• Polymer(Korea)
• /
• v.39 no.1
• /
• pp.99-106
• /
• 2015

The surface of nano-kenaf containing cellulose fibers was treated with alkali (NaOH) and their effects on the physical properties of the polypropylene (PP) composite were investigated. The treatment of alkali on the fibers increased the melt flow index (M.I.), elongation%, and impact strength, while it decreased the tensile strength, flexural modulus and heat deflection temperature (HDT) of the compound compared to the untreated one. It seemed the alkali treatment on the nano-kenaf fiber changed the character of the fiber due to removal of impurities and chemicals on the surface and resulted in decreased interfacial adhesion between the nano-fiber surface and the PP matrix and changed the character of the PP.

• Fibers and Polymers
• /
• v.3 no.1
• /
• pp.38-42
• /
• 2002

Polypropylene filaments were spun from a mixture of PP chips of two different Melt Flow Index (MFI) (3 MFI and 35 MFI). A significant difference was observed in the melting characteristics of the resultant filaments from either of the individual components as observed from the DSC. The main difference being in the degree of melting achieved at any temperature in the initial stages of the melting range, which was found to be higher in case of the filaments spun from the b]end. These filaments were then thermally bonded using silicon oil bath and heated roller method. Subsequently the bond strength of the filaments was measured on the Instron Tensile Tester using the loop technique. The values of the world strengths obtained from the blend were compared with those made from the individual component. It was found that the bond strength of the bonds obtained from the blended filament at a given temperature was higher than that of the bonds made from the filaments of either of the individual components, which is also suggested by the DSC curves. The difference in the bond strength was found to be as high as 25% in case of the blend with 60:40 composition ratios of the 3 MFI and 35 MFI components respectively.

• Elastomers and Composites
• /
• v.46 no.2
• /
• pp.125-131
• /
• 2011

The effects of chopped kenaf fiber concentration on mechanical property of polypropylene (PP) composite are investigated. The addition of kenaf increased the tensile strength, flexural modulus, impact strength, specific gravity, and HDT, while decreased the elongation%, flexural strength, and melt flow index. The increase of mechanical properties is due to increased surface area contacting between fiber and polymer matrix and fiber-fiber interaction. Volatile extractives in the kenaf seemed to decrease the interfacial adhesion between kenaf surface and PP.

• Macromolecular Research
• /
• v.17 no.12
• /
• pp.1021-1024
• /
• 2009

We successfully prepared high-flow polycarbonate (PC) by blending commercial PC with a low molecular weight PC oligomer. The oligomer was synthesized by the addition of a large quantity of mono functional phenol groups, and the chain end group was reacted with p-tertiary butyl phenol (PTBP) to block the reactivity. The viscosity average molecular weight ($M_v$) for the oligomer was about 4,000-5,000 g/mol, compared to ~19,000 g/mol for the PC blend obtained by blending 10 wt% of the prepared oligomer with the commercial grade PC ($M_v$ of 21,000 g/mol). The blended PC had a melt flow index of 45, which is 2.5 times higher, and a processing temperature that was $20^{\circ}C$ lower, than that of commercial grade PC having a similar $M_v$.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.1 no.2
• /
• pp.1-14
• /
• 1991

In growing single crystals, which exhibit incongruent melting behavor, it is extremely difficult to maintain the stoichiometry of its chemical compositions for given crystals. For instance, $LiNbO_3$ is a typical one which exhibits such incongruent melt, especially with a large solid solution region that makes it difficult to maintain the chemical compositions. Such a variation can then cause a serious problem for the practical applications in designing a precision electro /optic device. Of the known methods of determining its composition and quality, an optical technique of measuring refractive index of the crystals has been implemented. This technique is also capable of determining optical uniformity of the grown crystals and the chemical compositions. The technique used for such characterizations is herein described and some of results are discussed.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1985.01a
• /
• pp.21-23
• /
• 1985

By adding La$_2$O$_3$ to optical multicomponent glass composition, after making mother glass and core fiber that enable to enlarge the infrared transmittance region, then surveyed the optical properties. Through thermal analysis of the glass abstained by melt-quenching after selecting stable basic composition on devitrification and replace SiO$_2$ by 4-12wt% La$_2$O$_3$. As La$_2$O$_3$ increases up to l2wt% transition temperature, refractive index, density, deformation temperature increased, whereas thermal expansion coefficient decreased. As a result of inspectig transmittance in UV/VIS/IR region, visable region indicated the decrease of transmittance by increasing the La$_2$O$_3$ and transmittance region was enlarged by increasing the La$_2$O$_3$ in IR region. Also, fabricate core fiber at 820$^{\circ}C$ and severy the optical loss we could fact that La$_2$O$_3$ composition added 12wt% showed the minimum optical loss.

• Polymer(Korea)
• /
• v.39 no.2
• /
• pp.200-209
• /
• 2015

In this study, the influence of dilauroyl peroxide on mechanical and thermal properties of different polypropylene (PP) matrices was investigated. Polypropylene matrices, different molecular weight isotactic PP containing 0.01, 0.02, 0.04, 0.06, 0.08, and 0.1 wt% of dilauroyl peroxide (DLP) were prepared by using a single-screw extruder. The effect of the visbreaking agent (DLP) on mechanical, physical, thermal and morphological properties of different molecular weight PP had been studied. Mechanical properties (tensile strength at break point, at yield and elongation at break point), melt flow index (MFI), scanning electron microscope (SEM) and differential scanning calorimetric (DSC) analyses of these matrices were examined. Melting ($T_m$) and crystallization ($T_c$) temperatures, crystallinity ratio (%) and enthalpies were determined. The microstructure of isotactic polypropylene matrix was investigated by scanning electron microscopy (SEM). From SEM analysis, it was observed that the surface disorder increased by the increasing amount of DLP. As a result of DSC analyses, the crystallinity ratio of the PP matrices has varied between 1.64-7.27%. Mechanical properties of the matrices have been improved. Particularly, the mechanical tests of PP have given interesting results when compounded with 0.06-0.08 wt% dilauroyl peroxide (DLP). Mechanical properties and thermal decomposition processes were all changed by increasing the amount of DLP in the matrix structure.

• Elastomers and Composites
• /
• v.38 no.2
• /
• pp.122-127
• /
• 2003

Compounding, using such thermoplastic elastomer as styrene-ethylene-butadiene-styrene (SEBS) blended with polypropylene(PP), oil, and other ingredients, was studied to develop a new material with excellent impact resistance and resilience for the replacement of environmentally toxic PVC sheet. Hardness decreased linearly with oil content in the SEBS/oil blend, and the tensile strength increased with PP content whereas elongation showed no effects over 50 phr of PP in SEBS/oil/PP blend. In the practical SEBS composition, proposed to replace the PVC sheet material, tensile and tear strength, as well as hardness, increased proportionally with PP content, while melt index decreased.

• Polymer(Korea)
• /
• v.37 no.5
• /
• pp.613-617
• /
• 2013

The effects of nano size kenaf cellulose fiber on mechanical property of polypropylene (PP) composite were investigated. The addition of nano-kenaf in place of natural kenaf showed higher tensile strength, flexural strength, impact strength, and heat deflection temperature compared to the natural kenaf filled PP composite, while it shows lower melt flow index, elongation%, and flexural modulus. These seemed to be due to the increased surface area of nano-kenaf fiber contacting PP matrix and reduced impurities such as volatile extractives on the fiber surface.

• Korean Journal of Optics and Photonics
• /
• v.3 no.3
• /
• pp.198-202
• /
• 1992

Silver ion-exchanged glass waveguide with its large surface index difference and shallow depth is suitable to be used for the hybrid integration of semiconductor device and glass waveguide using the semiconductor film grafting technique. We report characteristics of the planar and channel glass waveguides exchanged in the diluted silver nitrate melt in the visible and infrared spectral region. Especially, we determined the fabrication parameters for single-mode channel waveguide at 1.5.$\mu$m, an important wavelength in the optical communication. Directional couplers with several different configurations were fabricated, and their 3 dB coupling length was determined as a function of wavelenGh and polarization.