• 대한치과의사협회지
• /
• 제15권11호
• /
• pp.757-761
• /
• 1977

The purpose of this study was to evaluate the marginal sealing ability of Hipol composite resin. Using freshly extracted human teeth and 2% acquous methylene blue, the marginal leakage of dye in restorative materials such as Hi-pol, Adaptic, Nuvasystem, Epolite and Amalgam was investigated at 37℃ and under temperature cycling between 4℃ and 60℃. The results were as follows; 1. All the filling materials revealed the penetration of dye between cavity walls and restorations. 2. Hi-pol and Adaptic showed more marginal leakage than other materials and the degree of dye penetration in Hi-pol was similar to that of Adaptic. 3. Nuva system showed the least marginal leakage at 37℃ and under temperature cycling between 4℃ and 60℃. 4. Under temperature cycling, all materials showed a slight increase in marginal leakage except Epolite, which showed the greastest change in leakage.

• 대한치과의사협회지
• /
• 제23권12호통권199호
• /
• pp.1031-1037
• /
• 1985

The purpose of this study was to evaluate the marginal sealing ability of 'vivadent.' Using freshly extracted human teeth and 2% aqueous methylene blue, the marginal leakage of dye in restorative materials such as vivadent with acid etching technique, Durafill with acid etching technique, silar with acid etching technique, Adaptic, and Amalgam were investigated at 37℃ and under temperature cycling in range of 4℃-60℃. The results were as follows; 1. All filling materials showed some degree of marginal penetration by 2% methylene blue dye. 2. Vivadent with acid etching technique revealed effective marginal sealing ability, but under temperature cycling it showed increased marginal leakage. 3. All resins showed greater marginal leakage than amalgam restoration. 4. Vivadent had the most effective marginal sealing ability in experimented resins.

• Restorative Dentistry and Endodontics
• /
• 제8권1호
• /
• pp.167-172
• /
• 1982

The purpose of this study was to evaluate the marginal sealing ability of "Silar". Using freshly extracted human teeth and 2% acquous methylene blue, the marginal leakage of dye in restorative materials such as Silar, Silar with acid etching technique, Hi-Pol, Hi-Pol Enamel Bond system, Adaptic and Amalgam were investigated at $37^{\circ}C$ and under temperature cycling in range of $4^{\circ}C-60^{\circ}C$. The results as follows; 1. All filling materials showed some degree of marginal penetration by 2% methylene blue dye. 2. Silar with acid etching technique revealed effective marginal sealing ability, but under temperature cycling it showed increased marginal leakage. 3. All composite resins showed greater marginal leakage than amalgam restoration. 4. Silar had the most effective marginal sealing ability in experimented composite resins.

• Restorative Dentistry and Endodontics
• /
• 제18권1호
• /
• pp.55-72
• /
• 1993

The aim of this study was to compare the marginal leakage of class II light curing composite resin restoration according to filling methods. With using acid etching technique and dentin bonding agent, various methods were suggested to eliminate or reduce the marginal leakage. In this study, class II cavities were prepared in 100 extracted human premolars with cementum margin(1mm below the CEJ) and the teeth were randomly assigned to 5 groups of 20 teeth each. The teeth in group 1, 2, 3 and 4 were restored by direct filling methods using P-50 and Clearfil Photoposterior of 10 teeth each, but the method of insertion of the restorative materials varied with each group. And the teeth in group 5 were restored by inlay method using Kulzer Inlay and CR Inlay. Filling methods are as follows : Group 1 : The composite resin was inserted in one layer in the proximal box and one layer in the occlusal portion. Group 2 : Insertion was in two equally thick horizontal layers in the proximal box. Group 3 : Insertion was in two diagonally placed layers in the proximal box. Group 4 : The composite resin was inserted in the same way as in group 3 except that a glass ionomer liner was first placed on the axial wall and gingival floor. Group 5 : The teeth were restored by Inlay technique using dure cure resin cement. All the teeth were thermocycled, stained with 1 % methylene blue solution, sectioned mesiodistally, and scored for marginal leakage. To compare the marginal leakage, ANOVA and T-test were used in analysis. The following results were obtained : 1. In direct filling methods, there was no significant difference in marginal leakage at both occlusal and cervical margins. 2. In all groups, occlusal margin showed significantly less leakage than cervical margin. 3. In group using glass ionomer liner, there was no significant reduction of marginal leakage at the cervical margin. 4. The group restored by inlay method showed significantly less marginal leakage than groups restored by direct filling methods at both occlusal and gingival margins. 5. There was no significant difference in each group according to filling materials.

• Restorative Dentistry and Endodontics
• /
• 제23권1호
• /
• pp.296-303
• /
• 1998

The purpose of this study was to assess the effects of cavity designs on the marginal leakage of class 5 glass ionomer restorations. The five cavity designs were as follows ; notch shape(A group), notch shape with groove(B group), combined lesion(C group), combined lesion with groove and deep chamfer margin(D group) and combined lesion with groove and shoulder(E group), and each design had 10 cavities. After the cavities were restored with GIC, they were immersed in 0.5% basic fuchsin solution for 6 hours. The specimens were washed thoroughly and sectioned longitudinally in a buccolingual direction through the center of the restorations. The degree of marginal leakage was measured as the extent of dye penetration under the stereoscope. The results of this study were as follows 1. The enamel margins of all groups showed lesser leakage than dentin/cementum margins(p<0.05). 2. The combined lesion(C group) showed more leakage than notch shape(A group), but there was no siginificant difference(p>0.05). 3. In the notch shape, there was no influence on the marginal leakage by the groove preparation. 4. In the combined lesion, marginal leakage was decreased by the groove preparation and marginal modification.

• 대한치과의사협회지
• /
• 제22권4호통권179호
• /
• pp.313-322
• /
• 1984

This study was designed to observe the marginal leakage of three permanent cements affected by three temporary cements. The temporary cements used in this study were Zinc oxide-eugenol, Non-eugenol, and Calcium hydroxide cements and the permanent cements were Zinc phosphate, Polycarboxylate and Alumina reinforced EBA cements. To measure the dye penetration into permanently cemented zone, the experimental specimens were treated with the temporary cements for a week. An analysis of the data obtained from 120 specimens resulted in the following conclusions: 1. Regardless of the types of the permanent cements used, using Calcium hydroxide cement as temporary cement showed higher marginal leakage than other temporary cements. 2. Using Polycarboxylate cement as permanent cement showed less marginal leakage than other permanent cements. 3. The marginal leakage in zinc phosphate cement was similar to Alumina reinforced EBA cement regardless of the types of the temporary cements.

• Restorative Dentistry and Endodontics
• /
• 제13권1호
• /
• pp.69-78
• /
• 1988

The study was designed to establish a more nearly quantitative method for assessing the marginal leakage of dental restorations. 27 Class V cavities with $45^{\circ}$ bevel joint were prepared and classified into 2 groups. One group was filled with Scotchbond and silux. The other group was filled with glass ionomer cement, Scotchbond and silux. After finishing, all specimens were subjected manually to 100 thermal cycles at $0^{\circ}C$ and $100^{\circ}C$ water-bath. They were soaked in a samarium nitrate solution for 3 hours, irradiated with flux of $6{\times}10^{12}$ neutrons/$cm^2$/sec for 11 hours, cooled for 200 hours, counted with the HPGE detector and the tracer uptake was determined by comparison with a standard of samarium (10 ${\mu}g$). The following results were obtained. 1. Both of the two groups showed a considerable amounts of marginal leakage. 2. The group filled without glass ionomer cement base showed more marginal leakage than the group filled with glass ionomer cement base. 3. Neutron Activation Analysis produced a good quantitative method to measure the marginal leakage and samarium was appropriate to measure the marginal leakage of resin restorations using neutron activation analysis.

• Restorative Dentistry and Endodontics
• /
• 제7권1호
• /
• pp.131-138
• /
• 1981

The purpose of this study was to evaluate the marginal leakage of composite resin. Preparing 144 class V cavities on freshly extracted noncarious teeth, composite resins were prepared and inserted by one dentist according to the manufacturer's instructions. The experiments were performed in two different groups; In group I; Class V cavities with $90^{\circ}$ cavosurface angle, In group II; Class V cavities with $135^{\circ}$ cavosurface angle. And each group was divided 2 subgroups; In control group; composite resin restoraions without acid etch technique. In experimental group; composite resin restorations with acid etch technique. All specimens were immersed in 0.05% crystal violet solution. Before examination, the restored teeth were subjected to thermal stress. The specimens were sectioned occlusogingivally through the center of the restorations with a diamond disk. The sections were examined under a reflected light microscope at 1 day, 7 days and 30 days after immersing the specimens in dye solution. The results were as follows; 1. Control group of group I and group II showed marginal leakage. 2. The degree of marginal leakage in experimental group was greater reduced than control group. 3. In control group, the degree of marginal leakage in group I was greater than group II. 4. In experimental group, there is not statistical differences of the degree of marginal leakage between group I & group II.

• Restorative Dentistry and Endodontics
• /
• 제26권2호
• /
• pp.162-170
• /
• 2001

The purpose of this study was to investigate the effect of cavity configurations on the marginal leakage of class 5 glass ionomer cement and composite resin restorations. Four types of cavities such as saucer shape. notch shape. combined shape(notch shape occlusally and saucer shape gingivally). and U shape were prepared on the buccal and lingual surfaces of 80 extracted premolars(40 cavities for each shape). Occlusal cavity margins were placed at enamel and cervical margins were placed at dentin. 10 cavities of each shape were restored with Ketac Fil as a conventional glass ionomer cement. Fuji II LC improved as a resin modified glass ionomer cement, Z 100 as a hybrid composite resin. and Tetric Flow as a flowable composite resin (40 cavities for each material). After thermocycling, teeth were immersed in 5% basic fuchsin solution for 6 hours and sectioned longitudinally in a buccolingual direction through the center of the restoration. The dye penetrations at the tooth restoration interface were examined by stereomicroscope. The Result were as follows 1. In saucer shape, notch shape and combined shape, composite resin restorations showed lesser leakage than glass ionomer restorations(p<0.05) and in U shape. Tetric Flow showed the least marginal leakage and others were decreased as Z 100. Fuji II LC improved, Ketac Fil in that order. There were statistically significant difference between Tetric Flow and Fuji II LC improved. Ketac Fil and between Z 100 and Ketac Fil(p<0.05). 2. In Ketac Fil restoration group, saucer shape showed the highest marginal leakage and U shape showed the least marginal leakage and others were decreased as notch shape, combined shape in that order. There were statistically significant difference between saucer shape and combined shape, U shape and between notch shape and U shape(p<0.05). 3. In Fuji II LC improved restoration group, U shape showed the least marginal leakage. There were statistically significant difference between U shape and other three shapes(p<0.05). 4. The cavity configuration had no significant effect on marginal leakage of composite resin restorations(p>0.05).

• Restorative Dentistry and Endodontics
• /
• 제9권1호
• /
• pp.69-79
• /
• 1983

This study was undertaken to evaluate the effects of varnish application and thermocycling on the marginal leakage. 240 cavities of Class V were prepared on the 120 extracted premolars, and the cavities were filled with amalgam, Heliosit$^{(R)}$, and Hipol$^{(R)}$ after application of Copalite$^{(R)}$ or Duraphat$^{(R)}$. All specimens were immersed in methylene blue solution for 24 hours after thermocycling at $4^{\circ}C$ and $60^{\circ}C$, embedded in acrylic resin, and sectioned with low speed saw into two parts. The sectioned specimens observed with the metallurgical microscope. The following results were obtained: 1. The marginal seal was more effective in the amalgam-filled cavities after application of Copalite$^{(R)}$ threetimes or an application of Duraphat$^{(R)}$ varnish than in those without varnish applications. 2. Of the composite resin-filled cavities, the leakage of the varnish applied cases showed much more than without application. 3. There was no significant difference in the effect of marginal sealing between Copalite$^{(R)}$ and Duraphat$^{(R)}$ applications. 4. There was a significant difference in the degree of the marginal leakage of amalgam-filled cavities between the groups of thermocycling times, but no significant difference in the resin-filled cavities. 5. There was no significant difference in the degree of the marginal leakage between the Heliosit$^{(R)}$ and the Hipol$^{(R)}$ resin-filled cavities.