothermal synthesis using the 2-methoxy-ethanol solvents and the emission intensity was investigated that applied with the 254 nm wavelength and the maximum excitation wavelength for energy source. The used solvents for the solvothermal synthesis were made of nitrate salt solutions of Y, Gd and Eu. These solutions dropped in autoclave have be reacted with the solvothermal synthesis at $200^{\circ}C$ for 5hrs and the red phosphors prepared here in were showed the pure cubic phase after annealing at $1000∼1200^{\circ}C$. The brightness of ($Y_{l-x}$ $Gd_{x}$)$_2$$O_3$: $Eu^{3＋}$ phosphors particles was increased as an increase of Gd ratio. The maximum excitation wavelengths of ($Y_{l-x}$ $Gd_{x}$ )$_2$$O_3$: $Eu^{3＋}$ / phosphors particles were increased according to increasing Gd ratio from 253 nm to 259 nm wavelength. The maximum emission intensity of $Gd_2$$O_3$: $Eu^{3＋}$ (Y/Gd = 1/0) phosphors particles under UV 259 nm was found to be higher than the commercial product of $Y_2$$O_3$: $Eu^{3＋}$ phosphors.

• 한국산학기술학회논문지
• /
• 제14권9호
• /
• pp.4117-4123
• /
• 2013

본 연구에서는 해수용 열교환기의 코팅에 따른 해수 부식특성을 조사하기 위해 실험이 수행되었다. 코팅은 테플론, 전착, 세라믹+실리콘 3종을 선정하였고, 코팅되지 않은 알루미늄 부식과 비교하였다. 해수부식을 가속시키기 위하여 $70^{\circ}C$ 고온의 농도 3.5% 인공해수를 제작하여 9주 동안 침지부식을 시켰다. 침지기간에 따른 코팅의 부식특성 변화를 관찰하기 위하여 임피던스 분광법과 SEM을 이용하였다. Bode 선도에서 얻어진 분극저항으로부터 코팅재질의 내부식성을 확인하였다. 이중코팅은 4주 이후에도 코팅의 내부식성을 유지하였다. 또한 침지기간에 따라서 금속모재와 점착된 코팅면 사이에 블리스터가 발생할 수 있음을 확인하였다.

• 자원리싸이클링
• /
• 제25권5호
• /
• pp.64-74
• /
• 2016

타이타늄은 지각 구성원소 중 아홉 번째로 풍부한 원소이며, 철과 밀접한 관계를 가지고 있다. 타이타늄 광석으로부터 안료급의 $TiO_2$나 금속 타이타늄 제조를 위한 순수한 $TiCl_4$를 제조하기 위해서는 일메나이트 중에 함유되어 있는 철 성분을 제거하여야 한다. 본 연구에서는 합성 루타일과 $TiO_2$를 제조하는 여러 가지 프로세스를 비교하여 고찰하였다. 대부분의 프로세스는 건식야금과 습식야금을 조합한 것이며, 이러한 프로세스에서는 상당한 량의 철염, 철 산화물 및 폐산이 발생하고 있다. 따라서 일메나이트를 처리하기 위한 새로운 프로세스를 개발하기 위해서는 폐산의 재이용과 철 부산물의 유가 자원화가 중요하다.

• 폴리머
• /
• 제24권3호
• /
• pp.382-388
• /
• 2000

이온전도도가 높으며 균일하고 또 기계적 강도와 전기화학적 안정성이 우수한 전해질막을 얻기 위하여 poly(vinylidenefluoride-hexafluoropropylene) (PVdF-HFP) 공중합체를 전해질의 지지체로 선택하고, LiClO$_4$ 염이 포함된 ethylene carbonate (EC)와 ${\gamma}$-butyrolactone (GBL)의 흔합용매를 사용하여 겔-전해질을 제조하였다. 다양한 조성의 겔-전해질에 대하여 이온전도도, 열분석 및 선형주사전위 실험을 수행하였다. 이온전도도는 30PVdF-HFP+7.8LiClO$_4$+62.2EC/GBL 전해질막에서 3.8$\times$$10^{-3}$ S$cm^{-1}$ /로 가장 높았다. 열분석 결과에서 대부분의 시료는 대략 10$0^{\circ}C$ 정도까지는 안정하였으며, 특히 염은 고분자 사슬과 민감하게 반응하여 PVdF 결정질의 고온용융점을 낮추는 건을 확인하였다. 리튬 금속과 전해질 사이의 부식에 의해 생성된 부동태막에 의해 계면저항이 시간에 따라 계속적으로 증가하는 것을 확인하였으며, anodic stability는 대략 4.5 V vs. Li까지 안정한 것으로 측정되었다.

• Elastomers and Composites
• /
• 제40권1호
• /
• pp.59-65
• /
• 2005

메타크릴산의 아연염인 ZMA를 EPDM고무와 직접 블렌딩하거나 또는 ZnO와 MAA의 형태로 첨가한 후 이들간의 중화반응을 유도하여 고무에 in-situ로 형성시키는 방법을 이용하여 EPDM/ZMA 복합체를 제조하였다. 인장시험, 인열시험, 열노화시험 결과 ZMA의 첨가는 EPDM의 기계적 물성 및 열노화에 대한 안정성을 현저히 향상시킬 수 있음을 알 수 있었다. 또한 ZMA의 첨가는 EPDM고무와 금속과의 접착력을 크게 향상시킬 수 있음을 알 수 있었다. 이러한 기계적물성 및 접착물성의 향상효과는 과량의 ZnO를 사용한 중화반응에 의해 ZMA를 형성시킨 복합체에서 더욱 크게 나타났다. 이는 ZMA의 도입에 의한 이온가교결합의 형성 및 고무매트리스에서의 ZMA 도메인의 분산도와 연관되는 것으로 판단되었다.

• 약학회지
• /
• 제41권4호
• /
• pp.421-432
• /
• 1997

A new lectin was partially purified from starfish,Asterina pectinifera by means of physiological saline extraction, salt fractionation, ion exchange chromatography and hy droxyapatite chromatography, and it was named APL. The biochemical properties of the APL were characterized. In addition, its effects on lymphocyte mitogenicity and cancer cell agglutinability were tested. The APL agglutinated nonspecifically human erythrocytes and rabbit blood cells. Agglutinability was decreased to 30% of control activity below pH 5 and above pH 9 and was relatively unstable at increasing temperatures above 60$^{\circ}C$. The activity was reduced by addition of two kinds of metal ions, $Ba^{2+},\;Mn^{2+}$ and chelating agent, EDTA. APL was proved to be glycoproteins containing 9% sugars. For carbohydrate specificity, it was found that the activity of APL was inhibited by D(+)-glucosamine, D(+)-galactosamine, stachyose, N-acetyl-galactosamine and methyl-${\alpha}$-D-galactopyranoside among 35 sugars tested. In amino acid composition, the contents of acidic amino acids such as aspartic acid and glutamic acid were relatively high. This result suggest that the isoelectric point would be in a lower range. APL was found that it promotes the division of human lymphocytes. APL was proved to be a potent agglutinin for cancer cells such as HeLa, L929 and L1210 cells. Significant changes on the HeLa cell surfaces affected by APL were observed under the electron microscope.

• 방사성폐기물학회지
• /
• 제17권2호
• /
• pp.139-165
• /
• 2019

한국원자력연구원에서 개발 중인 해체기술 현황 및 전망에 대해 기술하였다. 특히, 해체의 핵심기술인 제염, 원격절단, 해체 폐기물처리 및 부지 복원 분야를 중점적으로 다루었다. 제염기술로는 부품제염과 원자력시스템제염 부분을 고찰하였고, 원격절단기술 관련해서는 절단기술, 원격제어 및 해체공정 모사기술이 다루어졌다. 해체 폐기물처리기술 관련해서는, 비록 해체 후 다양한 폐기물이 발생하지만, 주 폐기물인 금속, 가연성폐기물과 난처리성 특수 폐기물인 고염 고방사성 폐액, 유기혼성폐기물 및 우라늄 복합폐기물 처리기술 등을 주로 기술하였다. 마지막으로, 해체부지 복원 분야에서는 방사선 측정, 부지재이용의 안전성평가 그리고 부지 복원기술 등을 중점적으로 기술하였다.

• 공업화학
• /
• 제22권5호
• /
• pp.526-531
• /
• 2011

본 연구는 이산화탄소 흡수성능을 향상시키기 위하여 아미노산에 알칼리금속을 함침시키는 것이다. 사용된 아미노산은 글리신이었으며, 알칼리성분 추가에 따라 pH가 11까지 증가하였다. 시험제조한 아미노산 염은 회분식과 연속식 흡수공정에서 이산화탄소의 포집능을 평가하였다. 치환된 금속종류에 따른 이산화탄소 흡수량은 Sodium Glycinate (Na-Gly) ${\geq}$ Lithium Glycinate (Li-Gly) > Potassium Glycinate (K-Gly) 순으로 나타났다. 흡수반응온도에 따른 $CO_2$ 흡수량 시험결과, $20^{\circ}C$에서는 알칼리금속을 함침시킨 아미노산 염이 1차 아민보다 약간 낮은 흡수능을 보였으나, 연속식 흡수반응기에서는 10% $CO_2$ 흐름에 대하여 반응기 내부온도가 상승하면서($40^{\circ}C$, $60^{\circ}C$) 아미노산 염의 흡수량 증가폭이 아민에 비하여 상대적으로 크게 나타났다.

• Nuclear Engineering and Technology
• /
• 제54권4호
• /
• pp.1206-1212
• /
• 2022

Cold-crucible induction melting (CCIM) technology has been intensively studied as an advanced vitrification process for the immobilization of highly radioactive waste. This technology uses high-frequency induction to melt a glass matrix and waste, while the outer surface of the crucible is water-cooled, resulting in the formation of a frozen glass layer (skull). In this study, for the fabrication of borosilicate glass waste form, CCIM operation test with 60 kg of glass per batch was conducted using surrogate wastes composed of Cs, Sr, and Nd as a representative of highly radioactive nuclides generated during spent nuclear fuel management. A 60 kg-scale glass waste form was successfully fabricated through melting and draining processes using a CCIM system, and its physicochemical properties were analyzed. In particular, to enhance the controllability and reliability of the draining process, an air-cooling drain control method that can control draining through air-cooling near drain holes was developed, and its validity for draining control was verified. The method can offer controllability on various draining processes, such as molten salt or molten metal draining processes, and can be applied to a process requiring high throughput draining.