• Fire Science and Engineering
• /
• v.30 no.3
• /
• pp.7-15
• /
• 2016

The cross-sectional shape factor is used worldwide to evaluate the scientific performance of fire-resistant structures. In South Korea, however, a system for applying a cross-sectional shape factor has not been arranged and circular or rectangular steel pipes are commonly used for large-scale steel frame buildings. On the other hand, coating material-spray steel beams and pillars that have received the certification of a fire-resistant structure from recognized organizations are mostly limited to a H-beam. A H-beam is granted a wide range of certifications without size limitations from a non-loading performance test with test standards based on the relevant provisions. Other types of steel pipe are to be certified for fireresistance according to shape. In this study, a cross-sectional shape factor was used to propose standard testing specifications for the application of coating material-sprayed circular and rectangular steel pipes, eventually to set the scope of certification for reasonable fire-resistant structures.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.20 no.1
• /
• pp.31-34
• /
• 2007

In this study, in order to develop multilayer ceramics vibrator for ultrasonic nozzle, PMN-PNN-PZT ceramics were fabricated using $Li_{2}CO_{3}-Na_{2}_CO_{3}$ as sintering aids and their piezoelectric and dielectric characteristics were investigated according to the amount of PbO. With increasing PbO contents, secondary phases were increased and phase structure was changed from tetragonal structure to rhombohedral structure and also electromechanical coupling factor was linearly decreased. At the composition ceramics with the sintering temperature of $870^{\circ}C$ and 1 mol% excess PbO, density, electromechanical coupling factor, dielectric constant, piezoelectric d constant and mechanical quality factor showed the optimum value of $7.879\;g/cm^{3}$, 0.55, 1149, 328 pC/N, 1224, respectively for multilayer ceramics vibrator application for ultrasonic nozzle.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.8 no.2
• /
• pp.213-220
• /
• 2004

The purpose of this study is to evaluate the shear strength of SFRC beam that has no stirrups by steel fiber strengthening factor. To achieve the goal of this study, two stage investigation, which is material and member level, is studied with literature and experimental side. From the reviewing of previous researches and analyzing of material and member test results, strengthening parameter of SFRC is defined as steel fiber coefficient. Based on above results, steel fiber strengthening factor is proposed. And by reviewing the proposed equation of shear strength estimation, equation of Shin was well estimated the shear strength of SFRC beams. Therefore, shear strength equation of SFRC, which is composed by Shin's Eq. and steel fiber strengthening factor, is proposed by regression analysis of test results.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.07a
• /
• pp.959-962
• /
• 2001

In this study, the piezoelectric and dielectric properties and Temperature stability of resonant frequency with MnO$_2$doped 0.36Pb(Sc$_{1}$2/Nb$_{1}$2/)O$_3$- 0.25Pb(Ni$_{1}$3/Nb$_{2}$3/)O$_3$-0.39PbTiO$_3$(hereafter PSNNT) were investigated. The tetagonality of crystal structure was developed with increasing MnO$_2$additive content. With increasing MnO$_2$additive content, the electromechanical coupling factor and quality factor were increased. Electromechanical coupling k$_{p}$ and quality factor Q$_{m}$ at MnO$_2$doped with 2.0mol% were showed highest value of 55.6% and 252. In the case of specimen for MnO$_2$doped with 2mol%, temperature dependance of resonant frequency had a good properties.ies.

• Journal of the Korean Society for Precision Engineering
• /
• v.14 no.8
• /
• pp.137-145
• /
• 1997

A two-dimensional program for the analysis of bimaterial inclusion has been developed using the bound- ary element method. In order to study the effects of circular inclusion on the stress field of the crack tip, numerical analysis was performed for the straight crack of finite length around the symmetric circular inclusion whose modulus of elasticity was different from that of the matrix material. In the case of inclusion whose stiffness was smaller than that of the matrix material, the stress intensity factor was found to increase as the crack enamated. The stress intensity factor was uninfluenced from the radial change in inclusion and remained constant for the stiffness equivalent to the matrix materials, where as it decreased for the inclusion with larger stiffness. For the vareation in the distance of the inclusion, a small increase in the stress intensity factor was observed for the case with small or equal stiffness compared with the matrix materials. The inclusion with larger stiffness showed a gradual decrease in the strss intensity factor as the crack emanated.

• Tribology and Lubricants
• /
• v.10 no.4
• /
• pp.13-26
• /
• 1994

Effects of resin contents, number of carbonization, graphitization, sliding speed, and oxidation on friction and wear behavior of carbon/carbon composite materials were investigated. Friction and wear tests were carried out under various sliding conditions. An experimental setup was designed and built in the laboratory. Stainless steel disks were used as the counterface material. Friction coefficient, emperature, and wear factor were measured with a data acquisition system. Wear surfaces were observed by the scanning electron microscope. It has been shown that the average friction coefficient was increased with the sliding speed in the range of 1.43~6.10 m/s, but it as decreased in the range of 6.10~17.35 m/s. Specimens prepared by different numbers of carbonization. showed variations in friction coefficient and friction coefficient of the graphitized specimen was the highest. Friction coefficients depended on contribution of the plowing and adhesive components. As the number of carbonization was increased, wear factor was reduced. Wear factor of the graphitized specimens dropped further. In the case of graphitized specimens, sliding speed had a large influence on wear behavior. When the tribological experiments were conducted in nitrogen atmosphere, the wear factor was decreased to two thirds of the wear factor obtained in air. It is obvious that the difference was affected by oxidation. Results of friction and wear tests were applied to a neural network system based on the backpropagation algorithm. A neural network may be a valuable tool for prediction of tribological behavior of the carbon/carbon composite material if ample data are present.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.17 no.5
• /
• pp.481-485
• /
• 2004

0.91 (PSN-PZT) －0.05BF －0.04PNW＋0.3wt%MnO$_2$＋0.6wt%CuO＋xwt%CeO$_2$ ceramics were fabricated with the variations of CeO$_2$addition at the sintering temperature of 95$0^{\circ}C$ and their microstructure, dielectric and piezoelectric characteristics were investigated. As the amount of CeO$_2$ addition increased, the grain size, density and electromechanical coupling factor(k$_{p}$) were increased and the mechanical quality factor(Q$_{m}$ ) was decreased. At the 0.3 wt% CeO$_2$, the density, grain size, electromechanical coupling factor(k$_{p}$), and pizoelectric constants(d$_{33}$, g$_{33}$) showed the maximum value of 7.87 g/㎤, 3.22 $\mu\textrm{m}$, 0.5, 289 pC/N, and 22.2 ㎷ㆍm/N, respectively. However, mechanical quality factor(Q$_{m}$ ) showed the minimum value of 807 at the 0.5 wt% CeO$_2$.$.EX>.EX>.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.27 no.1
• /
• pp.27-32
• /
• 2014

In this paper, PZT piezoelectric ceramic specimens with 4 compositions (Zr/Ti=50/50, 53/47, 56/44, 58/42) in $Pb(Zr,Ti)O_3$ system were fabricated. We studied effects of poling strength and thermal aging on the temperature characteristics of eletromechanical coupling factor k31 of the specimens, which were poled with the DC electric fields, 1.5, 2.5 and 3.5 kV/mm respectively and thermally aged for an hour at $200^{\circ}C$. The eletromechanical coupling factor k31 of the specimen with the composition Zr/Ti= 53/47, nearest to the morphotropic phase boundary decreased the most greatly, irrelevant to the intensity of poling field, due to 1st thermal aging. And the temperature coefficient of eletromechanical coupling factor k31 was (-) in the tetragonal phase composition and (+) in the rhombohedral phase composition, which is reverse in the temperature coefficient of resonance frequency. It is interesting that eletromechanical coupling factor k31 of PZT ceramics is shown to be able to increase as temperature increase in the interval $-20{\sim}80^{\circ}C$.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.17 no.5
• /
• pp.492-496
• /
• 2004

In this study, (0.96 －x)(PSN-PZT)－xBF－0.04 PNW＋0.3wt%MnO$_2$＋0.6wt%CuO ceramics were fabricated with the variations of the amount of BiFeO$_3$substitution and sintering temperature for the development of modified ceramics which can be sintered in the low temperature($\leq$100$0^{\circ}C$ ), and their microstructural, dielectric and piezoelectric characteristics were investigated. As the amount of BiFeO$_3$ substitution was increased, the density, mechanical quality factor(Q$_{m}$) and electromechanical coupling factor(k$_{p}$) showed the maximum value at each of sintering temperature. At sintering temperature of 98$0^{\circ}C$ and BiFeO$_3$substitution of 2 mol%, the density, dielectric constant and electromechanical coupling factor(k$_{p}$) showed the maximum value of 7.84 g/㎤, 1415 and 0.49, respectively. And at sintering temperature of 95$0^{\circ}C$ and BiFeO$_3$substitution of 3mol%, mechanical quality factor showed the maximum value of 1062. 1062.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2003.11a
• /
• pp.300-303
• /
• 2003

[ $0.91(PSN-PZT)-0.05BF-0.04PNW+0.3wt%MnO_2+0.6wt%CuO+xwt%CeO_2$ ] ceramics were fabricated with the variations of $CeO_2$ addition at the sintering temperature of $950^{\circ}C$ and their microstructure and dielectric and piezoelectric characteristics were investigated. As the amount of $CeO_2$ addition increased, the grain size, density and electromechanical coupling factor(kp) were increased and the mechanical quality factor(Qm) was decreased. At the $0.3wt%CeO_2$, density, grain size and electromechanical factor(kp) showed the maximum value of $7.87g/cm^3$, $3.22{\mu}m$ and 0.5, respectively. However, mechanical quality factor(Qm) showed the minimum value of 807 at the $0.5wt%CeO_2$.