• Journal of Magnetics
• /
• v.19 no.3
• /
• pp.232-236
• /
• 2014

Anisotropy coupling in thin films with mixed induced and shape anisotropies is investigated. A 200-nm-thick Co-Fe-Pd-B thin film with a large induced anisotropy of 57 Oe is fabricated and then patterned into micron-sized cells to provide shape anisotropy, whose strength has a similar magnitude to that of the induced anisotropy for enhancing the anisotropy coupling. The angles between the two mixed anisotropies considered are $0^{\circ}$, $90^{\circ}$, and $110^{\circ}$. Hysteresis loops measured under in-plane magnetic fields along various directions indicate no anisotropy coupling behaviour for all the three angles examined in this study.

• Proceedings of the KIEE Conference
• /
• 2008.07a
• /
• pp.723-724
• /
• 2008

The rotational loss is one of the most important problems for the practical applications of PM synchronous motor/generator. This rotational loss is divided as the mechanical loss by windage and bearing and iron loss by hysteresis loop and eddy current in the part of the magnetic field. So, In this paper, a double-sided PMSM/G without the iron loss is designed by analytical method of the magnetic field and estimation of the back-EMF constant represented as the design parameter. This design model consists of the double-sided PM rotor with Halbach magnetized array and coreless 3-phase winding stator. The results show that the double-sided PMSM/G without iron loss can be applicable to the required system without the rotational loss.

• The Transactions of the Korean Institute of Electrical Engineers A
• /
• v.52 no.3
• /
• pp.173-178
• /
• 2003

This paper proposes a three-winding transformer protective relaying algorithm based on the ratio of the induced voltages (RIV). The RIV of the two windings is the same as the turn ratio for all operating conditions except an internal fault. For a single phase and a three-phase transformer containing the wye-connected windings, the induced voltages of the windings are estimated. For a three-phase transformer containing the delta-connected windings, the induced voltage differences are estimated using the line currents, because the winding currents are practically unavailable. The algorithm can identify the faulted phase and winding if a fault occurs on one phase of a winding. The test results clearly show that the algorithm successfully discriminates internal winding faults from magnetic inrush. The algorithm not only does not require hysteresis data but also can reduce the operating time of a relay.

• Journal of Magnetics
• /
• v.18 no.3
• /
• pp.225-229
• /
• 2013

We report a measurement for the anomalous Nernst effects induced by a temperature gradient in [CoSiB/Pt] multilayer films with perpendicular magnetic anisotropy. The Nernst voltage shows a characteristic hysteresis which reflects the magnetization of the film as in the case of the anomalous Hall effects. With a local heating geometry, we also measure the dependence of the anomalous Nernst voltage on the distance d from the heating element. It is roughly proportional to $1/d^{1.3}$, which can be conjectured from the expected temperature gradient along the sample from the heat equation.

• Journal of the Korean Magnetics Society
• /
• v.15 no.2
• /
• pp.109-112
• /
• 2005

Electronic and magnetic properties of $Ti_{1-x}M_xO_{2-\delta}$ (M=Co and Fe) thin films grown by sol-gel method have been investigated. Anatase and rutile $Ti_{1-x}Co_xO_{2-\delta}$ films were successfully grown on $Al_2O_3$ (0001) substrates and exhibited p-type electrical conductivity while the undoped films n-type conductivity. Room temperature vibrating sample magnetometry measurements on the anatase and rutile $Ti_{1-x}Co_xO_{2-\delta}$ films with same x ($=4.8 at.{\%}$) showed quite similar magnetic hysteresis curves with the saturation magnetic moment of $\~4 {\mu}_B$ per Co ion despite their differences in structural and electronic properties. Such giant magnetic moment is attributable to the unquenched orbital moment of the $Co^{2+}$ ions substituting the octahedral $Ti^{4+}$ sites. Similar ferromagnetic behavior was observed for $Ti_{1-x}Fe_xO_{2-\delta}$ films that are highly resistive compared to the Co doped samples. Saturation magnetic moment was found to decrease for higher x, i.e., $\~2$ and $\~1.5 {\mu}_B$ per Fe ion for x=2.4 and 5.8 at. $\%$, respectively. Conversion electron $M\ddot{o}ssbauer$ spectroscopy measurements predicted the coexistence of $Fe^{2+}$ and $Fe^{3+}$ ions at the octahedral sites of $Ti_{1-x}Fe_xO_{2-\delta}$.

• Journal of the Korean Magnetics Society
• /
• v.10 no.2
• /
• pp.49-52
• /
• 2000

The changes of magnetic properties in neutron irradiated F $e_{81}$ $B_{13.5}$S $i_{3.5}$ $C_2$ amorphous ribbon were studied by X-ray diffraction, hysteresis loop, temperature dependence of magnetization and complex permeability. The fluences of thermal ( $n_{th}$) and fast ( $n_{f}$) neutron were 6.95$\times$10$^{18}$ $n_{th}$ c $m^{-2}$ and 4.56$\times$10$^{16}$ $n_{f}$c $m^{-2}$ , respectively. The changes of XRD Profiles were not observable at the neutron irradiated sample. The complex permeability spectra showed that the permeability from domain wall motion decreased due to the increase of pinning force against domain motion by the neutron irradiation, and the relaxation frequency of rotational magnetization moved to higher frequency region. The measurement of hysteresis loop showed the increase of magnetic softness, related to rotational magnetization, but saturation magnetization was decreased in neutron irradiation sample. The Curie temperature was decreased in the neutron irradiated sample.e.e.e.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.27 no.7
• /
• pp.462-467
• /
• 2014

In this paper, we studied the magnetic composite sheets for electromagnetic wave noise absorber of quasi-microwave band by using soft magnetic FeSiCr and Fe50Ni flakes with the thickness of about $1{\mu}m$ and polymer. The magnetic hysteresis curve including saturation magnetization and residual magnetization and the complex permeability characteristics of the composite sheets were investigated to clarify the mixing effect on electromagnetic wave absorption properties. The saturation magnetization was decreased about 10% while the residual magnetization was increased about 15% and the real parts of complex permeability at below 500 MHz were increased 0.6~4 while those values at above 500 MHz were decreased 0.4~2.5 according to the change of contents of FeSiCr and Fe50Ni powders. As a result, the reflection loss can be moved to the lower frequency from 2~3 GHz to 1~1.5 GHz as the contents of Fe50Ni flaky powder into FeSiCr flaky powder was increased up to 50%.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.28 no.2
• /
• pp.205-210
• /
• 2008

Magnetic hysteresis loops of a nickel strip and a Fe-Co alloy strip, which have been used in magnetostrictive strip type guided wave transducers for long range ultrasonic testing of pipelines, were measured and then magnetic property effects of a strip on transducer sensitivity were analyzed. The sensitivity of an optimized Fe-Co strip transducer was superior to that of the nickel strip transducer by a factor of about 30. It was shown that this was mainly attributed to the differences in remanence magnetization and coercivity of the two magnetostrictive materials.

• Journal of Magnetics
• /
• v.19 no.3
• /
• pp.227-231
• /
• 2014

We fabricated textured polycrystalline $CoFe_2O_4$ thin films on $Pt(111)/TiO_2/SiO_2/Si$ substrate through a sol-gel method. We varied the thickness of the films, by using precursor solutions with different concentrations of 0.1, 0.2, and 0.3 M, and by depositing 5, 8, or 10 layers on the substrate by spin-coating. X-ray diffraction spectra indicated that when the precursor concentration of the solution was higher than 0.1 M, the spin-coated films were preferentially oriented in the <111> direction. Inspection of the surface morphology by scanning electron microscopy revealed that $CoFe_2O_4$ thin films prepared with 0.2 M solution and 5-time spin-coatings had smoother surface, as compared to the other conditions. Each coating had an average thickness of about 50 nm. The magnetic properties measured by vibrating sample magnetometer showed magnetic anisotropy, as evidenced from the difference in the in-plane and out-of-plane hysteresis loops, which we attributed to the textured orientation of the $CoFe_2O_4$ thin films.

• Journal of Magnetics
• /
• v.16 no.4
• /
• pp.435-439
• /
• 2011

In this work, we prepared Fe-Ni alloy nanopowders by wire electrical explosion in deionized water and ethanol. Particles size and morphology of the as-synthesized nanoparticles prepared in water and ethanol were observed by transmission electron microscopy. In both cases, the as-synthesized nanoparticles were in nearly spherical shape and their size distribution was broad. The particles prepared in the water were in core-shell structure due to the oxidation of Fe element. X-ray diffraction was used to analyze the phase of the nanopowders. It showed that the nanopowders prepared in water had ${\gamma}$-Fe-Ni solid solution and FeO phase. The samples obtained in ethanol were in two phases of Fe-Ni solid solution, ${\gamma}$-Fe-Ni and ${\alpha}$-Fe-Ni. Bulk samples were made from the as-synthesized nanopowders by spark plasma sintering at $1000^{\circ}C$ for 10 min. Structure of the bulk sample was observed by scanning electron microscope. Magnetic properties of the as-synthesized nanopowders and the bulk samples were investigated by vibrating sample magnetometer. The hysteresis loop of the assynthesized nanopowders and the sintered bulk samples revealed a ferromagnetic characteristic.