• 한국분말재료학회지
• /
• 제10권2호
• /
• pp.83-88
• /
• 2003

Nanocrystalline materials of Ni and Ni-Cu alloy have been synthesized by the pulsed wire evaporation (PWE) method and these abnormal magnetic properties in the magnetic ordered state have been characterized using both VSM and SQUID in the range of high and low magnetic fields. Ni and Ni-Cu particles with an average size of 20 to 80 nm were found to influence magnetic hysterisis behavior and the results of powder neutron diffraction patterns and saturation magnetization curves are shown to indicate the absence of the NiO phase. The shifted hysterisis loop and irreversibility of the magnetization curve in the high field region were observed in the magnetic-ordered state of both Ni and Ni-Cu. The virgin magnetization curve for Ni slightly spillover on the limited hysterisis loop ($\pm$20kOe). This irreversibility in the high field of 50 kOe can be explained by non-col-linear behavior and the existence of the metastable states of the magnetization at the surface layer (or core) of the particle in the applied magnetic field. Immiscible alloy of Cu-Ni was also found to show irreversibility having two different magnetic phases.

• 한국자기학회지
• /
• 제14권5호
• /
• pp.186-191
• /
• 2004

250～850 $\mu\textrm{m}$ 크기의 FeCuNbSiB 나노결정립 합금분말에 3wt%의 전기절연체(glass frits, 활석 또는 폴리아미드 분말)를 혼합한 뒤 압축성형하여 분말코아를 만들었을 때, 절연물질의 종류에 따른 자기적 특성의 변화를 조사하고 그 결과를 비교하였다. 세라믹 물질인 glass frits와 활석은 폴리아미드에 비해 수백 kHz이하의 주파수 범위에서 높은 투자율을 나타내나 1 MHz 이상의 주파수에서는 투자율이 빠르게 낮아지는 거동을 보였다 자심손실은 glass frits와 활석을 첨가한 자심 쪽이 더 크며, 품질계수는 폴리아미드를 첨가한 자심보다 더 낮은 주파수에서 피크를 나타내고 그 값도 더 작았다. 반면 폴리아미드로 절연처리한 자심의 경우 수 MHz에 이르기까지 투자율의 저하가 거의 나타나지 않았으며, 더 우수한 자심손실 및 품질계수 특성을 보여 주었다. 그리고 직류중첩특성 또한 폴리아미드를 첨가한 자심이 100 Oe이상의 큰 자장에 이르기까지 더 우수하였다. 폴리아미드를 절연체로 사용한 경우 그 밀도가 낮음으로 인해 결국 더 많은 체적비로 혼합되므로 자성 입자 사이의 전기적 절연을 보다 더 충분히 해주고 있는 것으로 판단되었으며, 세라믹 물질을 절연체로 사용했을 때와의 이상과 같은 자기적 특성의 차이는 이 사실에 주로 의존하고 있는 것으로 평가되었다.

• 마이크로전자및패키징학회지
• /
• 제23권2호
• /
• pp.11-18
• /
• 2016

This study focused on examining the possibility for recycling of Fe-Si electric sheet. We manufactured Fe-6.5Si mother alloy using by Fe-Si electric sheet scrap for transformer core materials. And then, soft magnetic alloy powder which diameter and shape were $45{\sim}150{\mu}m$ and sphere type was prepared by gas atomization process. As we compared to commercial Fe-6.5Si powder, its diameter distribution and microstructure of recycled powder was a similar. To investigate the possibility of reusing the soft magnetic composite sheet for electronics, recycled powder was treated to have a high aspect ratio (AR), and we finally obtained the 65~66 AR and $2.3{\mu}m$ thickness powder. To release the residual stress of powder, heat treatment was conducted under $300{\sim}400^{\circ}C$, $N_2$ gas. And then, soft magnetic sheet was made by tape casting process using by those powders. After the density and permeability of tape was measured, and we confirmed that the recycled Fe-Si electric sheet scrap was possible to reuse the soft magnetic materials of electronics.

• Journal of Magnetics
• /
• 제21권2호
• /
• pp.192-196
• /
• 2016

The Fe-Si-B-Nb-Cu alloys containing Ca and Al were rapidly solidified to thin ribbons by melt-spinning. The ribbons were ball-milled to make powders, and then mixed with 1 wt.% water glass and 1.5 wt.% lubricant. The mixed powders were burn-off, and then compacted to form toroidal-shaped cores, which were heat treated to crystallize the nano-grain structure and to remove residual stress of material. The characteristics of the powder cores were analyzed using a differential scanning calorimetry (DSC) and a B-H meter. The microstructures were observed using transmission electron microscope (TEM). The optimized soft magnetic properties (${\mu}_i$ and $P_{cv}$) of the powder cores were obtained from the Ca and Al containing alloys after annealing at $530^{\circ}C$ for 1 h. The core loss of Fe-Si-B-Nb-Cu-based powder cores was reduced by the addition of Ca element, and the initial permeability increased due to the addition of Al element.

• 한국전자통신학회논문지
• /
• 제16권3호
• /
• pp.471-476
• /
• 2021

분말 야금 기술에 의한 복합 연자성 재료는 전기기기에 일반적으로 사용되는 종래의 전기강판보다 많은 장점을 가지고 있으며, 그 관련 기술은 최근에 상당한 발전을 거듭하고 있다. 복합 연자성 재료는 일반적으로 분말의 형태로 인해 자기적 등방성 가지므로 3차원 자속 및 복잡한 구조의 전기기기 구성에 적합하다. 하지만 SMC와 같이 등방성 자기 특성을 가지는 재료는 복잡한 벡터 히스테리시스를 가지므로 정확한 손실 특성을 예측하는 것이 매우 어렵다. 따라서 본 논문에서는 전기강판 및 SMC의 링 타입 시편을 제작하고 시편 크기에 따라 자기적 특성을 측정한 후, 측정된 자기적 정보를 이용하여 800Hz 이상에서 구동하는 고속 영구자석 전동기의 전자계 해석을 수행하였다. 또한, 해당 모델의 시작품을 제작하고 효율 측정 및 비교를 통해 본 논문의 신뢰성을 입증하였다.

• 한국분말재료학회지
• /
• 제11권1호
• /
• pp.16-21
• /
• 2004

The nano-sized Co particles were successfully synthesized by chemical vapor condensation (CVC) process using the precursor of cobalt carbonyl ($Co_2(CO)_8$). The influence of carrier gases on the microstructure and magnetic properties of nanoparticles was investigated by means of XRD, TEM, XPS and VSM. The Co nano-particles with different phases and shapes were synthesized with a change of carrier gas : long string morphologies with coexistence of fcc and hcp structure in Ar carrier gas condition; finer Co core in a mass of cobalt oxide with only fcc structure in He; rod type cobalt oxide phase in Ar＋6vol％$O_2$. The saturation magnetization and coercivity was lower in Co nanoparticles synthesized in He carrier gas, due to their finer size.

• 한국자기학회지
• /
• 제25권3호
• /
• pp.67-73
• /
• 2015

본 연구는 철기(Fe based) $Fe_{73.5}Si_{13.5}B_9Nb_3Cu_1$ 나노결정 합금의 분말코어(powder core)의 연자기적 특성 향상을 위한 기초연구로서, 절연 코팅제의 첨가량 및 분말입도에 따른 투자율, 코어손실 및 DC 바이어스 특성을 주로 조사하였다. 우선 합금조성을 PFC 장치를 이용하여 비정질 합금리본을 제조한 후, 열처리, 미분쇄 및 분급하여 얻어진 합금분말에 절연 코팅제(PEI)의 첨가량을 0.5, 1.0, 2.0, 2.5 wt%로 변화시켜 $16ton/cm^2$으로 압축성형 및 결정화 열처리하여 제조한 토로이달 나노결정 분말코어($OD12.7mm{\times}ID7.62mm{\times}H4.75mm$)는 절연 코팅제 함량이 증가할수록 투자율은 감소하였지만, 코어손실 및 DC 바이어스 특성은 향상됨을 확인하였다. 이러한 이유는 합금분말 절연 코팅제 첨가량이 증가할수록 비정질 합금분말 입자가 적어져 분말코어의 성형밀도가 낮아지기 때문으로 추정되었으며, 절연 코팅제의 함량은 1 wt%가 가장 적합한 것으로 판단되었다. 또한 절연 코팅제 함량을 1 wt%로 고정하고, 합금분말의 입도에 따라 제조한 분말코어의 경우, 실효투자율 및 코어손실은 입도가 클수록 우수하였지만, DC 바이어스 특성은 인가자장이 증가함에 따라 더욱 나빠짐을 확인하였다. 그 이유는 합금분말 표면의 코팅층 두께 차이에 의한 절연효과, 잔류기공 혹은 분말코어의 성형밀도 차이 등에 기인하는 것으로 추정되었다.

• 한국자기학회:학술대회 개요집
• /
• 한국자기학회 2006년도 동계학술연구발표회 및 자성 스핀트로닉스 국제학술대회
• /
• pp.24-25
• /
• 2006

• 한국자기학회:학술대회 개요집
• /
• 한국자기학회 2012년도 자성 및 자성재료 국제학술대회
• /
• pp.61-62
• /
• 2012

• 한국자기학회:학술대회 개요집
• /
• 한국자기학회 2013년도 자성 및 자성재료 국제학술대회
• /
• pp.57-58
• /
• 2013