• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2009년도 추계 학술논문 발표대회
• /
• pp.117-120
• /
• 2009

It has been gradually increased with the use of resin based membrane forming agent for curing method, which plays a role in protecting moisture evaporation by forming resin membrane at the surface of concrete. In this paper, tests were carried out to examine moisture retention capability of cement mortar applying membrane forming agent. Dosages and types of the membrane forming agent were varied. It is found that sheet curing sealed with the surface of concrete closely has favorable moisture retention capability. However, the application of membrane forming curing method had superiority in moisture retention capability at early stage but at later age, its capability is deteriorated. Hence, further study regarding altering application method was necessary to secure enhanced moisture retention capability.

• 멤브레인
• /
• 제14권3호
• /
• pp.207-217
• /
• 2004

본 연구에서는 복합막의 제조공법으로 가장 광범위하게 쓰이는 계면중합법을 이용하여 나노복합막을 제조하였다. Monomer의 농도 및 조성, curing 조건, 후처리 조건과 같은 복합막 제조조건과, 운전압력, 공급액의 농도와 같은 운전인자에 의한 막성능 변화를 조사하였고, 계면중합 과정중에 첨가제를 사용하여 막의 유효면적을 확대하여 투과유속을 증가시키고자 하였다. Monomer의 농도가 증가함에 따라 배제능은 일정하였지만 투과유속이 감소하였고, curing 온도가 증가함에 따라서는 오히려 안정적인 박막층의 형성이 저해되어서 배제능과 투과유속이 모두 감소하였고, curing 시간에 따른 막성능의 변화는 나타나지 않았다. Test solution의 농도가 올라감에 따라서 투과유속과 배제능 모두 감소하였으며, 운전압력이 증가함에 따라서는 배제능과 투과유속 모두 향상하는 경향을 보였다. 계면중합과정중에 사용하는 아민단량체(amine monomer) 중 방향족 다이아민(aromatic amine)인 MPD의 함량을 높임에 따라서 배제능은 증가하였지만 투과유속은 현저하게 떨어졌다. 첨가제의 농도에 따른 표면 거칠기 증가 경향은 MPD가 포함된 amine 조성일 때가 더 높았지만 투과유속은 piperazine만 단독으로 사용하였을 때보다 떨어졌다.

• 접착 및 계면
• /
• 제17권2호
• /
• pp.62-66
• /
• 2016

수용성 접착제의 경화 공정은 일반적으로 열풍건조기를 대부분 사용하고 있다. 열풍건조기는 열에 의해서만 수용성 접착제를 경화시키는 방법으로서, 충분한 경화를 위해 $100^{\circ}C$ 이상의 높은 온도와 최소 20 min 이상의 경화 공정을 요구하는 단점을 가지고 있다. 경화 과정 중에 온도가 너무 높을 경우, 접착제의 점도가 낮아져 접착에 방해가 될 수 있으며, 경화 과정 중에 발생하는 수분에 의해 경화 조건이 일정하게 유지되기 어렵다. 본 연구에서는 제습 막 건조기 시스템을 활용하여, 수용성 접착제의 경화 공정을 일정하게 유지시키고 공정 중의 제습을 통해 건조공기의 공급으로 경화시간을 단축하고자 한다. 제습 막 건조기 시스템을 활용한 최적의 경화 조건을 찾고, 제습 막 건조기 시스템의 효과를 확인하기 위하여, 제습 막 건조기와 강제순환 건조기를 적용한 경화 과정을 통해 접착력(peel strength)을 측정하여 비교 분석해 보았다.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2003년도 가을 학술발표회 논문집
• /
• pp.553-556
• /
• 2003

This study is analyzed about the factor of adhesive strength characteristics, curing time, asphalt application, test temperature which are liquid waterproofing membrane of rubber-asphalt and chloroprene-rubber type for concrete bridge deck. According to the results, curing time is shorter, adhesive strength is less in chloroprene-rubber type. And also chloroprene-rubber and rubber-asphalt type are showed high adhesive strength in low temperature.

• 한국도로학회논문집
• /
• 제7권2호
• /
• pp.45-55
• /
• 2005

시멘트 콘크리트 포장은 시공초기의 품질관리가 포장의 장기공용성에 큰 영향을 주는 것으로 알려져 있다. 따라서 시공초기에 발생되는 문제점을 최소화하기 위한 다양한 연구가 국내외에서 활발하게 진행되고 있다. 일반적으로 시멘트 콘크리트의 품질관리에서 양생은 중요한 사항이며, 포장용 시멘트 콘크리트에서도 양생시에 양생제를 사용하여 슬래브 표면에 불투수 막을 형성하여 수분증발을 방지하는 피막양생 (membrane curing)을 많이 사용하고 있다. 양생제의 역할은 콘크리트 표면의 수분증발억제에 있다. 국내에서 사용되고 있는 양생제는 시공품질관리 측면에서 살포량이 적정한지에 대한의문이 계속 제기되어 왔다. 본 연구에서는 시멘트 콘크리트 포장 시공시 살포되는 양생제의 양을 조정하여 다양한 살포량에 따른 증발량 관측을 통해 양생제 살포량과 수분증발량 변화와의 상관관계를 제시하였다. 이를 위해 2002년과 2003년 여름철에 고속도로 시공현장에서 4회에 걸쳐 다양한 양생제 살포량$(0에 따른 증발량 콘크리트 포장의 온도변화, 콘크리트 표면의 강도발현속도(초음파 전달속도) 등을 측정하였다. 본 연구에서 얻은 결론은 현재 국내 시공현장에서의 양생제 살포량은 약 $160ml/m^2$으로 나타났고, 수분증발은 억제하고 적정한 보습효과를 얻기 위한 최적 양생제 살포량은 약 $400ml/m^2$인 것으로 분석되었다. 강도발현속도 시험결과 양생제의 살포량의 변화가 장기강도에 큰 영향을 미치지 않는 것으로 판단되었다.

• 한국막학회:학술대회논문집
• /
• 한국막학회 1999년도 The 7th Summer Workshop of the Membrane Society of Korea
• /
• pp.83-86
• /
• 1999

The imidization effect of a poly (amic acid) dope solution on membrane formation has been investigated. Poly (amic acid) solution in S-methyl-2-pyrrolidione hs been thermally imidized at $120^{\circ}C$ with different curing time and its degree of imidization was determined by infrared spectroscopy. The solution properties have been studied as a function of concentration and curing time by dynamic light scattering. The quality of a solvent was changed from good to poor with increasing imidization of poly(amic acid).The reduced polymer-solvent interaction diminishes the membrane formation time. The morphology of a membrane was able to be controlled by the characteristics of dope solution.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2013년도 춘계 학술논문 발표대회
• /
• pp.329-331
• /
• 2013

The salt damage resistance of waterproofing membrane was evaluated on the cracked mortar substrate. The types of specimens are urethane, acrylic waterproofing membrane, and no coating mortar substrate. After these specimens were cured by water curing for 4 weeks, they were cured by atmospheric curing at 20±2Co for 8 weeks. The salt water immersion test was carried out by following KS F 2737, and the penetration depth of chloride ion into substrate was measured in 1, 4, 8, and 13 weeks. As a result, in the case of non coating specimen, the chloride ion penetrated within one week. In the coated specimens, a regardless of the membrane type, the chloride ion did not penetrate during 13 weeks-tests on condition that the cracked width of substrate is less than 0.3mm. Also, the penetration speeds of the coated specimens were lower than that of non coating specimen. Therefore, our results reached a conclusion that waterproofing membrane has high salt damage resistance.

• 멤브레인
• /
• 제4권1호
• /
• pp.46-56
• /
• 1994

새로운 복합막의 제조를 위하여 기존의 복합막에서 지지막으로 주로 사용되던 Polysulfone을 이보다 친수성이 뛰어난 Polyethersulfone막으로 대체하여 지지막을 직접 제조하고 이에 따른 복합막의 성능을 살펴 보았으며 이때 각 단계별로 제조막의 성능을 평가하여 각 단계별 최적 조건을 찾고자 하였다. 지지막은 Polythersulfone과 Polyvinylpyrrolidone의 조성에 따라 각각 실험하였으며, 활성층은 계면중합법에 의하여 m-Phenylene diamine과 Trimesoyl chloride를 반응시켜 제조하였다.

• Membrane and Water Treatment
• /
• 제8권4호
• /
• pp.323-336
• /
• 2017

The main challenge in many applications of acetic acid is acid dehydration and its recovery from wastewater streams. Therefore, the performance of polyamide thin film composite is evaluated to separate acetic acid from water. To reach this goal, the formation of polyamide layer on polysulfone support membrane was investigated via interfacial polymerization (IP) of meta-phenylenediamine (MPD) in water with trimesoyl chloride (TMC) in hexane. Also, the effect of synthesis conditions, such as concentration of monomers and curing temperature on separation of acetic acid from water were investigated by reverse osmosis process. Moreover, the separation mechanism was discussed. The solute permeation was carried out under applied pressure of 5 bar at $25^{\circ}C$. Surface properties of TFC membrane were characterized by ATR-FTIR, SEM and AFM. The performance test indicated that 3.5 wt% of MPD, 0.35 wt% of TMC and curing temperature of $75^{\circ}C$ are the optimum conditions. Moreover, the permeate flux was $4.3{\frac{L}{m^2\;h}}$ and acetic acid rejection was about 43% at these conditions.

• 멤브레인
• /
• 제33권6호
• /
• pp.369-376
• /
• 2023

본 연구에서는 에너지 소모가 큰 기존 진공 증류 공정의 대안으로 친환경이면서 에너지 효율적인 투과증발 분리공정을 이용하여 1,2 hexane diol/water (1,2 HDO/water) 혼합물에서 물을 분리하는 데 적용되었다. 사용한 분리막은 glutaraldehyde (GA)로 가교된 PVA를 알루미나 중공사 막(Al-HF) 내부에 코팅하여 사용하였다. 1,2 HDO/water 투과증발 분리공정에서는 PVA/GA 비율, 경화 온도 및 투과증발 분리공정 운전 조건에 대한 막의 최적화를 연구하였다. 장기 안정성 시험에서 PVA/GA (몰 비율 = 0.08, 경화 온도 = 80℃) 로 코팅된 Al-HF 막이 공정온도 40℃에서 1.90~2.16 kg/m²h 범위의 투과도를 보였으며, 투과용액의 수분 함량은 99.5% (separation factor = 68) 이상이었다.